CN106673519A - High-performance decorative board - Google Patents
High-performance decorative board Download PDFInfo
- Publication number
- CN106673519A CN106673519A CN201611144469.8A CN201611144469A CN106673519A CN 106673519 A CN106673519 A CN 106673519A CN 201611144469 A CN201611144469 A CN 201611144469A CN 106673519 A CN106673519 A CN 106673519A
- Authority
- CN
- China
- Prior art keywords
- powder
- decorative panel
- decorative board
- performance
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance decorative board which is made of the following components: bauxite, dolomite, blast furnace slag, cement, glass powder, stone needle powder, modified pitchstone, micro silica powder, maleated rosin and water. The synergistic effect of the modified pitchstone and the maleated rosin in the invention not only greatly improves the strength of the decorative board, but also improves the compressive cushioning property of the decorative board, significantly improves the overall compression and scratch resistance of the decorative board, can ensure that the surface of the decorative board is not damaged for long time, improves the use quality of the decorative board, and guarantees the service life of the decorative board; the synergistic effect of the modified micro perlite powder prepared in the invention is added to greatly improve the thermal insulation and sound insulation performance of the decorative board of the invention.
Description
Technical field
The present invention relates to decoration material field, more particularly to a kind of high-performance decorative panel.
Background technology
At present decorative panel is to be mixed into material by a certain percentage with water by oxidation siliceous material, oxidation calcareous material, asbestos etc.
Slurry is made, and oxidation siliceous material generally adopts silica flour, and cost is of a relatively high, and asbestos have certain toxicity, and at present
Decorative panel insufficient strength, do not reach the demand of some occasions, how to provide a kind of nontoxic, low price, raw material be easy to get, it is high
The plaque of performance, is the problem for needing to solve.
The content of the invention
It is an object of the invention to provide a kind of high-performance decorative panel, is achieved through the following technical solutions:
A kind of high-performance decorative panel, is made up of the raw material of following weight portion:Bauxite 18-22, dolomite 13-15, blast-furnace cinder
23-25, cement 11-13, glass dust 12-14, stone needle powder 0.3-0.5, modified rosin rock 6-9, silicon powder 0.4-0.7, Malaysia pine
Fragrant 0.4-0.8, modified pearl rock micropowder 5-8, water 22-24.
Further, the bauxite, dolomite, the granularity of blast furnace slag are 200 mesh.
Further, the granularity of the glass dust is 250 mesh.
Further, the modified rosin rock is made up by weight of following component:Pitchstone 22, andalusite powder 0.1,
Potassium feldspar 0.2, its preparation method is:Pitchstone is crossed into 150 mesh, andalusite powder and potassium feldspar are crossed into 180 mesh, by pitchstone, red
Pillar powder and potassium feldspar are uniformly admixed together, in being added to the Monosodium maleate solution that mass concentration is 1.75%, soak at 50 DEG C
Bubble 2 hours, then, filters, and clear water washing is then heated to 328 DEG C, is incubated 20min, then clear-cutting forestland to room temperature, crosses 200 mesh
Sieve, you can.
Further, the modified pearl rock micropowder is made up by weight of following component:Perlite powder 32, tea seed cake
Powder 2, camellia oleosa seed powder 1, tapioca 2, its preparation method is:After perlite powder is uniformly mixed with tea seed cake powder, add its mixing
Afterwards the deionized water of 3 times of quality, after stirring, using 300W microwave treatment 45s, while being stirred with 300r/min rotating speeds, stirs
The time is mixed for 15min, then adds camellia oleosa seed powder, tapioca, then it is 2.5% to add the mass concentration of tapioca quality 12%
Liquor natrii hypochloritises, after stirring, using being heated to 65 DEG C, are incubated 25min, then naturally cool to room temperature, are dried, then enter
Row grinding, crosses 200 mesh sieves, you can.
Further, the preparation method of the high-performance decorative panel is:
(1) dispensing is carried out by each Parts by Ingredients
(2) maleic rosin is preheated
Maleic rosin is heated to into 108 DEG C, 30min is incubated;
(3) slip is made
Bauxite, dolomite, blast-furnace cinder, cement, glass dust, stone needle powder, silicon powder and water are put in order, with 150r/min
Rotating speed, stirs 20min, then adds modified rosin rock and preheats the maleic rosin after finishing, and continues to stir 15min, makes institute
Need slip;
(4) into base
Slip is poured in shaping mould, is uniformly paved;After slip slightly gel, force pressurizing and dehydrating to make material base, pressurize
Pressure is 3.95MPa;
(5) decorative pattern is suppressed
To expecting that embryo surface carries out compacting decorative pattern;
(6) conserve
The material embryo for suppressing decorative pattern is placed at 110 DEG C, relative air humidity is 65%, pressure is in the environment of 0.79MPa
Maintenance 5 hours, is then placed on again at 92 DEG C, and relative air humidity is 50%, and pressure is to conserve 5 hours in the environment of 0.61MPa,
Obtain semi-finished product;
(7) trimming
The semi-finished product for having conserved are carried out into trimming;
(8) dry
Semi-finished product after trimming are dried to moisture content less than 11%, decorative panel is got product.
Beneficial effect of the present invention:The present invention adopt bauxite, dolomite, blast furnace slag synergism, enable to made by
Decorative panel has the premium properties of high-strength light, fire-proof and thermal-insulation, by the glass dust for adding 200 mesh, can greatly improve dress
The processing characteristics of plaque, modified rosin rock of the present invention coordinates the synergism of maleic rosin, not only greatly improves decorative panel
Intensity, also improve the resistance to compression shock-absorbing capacity of decorative panel, the entire compression of decorative panel, anti-scratch performance are significantly carried
Height, can for a long time ensure that plaque surface is injury-free, improve the use quality of decorative panel, ensure the use of decorative panel
Life-span, the synergism of the modified pearl rock micropowder prepared by the addition present invention can greatly improve decorative panel of the present invention
Heat preservation and soundproof performance, decorative panel of the present invention can be positioned over the outside in roof or house, and on the ceiling of burglary-resisting window
Face, so Sometimes When It Rains, tiny sound can directly be filtered, even if running into hail, heavy rain, sound also will not be too
Greatly, the ear-piercing sound will not be given people, the sleep quality of the indoor people of guarantee that can be good.
Specific embodiment
Embodiment 1
A kind of high-performance decorative panel, is made up of the raw material of following weight portion:Bauxite 18, dolomite 13, blast-furnace cinder 23, cement
11st, glass dust 12, stone needle powder 0.3, modified rosin rock 6, silicon powder 0.4, maleic rosin 0.4, modified pearl rock micropowder 5, water 22.
Embodiment 2
A kind of high-performance decorative panel, is made up of the raw material of following weight portion:Bauxite 22, dolomite 15, blast-furnace cinder 25, cement
13rd, glass dust 14, stone needle powder 0.5, modified rosin rock 9, silicon powder 0.7, maleic rosin 0.8, modified pearl rock micropowder 8, water 24.
Embodiment 3
A kind of high-performance decorative panel, is made up of the raw material of following weight portion:Bauxite 20, dolomite 14, blast-furnace cinder 24, cement
12nd, glass dust 13, stone needle powder 0.4, modified rosin rock 8, silicon powder 0.6, maleic rosin 0.5, modified pearl rock micropowder 7, water 23.
In above-described embodiment:
Further, the bauxite, dolomite, the granularity of blast furnace slag are 200 mesh.
Further, the granularity of the glass dust is 250 mesh.
Further, the modified rosin rock is made up by weight of following component:Pitchstone 22, andalusite powder 0.1,
Potassium feldspar 0.2, its preparation method is:Pitchstone is crossed into 150 mesh, andalusite powder and potassium feldspar are crossed into 180 mesh, by pitchstone, red
Pillar powder and potassium feldspar are uniformly admixed together, in being added to the Monosodium maleate solution that mass concentration is 1.75%, soak at 50 DEG C
Bubble 2 hours, then, filters, and clear water washing is then heated to 328 DEG C, is incubated 20min, then clear-cutting forestland to room temperature, crosses 200 mesh
Sieve, you can.
Further, the modified pearl rock micropowder is made up by weight of following component:Perlite powder 32, tea seed cake
Powder 2, camellia oleosa seed powder 1, tapioca 2, its preparation method is:After perlite powder is uniformly mixed with tea seed cake powder, add its mixing
Afterwards the deionized water of 3 times of quality, after stirring, using 300W microwave treatment 45s, while being stirred with 300r/min rotating speeds, stirs
The time is mixed for 15min, then adds camellia oleosa seed powder, tapioca, then it is 2.5% to add the mass concentration of tapioca quality 12%
Liquor natrii hypochloritises, after stirring, using being heated to 65 DEG C, are incubated 25min, then naturally cool to room temperature, are dried, then enter
Row grinding, crosses 200 mesh sieves, you can.
Further, the preparation method of the high-performance decorative panel is:
(1) dispensing is carried out by each Parts by Ingredients
(2) maleic rosin is preheated
Maleic rosin is heated to into 108 DEG C, 30min is incubated;
(3) slip is made
Bauxite, dolomite, blast-furnace cinder, cement, glass dust, stone needle powder, silicon powder and water are put in order, with 150r/min
Rotating speed, stirs 20min, then adds modified rosin rock and preheats the maleic rosin after finishing, and continues to stir 15min, makes institute
Need slip;
(4) into base
Slip is poured in shaping mould, is uniformly paved;After slip slightly gel, force pressurizing and dehydrating to make material base, pressurize
Pressure is 3.95MPa;
(5) decorative pattern is suppressed
To expecting that embryo surface carries out compacting decorative pattern;
(6) conserve
The material embryo for suppressing decorative pattern is placed at 110 DEG C, relative air humidity is 65%, pressure is in the environment of 0.79MPa
Maintenance 5 hours, is then placed on again at 92 DEG C, and relative air humidity is 50%, and pressure is to conserve 5 hours in the environment of 0.61MPa,
Obtain semi-finished product;
(7) trimming
The semi-finished product for having conserved are carried out into trimming;
(8) dry
Semi-finished product after trimming are dried to moisture content less than 11%, decorative panel is got product.
Modified rosin rock addition and the relation of decorative panel intensity of the present invention that the present invention is prepared:
Table 1
Addition(Weight portion) | Rupture strength(MPa) | Impact strength(KJ/m²) |
0 | 8.34 | 1.32 |
3 | 10.60 | 1.64 |
6 | 13.26 | 1.95 |
9 | 13.44 | 1.97 |
10 | 12.98 | 1.87 |
9(Without maleic rosin) | 12.14 | 1.79 |
The modified rosin rock addition that as can be seen from Table 1 present invention is prepared is in certain limit to the anti-folding of decorative panel of the present invention
Intensity is significantly improved with impact strength tool.
After testing, the decorative panel bulking factor of embodiment 1 is 0.16%, and percent thermal shrinkage is 0.91%, the decorative panel bulking factor of embodiment 2
For 0.15%, percent thermal shrinkage is 0.90%, and the decorative panel bulking factor of embodiment 3 is 0.17%, and percent thermal shrinkage is 0.91%, and embodiment 1 is filled
When plaque is without modified pearl rock micropowder, bulking factor is 0.20%, and percent thermal shrinkage is 1.02%, shows the modified of present invention preparation
Perlite powder has obvious inhibition to the bulking factor and percent thermal shrinkage of decorative panel.
Through detection, specification can compared to common decorative for the decorative panel of the present invention of 2440mm × 1220mm × 1.5mm
Increase by 12 decibels or so of oise insulation factor;When the decoration that modified pearl rock micropowder in the present invention is substituted for the preparation of ordinary pearl rock micropowder
Plate can only increase by 7 decibels or so of oise insulation factor compared to common decorative.
Claims (6)
1. a kind of high-performance decorative panel, it is characterised in that be made up of the raw material of following weight portion:Bauxite 18-22, dolomite
13-15, blast-furnace cinder 23-25, cement 11-13, glass dust 12-14, stone needle powder 0.3-0.5, modified rosin rock 6-9, silicon powder
0.4-0.7, maleic rosin 0.4-0.8, modified pearl rock micropowder 5-8, water 22-24.
2. a kind of high-performance decorative panel according to claim 1, it is characterised in that the bauxite, dolomite, blast furnace slag
Granularity be 200 mesh.
3. a kind of high-performance decorative panel according to claim 1, it is characterised in that the granularity of the glass dust is 250 mesh.
4. a kind of high-performance decorative panel according to claim 1, it is characterised in that the modified rosin rock is by weight
It is made up of following component:Pitchstone 22, andalusite powder 0.1, potassium feldspar 0.2, its preparation method is:Pitchstone is crossed into 150 mesh, will
Andalusite powder crosses 180 mesh with potassium feldspar, and pitchstone, andalusite powder and potassium feldspar is uniformly admixed together, is added to quality dense
In spending the Monosodium maleate solution for 1.75%, soak at 50 DEG C 2 hours, then, filter, clear water washing is then heated to 328
DEG C, 20min, then clear-cutting forestland are incubated to room temperature, cross 200 mesh sieves, you can.
5. a kind of high-performance decorative panel according to claim 1, it is characterised in that the modified pearl rock micropowder is by weight
Part meter is made up of following component:Perlite powder 32, tea seed cake powder 2, camellia oleosa seed powder 1, tapioca 2, its preparation method is:By Margarita
After rock micropowder uniformly mixes with tea seed cake powder, add the deionized water of 3 times of quality after its mixing, it is micro- using 300W after stirring
Ripple processes 45s, while with the stirring of 300r/min rotating speeds, mixing time is 15min, then adds camellia oleosa seed powder, tapioca, then adds
With tapioca quality 12% mass concentration be 2.5% liquor natrii hypochloritises, after stirring, using being heated to 65 DEG C, protect
Warm 25min, then naturally cools to room temperature, is dried, then is ground, and crosses 200 mesh sieves, you can.
6. a kind of high-performance decorative panel according to any one of claim 1-5, it is characterised in that the high-performance decorative panel
Preparation method be:
(1) dispensing is carried out by each Parts by Ingredients
(2) maleic rosin is preheated
Maleic rosin is heated to into 108 DEG C, 30min is incubated;
(3) slip is made
Bauxite, dolomite, blast-furnace cinder, cement, glass dust, stone needle powder, silicon powder and water are put in order, with 150r/min
Rotating speed, stirs 20min, then adds modified rosin rock and preheats the maleic rosin after finishing, and continues to stir 15min, makes institute
Need slip;
(4) into base
Slip is poured in shaping mould, is uniformly paved;After slip slightly gel, force pressurizing and dehydrating to make material base, pressurize
Pressure is 3.95MPa;
(5) decorative pattern is suppressed
To expecting that embryo surface carries out compacting decorative pattern;
(6) conserve
The material embryo for suppressing decorative pattern is placed at 110 DEG C, relative air humidity is 65%, pressure is in the environment of 0.79MPa
Maintenance 5 hours, is then placed on again at 92 DEG C, and relative air humidity is 50%, and pressure is to conserve 5 hours in the environment of 0.61MPa,
Obtain semi-finished product;
(7) trimming
The semi-finished product for having conserved are carried out into trimming;
(8) dry
Semi-finished product after trimming are dried to moisture content less than 11%, decorative panel is got product.