CN107936804A - A kind of cold lead ingot granulator surface coating - Google Patents
A kind of cold lead ingot granulator surface coating Download PDFInfo
- Publication number
- CN107936804A CN107936804A CN201711088389.XA CN201711088389A CN107936804A CN 107936804 A CN107936804 A CN 107936804A CN 201711088389 A CN201711088389 A CN 201711088389A CN 107936804 A CN107936804 A CN 107936804A
- Authority
- CN
- China
- Prior art keywords
- surface coating
- silicon dioxide
- starch
- lead ingot
- sodium alginate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cold lead ingot granulator surface coating, it is related to lead-acid storage battery production equipment technical field, is made of following component:Aqueous polyurethane emulsion, coupling agent modified nano silicon dioxide, benzene sulfonic acid, pentaerythrite, poly- terephthalyl alcohol, molybdenum dialkyldithiocarbamacompositions, acidified starch, sodium alginate-modified attapulgite, water;The present invention reasonably matches paint ingredient by many experiments, can effectively improve the overall performance of coating film.This coating is using aqueous polyurethane emulsion as main base matter, it with the addition of the modification that poly- terephthalyl alcohol, molybdenum dialkyldithiocarbamacompositions can be to aqueous polyurethane emulsion progress to a certain extent again, the branched structure of the loose molecule of energy, the film forming speed and quality of forming film of coating can effectively be improved, the present invention is by coupling agent modified nano silicon dioxide, the problem of can effectively improving easy reunion, poor compatibility, the bad dispersibility of common nano silicon dioxide.
Description
Technical field
The invention belongs to lead-acid storage battery production equipment technical field, and in particular to a kind of cold lead ingot granulator surface applies
Material.
Background technology
Cold lead ingot granulator is the state-of-the-art production equipment in front end in lead-acid storage battery production line, is mainly matched somebody with somebody with lead-power machine
Set uses, and is also matched with pole plate full-automation production line, and instead of tradition granulation is to use lead melting furnace founding into leads, cutting
Into lead button, cold lead ingot granulator surface in production application can touch certain chemical substance, can give cold lead ingot granulator table
Face causes to corrode, meanwhile, if not doing safeguard procedures, various corrosion can also occur for cold lead ingot granulator existing in an atmosphere
, all it is that brushing paint is carried out to protect to cold lead ingot granulator surface in the prior art therefore, and existing coating pair
Cold lead ingot granulator surface corrosion-resistant erosion it is ineffective, can not be well cold lead ingot granulator is effectively protected.
The content of the invention
The purpose of the present invention is for it is existing the problem of, there is provided a kind of cold lead ingot granulator surface coating.
The present invention is achieved by the following technical solutions:
A kind of cold lead ingot granulator surface coating, is made of following component by weight:Aqueous polyurethane emulsion 80-90, idol
Join agent modified manometer silicon dioxide 3-5, benzene sulfonic acid 4-6, pentaerythrite 12-18, poly- terephthalyl alcohol 0.5-0.8, dialkyl group two
Thiocarbamic acid molybdenum 1.2-1.8, acidified starch 20-25, sodium alginate-modified attapulgite 5-10, water 60-80.
Further:The acidified starch preparation method is:The organic acid soln that mass fraction is 5% is prepared, starch is adopted
With 350W microwave treatment 2min, the starch after microwave treatment and organic acid soln are then pressed into 200g again:The ratio of 450mL
It is uniformly admixed together, 90 DEG C are heated to, 40min is stirred with 3000r/min rotating speeds, then stands and is cooled to room temperature, filter, adopt
Starch is cleaned to neutrality with deionized water, then drying to constant weight, to obtain the final product.
Further:The organic acid is any of ethanedioic acid, malonic acid, succinic acid, maleic acid.
Further:The starch is cornstarch, tapioca presses 3:1 mass ratio mixes.
Further:The coupling agent modified method for preparing nano silica be prepare mass fraction be 5.5% it is organic
Silane coupler solution, then presses 50g by nano silicon dioxide:The ratio uniform of 180mL is admixed together, is then heated to 75
DEG C, when insulation 1.5 is small, then filtered, then nano silicon dioxide is cleaned using deionized water, drying to constant weight,
To obtain the final product.
Further:The sodium alginate-modified preparation method of attapulgite is:Sodium alginate and water are configured to quality
Fraction is 3.5% sodium alginate soln, is heated to 60 DEG C, 40min is kept the temperature, then again by attapulgite and sodium alginate soln
By 150:The ratio uniform mixing of 300mL, carries out vacuum impregnation 30min, is then filtered, drying to constant weight, to obtain the final product.
Further:The vacuum impregnation vacuum is 0.035MPa, and temperature is 80 DEG C.
The present invention has the following advantages compared with prior art:The present invention carries out paint ingredient by many experiments rational
Proportioning, can effectively improve the overall performance of coating film.This coating is using aqueous polyurethane emulsion as main base
Material, but with the addition of poly- terephthalyl alcohol, molybdenum dialkyldithiocarbamacompositions aqueous polyurethane emulsion can be carried out it is certain
Modification in degree, can effectively reduce the degree of polymerization of raw material, the branched structure of loose molecule, can effectively improve coating into
Film speed and quality of forming film, the present invention can effectively improve common nano-silica by coupling agent modified nano silicon dioxide
The problem of easy reunion, poor compatibility, bad dispersibility of SiClx, by carrying out acidification to starch, by acidified starch and seaweed
Sour sodium is attapulgite modified to be added in coating system, is capable of the logical of the corrosion factor such as shield water, oxygen, ion to a certain extent
Cross, cut off the pore in paint film, then by the effect of coupling agent modified nano silicon dioxide, further improve coating
Anti-corrosion capability.
Embodiment
Embodiment 1
A kind of cold lead ingot granulator surface coating, is made of following component by weight:Aqueous polyurethane emulsion 80, coupling agent
Modified manometer silicon dioxide 3, benzene sulfonic acid 4, pentaerythrite 12, poly- terephthalyl alcohol 0.5, molybdenum dialkyldithiocarbamacompositions
1.2nd, acidified starch 20, sodium alginate-modified attapulgite 5, water 60.
Further:The acidified starch preparation method is:The organic acid soln that mass fraction is 5% is prepared, starch is adopted
With 350W microwave treatment 2min, the starch after microwave treatment and organic acid soln are then pressed into 200g again:The ratio of 450mL
It is uniformly admixed together, 90 DEG C are heated to, 40min is stirred with 3000r/min rotating speeds, then stands and is cooled to room temperature, filter, adopt
Starch is cleaned to neutrality with deionized water, then drying to constant weight, to obtain the final product.
Further:The organic acid is any of ethanedioic acid, malonic acid, succinic acid, maleic acid.
Further:The starch is cornstarch, tapioca presses 3:1 mass ratio mixes.
Further:The coupling agent modified method for preparing nano silica be prepare mass fraction be 5.5% it is organic
Silane coupler solution, then presses 50g by nano silicon dioxide:The ratio uniform of 180mL is admixed together, is then heated to 75
DEG C, when insulation 1.5 is small, then filtered, then nano silicon dioxide is cleaned using deionized water, drying to constant weight,
To obtain the final product.
Further:The sodium alginate-modified preparation method of attapulgite is:Sodium alginate and water are configured to quality
Fraction is 3.5% sodium alginate soln, is heated to 60 DEG C, 40min is kept the temperature, then again by attapulgite and sodium alginate soln
By 150:The ratio uniform mixing of 300mL, carries out vacuum impregnation 30min, is then filtered, drying to constant weight, to obtain the final product.
Further:The vacuum impregnation vacuum is 0.035MPa, and temperature is 80 DEG C.
Embodiment 2
A kind of cold lead ingot granulator surface coating, is made of following component by weight:Aqueous polyurethane emulsion 90, coupling agent
Modified manometer silicon dioxide 5, benzene sulfonic acid 6, pentaerythrite 18, poly- terephthalyl alcohol 0.8, molybdenum dialkyldithiocarbamacompositions
1.8th, acidified starch 25, sodium alginate-modified attapulgite 10, water 80.
Further:The acidified starch preparation method is:The organic acid soln that mass fraction is 5% is prepared, starch is adopted
With 350W microwave treatment 2min, the starch after microwave treatment and organic acid soln are then pressed into 200g again:The ratio of 450mL
It is uniformly admixed together, 90 DEG C are heated to, 40min is stirred with 3000r/min rotating speeds, then stands and is cooled to room temperature, filter, adopt
Starch is cleaned to neutrality with deionized water, then drying to constant weight, to obtain the final product.
Further:The organic acid is any of ethanedioic acid, malonic acid, succinic acid, maleic acid.
Further:The starch is cornstarch, tapioca presses 3:1 mass ratio mixes.
Further:The coupling agent modified method for preparing nano silica be prepare mass fraction be 5.5% it is organic
Silane coupler solution, then presses 50g by nano silicon dioxide:The ratio uniform of 180mL is admixed together, is then heated to 75
DEG C, when insulation 1.5 is small, then filtered, then nano silicon dioxide is cleaned using deionized water, drying to constant weight,
To obtain the final product.
Further:The sodium alginate-modified preparation method of attapulgite is:Sodium alginate and water are configured to quality
Fraction is 3.5% sodium alginate soln, is heated to 60 DEG C, 40min is kept the temperature, then again by attapulgite and sodium alginate soln
By 150:The ratio uniform mixing of 300mL, carries out vacuum impregnation 30min, is then filtered, drying to constant weight, to obtain the final product.
Further:The vacuum impregnation vacuum is 0.035MPa, and temperature is 80 DEG C.
Embodiment 3
A kind of cold lead ingot granulator surface coating, is made of following component by weight:Aqueous polyurethane emulsion 85, coupling agent
Modified manometer silicon dioxide 4, benzene sulfonic acid 5, pentaerythrite 15, poly- terephthalyl alcohol 0.6, molybdenum dialkyldithiocarbamacompositions
1.5th, acidified starch 22, sodium alginate-modified attapulgite 8, water 70.
Further:The acidified starch preparation method is:The organic acid soln that mass fraction is 5% is prepared, starch is adopted
With 350W microwave treatment 2min, the starch after microwave treatment and organic acid soln are then pressed into 200g again:The ratio of 450mL
It is uniformly admixed together, 90 DEG C are heated to, 40min is stirred with 3000r/min rotating speeds, then stands and is cooled to room temperature, filter, adopt
Starch is cleaned to neutrality with deionized water, then drying to constant weight, to obtain the final product.
Further:The organic acid is any of ethanedioic acid, malonic acid, succinic acid, maleic acid.
Further:The starch is cornstarch, tapioca presses 3:1 mass ratio mixes.
Further:The coupling agent modified method for preparing nano silica be prepare mass fraction be 5.5% it is organic
Silane coupler solution, then presses 50g by nano silicon dioxide:The ratio uniform of 180mL is admixed together, is then heated to 75
DEG C, when insulation 1.5 is small, then filtered, then nano silicon dioxide is cleaned using deionized water, drying to constant weight,
To obtain the final product.
Further:The sodium alginate-modified preparation method of attapulgite is:Sodium alginate and water are configured to quality
Fraction is 3.5% sodium alginate soln, is heated to 60 DEG C, 40min is kept the temperature, then again by attapulgite and sodium alginate soln
By 150:The ratio uniform mixing of 300mL, carries out vacuum impregnation 30min, is then filtered, drying to constant weight, to obtain the final product.
Further:The vacuum impregnation vacuum is 0.035MPa, and temperature is 80 DEG C.
Comparative example 1:Differed only in embodiment 1 and acidified starch is replaced with into common corn starch.
Comparative example 2:Differed only in embodiment 1 and coupling agent modified nano silicon dioxide is replaced with into untreated nanometer
Silica.
Comparative example 3:Differed only in embodiment 1 sodium alginate-modified attapulgite is replaced with it is common untreated recessed
Convex rod soil.
Experiment:
Embodiment and comparative example coating are uniformly coated on glass plate, are dried at the same temperature, coating layer thickness is
0.2mm, then according to the regulation of GB/T1732-93 national standards, the adhesive force of testing coating:
Table 1
As can be seen from Table 1, the paint adhesion that prepared by the present invention is excellent.
Film to forming 10 micron thickness after drying in embodiment and comparative example coating film to glass plate, carries out resistance to
Chemically test(GB/1763-1979):
2 acid resistance of table(Mass fraction is 1% sulfuric acid solution, room temperature)
1 day | 8 days | 20 days | 45 days | 90 days | |
Embodiment average | It is unchanged | It is unchanged | It is unchanged | It is unchanged | Somewhat change colour |
Comparative example 1 | It is unchanged | It is unchanged | Slightly loss of gloss | 3% vesicle | 10% vesicle |
Comparative example 2 | It is unchanged | It is unchanged | Slightly loss of gloss | 4% vesicle | 12% vesicle |
Comparative example 3 | It is unchanged | Slightly loss of gloss | 3% vesicle | 9% vesicle | 20% vesicle |
3 alkali resistance of table(Mass fraction is 1% sodium hydroxide solution, room temperature)
1 day | 8 days | 20 days | 45 days | 90 days | |
Embodiment average | It is unchanged | It is unchanged | It is unchanged | It is unchanged | Somewhat change colour |
Comparative example 1 | It is unchanged | It is unchanged | Slightly change colour | Loss of gloss | Paint film spalling |
Comparative example 2 | It is unchanged | It is unchanged | Slightly change colour | Loss of gloss | Paint film spalling |
Comparative example 3 | It is unchanged | Slightly darkening | Loss of gloss | Paint film spalling | Paint film spalling |
The coating film chemical resistance excellent performance that it can be seen from table 2 and table 3 prepared by the present invention.
Claims (7)
1. a kind of cold lead ingot granulator surface coating, it is characterised in that be made by weight of following component:Aqueous polyurethane
Lotion 80-90, coupling agent modified nano silicon dioxide 3-5, benzene sulfonic acid 4-6, pentaerythrite 12-18, poly- terephthalyl alcohol 0.5-
0.8th, molybdenum dialkyldithiocarbamacompositions 1.2-1.8, acidified starch 20-25, sodium alginate-modified attapulgite 5-10, water
60-80。
A kind of 2. cold lead ingot granulator surface coating according to claim 1, it is characterised in that:It is prepared by the acidified starch
Method is:The organic acid soln that mass fraction is 5% is prepared, starch is used into 350W microwave treatment 2min, then will be passed through again micro-
Starch after ripple processing presses 200g with organic acid soln:The ratio uniform of 450mL is admixed together, is heated to 90 DEG C, with
3000r/min rotating speeds stir 40min, then stand and are cooled to room temperature, filter, starch is cleaned into using deionized water
Property, then drying to constant weight, to obtain the final product.
A kind of 3. cold lead ingot granulator surface coating according to claim 2, it is characterised in that:The organic acid is second two
Any of acid, malonic acid, succinic acid, maleic acid.
A kind of 4. cold lead ingot granulator surface coating according to claim 2, it is characterised in that:The starch forms sediment for corn
Powder, tapioca press 3:1 mass ratio mixes.
A kind of 5. cold lead ingot granulator surface coating according to claim 1, it is characterised in that:It is described coupling agent modified to receive
Rice process for preparing silicon dioxide is to prepare the organo silane coupling agent solution that mass fraction is 5.5%, then by nano silicon dioxide
By 50g:The ratio uniform of 180mL is admixed together, is then heated to 75 DEG C, when insulation 1.5 is small, is then filtered, then adopt
Nano silicon dioxide is cleaned with deionized water, drying to constant weight, to obtain the final product.
A kind of 6. cold lead ingot granulator surface coating according to claim 1, it is characterised in that:It is described sodium alginate-modified
Preparation method of attapulgite is:Sodium alginate and water are configured to the sodium alginate soln that mass fraction is 3.5%, are heated to 60
DEG C, 40min is kept the temperature, attapulgite and sodium alginate soln are then pressed 150 again:The ratio uniform mixing of 300mL, carries out vacuum
Impregnate 30min, then filtered, drying to constant weight, to obtain the final product.
A kind of 7. cold lead ingot granulator surface coating according to claim 6, it is characterised in that:The vacuum impregnation vacuum
It is 80 DEG C to spend for 0.035MPa, temperature.