CN106637217A - Polishing grease for valve handle casting - Google Patents
Polishing grease for valve handle casting Download PDFInfo
- Publication number
- CN106637217A CN106637217A CN201611166506.5A CN201611166506A CN106637217A CN 106637217 A CN106637217 A CN 106637217A CN 201611166506 A CN201611166506 A CN 201611166506A CN 106637217 A CN106637217 A CN 106637217A
- Authority
- CN
- China
- Prior art keywords
- parts
- polishing
- heated
- nano
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a polishing grease for a valve handle casting, and relates to the technical field of polishing agents. The polishing grease is prepared from the following raw materials in parts by weight: 30-40 parts of quartz sand, 12-17 parts of hydrogenated rosin, 10-15 parts of paraffin oil, 8-12 parts of sodium carboxymethylcellulose, 8-12 parts of palm wax, 6-10 parts of soybean phospholipids, 5-8 parts of modified sea-foam stone powder, 4-6 parts of polyacrylamide, 3-5 parts of nano-alumina, 2-4 parts of cetostearyl alcohol, 1-2 parts of nano-cuprous oxide, 10-15 parts of polyethylene glycol and 35-40 parts of ethyl alcohol. The polishing grease disclosed by the invention is proper in viscosity, capable of being uniformly coated on the surface of a handle, beneficial to the progress of a polishing process and capable of adequately improving the polishing effect; and moreover, the polishing grease has an antirust function for the polished surface of the handle, thus improving the quality of the surface of the handle.
Description
Technical field：
The present invention relates to polishing agent technical field, and in particular to a kind of valve handle foundry goods polishing fat.
Background technology：
Valve has cut-off, regulation, water conservancy diversion, prevents the functions such as adverse current, voltage stabilizing, shunting or overflow pressure relief, generally all adopts
Handwheel control valve.Handwheel cast(ing) surface after cast has some raised burrs and impression, makes rough surface uneven, such as
It is not processed by shot blasting to directly affect and uses feel, hand can be damaged when serious.Common finishing method is using grinding tool pair
Handwheel foundry goods is polished, but there is a problem of that polishing effect is poor, reduces product size precision.
The content of the invention：
The technical problem to be solved is to provide a kind of valve handle foundry goods for having lubrication and antirust function concurrently
With polishing fat.
The technical problem to be solved is realized using following technical scheme：
A kind of valve handle foundry goods polishing fat, is made up of the raw material of following parts by weight：
Quartz sand 30-40 parts, hydrogenated rosin 12-17 parts, paraffin oil 10-15 parts, sodium carboxymethylcellulose 8-12 parts, palm
Wax 8-12 parts, soybean lecithin 6-10 parts, modified meerschaum powder 5-8 parts, polyacrylamide 4-6 parts, nano aluminium oxide 3-5 parts, whale
Wax stearyl alcohol 2-4 parts, nano cuprous oxide 1-2 parts, polyethylene glycol 10-15 parts, ethanol 35-40 parts；
Its preparation method is as follows：
(1) first hydrogenated rosin is dissolved in ethanol, adds palm wax and nano aluminium oxide, mixture is heated to backflow
State isothermal holding 15min, obtains final product material I；
(2) soybean lecithin and polyacrylamide are added in paraffin oil, 60-70 DEG C of insulation mixing 10min is heated to, then is added
Enter cetostearyl alcohol, continue to be heated to 90-100 DEG C of insulation mixing 10min, obtain final product material II；
(3) material II, quartz sand, sodium carboxymethylcellulose, modified meerschaum powder, nano oxidized Asia are added in material I
Copper and polyethylene glycol, be sufficiently mixed it is uniform, most after Jing ball mills be milled to fineness less than 50 μm.
The preparation method of the modified meerschaum powder is：6-10 part nano-graphites are added in 100-120 part sepiolite powders
Powder and 3-5 part nanometer rubber powders, are first heated to 70-80 DEG C of grinding 10min, are again heated to 100-110 degree Celsius of grinding 5min, treat certainly
2-4 parts Sodium Polyacrylate and 7-12 part stearic acid, insulation grinding 15min is added finally to mix gained after being so cooled to 40-50 DEG C
Compound calcines 3h at 300-350 DEG C.
The invention has the beneficial effects as follows：The present invention is aided with several functions and helps with quartz sand and hydrogenated rosin as primary raw material
Agent is obtained valve handle foundry goods polishing fat, and the polishing fat viscosity is suitable, handwheel surface can be evenly applied to, beneficial to polishing process
Carrying out and fully improve polishing effect, and there is rust inhibition to the handwheel surface after polishing, so as to improve handwheel surface
Quality.
Specific embodiment：
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) first 12 parts of hydrogenated rosins are dissolved in 35 parts of ethanol, add 8 parts of palm waxs and 3 parts of nano aluminium oxides, mixed
Compound is heated to reflux state isothermal holding 15min, obtains final product material I；
(2) 8 parts of soybean lecithins and 4 parts of polyacrylamides are added in 12 parts of paraffin oils, 60-70 DEG C of insulation mixing is heated to
10min, adds 3 parts of cetostearyl alcohols, continues to be heated to 90-100 DEG C of insulation mixing 10min, obtains final product material II；
(3) add in material I material II, 30 parts of quartz sand, 10 parts of sodium carboxymethylcelluloses, 5 parts of modified meerschaum powder,
1 part of nano cuprous oxide and 10 parts of polyethylene glycol, be sufficiently mixed it is uniform, most after Jing ball mills be milled to fineness less than 50 μm.
The preparation of modified meerschaum powder：6 parts of Nano graphite powders and 3 parts of nanometer rubber powders are added in 100 parts of sepiolite powders, first
70-80 DEG C of grinding 10min is heated to, 100-110 degree Celsius of grinding 5min is again heated to, is added after naturally cool to after 40-50 DEG C
Enter 4 parts of Sodium Polyacrylates and 8 parts of stearic acid, gained mixture is finally calcined 3h by insulation grinding 15min at 300-350 DEG C.
Embodiment 2
(1) first 16 parts of hydrogenated rosins are dissolved in 40 parts of ethanol, add 10 parts of palm waxs and 4 parts of nano aluminium oxides,
Mixture is heated to reflux state isothermal holding 15min, obtains final product material I；
(2) 6 parts of soybean lecithins and 6 parts of polyacrylamides are added in 15 parts of paraffin oils, 60-70 DEG C of insulation mixing is heated to
10min, adds 4 parts of cetostearyl alcohols, continues to be heated to 90-100 DEG C of insulation mixing 10min, obtains final product material II；
(3) add in material I material II, 40 parts of quartz sand, 8 parts of sodium carboxymethylcelluloses, 6 parts of modified meerschaum powder, 2
Part nano cuprous oxide and 15 parts of polyethylene glycol, be sufficiently mixed it is uniform, most after Jing ball mills be milled to fineness less than 50 μm.
The preparation of modified meerschaum powder：8 parts of Nano graphite powders and 5 parts of nanometer rubber powders are added in 120 parts of sepiolite powders, first
70-80 DEG C of grinding 10min is heated to, 100-110 degree Celsius of grinding 5min is again heated to, is added after naturally cool to after 40-50 DEG C
Enter 3 parts of Sodium Polyacrylates and 10 parts of stearic acid, insulation grinding 15min finally calcines gained mixture at 300-350 DEG C
3h。
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (2)
1. a kind of valve handle foundry goods is used and polishes fat, it is characterised in that be made up of the raw material of following parts by weight：
Quartz sand 30-40 parts, hydrogenated rosin 12-17 parts, paraffin oil 10-15 parts, sodium carboxymethylcellulose 8-12 parts, palm wax 8-
12 parts, soybean lecithin 6-10 parts, modified meerschaum powder 5-8 parts, polyacrylamide 4-6 parts, nano aluminium oxide 3-5 parts, spermaceti it is hard
Lipidol 2-4 parts, nano cuprous oxide 1-2 parts, polyethylene glycol 10-15 parts, ethanol 35-40 parts；
Its preparation method is as follows：
(1) first hydrogenated rosin is dissolved in ethanol, adds palm wax and nano aluminium oxide, mixture is heated to reflux state
Isothermal holding 15min, obtains final product material I；
(2) soybean lecithin and polyacrylamide are added in paraffin oil, 60-70 DEG C of insulation mixing 10min is heated to, whale is added
Wax stearyl alcohol, continues to be heated to 90-100 DEG C of insulation mixing 10min, obtains final product material II；
(3) in material I add material II, quartz sand, sodium carboxymethylcellulose, modified meerschaum powder, nano cuprous oxide and
Polyethylene glycol, be sufficiently mixed it is uniform, most after Jing ball mills be milled to fineness less than 50 μm.
2. valve handle foundry goods according to claim 1 is used and polishes fat, it is characterised in that the system of the modified meerschaum powder
Preparation Method is：6-10 parts Nano graphite powder and 3-5 part nanometer rubber powders are added in 100-120 part sepiolite powders, 70- is first heated to
80 DEG C of grinding 10min, are again heated to 100-110 degree Celsius of grinding 5min, gather after naturally cool to 2-4 parts are added after 40-50 DEG C
PAA and 7-12 part stearic acid, insulation grinding 15min, finally calcine 3h by gained mixture at 300-350 DEG C.