CN106673684A - Refractory mortar formula - Google Patents

Refractory mortar formula Download PDF

Info

Publication number
CN106673684A
CN106673684A CN201710016742.7A CN201710016742A CN106673684A CN 106673684 A CN106673684 A CN 106673684A CN 201710016742 A CN201710016742 A CN 201710016742A CN 106673684 A CN106673684 A CN 106673684A
Authority
CN
China
Prior art keywords
parts
fire
clay
fire clay
refractory mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710016742.7A
Other languages
Chinese (zh)
Inventor
陈超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui University of Science and Technology
Original Assignee
Anhui University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui University of Science and Technology filed Critical Anhui University of Science and Technology
Priority to CN201710016742.7A priority Critical patent/CN106673684A/en
Publication of CN106673684A publication Critical patent/CN106673684A/en
Pending legal-status Critical Current

Abstract

The invention discloses a refractory mortar formula and relates to the field of building materials. The refractory mortar formula adopts chlorinated paraffin and fire-resistant clay as binders and china clay powder, feldspar, quartz, iron ore, high bauxite, magnesia and silica as filling materials. The fire-resistant clay has good high-temperature resistance and can serve as a good paving seam material to guarantee good fire resistance of a building.

Description

A kind of fire clay formula
Technical field
The present invention relates to building material field, a kind of fire clay formula is related in particular to.
Background technology
Fire clay is made up of refractory powder, bonding agent and additive, and fire clay is used as the puzzle joint material of refractory product masonry Material.Traditional fire clay is made so that grog refractory powder adds appropriate plastic clay to make bonding agent and plasticizer, and resistance to elevated temperatures is general, Using effect is poor.
The content of the invention
Problem to be solved by this invention is to provide a kind of fire clay formula.
To achieve these goals, the technical scheme taken of the present invention is：A kind of fire clay formula, it is characterised in that should Fire clay formula includes the raw material of following parts by weight：16~25 parts of chlorinated paraffin, 16~25 parts of fire clay, china clay in powder 17~ 22 parts, 11~21 parts of feldspar, quartz 15~22 parts, 18~21 parts of iron ore, 26~35 parts of alumine, 17~23 parts of magnesia, two 25~35 parts of silica.
Beneficial effect：It is bonding agent that the fire clay formula uses chlorinated paraffin and fire clay, using china clay in powder, feldspar, Quartz, iron ore, alumine, magnesia, silica are packing material.The fire clay has good resistance to elevated temperatures, can be with As excellent puzzle joint material, ensure that building has good fire protecting performance.
Specific embodiment
Embodiment 1：
The fire clay formula includes the raw material of following parts by weight：16 parts of chlorinated paraffin, 25 parts of fire clay, china clay in powder 17 Part, 11 parts of feldspar, 15 parts of quartz, 21 parts of iron ore, 35 parts of alumine, 23 parts of magnesia, 35 parts of silica.
Embodiment 2：
The fire clay formula includes the raw material of following parts by weight：19 parts of chlorinated paraffin, 21 parts of fire clay, china clay in powder 19 Part, 16 parts of feldspar, 18 parts of quartz, 20 parts of iron ore, 28 parts of alumine, 19 parts of magnesia, 29 parts of silica.
Embodiment 3：
The fire clay formula includes the raw material of following parts by weight：25 parts of chlorinated paraffin, 16 parts of fire clay, china clay in powder 22 Part, 21 parts of feldspar, 22 parts of quartz, 18 parts of iron ore, 26 parts of alumine, 17 parts of magnesia, 25 parts of silica.
Embodiments of the invention are the foregoing is only, the scope of the claims of the invention is not thereby limited, it is every to utilize this hair Equivalent structure or equivalent flow conversion that bright specification and implementation method content are made, or directly or indirectly it is used in other correlations Technical field, be included within the scope of the present invention.

Claims (1)

1. a kind of fire clay formula, it is characterised in that the fire clay formula includes the raw material of following parts by weight：Chlorinated paraffin 16 ~25 parts, 16~25 parts of fire clay, 17~22 parts of china clay in powder, 11~21 parts of feldspar, quartzy 15~22 parts, iron ore 18~21 Part, 26~35 parts of alumine, 17~23 parts of magnesia, 25~35 parts of silica.
CN201710016742.7A 2017-01-10 2017-01-10 Refractory mortar formula Pending CN106673684A (en)