CN106479630A - A kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil and preparation method thereof - Google Patents
A kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil and preparation method thereof Download PDFInfo
- Publication number
- CN106479630A CN106479630A CN201610830597.1A CN201610830597A CN106479630A CN 106479630 A CN106479630 A CN 106479630A CN 201610830597 A CN201610830597 A CN 201610830597A CN 106479630 A CN106479630 A CN 106479630A
- Authority
- CN
- China
- Prior art keywords
- oil
- epoxidized soybean
- soybean oil
- low temperature
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, which is obtained by the raw material of following weight parts:Mineral base oil 1,000 1500, epoxidized soybean oil 40 60, dimethicone 35, silane coupler KH 570 0.15 0.25, azodiisobutyronitrile 0.01 0.015, dioctyl adipate 12, methyl methacrylate 0.5 1, nano aluminium oxide 0.5 1,2,6 DI-tert-butylphenol compounds 1 1.5, BTA 0.5 1, ethoxylated dodecyl alcohol 0.5 1.The transformer insulation oil of the present invention can be stored for a long time and keep good performance with excellent stability and insulating properties, while with good resistance to low temperature, being suitable for using under cold conditions, with higher practical value.
Description
Technical field
The present invention relates to transformer oil technical field, more particularly to a kind of low temperature resistant high-insulativity containing epoxidized soybean oil is received
Modified transformer insulation oil of rice and preparation method thereof.
Background technology
Paper oil insulation is a kind of typical liquid-solid composite insulation, has a wide range of applications in oil-filled transformer.With
Voltage class of electric power system and the continuous lifting of transmission capacity, oil-paper combination insulation have been increasingly difficult to meet voltage levels
To Large Copacity, miniaturization, the requirement of high stability insulation system.In order to lift the performance of transformer insulating system, how to improve
The insulation characterisitic of dielectric has become as one of current study hotspot.Transformer oil is that important insulation in transformer is situated between
Matter, seeks to improve the effective way of transformer oil insulating properties and heat dispersion, to improving efficiency and the safety of transformer station high-voltage side bus
Reliability is significant.
At present, be improve insulating materials performance, insulating materials field introduce nanometer technology be an important development
Direction.Wherein, the research of nano modification transformer oil brings new raising to traditional transformer oilpaper composite insulation structure
Space.Document《The insulating properties and Mechanism Study of semi-conductor nano particles modification transformer oil》Using nano-particle TiO2To becoming
Depressor oil is modified, it is found that the addition of nano-particle can significantly improve the insulation characterisitic of transformer oil.But in practical application,
Nano particle is susceptible to reunite, and causes the reduction of reliability.Dispersion of the conventional surfactant facture to nano-particle
The improvement of property and stability is limited, and the insulating properties of nano modification transformer oil can be had a negative impact.Therefore, how
Dispersion of the nano-particle in transformer oil, stability and insulating properties are taken into account, becomes the major issue for needing at present to solve.
Content of the invention
The object of the invention is exactly to make up the defect of prior art, provides one kind and takes into account nano-particle dispersion, stability
And the low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil and its preparation side of superior isolation performance
Method.
The present invention is achieved by the following technical solutions:
A kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, its be by the original of following weight parts
Material is obtained:
Mineral base oil 1000-1500, epoxidized soybean oil 40-60, dimethicone 3-5, Silane coupling reagent KH-570 0.15-
0.25, azodiisobutyronitrile 0.01-0.015, dioctyl adipate 1-2, methyl methacrylate 0.5-1, nano aluminium oxide
0.5-1,2,6- DI-tert-butylphenol compounds 1-1.5, BTA 0.5-1, ethoxylated dodecyl alcohol 0.5-1.
A kind of preparation method of the low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, including with
Lower step:
(1)By Silane coupling reagent KH-570 by weight 1:100-1:150 are mixed with absolute ethyl alcohol, are subsequently adding nano oxygen
Change aluminium ultrasonic disperse 5-10min, then in 40-50 DEG C stir 1-2h, centrifugation after cooling, by the solid particle for obtaining in
90-100 DEG C of drying and processing 10-15min;
(2)By step(1)In the material that obtains by weight 1:40-1:50 are mixed with absolute ethyl alcohol and ultrasonic disperse 10-
20min, is then slowly added to methyl methacrylate and azodiisobutyronitrile and stirs anti-in 60-70 DEG C under nitrogen protection successively
2-4h is answered, centrifugation after cooling, by the solid particle for obtaining again with absolute ethyl alcohol cyclic washing 2-4 time;
(3)First mixed to epoxidized soybean oil, dimethicone and ethoxylated dodecyl alcohol being incorporated in after 60-80 DEG C of stirring 1-2h is added
Enter 50-60 DEG C of stirring 0.5-1h in mineral base oil, after cooling, add step(2)In material and remaining raw material ultrasonic disperse
Uniformly, then carry out refined filtration and impurity is removed, vacuum dehydration degassing is eventually passed, obtain final product the low temperature resistant high insulation containing epoxidized soybean oil
Property nano modification transformer insulation oil.
It is an advantage of the invention that:
The present invention carries out surface silanization by Silane coupling reagent KH-570 to nano-particle, then grafted methacrylic acid first
Ester, can substantially increase sterically hindered between nano-particle, effective mutual aggtegation for reducing nano-particle, improve nanoparticle
Dispersiveness and stability of the son in transformer oil, while improve the insulating properties of nano-particle;By originals such as epoxidized soybean oils
The compound synergic of material, is effectively improved the low temperature flow of transformer oil, rear obtained transformer insulation oil compound with remaining raw material
With excellent stability and insulating properties, can store for a long time and good performance is kept, while with good resistance to low
Warm nature energy, is suitable for using under cold conditions, with higher practical value.
Specific embodiment
A kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, by following weight (kg)
Component raw material is prepared from:
Mineral base oil 1000, epoxidized soybean oil 40, dimethicone 3, Silane coupling reagent KH-570 0.15, two isobutyl of azo
Nitrile 0.01, dioctyl adipate 1, methyl methacrylate 0.5, nano aluminium oxide 0.5,2,6- DI-tert-butylphenol compounds 1, benzo three
Nitrogen azoles 0.5, ethoxylated dodecyl alcohol 0.5.
A kind of preparation method of the low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, including with
Lower step:
(1)By Silane coupling reagent KH-570 by weight 1:100 are mixed with absolute ethyl alcohol, are subsequently adding nano aluminium oxide and are surpassed
Sound disperses 5min, then stirs 1h in 40 DEG C, and centrifugation after cooling, by the solid particle for obtaining in 90 DEG C of drying and processings
10min;
(2)By step(1)In the material that obtains by weight 1:40 are mixed with absolute ethyl alcohol and ultrasonic disperse 10min, then nitrogen
Methyl methacrylate and azodiisobutyronitrile stirring reaction 2h are slowly added to successively in 60 DEG C under gas shielded, are centrifuged after cooling
Separate, by the solid particle for obtaining again with absolute ethyl alcohol cyclic washing 2 times;
(3)First mixed to epoxidized soybean oil, dimethicone and ethoxylated dodecyl alcohol being incorporated in after 60 DEG C of stirring 1h is added ore deposit
50 DEG C of stirring 0.5h in thing base oil, add step after cooling(2)In material and remaining raw material ultrasonic disperse uniform, then
Carry out refined filtration and impurity is removed, vacuum dehydration degassing is eventually passed, is obtained final product the low temperature resistant high-insulativity nanometer containing epoxidized soybean oil and changes
Property transformer insulation oil.
Above-mentioned mineral base oil chooses 60 base oil of sinopec HVI Ia.
Through inspection, transformer insulation oil performance obtained above is as follows:
Average frequency breakdown voltage:88.2kV;
Dielectric dissipation factor(90℃):0.00081;
185 DEG C, the heat ageing of 12 weeks process after dielectric dissipation factor(90℃):0.0261;
Standing still keeps transparent clarification after 1 year, nothing is precipitated.
Claims (2)
1. a kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil, it is characterised in that its be by
The raw material of following weight parts is obtained:
Mineral base oil 1000-1500, epoxidized soybean oil 40-60, dimethicone 3-5, Silane coupling reagent KH-570 0.15-
0.25, azodiisobutyronitrile 0.01-0.015, dioctyl adipate 1-2, methyl methacrylate 0.5-1, nano aluminium oxide
0.5-1,2,6- DI-tert-butylphenol compounds 1-1.5, BTA 0.5-1, ethoxylated dodecyl alcohol 0.5-1.
2. a kind of low temperature resistant high-insulativity nano modification transformer insulation oil containing epoxidized soybean oil according to claim 1
Preparation method, it is characterised in that comprise the following steps:
(1)By Silane coupling reagent KH-570 by weight 1:100-1:150 are mixed with absolute ethyl alcohol, are subsequently adding nano oxygen
Change aluminium ultrasonic disperse 5-10min, then in 40-50 DEG C stir 1-2h, centrifugation after cooling, by the solid particle for obtaining in
90-100 DEG C of drying and processing 10-15min;
(2)By step(1)In the material that obtains by weight 1:40-1:50 are mixed with absolute ethyl alcohol and ultrasonic disperse 10-
20min, is then slowly added to methyl methacrylate and azodiisobutyronitrile and stirs anti-in 60-70 DEG C under nitrogen protection successively
2-4h is answered, centrifugation after cooling, by the solid particle for obtaining again with absolute ethyl alcohol cyclic washing 2-4 time;
(3)First mixed to epoxidized soybean oil, dimethicone and ethoxylated dodecyl alcohol being incorporated in after 60-80 DEG C of stirring 1-2h is added
Enter 50-60 DEG C of stirring 0.5-1h in mineral base oil, after cooling, add step(2)In material and remaining raw material ultrasonic disperse
Uniformly, then carry out refined filtration and impurity is removed, vacuum dehydration degassing is eventually passed, obtain final product the low temperature resistant high insulation containing epoxidized soybean oil
Property nano modification transformer insulation oil.