CN106635270A - Salt-fog-resistant core-shell structure nano-modified transformer oil containing tea seed oil and preparation method thereof - Google Patents
Salt-fog-resistant core-shell structure nano-modified transformer oil containing tea seed oil and preparation method thereof Download PDFInfo
- Publication number
- CN106635270A CN106635270A CN201610830462.5A CN201610830462A CN106635270A CN 106635270 A CN106635270 A CN 106635270A CN 201610830462 A CN201610830462 A CN 201610830462A CN 106635270 A CN106635270 A CN 106635270A
- Authority
- CN
- China
- Prior art keywords
- nano
- transformer oil
- oleum camelliae
- shell structure
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses salt-fog-resistant core-shell structure nano-modified transformer oil containing tea seed oil and a preparation method thereof; the salt-fog-resistant core-shell structure nano-modified transformer oil containing tea seed oil is prepared from, by weight, 100-150 parts of naphthenic base oil, 10-15 parts of tea seed oil, 0.1-0.15 part of nano titanium dioxide, 0.3-0.5 part of 2,6-di-tert-butyl-p-cresol, 0.1-0.15 part of benzotriazole, 1-2 parts of castor-base dioctyl sebacate, 0.01-0.015 part of tetraethoxysilane, 0.01-0.015 part of vinyltrimethoxysilane, 0.1-0.15 part of barium dinonylnaphthalenesulfonate, and 0.03-0.05 part of N,N'-bis(salicylidene)propanediamine. The transformer oil has excellent insulation and heat dissipation, has stable properties and long life, and also has good salt fog resistance, good environmental adaptability and high practicality.
Description
Technical field
The present invention relates to transformer oil technical field, more particularly to a kind of nuclear shell structure nano of salt spray resistance containing Oleum Camelliae changes
Property transformer oil and preparation method thereof.
Background technology
As power transformer constantly develops toward the direction of high insulation, Large Copacity and miniaturization, the property of dielectric is lifted
Can increasingly be taken seriously.Transformer oil is a kind of light viscosity oil, is that current transformator is exhausted with insulation and the two big functions that radiate
Important component part in edge system, its performance plays an important role to the safety and reliability of transformator longtime running.Cause
This, the performance for how lifting transformer oil has become one of study hotspot.
Nano modification transformer oil is to be modified the novel transformer oil for obtaining, tool to transformer oil using nano-particle
There is the electric property of its high-cooling property and uniqueness, just widely paid close attention to by increasingly.In actual applications, nano-particle is becoming
Easily occur to reunite sedimentation and make performance degradation in depressor oil, had a strong impact on the service life of nano modification transformer oil.Document
《Impact of the oleic acid modified to nano titanium oxide dispersibility in transformer oil》Nano titanium oxide is had using Oleic acid
Machine surface modification, by the nano-powder ultrasonic disperse after modification nano-titanium dioxide modified transformator is prepared in transformer oil
Oil, so that dispersibility and stability of the nano-titania particle in transformer oil is improved.Although this method energy
Improve dispersion, stability of the nano-particle in transformer oil, but Oleic acid is the characteristics of have apt to deteriorate in atmosphere, especially
It is easily oxidation, decomposition under hot conditionss, is difficult to maintain the steady in a long-term of nano modification transformer oil in actual motion.Cause
This, is to maintain nano modification transformer oil performance in actual applications, improves its service life, still needs to improve its life-time service
Stability.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided one kind insulation, heat conductivility are excellent, long-term steady
Modified transformer oil of nuclear shell structure nano of the salt spray resistance of qualitative good, long service life containing Oleum Camelliae and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of modified transformer oil of nuclear shell structure nano of salt spray resistance containing Oleum Camelliae, it is obtained by the raw material of following weight parts:
Naphthenic base oils 100-150, Oleum Camelliae 10-15, nano titanium oxide 0.1-0.15,2,6 ditertiary butyl p cresol
0.3-0.5, BTA 0.1-0.15, Semen Ricini base di-n-octyl sebacate 1-2, tetraethyl orthosilicate 0.01-0.015, vinyl
The salicylidene propane diamine 0.03-0.05 of triethoxysilane 0.01-0.015, dinonyl naphthalene sulfonate barium 0.1-0.15, N, N'- bis-.
A kind of preparation method of the modified transformer oil of nuclear shell structure nano of salt spray resistance containing Oleum Camelliae, comprises the following steps:
(1)First nano titanium oxide is compared into 1 by solid-liquid weight:100-1:200 add ultrasonic disperse in dehydrated alcohol uniform, then
It is slowly added to tetraethyl orthosilicate and VTES and stirs 0.5-1h to obtain mixed liquor, is finally slowly added dropwise quite
In 1/20-1/10 mixeding liquid volumes acetum and in 50-60 DEG C stir 2-4h, after cooling centrifugation and by the solid for obtaining use
Absolute ethanol washing for several times, obtains modified Nano grain, and the mass fraction of the acetum is 4-6%;
(2)Oleum Camelliae is processed through alkali-refining deacidification, distillation, the deodorize of active hargil adsorption bleaching and obtains refined Oleum Camelliae, then
80-90 DEG C of stirring 1-2h of Semen Ricini base di-n-octyl sebacate and dinonyl naphthalene sulfonate barium is added, naphthenic base oils 50- is eventually adding
60 DEG C of mixing 0.5-1h, obtain compound oil after cooling;
(3)By step(1)The modified Nano grain for obtaining adds step(2)Ultrasonic disperse is uniform in the compound oil for obtaining, Ran Houjia
Enter 50-60 DEG C of stirring 0.5-1h of remaining raw material, distillation, filtration are refined after cooling, obtain final product nucleocapsid structure of the salt spray resistance containing Oleum Camelliae
Nano modification transformer oil.
It is an advantage of the invention that:
The present invention forms polysiloxanes using tetraethyl orthosilicate and VTES hydrolytie polycondensation cladding nanoparticle
Coated core-shell structure nanometer grain, the stability with good dispersibility, resistance to ag(e)ing and height can stably be scattered in transformation
In device oil, insulation, radiating, the ageing resistance of transformer oil can be effectively lifted, and be not easily susceptible to the shadow of extraneous service condition
Ring and rotten, precipitation occurs, affect the performance of transformer oil;Meanwhile, the compounding using the refine of Oleum Camelliae and with remaining raw material
With potentiation, so as to get transformer oil both there is excellent insulation, heat dispersion, while stable in properties, long service life,
The characteristics of also having salt spray resistance good, good environmental adaptability is practical.
Specific embodiment
The modified transformer oil of nuclear shell structure nano of a kind of salt spray resistance containing Oleum Camelliae, by the component raw material of following weight (kg)
It is prepared from:
Naphthenic base oils 100, Oleum Camelliae 10, nano titanium oxide 0.1,2,6 ditertiary butyl p cresol 0.3, BTA
0.1, Semen Ricini base di-n-octyl sebacate 1, tetraethyl orthosilicate 0.01, VTES 0.01, dinonyl naphthalene sulfonate barium
The salicylidene propane diamine 0.03 of 0.1, N, N'- bis-.
A kind of preparation method of the modified transformer oil of nuclear shell structure nano of salt spray resistance containing Oleum Camelliae, comprises the following steps:
(1)First nano titanium oxide is compared into 1 by solid-liquid weight:100 add ultrasonic disperse in dehydrated alcohol uniform, then slowly add
Enter tetraethyl orthosilicate and VTES and stir 0.5h and obtain mixed liquor, be finally slowly added dropwise mixed equivalent to 1/20
The acetum for closing liquid product simultaneously stirs 2h in 50 DEG C, after cooling centrifugation and by the solid for obtaining with absolute ethanol washing for several times,
Modified Nano grain is obtained, the mass fraction of the acetum is 4%;
(2)Oleum Camelliae is processed through alkali-refining deacidification, distillation, the deodorize of active hargil adsorption bleaching and obtains refined Oleum Camelliae, then
80 DEG C of stirring 1h of Semen Ricini base di-n-octyl sebacate and dinonyl naphthalene sulfonate barium are added, 50 DEG C of mixing of naphthenic base oils are eventually adding
0.5h, obtains compound oil after cooling;
(3)By step(1)The modified Nano grain for obtaining adds step(2)Ultrasonic disperse is uniform in the compound oil for obtaining, Ran Houjia
Enter 50 DEG C of stirring 0.5h of remaining raw material, distillation, filtration are refined after cooling, obtain final product nuclear shell structure nano of the salt spray resistance containing Oleum Camelliae and change
Property transformer oil.
Wherein naphthenic base oils select 75DN models.
Transformer oil frequency breakdown voltage >=80kV obtained above, remaining index reaches GB2536-2011 standards,
120 DEG C of operation 1000h remain to keep it is stable, without precipitation, meet actually used demand.
Claims (2)
1. a kind of salt spray resistance contains the modified transformer oil of nuclear shell structure nano of Oleum Camelliae, it is characterised in that it is by following weight
The raw material of part is obtained:
Naphthenic base oils 100-150, Oleum Camelliae 10-15, nano titanium oxide 0.1-0.15,2,6 ditertiary butyl p cresol
0.3-0.5, BTA 0.1-0.15, Semen Ricini base di-n-octyl sebacate 1-2, tetraethyl orthosilicate 0.01-0.015, vinyl
The salicylidene propane diamine 0.03-0.05 of triethoxysilane 0.01-0.015, dinonyl naphthalene sulfonate barium 0.1-0.15, N, N'- bis-.
2. a kind of salt spray resistance according to claim 1 contains the preparation side of the modified transformer oil of nuclear shell structure nano of Oleum Camelliae
Method, it is characterised in that comprise the following steps:
(1)First nano titanium oxide is compared into 1 by solid-liquid weight:100-1:200 add ultrasonic disperse in dehydrated alcohol uniform, then
It is slowly added to tetraethyl orthosilicate and VTES and stirs 0.5-1h to obtain mixed liquor, is finally slowly added dropwise quite
In 1/20-1/10 mixeding liquid volumes acetum and in 50-60 DEG C stir 2-4h, after cooling centrifugation and by the solid for obtaining use
Absolute ethanol washing for several times, obtains modified Nano grain, and the mass fraction of the acetum is 4-6%;
(2)Oleum Camelliae is processed through alkali-refining deacidification, distillation, the deodorize of active hargil adsorption bleaching and obtains refined Oleum Camelliae, then
80-90 DEG C of stirring 1-2h of Semen Ricini base di-n-octyl sebacate and dinonyl naphthalene sulfonate barium is added, naphthenic base oils 50- is eventually adding
60 DEG C of mixing 0.5-1h, obtain compound oil after cooling;
(3)By step(1)The modified Nano grain for obtaining adds step(2)Ultrasonic disperse is uniform in the compound oil for obtaining, Ran Houjia
Enter 50-60 DEG C of stirring 0.5-1h of remaining raw material, distillation, filtration are refined after cooling, obtain final product nucleocapsid structure of the salt spray resistance containing Oleum Camelliae
Nano modification transformer oil.