CN106675408A - Environment-friendly coating used for being sprayed on surface layer of board of furniture - Google Patents
Environment-friendly coating used for being sprayed on surface layer of board of furniture Download PDFInfo
- Publication number
- CN106675408A CN106675408A CN201611095008.6A CN201611095008A CN106675408A CN 106675408 A CN106675408 A CN 106675408A CN 201611095008 A CN201611095008 A CN 201611095008A CN 106675408 A CN106675408 A CN 106675408A
- Authority
- CN
- China
- Prior art keywords
- parts
- flos
- environmental protection
- coating material
- folium camelliae
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An environment-friendly coating used for sprayed on a surface layer of a board of furniture is prepared from the following ingredients in parts by weight: 20-35 parts of natural plant oleoresin, 15-25 parts of plant oily color paste, 15-25 parts of rosin, 5-15 parts of epoxidized soybean oil, 5-15 parts of gypsum powder, 5-10 parts of olibanum, 10-15 parts of arabian jasmine flowers, 5-8 parts of tea, 5-8 parts of chrysanthemums, 2-3 parts of omanthus fragrans, 3-5 parts of a dispersing aid, 3-5 parts of an antifoaming agent and 3-5 parts of a diluent. According to the environment-friendly coating provided by the invention, the release of harmful gases inside a board of furniture in the prior art can be effectively improved, so that the harm of harmful gases to human bodies is reduced; in addition, after the coating is sprayed on the surface of the furniture, the coating gives out slight and special fragrance and is environment-friendly; according to a preparation method provided by the invention, the whole preparation process is environment-friendly and pollution-free.
Description
Technical field：
The present invention relates to sheet fabrication production technical field, and in particular to a kind of environmental protection for the spraying of furniture board top layer
Coating.
Background technology：
In the middle of the building materials of house fitting-up at present, many timber, all containing harmful gass such as substantial amounts of formaldehyde, are made when processing
After furniture, during life-time service, it is easy to which human body is worked the mischief, prior art is often the furniture board made by
Top layer painted, moistureproof and waterproof can only be played a part of, improvement can not be made to the harmful gass of plank itself.
The content of the invention：
Defect of the present invention based on prior art, there is provided a kind of environmental protection coating material for the spraying of furniture board top layer, the painting
Material can be effectively improved the release of the furniture board inside harmful gass of prior art, reduce harm of the harmful gass to human body,
And the coating is sprayed on furniture surface and can also distribute a kind of light special fragrance, environmental protection.
The technical problem to be solved is realized using following technical scheme：
A kind of environmental protection coating material for the spraying of furniture board top layer, it is characterised in that make including following composition by weight：My god
Right plant oleoresin 20-35 parts, plant oil pastes 15-25 parts, Colophonium 15-25 parts, epoxy soybean oil 5-15 parts, Gypsum Fibrosum powder
5-15 parts, Olibanum 5-10 parts, Flos Jasmini Sambac 10-15 parts, Folium Camelliae sinensis 5-8 parts, Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersing aid 3-5 parts,
Defoamer 3-5 parts, diluent 3-5 parts.
Further, the environmental protection coating material is made including following composition by weight：Plant oleoresin 25-30 parts, vegetable oil
Property mill base 18-20 parts, Colophonium 18-20 parts, epoxy soybean oil 8-10 parts, Gypsum Fibrosum powder 10-13 parts, Olibanum 6-8 parts, Flos Jasmini Sambac 10-
15 parts, Folium Camelliae sinensis 5-8 parts, Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersing aid 3-5 parts, defoamer 3-5 parts, diluent 3-5 parts.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Beneficial effect of the present invention is：Provided by the present invention for the environmental protection coating material of furniture board top layer spraying, the coating
The release of the furniture board inside harmful gass of prior art can be effectively improved, harm of the harmful gass to human body is reduced, and
And the coating is sprayed on furniture surface and can also distribute a kind of light special fragrance, environmental protection；There is provided according to the present invention
Preparation method, its whole preparation process is green, environment friendly and pollution-free.
Specific embodiment：
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment one
A kind of environmental protection coating material for the spraying of furniture board top layer, including following composition by weight makes：Natural plants oiliness
Resin 20-35 parts, plant oil pastes 15-25 parts, Colophonium 15-25 parts, epoxy soybean oil 5-15 parts, Gypsum Fibrosum powder 5-15 parts, breast
Fragrant 5-10 parts, Flos Jasmini Sambac 10-15 parts, Folium Camelliae sinensis 5-8 parts, Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersing aid 3-5 parts, defoamer 3-5
Part, diluent 3-5 parts.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Embodiment two
A kind of environmental protection coating material for the spraying of furniture board top layer, further, the environmental protection coating material includes following weight
Component is made：Plant oleoresin 25-30 parts, plant oil pastes 18-20 parts, Colophonium 18-20 parts, epoxy soybean oil 8-10
Part, Gypsum Fibrosum powder 10-13 parts, Olibanum 6-8 parts, Flos Jasmini Sambac 10-15 parts, Folium Camelliae sinensis 5-8 parts, Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersion are helped
Agent 3-5 parts, defoamer 3-5 parts, diluent 3-5 parts.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Embodiment three
A kind of environmental protection coating material for the spraying of furniture board top layer, the environmental protection coating material is made including following composition by weight：
25 parts of plant oleoresin, 18 parts of plant oil pastes, 18 parts of Colophonium, 8 parts of epoxy soybean oil, 10 parts of Gypsum Fibrosum powder, 6 parts of Olibanum,
10 parts of Flos Jasmini Sambac, 5 parts of Folium Camelliae sinensis, 5 parts of Flos Chrysanthemi, 2 parts of Flos Osmanthi Fragrantis, 3 parts of dispersing aid, 3 parts of defoamer, 3 parts of diluent.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Example IV
A kind of environmental protection coating material for the spraying of furniture board top layer, the environmental protection coating material is made including following composition by weight：
28 parts of plant oleoresin, 20 parts of plant oil pastes, 20 parts of Colophonium, 9 parts of epoxy soybean oil, 12 parts of Gypsum Fibrosum powder, 7 parts of Olibanum,
13 parts of Flos Jasmini Sambac, 7 parts of Folium Camelliae sinensis, 7 parts of Flos Chrysanthemi, 3 parts of Flos Osmanthi Fragrantis, 4 parts of dispersing aid, 4 parts of defoamer, 4 parts of diluent.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Embodiment five
A kind of environmental protection coating material for the spraying of furniture board top layer, the environmental protection coating material is made including following composition by weight：
30 parts of plant oleoresin, 20 parts of plant oil pastes, 20 parts of Colophonium, 10 parts of epoxy soybean oil, 13 parts of Gypsum Fibrosum powder, 8 parts of Olibanum,
15 parts of Flos Jasmini Sambac, 8 parts of Folium Camelliae sinensis, 8 parts of Flos Chrysanthemi, 3 parts of Flos Osmanthi Fragrantis, 5 parts of dispersing aid, 5 parts of defoamer, 5 parts of diluent.
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, close
Envelope heated and stirred, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is that 1.5-2 is little
When, found by observation window, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120
Rev/min rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken by C
Go out, Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent is added in sealing container, sequentially add leaching
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis after bubble, keeps 60-70 DEG C of temperature seal to decoct 40 minutes, and perfume liquid is obtained, and takes out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, and above-mentioned components by weight percent dilution is added successively
Agent and defoamer, to 100-120 DEG C, with 40-45 rev/min of rotating speed sealing stirring 40 minutes, cooling down was to normal for heated sealed
Temperature, that is, be obtained environmental protection coating material.
Claims (5)
1. it is a kind of for furniture board top layer spraying environmental protection coating material, it is characterised in that make including following composition by weight：It is natural
Plant oleoresin 20-35 parts, plant oil pastes 15-25 parts, Colophonium 15-25 parts, epoxy soybean oil 5-15 parts, Gypsum Fibrosum powder 5-
15 parts, Olibanum 5-10 parts, Flos Jasmini Sambac 10-15 parts, Folium Camelliae sinensis 5-8 parts, Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersing aid 3-5 parts, disappear
Infusion 3-5 parts, diluent 3-5 parts；
The preparation method of the environmental protection coating material, also including following step processed：
The plant oleoresin of above-mentioned components by weight percent, Colophonium, epoxy soybean oil, Olibanum are sequentially added reactor by A, and sealing adds
Thermal agitation, heating-up temperature is 200-230 DEG C, and speed of agitator is 300-350 rev/min, and the stirring reaction time is 1.5-2 hours, is led to
Cross observation window discovery, reactor inside raw material stirring is when mixing to uniform mixing liquid, be cooled to 70-85 DEG C it is standby；
The reactor of B opening steps A, adds successively vegetable oil oil pastes, Gypsum Fibrosum powder, dispersing aid, with 100-120 rev/min
Rotating speed, sealing keep 70-85 DEG C, continue stir mixing 40-45 minutes, be obtained compound；
The Flos Jasmini Sambac of above-mentioned components by weight percent, Folium Camelliae sinensis, Flos Chrysanthemi, Flos Osmanthi Fragrantis are put successively 40-60 DEG C of warm water soaking 8-10 minute and are taken out by C,
Add Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi, the decocting in water boiling of 5 times of amounts of Flos Osmanthi Fragrantis of above-mentioned components by weight percent in sealing container, after sequentially adding immersion
Flos Jasmini Sambac, Folium Camelliae sinensis, Flos Chrysanthemi and Flos Osmanthi Fragrantis, keep 60-70 DEG C of temperature seal to decoct 40 minutes, perfume liquid is obtained, take out standby；
D adds fragrant liquid obtained in C into B in the reactor for containing compound, add successively above-mentioned components by weight percent diluent and
Defoamer, heated sealed is stirred 40 minutes, cooling down to room temperature, i.e., to 100-120 DEG C with 40-45 rev/min of rotating speed sealing
Prepared environmental protection coating material.
2. a kind of environmental protection coating material for the spraying of furniture board top layer according to claim 1, it is characterised in that further
, the environmental protection coating material is made including following composition by weight：Plant oleoresin 25-30 parts, plant oil pastes 18-20 parts,
Colophonium 18-20 parts, epoxy soybean oil 8-10 parts, Gypsum Fibrosum powder 10-13 parts, Olibanum 6-8 parts, Flos Jasmini Sambac 10-15 parts, Folium Camelliae sinensis 5-8 parts,
Flos Chrysanthemi 5-8 parts, Flos Osmanthi Fragrantis 2-3 parts, dispersing aid 3-5 parts, defoamer 3-5 parts, diluent 3-5 parts.
3. it is according to claim 1 it is a kind of for furniture board top layer spraying environmental protection coating material, it is characterised in that the ring
Friendly coating is made including following composition by weight：25 parts of plant oleoresin, 18 parts of plant oil pastes, 18 parts of Colophonium, epoxy are big
8 parts of Oleum Glycines, 10 parts of Gypsum Fibrosum powder, 6 parts of Olibanum, 10 parts of Flos Jasmini Sambac, 5 parts of Folium Camelliae sinensis, 3 parts of dispersing aid, disappear at 5 parts of Flos Chrysanthemi, 2 parts of Flos Osmanthi Fragrantis
3 parts of infusion, 3 parts of diluent.
4. it is according to claim 1 it is a kind of for furniture board top layer spraying environmental protection coating material, it is characterised in that the ring
Friendly coating is made including following composition by weight：28 parts of plant oleoresin, 20 parts of plant oil pastes, 20 parts of Colophonium, epoxy are big
9 parts of Oleum Glycines, 12 parts of Gypsum Fibrosum powder, 7 parts of Olibanum, 13 parts of Flos Jasmini Sambac, 7 parts of Folium Camelliae sinensis, 4 parts of dispersing aid, disappear at 7 parts of Flos Chrysanthemi, 3 parts of Flos Osmanthi Fragrantis
4 parts of infusion, 4 parts of diluent.
5. it is according to claim 1 it is a kind of for furniture board top layer spraying environmental protection coating material, it is characterised in that the ring
Friendly coating is made including following composition by weight：30 parts of plant oleoresin, 20 parts of plant oil pastes, 20 parts of Colophonium, epoxy are big
10 parts of Oleum Glycines, 13 parts of Gypsum Fibrosum powder, 8 parts of Olibanum, 15 parts of Flos Jasmini Sambac, 8 parts of Folium Camelliae sinensis, 5 parts of dispersing aid, disappear at 8 parts of Flos Chrysanthemi, 3 parts of Flos Osmanthi Fragrantis
5 parts of infusion, 5 parts of diluent.