CN109054650A - A kind of super flatness stainless steel Wax special and preparation method thereof - Google Patents
A kind of super flatness stainless steel Wax special and preparation method thereof Download PDFInfo
- Publication number
- CN109054650A CN109054650A CN201810885084.XA CN201810885084A CN109054650A CN 109054650 A CN109054650 A CN 109054650A CN 201810885084 A CN201810885084 A CN 201810885084A CN 109054650 A CN109054650 A CN 109054650A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- wax special
- super flatness
- graphene
- grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of super flatness stainless steel Wax specials, by following weight percent at being grouped as: abrasive material 50-60%, grease 10-15%, lubricant 3-5%, glossiness additive 2-3%, stearic acid 3-8%, palmitic acid 5-10%, rosin 2-4%, feldspar powder 2-4%, chromium oxide 0.1-0.3%, corundum 1-2%, graphene 0.01-0.03% and iron oxide red surplus.Alpha-alumina is used in the present invention, grain diameter 800-1200nm, is presented ellipse and column is conducive to polish without obvious sharp corners；A small amount of feldspar powder and corundum is added, grinding effect can be promoted, has extraordinary grinding effect for obstinate spot and scratch；Graphene, which is added, extraordinary can promote the grinding effect to rough surfaces such as trachoma, burrs and fill and lead up effect, to reach extraordinary surface smoothness.
Description
Technical field
The present invention relates to stainless steel Wax special technical field more particularly to a kind of super flatness stainless steel Wax special and its systems
Preparation Method.
Background technique
Stainless steel Wax special is mainly used for roughly grinding operation, is suitable for the polishing such as stainless steel, copper, aluminium, as tableware, fishing gear are matched
Part, all kinds of handwares, main function are except the leveling of the rough surfaces such as trachoma, burr reaches glossy effect.Its feature: middle rugosity mill
Material, cutting force is strong, and grease is abundant, versatile.
Currently, the quality of stainless steel Wax special in the market is not well positioned to meet the demand in market, it is flat using rear surface
The problems such as market demands are not achieved in whole degree, and using effect is undesirable, and have complex manufacturing technology, at high cost.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of super flatness stainless steel Wax special and its systems
Preparation Method.
Technical scheme is as follows:
A kind of super flatness stainless steel Wax special, by following weight percent at being grouped as: abrasive material 50-60%, grease 10-
15%, lubricant 3-5%, glossiness additive 2-3%, stearic acid 3-8%, palmitic acid 5-10%, rosin 2-4%, feldspar powder
2-4%, chromium oxide 0.1-0.3%, corundum 1-2%, graphene 0.01-0.03% and iron oxide red surplus.
Preferably, the abrasive material is micro/nano level alpha-alumina；Partial size is 800-1200nm.
Preferably, the grease is methyl-silicone oil.
Preferably, the lubricant is triethanolamine.
Preferably, the glossiness additive is barium mahogany sulfonate.
A kind of preparation method of super flatness stainless steel Wax special, includes the following steps: to add abrasive material, grease, glossiness
It is heated after adding agent, rosin, feldspar powder and corundum mixing, heating temperature is 90-120 DEG C, then oxygen is added in time 30-50min
Change chromium, graphene, iron oxide red and lubricant, stirs evenly；Then stearic acid and palmitic acid is added, increasing temperature to heating temperature is
130-150 DEG C, heat 60-90min；Stand 10-15min；Material after standing is poured into prefabricated mould, after cooled and solidified
Form buffing wax.
The invention has the beneficial effects that:
1, Alpha-alumina is used in the present invention, which is 800-1200nm, ellipse and column is presented,
There is no obvious sharp corners, is conducive to polish；Abrasive material mainly plays ablation, and causes the principal element of scratch, stainless steel
After superfinishing polishes, mirror effect will be presented in surface, and be invisible to the naked eye any scratch, therefore requires the partial size of abrasive material very small, and
Corner angle cannot be too sharp；
2, a small amount of feldspar powder and corundum is added, the hardness that can promote grinding effect, especially corundum is larger, for stubbornness
Spot and scratch have extraordinary grinding effect；
3, graphene, which is added, extraordinary can promote the grinding effect to rough surfaces such as trachoma, burrs and fill and lead up effect, from
And reach extraordinary surface smoothness.
Specific embodiment
Embodiment 1:
A kind of super flatness stainless steel Wax special, by following weight percent at being grouped as: abrasive material 58%, grease 12%, profit
Lubrication prescription 4%, glossiness additive 2.5%, stearic acid 5%, palmitic acid 6%, rosin 3%, feldspar powder 2.5%, chromium oxide
0.25%, corundum 1.5%, graphene 0.025% and iron oxide red surplus.
The abrasive material is micro/nano level alpha-alumina；Partial size is 800-1200nm.
The grease is methyl-silicone oil.
The lubricant is triethanolamine.
The glossiness additive is barium mahogany sulfonate.
A kind of preparation method of super flatness stainless steel Wax special, include the following steps: by micro/nano level alpha-alumina,
It being heated after methyl-silicone oil, barium mahogany sulfonate, rosin, feldspar powder and corundum mixing, heating temperature is 115 DEG C, time 45min,
Then chromium oxide, graphene, iron oxide red and triethanolamine is added, stirs evenly；Then stearic acid and palmitic acid is added, increases temperature
It is 135 DEG C to heating temperature, heats 70min；Stand 12min；Material after standing is poured into prefabricated mould, through cooled and solidified
After form buffing wax.
Embodiment 2:
A kind of super flatness stainless steel Wax special, by following weight percent at being grouped as: abrasive material 50%, grease 15%, profit
Lubrication prescription 3%, glossiness additive 3%, stearic acid 3%, palmitic acid 10%, rosin 2%, feldspar powder 4%, chromium oxide 0.1%, just
Jade 2%, graphene 0.01% and iron oxide red surplus.
The abrasive material is micro/nano level alpha-alumina；Partial size is 800-1200nm.
The grease is methyl-silicone oil.
The lubricant is triethanolamine.
The glossiness additive is barium mahogany sulfonate.
A kind of preparation method of super flatness stainless steel Wax special, include the following steps: by micro/nano level alpha-alumina,
It being heated after methyl-silicone oil, barium mahogany sulfonate, rosin, feldspar powder and corundum mixing, heating temperature is 120 DEG C, time 30min,
Then chromium oxide, graphene, iron oxide red and triethanolamine is added, stirs evenly；Then stearic acid and palmitic acid is added, increases temperature
It is 150 DEG C to heating temperature, heats 60min；Stand 15min；Material after standing is poured into prefabricated mould, through cooled and solidified
After form buffing wax.
Embodiment 3:
A kind of super flatness stainless steel Wax special, by following weight percent at being grouped as: abrasive material 60%, grease 10%, profit
Lubrication prescription 5%, glossiness additive 2%, stearic acid 8%, palmitic acid 5%, rosin 4%, feldspar powder 2%, chromium oxide 0.3%, just
Jade 1%, graphene 0.03% and iron oxide red surplus.
The abrasive material is micro/nano level alpha-alumina；Partial size is 800-1200nm.
The grease is methyl-silicone oil.
The lubricant is triethanolamine.
The glossiness additive is barium mahogany sulfonate.
A kind of preparation method of super flatness stainless steel Wax special, include the following steps: by micro/nano level alpha-alumina,
It is heated after methyl-silicone oil, barium mahogany sulfonate, rosin, feldspar powder and corundum mixing, heating temperature is 90 DEG C, time 50min, so
Chromium oxide, graphene, iron oxide red and triethanolamine are added afterwards, stirs evenly；Then stearic acid and palmitic acid is added, increases temperature extremely
Heating temperature is 130 DEG C, heats 90min；Stand 10min；Material after standing is poured into prefabricated mould, after cooled and solidified
Form buffing wax.
Through detecting, after the sample of 1-3 of the embodiment of the present invention grinds stainless steel 304, the flatness of stainless steel surface
Very good, the thickness difference on surface can control within 0.02mm.
Comparative example 1
By the graphene removal in embodiment 1, remaining proportion and preparation method are constant.
Comparative example 2
By the corundum removal in embodiment 1, remaining proportion and preparation method are constant.
Through detecting, the sample of comparative example 1 grinding effect to rough surfaces such as trachoma, burrs and is filled out compared to embodiment 1
Flat effect wants far short of what is expected, and the thickness difference on surface is more than 0.2mm.
Through detecting, the sample of comparative example 2 is compared to embodiment 1, the thickness on surface far short of what is expected to the removal effect of scratch
Difference is more than 0.1mm.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of super flatness stainless steel Wax special, which is characterized in that by following weight percent at being grouped as: abrasive material 50-
60%, grease 10-15%, lubricant 3-5%, glossiness additive 2-3%, stearic acid 3-8%, palmitic acid 5-10%, rosin
2-4%, feldspar powder 2-4%, chromium oxide 0.1-0.3%, corundum 1-2%, graphene 0.01-0.03% and iron oxide red surplus.
2. super flatness stainless steel Wax special as described in claim 1, which is characterized in that the abrasive material is micro/nano level α-
Alumina powder；Partial size is 800-1200nm.
3. super flatness stainless steel Wax special as described in claim 1, which is characterized in that the grease is methyl-silicone oil.
4. super flatness stainless steel Wax special as described in claim 1, which is characterized in that the lubricant is three ethyl alcohol
Amine.
5. super flatness stainless steel Wax special as described in claim 1, which is characterized in that the glossiness additive is stone
Oily barium sulfonate.
6. a kind of preparation method of super flatness stainless steel Wax special, which comprises the steps of: by abrasive material, grease,
It is heated after glossiness additive, rosin, feldspar powder and corundum mixing, heating temperature is 90-120 DEG C, time 30-50min, so
Chromium oxide, graphene, iron oxide red and lubricant are added afterwards, stirs evenly；Then stearic acid and palmitic acid is added, increases temperature and extremely adds
Hot temperature is 130-150 DEG C, heats 60-90min；Stand 10-15min；Material after standing is poured into prefabricated mould, through cold
But buffing wax is formed after solidifying.