CN106637581A - Three-layer worsted fabric and finishing method thereof - Google Patents
Three-layer worsted fabric and finishing method thereof Download PDFInfo
- Publication number
- CN106637581A CN106637581A CN201611138976.0A CN201611138976A CN106637581A CN 106637581 A CN106637581 A CN 106637581A CN 201611138976 A CN201611138976 A CN 201611138976A CN 106637581 A CN106637581 A CN 106637581A
- Authority
- CN
- China
- Prior art keywords
- layers
- worsted fabric
- layer
- worsted
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a three-layer worsted fabric and a finishing method thereof. The three-layer worsted fabric comprises a surface layer, a middle layer and an inner layer. The surface layer and the middle layer are arranged with a pure wool worsted yarn, and the inner layer is arranged with a wool/ bamboo charcoal fiber and twisted yarn. The surface layer comprises the table warp yarn and the table weft yarn, the middle layer comprises the middle warp yarn and the middle weft yarn, and the inner layer comprises the inner weft yarn. The three-layer worsted fabric and the finishing method thereof utilizes the wet permeability and quick drying of the bamboo charcoal fiber to promote the water vapor and the sweat to excrete to the outside through the middle layer and the surface layer. High warmth is achieved through the air layer microcirculation between the layer and the layer, and the three-layer structure is stable and the fabric size is good in stability. The three-layer worsted fabric also has good sewing processability, odor resistant and anti-ultraviolet performance.
Description
Technical field
The present invention relates to textile technology field, more particularly to a kind of three layers of worsted fabric and its afterfinish method.
Background technology
With the continuous improvement of people's living standard, people are also on the increase for the requirement of worsted fabric, and this is not only
Show in the requirement of physical index, and show in the requirement to its style and function.Existing conventional autumn and winter Worsted
Fabric mostly is simple tissue fabric.So-called simple tissue fabric, refers to the weft yarn structure of warp thread by a system and a system
Into.When yarn is thinner used by fabric, the application of simple tissue can not realize the style that abundant and surface exquisiteness has both, and knit
Thing structural stability is poor, is also easy to produce wrinkle.In addition, though conventional autumn and winter worsted fabric can take hydroscopic fast-drying to arrange, with
Using the increase with wash time, the effect of hydroscopic fast-drying gradually weakens.Therefore, the size for how improving worsted fabric is steady
It is qualitative, and lasting hydroscopic fast-drying characteristic is made it have, it is technical problem urgently to be resolved hurrily at present.
The content of the invention
The present invention provides a kind of three layers of worsted fabric and its afterfinish method, to solve existing worsted fabric chi
Very little stability and the poor problem of hydroscopic fast-drying.
In order to solve the above problems, the invention provides a kind of three layers of worsted fabric, including top layer, middle level, nexine, institute
State top layer and the middle level and configure the pure wool spun yarn of 60 public affairs/2, hair/bamboo-carbon fibre that the nexine configuration 60 is public/2
And twist yarn；The top layer is interwoven by table warp thread with outer weft yarn, and the middle level is formed by middle warp thread with middle weft yarns, described
Nexine is interwoven by back warp yarn with back weft yarn；The middle warp thread connects the outer weft yarn and the back weft yarn.
Preferably, the top layer, middle level, the wool fibre total content of nexine reach 70%～85%, bamboo-carbon fibre total content
Reach 15%～30%.
Preferably, the total content of wool fibre and the ratio of the total content of bamboo-carbon fibre are 4 in three layers of worsted fabric:1.
Preferably, it is 730/10cm-780 roots/10cm that the Jing of three layers of worsted fabric is close, filling density is 756/
10cm-766 roots/10cm, weight is 408g/m2-468g/m2。
Preferably, the longitude and latitude tightness ratio of three layers of worsted fabric is 1.2：1.
Present invention also offers a kind of afterfinish method of three layers of worsted fabric, comprises the steps：There is provided just like power
Profit requires three layers of worsted fabric any one of 1-5；First time braying is carried out to three layers of worsted fabric；To Jing
Crossing three layers of worsted fabric of first time braying carries out first time crabbing；Three layers of worsted fabric through first time crabbing are entered
Second braying of row；Second crabbing is carried out to three layers of worsted fabric through second braying；To through second crabbing
Three layers of worsted fabric carry out decatizing；Thermal finalization is carried out to three layers of worsted fabric through decatizing；To through thermal finalization
Three layers of worsted fabric carry out dewing.
Preferably, when carrying out first time braying to three layers of worsted fabric, temperature of soaping is 40 DEG C -45 DEG C, bath raio
For 1：(5～8), process time is 45 minutes.
Preferably, to when three layers of worsted fabric of first time braying carry out first time crabbing, temperature is 95 DEG C, place
The reason time is 20 minutes.
Preferably, to when three layers of worsted fabric of second braying carry out second crabbing, temperature is 95 DEG C, place
The reason time is 60 minutes, and 100 milliliters of 98% acetic acid is added during crabbing.
Preferably, the concrete steps that three layers of worsted fabric through second crabbing carry out decatizing are included：To passing through
Three layers of worsted fabric of second crabbing carry out first time decatize 10 minutes, and take out cold 10 minutes；To through above-mentioned process
Three layers of worsted fabric carries out second decatize 15 minutes, and takes out cold 20 minutes.
Three layers of worsted fabric and its afterfinish method that the present invention is provided, by three layers of worsted fabric
Table, in, nexine be respectively configured the botany with different hydroscopic fast-drying effects, wherein top layer, middle level configuration 60 public/2
Pure wool worsted yarn, 60 public/2 maos/bamboo fibres of nexine configuration and twist yarn, using leading for bamboo-carbon fibre be wet, quick-drying, promote water
Steam, sweat are derived to the external world by middle level, top layer, realize quick-drying；By air layer microcirculation between layers, realize high
Warmth retention property；And three-layer weave Stability Analysis of Structures, dimensional stability for fabric is good；Simultaneously using afterfinish method of the present invention to institute
Stating three layers of worsted fabric carries out Final finishing so as to preferably sewing processability, anti-peculiar smell, antiultraviolet.
Description of the drawings
Accompanying drawing 1 is the dimensional structure diagram of three layers of worsted fabric of the specific embodiment of the invention；
Accompanying drawing 2 is the transverse cross-sectional view of three layers of worsted fabric of the specific embodiment of the invention；
Accompanying drawing 3 is the radial cutaway view of three layers of worsted fabric of the specific embodiment of the invention；
Accompanying drawing 4 is the afterfinish method flow chart of three layers of worsted fabric of the specific embodiment of the invention.
Specific embodiment
The present invention is provided three layers of worsted fabric below in conjunction with the accompanying drawings and its specific embodiment of afterfinish method
Elaborate.
This specific embodiment provides a kind of three layers of worsted fabric, and accompanying drawing 1 is the three of the specific embodiment of the invention
The dimensional structure diagram of layer worsted fabric, accompanying drawing 2 is the horizontal of three layers of worsted fabric of the specific embodiment of the invention
Profile, accompanying drawing 3 is the radial cutaway view of three layers of worsted fabric of the specific embodiment of the invention.
As Figure 1-3, three layers of worsted fabric include top layer 1, middle level 2, nexine 3, the top layer 1 and it is described in
The pure wool spun yarn of the configuration 60 public/2 of layer 2, hair/bamboo-carbon fibres that the configuration of the nexine 3 60 is public/2 and twist yarn (i.e. hair with
Bamboo-carbon fibre and twist yarn)；The top layer 1 is interwoven by table warp thread with outer weft yarn 13, and the middle level 2 is by middle warp thread and middle weft yarn
23 are interwoven, and the nexine 3 is interwoven by back warp yarn with back weft yarn 33；The middle warp thread connects the outer weft yarn 13 and institute
Back weft yarn 33 is stated, so as to the top layer 1, the middle level 2 and the nexine 3 are connected to become into an entirety.Wherein, the pure sheep
Wool worsted yarn is 82 sth. made by twisting/10cm with the twist of the wool/bamboo-carbon fibre and twist yarn.The pure wool spun yarn is to contaminate wool
Color, recombing are simultaneously carded to vitta, by vitta drawing-off, plus are twisted rove, then make ring spinning spun yarn；Hair/bamboo charcoal is fine
Simultaneously twist yarn is the complex yarn for processing pure wool spun yarn and hydroscopic fast-drying bamboo charcoal polyester filament yarn by doubler twister to dimension.Its
In, the nexine not only can adopt hair/bamboo-carbon fibre and twist yarn, can also be fine with other moisture absorbing and sweat releasing blending using other hairs
Dimension, this specific embodiment is not especially limited to this, and those skilled in the art can be selected according to actual needs.It is preferred that
, the top layer 1, the middle level 2, the nexine 3 are plain weave, it is also possible to replaced with twill-weave, satin weave etc..By
This, compared with individual layer, bilayer, three layers of worsted fabric structure that this specific embodiment is provided are more stable, are to improve product chi
Very little stability is provided convenience condition.
In order to further improve the dimensional stability of three layers of worsted fabric, it is preferred that the top layer, middle level, inner
The wool fibre total content of layer reaches 70%～85%, and bamboo-carbon fibre total content reaches 15%～30%.It is furthermore preferred that described three layers
The total content of wool fibre and the ratio of the total content of bamboo-carbon fibre are 4 in worsted fabric:1.Three layers described in this specific embodiment
It is 730/10cm-780 roots/10cm that the Jing of worsted fabric is close, and filling density is 756/10cm-766 roots/10cm, and weight is
408g/m2-468g/m2.The longitude and latitude tightness ratio of three layers of worsted fabric is 1.2: 1.Wherein, the longitude and latitude tightness ratio, refers to
The ratio of yarns in worsted fabric projected area and fabric entire area.Thus, the dimensional stability of three layers of worsted fabric of formation
Most preferably, Moisture absorbing ＆ quick drying property is preferably also.
This specific embodiment provide three layers of worsted fabric, by the table of three layers of worsted fabric, in, it is inner
Layer is respectively configured the botany of different hydroscopic fast-drying effects, wherein top layer, the botany of the public affairs/2 of middle level configuration 60, nexine
Public/2 maos/bamboo fibres of configuration 60 and twist yarn, using bamboo-carbon fibre lead wet, quick-drying or by middle level, top layer derive it is external or
The external world, realizes quick-drying；Air layer microcirculation between layers, realizes warming；Three-layer weave Stability Analysis of Structures, fabric size is stable
Property is good.
Moreover, this specific embodiment additionally provides a kind of Final finishing side for above-mentioned three layers of worsted fabric
Method, accompanying drawing 4 is the afterfinish method flow chart of three layers of worsted fabric of the specific embodiment of the invention.As shown in figure 4, this tool
The afterfinish method of three layers of worsted fabric that body embodiment is provided comprises the steps：
Step S41, there is provided three layers of above-mentioned worsted fabric.
Step S42, to three layers of worsted fabric first time braying is carried out.Is carried out to three layers of worsted fabric
During braying, temperature of soaping is 40 DEG C -45 DEG C, and bath raio is 1：(5～8), process time is 45 minutes.The first time braying
It is, in order to clean the greasy dirt on greasy fabric, dust, impurity etc., to obtain clean, uniform greasy fabric, it is preliminary to obtain with soft and full
The fabric of feel and intrinsic elasticity.
Three layers of worsted fabric through first time braying are carried out first time crabbing by step S43.To through washing for the first time
Three layers of worsted fabric when carrying out first time crabbing, temperature is 95 DEG C, and process time is 20 minutes, small tension receiving coil.Described
Crabbing causes three layers of worsted fabric under the effect of certain temperature, humidity, time, tension force and pressure, reaches just
Step fixed effect.After the completion of first time crabbing step, after three layers of worsted fabric is progressively cooled to into 45 DEG C, then enter
Row next step.
Three layers of worsted fabric through first time crabbing are carried out second braying by step S44.Second braying
Process conditions it is identical with the process conditions of first time braying, that is, temperature of soaping be 40 DEG C -45 DEG C, bath raio is 1: (5～8), place
The reason time is 45 minutes.Second braying is profound cleaning, is rich in order to increase by three layers of worsted fabric softness
Thick handle effect.
Three layers of worsted fabric through second braying are carried out second crabbing by step S45.To washing through for the second time
Three layers of worsted fabric when carrying out second crabbing, temperature is 95 DEG C, and process time is 60 minutes, and during crabbing
Add 100 milliliters of 98% acetic acid, small tension receiving coil, natural cooling 8 hours.Second crabbing is in order to three layers of Worsted
Fabric is further shaped, and increases dimensional stability for fabric, lifts fabric feeling, gloss, elasticity.
Three layers of worsted fabric through second crabbing are carried out decatizing by step S45.To through the three of second crabbing
Layer worsted fabric carries out the concrete steps of decatizing to be included：Three layers of worsted fabric through second crabbing are carried out for the first time
Decatize 10 minutes, and take out cold 10 minutes；Three layers of worsted fabric through above-mentioned process are carried out with second decatize 15 minutes, and
Take out cold 20 minutes.Three layers of worsted fabric under tension force, pressure state, determined by the decatize, cooling through certain hour
Shape effect, promotes feel, gloss, elasticity and dimensional stability.
Three layers of worsted fabric through decatizing are carried out thermal finalization by step S47.In the heat-setting process, temperature
At 170 DEG C, process time is 3 seconds for control.The step is used to remove existing fine wrinkle on three layers of worsted fabric, improves institute
The dimensional stability of three layers of worsted fabric is stated, and makes it be not likely to produce the fine wrinkle for being difficult to remove.
Three layers of worsted fabric through thermal finalization are carried out dewing by step S48.The step causes three layers of worsted fabric
Certain regain is reached, to improve the decatizing effect of decatizing or voltage.
The longitude and latitude decatize shrinkage factor scope of existing combing worsted spinning (FZ/T24002-1993) high-class product be -1.0%～
1.5%.And the decatize contraction test result through three layers of worsted fabric of above-mentioned Final finishing process is：Through 30S decatizes,
Fabric warp-wise shrinkage factor is 0 after the 30s types of cooling circulate 3 times, and broadwise shrinkage factor is 1.25%.As can be seen here, it is concrete using this
After three layers of worsted fabric of embodiment offer and the afterfinish method carried out to it described in this specific embodiment are processed, institute
The dimensional stability for stating worsted fabric is improved.Moreover, the Final finishing side for providing through this specific embodiment
The warming rate of three layers of worsted fabric after method process is 32.5%, higher than the warming rate of current conventional cold-proof underwear
(30%).
Three layers of worsted fabric and its afterfinish method that the present invention is provided, by three layers of worsted fabric
Table, in, nexine be respectively configured the botany with different hydroscopic fast-drying effects, wherein top layer, middle level configuration 60 public/2
Pure wool worsted yarn, 60 public/2 maos/bamboo fibres of nexine configuration and twist yarn, using leading for bamboo-carbon fibre be wet, quick-drying, promote water
Steam, sweat are derived to the external world by middle level, top layer, realize quick-drying；By air layer microcirculation between layers, realize high
Warmth retention property；And three-layer weave Stability Analysis of Structures, dimensional stability for fabric is good；Simultaneously using afterfinish method of the present invention to institute
Stating three layers of worsted fabric carries out Final finishing so as to preferably sewing processability, anti-peculiar smell, antiultraviolet.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
Member, under the premise without departing from the principles of the invention, can also make some improvements and modifications, and these improvements and modifications also should be regarded as
Protection scope of the present invention.
Claims (10)
1. a kind of three layers of worsted fabric, it is characterised in that including top layer, middle level, nexine, the top layer and the middle level are matched somebody with somebody
Put the pure wool spun yarn of 60 public/2, hair/bamboo-carbon fibre that the nexine configuration 60 is public/2 and twist yarn；The top layer is by table Jing
Yarn is interwoven with outer weft yarn, and the middle level is formed by middle warp thread with middle weft yarns, and the nexine is by back warp yarn and back weft yarn
It is interwoven；The middle warp thread connects the outer weft yarn and the back weft yarn.
2. three layers of worsted fabric according to claim 1, it is characterised in that the top layer, middle level, the wool fibre of nexine
Total content reach 70%～85%, bamboo-carbon fibre total content reaches 15%～30%.
3. three layers of worsted fabric according to claim 1, it is characterised in that wool fibre in three layers of worsted fabric
The ratio of total content of total content and bamboo-carbon fibre be 4:1.
4. three layers of worsted fabric according to claim 1, it is characterised in that the Jing of three layers of worsted fabric is close to be
730/10cm-780 roots/10cm, filling density is 756/10cm-766 roots/10cm, and weight is 408g/m2-468g/m2。
5. three layers of worsted fabric according to claim 1, it is characterised in that the longitude and latitude of three layers of worsted fabric is tight
Degree is than being 1.2：1.
6. a kind of afterfinish method of three layers of worsted fabric, it is characterised in that comprise the steps：
There is provided just like three layers of worsted fabric any one of claim 1-5；
First time braying is carried out to three layers of worsted fabric；
First time crabbing is carried out to three layers of worsted fabric through first time braying；
Second braying is carried out to three layers of worsted fabric through first time crabbing；
Second crabbing is carried out to three layers of worsted fabric through second braying；
Decatizing is carried out to three layers of worsted fabric through second crabbing；
Thermal finalization is carried out to three layers of worsted fabric through decatizing；
Dewing is carried out to three layers of worsted fabric through thermal finalization.
7. the afterfinish method of three layers of worsted fabric according to claim 6, it is characterised in that spinning to described three layers
When wool fabric carries out first time braying, temperature of soaping is 40 DEG C -45 DEG C, and bath raio is 1：(5～8), process time is 45 minutes.
8. the afterfinish method of three layers of worsted fabric according to claim 6, it is characterised in that to through washing for the first time
Three layers of worsted fabric when carrying out first time crabbing, temperature is 95 DEG C, and process time is 20 minutes.
9. the afterfinish method of three layers of worsted fabric according to claim 6, it is characterised in that to washing through for the second time
Three layers of worsted fabric when carrying out second crabbing, temperature is 95 DEG C, and process time is 60 minutes, and during crabbing
Add 100 milliliters of 98% acetic acid.
10. the afterfinish method of three layers of worsted fabric according to claim 6, it is characterised in that to through second
The concrete steps that three layers of worsted fabric of crabbing carry out decatizing include：
First time decatize is carried out 10 minutes to three layers of worsted fabric through second crabbing, and is taken out cold 10 minutes；
Three layers of worsted fabric through above-mentioned process are carried out with second decatize 15 minutes, and taken out cold 20 minutes.