CN105018935A - Metalware buffing compound and preparing method thereof - Google Patents
Metalware buffing compound and preparing method thereof Download PDFInfo
- Publication number
- CN105018935A CN105018935A CN201510483643.0A CN201510483643A CN105018935A CN 105018935 A CN105018935 A CN 105018935A CN 201510483643 A CN201510483643 A CN 201510483643A CN 105018935 A CN105018935 A CN 105018935A
- Authority
- CN
- China
- Prior art keywords
- parts
- metalware
- water
- polish
- fatty acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a metalware buffing compound and a preparing method thereof. The buffing compound comprises, by weight, 10-15 parts of bentonite, 20-30 parts of coconut oil fatty acid, 120-150 parts of quartz sand, 5-10 parts of paraffin oil, 2-6 parts of turpentine oil, 20-30 parts of calcium carbonate, 10-20 parts of alcohol, 20-30 parts of ammonium hydroxide and 360-400 parts of water. The preparing method of the metalware buffing compound comprises the steps that the ammonium hydroxide is dissolved in one third of the water; the coconut oil fatty acid is added, and stirring is continuously carried out until an ointment object is formed; then the bentonite is added into the residual hot water and stirred to be dispersed; the ointment object is added, and the mixture is stirred continuously to be evenly dispersed; and the rest of the components are added; and the buffing compound is obtained after even stirring is carried out. After metalware is wiped through the buffing compound, surface dirt can be removed, and the original gloss of the metalware can be restored.
Description
Technical field
The invention belongs to chemical products field, particularly a kind of metalware polish and preparation method thereof.
Background technology
Household metal kitchen tools, ornaments are long placed in atmosphere, can be subject to the erosion of the hydrogen sulfide in air, moisture and other compositions, slowly can be oxidized blackening, even form black patches, tarnish on its surface.Metal cleaner on existing market, there is pulvis, mainly based on friction, remove blackspot and the dirt of metallic surface, rinse well with water again, there is aqua, as patent application (200610096773X) a kind of cleaning agent for dinnerware, patent (CN2008100460156) a kind of metal watch table cleaning agent of grease stain and using method thereof, all based on the greasy dirt on clean metal surface, adopt by force compared with acid or alkali clean greasy dirt, this method inherently easily causes the oxygenizement of inhibition for metallic surface, make metallic surface promote gloss, present corvinus.And some lustering agent is for leatherware, its cortex and metal all have gap in hardness and weave construction, can not use with.
Summary of the invention
The object of the invention is to provide a kind of metalware polish and preparation method thereof to overcome above the deficiencies in the prior art.
The present invention is realized by following technique means:
A kind of metalware polish, comprises wilkinite 10-15 part in components by weight percent, coco-nut oil fatty acid 20-30 part, quartz sand 120-150 part, paraffin oil 5-10 part, turps 2-6 part, calcium carbonate 20-30 part, alcohol 10-20 part, ammoniacal liquor 20-30 part, water 360-400 part.
Described metalware polish, preferably comprises wilkinite 12-14 part in components by weight percent, coco-nut oil fatty acid 26-29 part, quartz sand 135-143 part, paraffin oil 6-8 part, turps 3-5 part, calcium carbonate 26-28 part, alcohol 12-16 part, ammoniacal liquor 25-29 part, water 380-390 part.
The preparation method of the metalware polish described in more than one, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 60-70 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
In wiping process, this product of aqueous-based form using wilkinite as abrasive material, the greasy dirt of decontamination metallic surface, alcohol, ammoniacal liquor can in and oxide compound (the crow point of metallic surface is mainly oxide compound), go crow to return newly metallic surface.Coco-nut oil fatty acid in this product and turps mixing, generate tough and tensile film, leaves the film of one deck protection light on the surface wiped across, both metalic kitchenware can have been protected not by aqueous vapor corrosion, kitchen tools can be made again to seem, and light is as new, and wilkinite makes film formation time shorten simultaneously, and sticking power is stronger; And calcium carbonate can absorb the moisture in air, again reduce the chance that moisture directly contacts with metal, prevent corrosion.
Frequent use this product wiping hardware, has decontamination, goes crow to return new effect, have the effect of polishing simultaneously.
Embodiment
Embodiment 1
A kind of metalware polish, comprises wilkinite 10 parts in components by weight percent, coco-nut oil fatty acid 20 parts, quartz sand 120 parts, paraffin oil 5 parts, 2 parts, turps, 20 parts, calcium carbonate, alcohol 10 parts, ammoniacal liquor 20 parts, 360 parts, water.
The preparation method of above-described metalware polish, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 60 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
Embodiment 2
A kind of metalware polish, comprises wilkinite 12 parts in components by weight percent, coco-nut oil fatty acid 26 parts, quartz sand 135 parts, paraffin oil 6 parts, 3 parts, turps, 26 parts, calcium carbonate, alcohol 12 parts, ammoniacal liquor 25 parts, 380 parts, water.
The preparation method of above-described metalware polish, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 65 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
Embodiment 3
A kind of metalware polish, comprises wilkinite 13 parts in components by weight percent, coco-nut oil fatty acid 28 parts, quartz sand 138 parts, paraffin oil 7 parts, 4 parts, turps, 27 parts, calcium carbonate, alcohol 15 parts, ammoniacal liquor 26 parts, 385 parts, water.
The preparation method of above-described metalware polish, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 68 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
Embodiment 4
A kind of metalware polish, comprises wilkinite 14 parts in components by weight percent, coco-nut oil fatty acid 29 parts, quartz sand 143 parts, paraffin oil 8 parts, 5 parts, turps, 28 parts, calcium carbonate, alcohol 16 parts, ammoniacal liquor 29 parts, 390 parts, water.
The preparation method of above-described metalware polish, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 70 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
Embodiment 5
A kind of metalware polish, comprises wilkinite 15 parts in components by weight percent, coco-nut oil fatty acid 30 parts, quartz sand 150 parts, paraffin oil 10 parts, 6 parts, turps, 30 parts, calcium carbonate, alcohol 20 parts, ammoniacal liquor 30 parts, 400 parts, water.
The preparation method of above-described metalware polish, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 70 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.
This polish is directly poured on clean cloth or towel in use, to the direct wiping of metalware, dries after cleaning, and without the need to water, not skin irritation, metalware light is as new.
Claims (3)
1. a metalware polish, is characterized in that, comprises in components by weight percent: wilkinite 10-15 part, coco-nut oil fatty acid 20-30 part, quartz sand 120-150 part, paraffin oil 5-10 part, turps 2-6 part, calcium carbonate 20-30 part, alcohol 10-20 part, ammoniacal liquor 20-30 part, water 360-400 part.
2. metalware polish according to claim 1, it is characterized in that, wilkinite 12-14 part is comprised, coco-nut oil fatty acid 26-29 part, quartz sand 135-143 part in components by weight percent, paraffin oil 6-8 part, turps 3-5 part, calcium carbonate 26-28 part, alcohol 12-16 part, ammoniacal liquor 25-29 part, water 380-390 part.
3. a preparation method for the metalware polish described in claim 1 or 2, is characterized in that, carries out according to following steps:
(1) each component is taken according to weight part;
(2) be dissolved in by ammoniacal liquor in the water of full dose 1/3rd, stirring and dissolving, adds coco-nut oil fatty acid, continues to be stirred to form soft paste;
(3) water of its surplus is heated to 60-70 DEG C, adds wilkinite, dispersed with stirring, then add the soft paste that step (2) obtains, continue dispersed with stirring even, add all the other components, stir and namely obtain metalware polish.