CN106675364A - Aluminum case coating paint of capacitor - Google Patents
Aluminum case coating paint of capacitor Download PDFInfo
- Publication number
- CN106675364A CN106675364A CN201611146685.6A CN201611146685A CN106675364A CN 106675364 A CN106675364 A CN 106675364A CN 201611146685 A CN201611146685 A CN 201611146685A CN 106675364 A CN106675364 A CN 106675364A
- Authority
- CN
- China
- Prior art keywords
- parts
- capacitor
- standby
- coating paint
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an aluminum case coating paint of a capacitor. The aluminum case coating paint is prepared from the following substances: polyurethane, polycarbonate, acetophenone, ethyl acetate, glycerin monostearate, modified diatomite, magnesium stearate, sodium carboxymethylcellulose, silicon nitride, polyoxyethylene polyoxypropylene ether and oleamide. The modified diatomite has relatively high heat resistance, abrasive resistance and adsorptive property, the curing effect of the paint is greatly strengthened through cooperation with the combined action of other ingredients, the abrasive resistance, the impact resistance and the corrosion resistance of the surface of the capacitor are improved, a high temperature over 320 DEG C can be tolerated, the conditions of explosion, spontaneous ignition and the like when the capacitor works are greatly reduced, the service life of the capacitor is prolonged by 60%-70% and the aluminum case coating paint has a good practical value.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of capacitor aluminum housing coating paint.
Background technology
With the progress of electron trade technology, the manufacturing technology of electronic circuit board is also greatly improved, in order to reduce electricity
The volume of sub- product and reduce consuming, electrolysis condenser as one of universal component on electronic circuit board, not only to the resistance to of it
Warm, resistance to puncture requirement be more and more higher, and requires that its footprints is also the smaller the better.Electrolysis condenser footprints will
It is little, first it is that aluminium shell of capacitor will have high draw ratio, capacitor diameter reduced dimension area is just little;Next to that capacitor case will
There is high air heat resistance, be otherwise easily damaged and reduction of service life in compact sky is asked, traditional aluminium shell of capacitor
It is first punching shaping, rear pyrocondensation is sealed last layer insulant, is tightly rolled on capacitor case after making insulant heated.This
It has the disadvantage that the resistance to air themperature of insulant for sealing is not high enough to plant hot shortness's plastic film capacitor, during heat-seal process
Many plastic film waste materials can be produced.A kind of polarized capacitor aluminum case body disclosed in Ye You TaiWan, Chinas Yabo Company
The painting method of dielectric film, Chinese invention patent application publication number CNl944704, the method mainly takes 1000 ~ 20000
The high potential difference of volt, makes gas ion clash into polytetrafluoroethylene politef (polytetrafluoroethylene), clashes into
Go out fluorine atom, simultaneous oxidation generates fluorine oxide, and fluorine oxide can produce strength cohesiveness under high temperature action, and be deposited on aluminum hull
The insulated hull film layer for covering and being formed fluorine oxide is sticked on body surface face.What this method was actually only reduced chloride covers the secondary of material
Pollution, but there is a problem that temperature tolerance is poor, production cost is higher.
The content of the invention
In order to solve the above problems, the invention provides a kind of capacitor aluminum housing coating paint, can be effectively protected electric capacity
Device, extends its service life.
The present invention is achieved through the following technical solutions:
A kind of capacitor aluminum housing coating paint, is made up of the material of following weight portion:
30 parts of polyurethanes, 15 parts of Merlon, 50 parts of 1-Phenylethanone .s, 10 parts of ethyl acetate, 10 parts of glyceryl monostearates,
12 parts of modification infusorial earths, 6 parts of magnesium stearate, 8 parts of sodium carboxymethyl cellulose, 5 parts of silicon nitrides, 10 parts of Polyethylene oxide polyoxy Propanolamines
Ether, 8 parts of oleamides;The modification infusorial earth is made up of the material of following weight portion:35 parts of kieselguhr, 7 parts of CNTs, 3
Part toughened zirconium oxide, 2 parts of phosphoric acid, 4 parts of thio-2 acid dibasic acid esters.
Further, the preparation method of the modification infusorial earth comprises the steps:
(1)First kieselguhr is put into into immersion treatment 1.5h in the daucic acid solution that mass fraction is 4.5%, matter is placed into after taking-up
Immersion treatment 1.5h in the hydrochloric acid solution that fraction is 3.5% is measured, is placed into after taking-up in the salpeter solution that mass fraction is 2.5% and is soaked
Bubble processes 1.5h, and deionized water is rinsed well standby after taking-up;Kieselguhr is processed with three kinds of different acid solutions, can
Diatomaceous surface texture is significantly improved, impurity component has effectively been dispelled, its specific surface area is improve into more than 7 times;
(2)By step(1)The kieselguhr of gained is put in the calcining furnace that temperature is 750 DEG C calcines 1h, then with the liter of 5 DEG C/min
Warm speed carries out warming temperature, and continuous warming is processed after 1h, and being drawn off natural cooling, to obtain calcined diatomite standby;To kieselguhr
High-temperature calcination process is carried out, its internal structure is further improved, its physicochemical stability is enhanced, tolerable temperature improves 1 times;
(3)By step(2)The calcined diatomite of gained carries out ball mill pulverizing, and kieselguhr of the granular size for 550 ~ 650 mesh is obtained
Powder is standby;
(4)Take step(3)The deionized water of 2 times of gained diatomite in powder quality, toughened zirconium oxide, phosphoric acid and thio-2 acid is double
Ester is added, and is again jointly mixed into diatomite in powder, CNT after stirring, and is stirred into 400 ~ 500 revs/min of rotating speed
Even pasty mass is standby;
(5)By step(4)The pastel of gained is put into temperature and is less than 6% for heat drying under conditions of 50 ~ 53 DEG C to its water content
When get product modification infusorial earth.
A kind of preparation method of capacitor aluminum housing coating paint, comprises the steps:
(1)Polyurethanes, Merlon, 1-Phenylethanone., ethyl acetate, glyceryl monostearate and modification infusorial earth is common
Mixing, heating keeping temperature is 40 ~ 42 DEG C, is stirred with 350 revs/min of rotating speed, then stands insulation 15min, last cold
But mixture A is obtained to room temperature standby;
(2)Magnesium stearate, sodium carboxymethyl cellulose, silicon nitride, Polyethylene oxide polyoxy propanol amidogen ether and oleamide are mixed jointly
Close, after stirring with 400 revs/min of rotating speed, obtain mixture B standby;
(3)Mixture A and mixture B are mixed jointly, and is stirred with 700 revs/min of rotating speed, got product.
The present invention has the advantages that:Modified kieselguhr has stronger heat-resisting, wear-resisting and absorption property, matches somebody with somebody
The collective effect of remaining composition is closed, the solidification effect of coating is greatly strengthen, wear-resisting capacitor surface, impact resistance is improve and is resisted
Corrosive nature, tolerates more than 320 DEG C of high temperature, greatly reduces the generation that situations such as explosion, spontaneous combustion occurs when capacitor works,
The service life of capacitor extends 60 ~ 70%, there is good practical value.
Specific embodiment
Embodiment 1
A kind of capacitor aluminum housing coating paint, is made up of the material of following weight portion:
30 parts of polyurethanes, 15 parts of Merlon, 50 parts of 1-Phenylethanone .s, 10 parts of ethyl acetate, 10 parts of glyceryl monostearates,
12 parts of modification infusorial earths, 6 parts of magnesium stearate, 8 parts of sodium carboxymethyl cellulose, 5 parts of silicon nitrides, 10 parts of Polyethylene oxide polyoxy Propanolamines
Ether, 8 parts of oleamides;The modification infusorial earth is made up of the material of following weight portion:35 parts of kieselguhr, 7 parts of CNTs, 3
Part toughened zirconium oxide, 2 parts of phosphoric acid, 4 parts of thio-2 acid dibasic acid esters.
Further, the preparation method of the modification infusorial earth comprises the steps:
(1)First kieselguhr is put into into immersion treatment 1.5h in the daucic acid solution that mass fraction is 4.5%, matter is placed into after taking-up
Immersion treatment 1.5h in the hydrochloric acid solution that fraction is 3.5% is measured, is placed into after taking-up in the salpeter solution that mass fraction is 2.5% and is soaked
Bubble processes 1.5h, and deionized water is rinsed well standby after taking-up;
(2)By step(1)The kieselguhr of gained is put in the calcining furnace that temperature is 750 DEG C calcines 1h, then with the liter of 5 DEG C/min
Warm speed carries out warming temperature, and continuous warming is processed after 1h, and being drawn off natural cooling, to obtain calcined diatomite standby;
(3)By step(2)The calcined diatomite of gained carries out ball mill pulverizing, and kieselguhr of the granular size for 550 ~ 650 mesh is obtained
Powder is standby;
(4)Take step(3)The deionized water of 2 times of gained diatomite in powder quality, toughened zirconium oxide, phosphoric acid and thio-2 acid is double
Ester is added, and is again jointly mixed into diatomite in powder, CNT after stirring, and is stirred into 400 ~ 500 revs/min of rotating speed
Even pasty mass is standby;
(5)By step(4)The pastel of gained is put into temperature and is less than 6% for heat drying under conditions of 50 ~ 53 DEG C to its water content
When get product modification infusorial earth.
A kind of preparation method of capacitor aluminum housing coating paint, comprises the steps:
(1)Polyurethanes, Merlon, 1-Phenylethanone., ethyl acetate, glyceryl monostearate and modification infusorial earth is common
Mixing, heating keeping temperature is 40 ~ 42 DEG C, is stirred with 350 revs/min of rotating speed, then stands insulation 15min, last cold
But mixture A is obtained to room temperature standby;
(2)Magnesium stearate, sodium carboxymethyl cellulose, silicon nitride, Polyethylene oxide polyoxy propanol amidogen ether and oleamide are mixed jointly
Close, after stirring with 400 revs/min of rotating speed, obtain mixture B standby;
(3)Mixture A and mixture B are mixed jointly, and is stirred with 700 revs/min of rotating speed, got product.
Comparative example 1
This comparative example 1 is modified compared with Example 1, not to kieselguhr process, is entered with the common kieselguhr of equivalent
Row is replaced, composition in addition, method all same.
Matched group
Existing capacitor aluminum housing coating paint.
To contrast effect of the present invention, respectively experiment is coated to aluminum hull surface with above-mentioned three kinds of coating, during coating aluminum hull,
Aluminum hull needs first to be cleaned with the hot water of addition NaOH, and the mass concentration of NaOH is 4 ~ 6%, and 175 ~ 185 DEG C are placed on after cleaning
Under conditions of be dried oxidation 1 ~ 2 minute, then by above-mentioned three kinds of coating paints in the environment of room temperature even spread to pretreatment
Surface of aluminum plate on, at least 1 minute is solidified in the environment of finally aluminium sheet being placed on into 210 ~ 220 DEG C.Following table is three kinds of modes pair
The correction data of the solidification temperature, time and capacitor overlay film aluminum hull technical specification made by gained overlay film aluminum hull answered:
Embodiment 1 | Comparative example 1 | Matched group | |
Solidification temperature(℃) | 212 | 215 | 215 |
Hardening time(s) | 60 | 60 | 60 |
Require index | Meet | Meet | Meet |
Draw ratio | 3.53:1 | 3:1 | 2:1 |
Resistance to temperature value(℃) | 326 | 302 | 263 |
Note:The determination step of resistance to temperature value described in upper table is:Overlay film aluminum hull is placed on thin aluminum top and sends into GZX-9076 digital displays drum
In wind drying baker, and drying baker temperature is set to into a field planting, continues drying out the time for 5min, observe its surface chromatic aberration invariant color,
The maximum temperature that can bear that do not turn yellow is resistance to temperature value.
Claims (3)
1. a kind of capacitor aluminum housing coating paint, it is characterised in that be made up of the material of following weight portion:
30 parts of polyurethanes, 15 parts of Merlon, 50 parts of 1-Phenylethanone .s, 10 parts of ethyl acetate, 10 parts of glyceryl monostearates,
12 parts of modification infusorial earths, 6 parts of magnesium stearate, 8 parts of sodium carboxymethyl cellulose, 5 parts of silicon nitrides, 10 parts of Polyethylene oxide polyoxy Propanolamines
Ether, 8 parts of oleamides;The modification infusorial earth is made up of the material of following weight portion:35 parts of kieselguhr, 7 parts of CNTs, 3
Part toughened zirconium oxide, 2 parts of phosphoric acid, 4 parts of thio-2 acid dibasic acid esters.
2. a kind of capacitor aluminum housing coating paint according to claim 1, it is characterised in that the system of the modification infusorial earth
Preparation Method comprises the steps:
(1)First kieselguhr is put into into immersion treatment 1.5h in the daucic acid solution that mass fraction is 4.5%, matter is placed into after taking-up
Immersion treatment 1.5h in the hydrochloric acid solution that fraction is 3.5% is measured, is placed into after taking-up in the salpeter solution that mass fraction is 2.5% and is soaked
Bubble processes 1.5h, and deionized water is rinsed well standby after taking-up;
(2)By step(1)The kieselguhr of gained is put in the calcining furnace that temperature is 750 DEG C calcines 1h, then with the liter of 5 DEG C/min
Warm speed carries out warming temperature, and continuous warming is processed after 1h, and being drawn off natural cooling, to obtain calcined diatomite standby;
(3)By step(2)The calcined diatomite of gained carries out ball mill pulverizing, and kieselguhr of the granular size for 550 ~ 650 mesh is obtained
Powder is standby;
(4)Take step(3)The deionized water of 2 times of gained diatomite in powder quality, toughened zirconium oxide, phosphoric acid and thio-2 acid is double
Ester is added, and is again jointly mixed into diatomite in powder, CNT after stirring, and is stirred into 400 ~ 500 revs/min of rotating speed
Even pasty mass is standby;
(5)By step(4)The pastel of gained is put into temperature and is less than 6% for heat drying under conditions of 50 ~ 53 DEG C to its water content
When get product modification infusorial earth.
3. a kind of preparation method of capacitor aluminum housing coating paint as claimed in claim 1, it is characterised in that including following step
Suddenly:
(1)Polyurethanes, Merlon, 1-Phenylethanone., ethyl acetate, glyceryl monostearate and modification infusorial earth is common
Mixing, heating keeping temperature is 40 ~ 42 DEG C, is stirred with 350 revs/min of rotating speed, then stands insulation 15min, last cold
But mixture A is obtained to room temperature standby;
(2)Magnesium stearate, sodium carboxymethyl cellulose, silicon nitride, Polyethylene oxide polyoxy propanol amidogen ether and oleamide are mixed jointly
Close, after stirring with 400 revs/min of rotating speed, obtain mixture B standby;
(3)Mixture A and mixture B are mixed jointly, and is stirred with 700 revs/min of rotating speed, got product.