CN106634358A - High-elasticity external wall coating with enhanced anti-corrosive performance of composite epoxy resin emulsion - Google Patents
High-elasticity external wall coating with enhanced anti-corrosive performance of composite epoxy resin emulsion Download PDFInfo
- Publication number
- CN106634358A CN106634358A CN201611010807.9A CN201611010807A CN106634358A CN 106634358 A CN106634358 A CN 106634358A CN 201611010807 A CN201611010807 A CN 201611010807A CN 106634358 A CN106634358 A CN 106634358A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- parts
- minutes
- resin emulsion
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a high-elasticity external wall coating with enhanced anti-corrosive performance of composite epoxy resin emulsion. The high-elasticity external wall coating is prepared from, by weight, 20-22 parts of methyl methacrylate, 29-31 parts of butyl acrylate, 8.5-9.5 parts of hexafluorobutyl acrylate, 4-5 parts of vinyl triethoxy silane, 0.1-0.12 part of ammonium persulfate, 2-3 parts of OP-1, proper amount of deionized water, proper amount of amino water, 1.5-2 parts of n-dodecanol ester, 8-10 parts of superfine kaoline, 3-4 parts of polyether polyol, 2-3 parts of epoxy resin, 7-8 parts of epoxy resin emulsion, and 1-2 parts of boron trifluoride diethyl etherate. The high-elasticity coating has water-based formula and is free from toxic and pollution, high in ductility, excellent in weather fastness, convenient to construct; the coating is especially suitable for the waterproof use of the external wall of the building engineering; the coating film is smooth and beautiful.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of composite epoxy resin emulsion antiseptic property is enhanced high-elastic
Property exterior coating.
Background technology
At present, an important development direction of building external paint is exactly energy-saving heat preserving, and the performance of finish coat emulsion is excellent
The resistance to water of bad External Thermal Insulation Composite Systems, resistance to soiling, durability and temperature-change resistance have a direct impact relation, and wall body slit
Rainwater and carbon dioxide invasion can be caused, cause steel bar corrosion, accelerate body of wall carbonization speed, building masonry wall crackle into
One of common fault for impact construction engineering quality.Elastic building paint preferable extensibility because coating has, to a certain extent may be used
The crack of basic unit's generation is resisted and covered, is favored by market.Conventional coating can not accomplish both there is excellent weatherability, resistance to
Aqueous and resistance to soiling, and while with good elasticity, pliability and splitting resistance, so a kind of new high-performance of exploitation
Elastic water proofing paint becomes an important topic of research external wall heat insulation system project.
《The research and its application of tenacity acrylic's water-repellent paint》By organic silicon monomer, organic fluorine monomer and third in one text
Olefin(e) acid esters monomer carries out copolymerization, and using soap-free core-shell emulsion polymerization technique a kind of high performance fluorine fluorine-silicon modified acrylic bullet is prepared for
Property emulsion, with good elasticity, water proofing property and resistance to soiling, but due to the development of building trade, need further externally
Wall coating carries out the improvement of other additional properties, and needed for meet industry, this is accomplished by changing coating made by its emulsion
Property.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of composite epoxy resin emulsion antiseptic property
Enhanced elastic exterior wall paint.
The present invention is achieved by the following technical solutions:
A kind of enhanced elastic exterior wall paint of composite epoxy resin emulsion antiseptic property, is prepared by the raw materials in:
Methyl methacrylate 20-22, butyl acrylate 29-31, hexafluorobutyl acrylate 8.5-9.5, VTES
4-5, ammonium persulfate 0.1-0.12, OP-102-3, appropriate deionized water, appropriate ammoniacal liquor, Lauryl Alcohol ester 1.5-2, ultra-fine kaolinite
Native 8-10, PPG 3-4, epoxy resin 2-3, epoxy resin latex 7-8, BFEE 1-2.
A kind of enhanced elastic exterior wall paint of the composite epoxy resin emulsion antiseptic property according to claims 1,
It is prepared from by following concrete grammar:
(1)OP-10 is dissolved in the 35-30 times of deionized water measured, is stirred to after being completely dissolved with 200-300 rev/min of speed
Methyl methacrylate, butyl acrylate are slowly added to, to be warming up to 80-85 after 800 revs/min of speed stirring 20-30 minutes
DEG C insulation 15-20 minutes, ammonium persulfate is added, hexafluorobutyl acrylate and the ethoxy of vinyl three are slowly added dropwise after stirring
The mixed liquor of base silane, time for adding is controlled in 2.5-3 hours, after dripping off, at 80-85 DEG C 60-90 minutes is incubated, and is cooled to
40 DEG C, it is 7-8 to adjust pH with ammoniacal liquor, then crosses 200 mesh sieves, obtains fluorinated silicone modified acrylic elastic emulsion;
(2)PPG is mixed with epoxy resin, 80-85 DEG C is heated to until both fully dissolvings, are subsequently adding trifluoro
Change borate ether, under nitrogen protection, be heated to 100 DEG C, after stirring reaction 5-6 hour emulsifying agent is obtained;By epoxy resin latex with
Mentioned emulsifier mixes, and with 600-800 rev/min of speed 60-90 minutes are stirred, and obtains composite epoxy resin emulsion;
(3)By step(1)(2)The product mixing for obtaining, adds appropriate amount of deionized water and remaining residual components, controls solid content
For 68-70%, ball milling 40-60 minutes in ball mill are put into after stirring 15-20 minutes with 300-400 rev/min of speed, finally mistake
200 mesh sieves are obtained final product.
It is an advantage of the invention that:The present invention is introduced using core-shell emulsion polymerization technique in acrylic emulsion polymerization process
Organosilicon and organic fluorin radical, reduce the surface energy of polymer, and good protective effect can be formed to matrix polymer segment,
Its non-oxidizability is improved, while fluorine and silicon can be made to be enriched in coating surface after film forming, fluorine and silicon list in emulsion can be so reduced
The consumption of body, neither reduce material cost does not reduce the combination property of coating again;Using coating temperature-change resistance made by its emulsion
Greatly improved with durability, the film after film forming has extremely low surface energy, impart again the higher resistance to water of film,
The performance such as oil resistivity and resistance to soiling;Coating made by the present invention has excellent outdoor decorative, long durability and temp. variation resistant
Cracking behavior, can solve the problems, such as that conventional outer wall external thermal insulation emulsion system is easy to crack, come off and reduce service life.
The present invention carries out reaction and generates wax-like emulsifying agent by using epoxy resin and PPG, then again with epoxy
Resin emulsion is compounded, and makes complex emulsions, in being added to the preparation of coating, the waterproof effect of coating is enhanced, while enhancing
The weatherability and antiseptic property of coating;High elastic coating of the present invention, water prescription, nontoxic pollution-free, elongation percentage is high, weatherability
Excellent, easy construction is particularly suitable for being used in architectural engineering external wall waterproof, film smooth and beautiful appearance.
Specific embodiment
The enhanced elastic exterior wall paint of a kind of composite epoxy resin emulsion antiseptic property, by following weight portion(Kilogram)'s
Raw material is made:Methyl methacrylate 20, butyl acrylate 29, hexafluorobutyl acrylate 8.5, VTES 4,
Ammonium persulfate 0.1, OP-10 2, appropriate deionized water, appropriate ammoniacal liquor, Lauryl Alcohol ester 1.5, ultrafine kaolin 8, polyether polyols
Alcohol 3, epoxy resin 2, epoxy resin latex 7, BFEE 1.
A kind of enhanced elastic exterior wall paint of the composite epoxy resin emulsion antiseptic property according to claims 1,
It is prepared from by following concrete grammar:
(1)OP-10 is dissolved in the deionized water of 35 times of amounts, is stirred to after being completely dissolved with 200 revs/min of speed and is slowly added to
Methyl methacrylate, butyl acrylate, are warming up to 80 DEG C and are incubated 15 minutes after being stirred 20 minutes with 800 revs/min of speed, then
Ammonium persulfate is added, the mixed liquor of hexafluorobutyl acrylate and VTES is slowly added dropwise after stirring, dripped
Plus time control was at 2.5 hours, after dripping off, 60 minutes are incubated at 80 DEG C, cool to 40 DEG C, it is 7 to adjust pH with ammoniacal liquor, then
200 mesh sieves are crossed, fluorinated silicone modified acrylic elastic emulsion is obtained;
(2)PPG is mixed with epoxy resin, 80 DEG C is heated to until both fully dissolvings, are subsequently adding boron trifluoride
Ether, under nitrogen protection, is heated to 100 DEG C, and stirring reaction obtains emulsifying agent after 5 hours;By epoxy resin latex and above-mentioned breast
Agent mixes, and is stirred 60 minutes with 600 revs/min of speed, obtains composite epoxy resin emulsion;
(3)By step(1)(2)The product mixing for obtaining, adds appropriate amount of deionized water and remaining residual components, controls solid content
For 68%, ball milling 40 minutes in ball mill are put into after stirring 15 minutes with 300 revs/min of speed, finally cross 200 mesh sieves and obtain final product.
The present embodiment coating is detected according to the requirement of JC/T 864-2008, after product is agitated, uniformly, without knot
Block, solid content is more than 65%, and tensile strength is more than 1MPa, and elongation at break is more than 300%, meets professional standard.
Claims (2)
1. the enhanced elastic exterior wall paint of a kind of composite epoxy resin emulsion antiseptic property, it is characterised in that by following weight
The raw material of part is made:Methyl methacrylate 20-22, butyl acrylate 29-31, hexafluorobutyl acrylate 8.5-9.5, vinyl
Triethoxysilane 4-5, ammonium persulfate 0.1-0.12, OP-102-3, appropriate deionized water, appropriate ammoniacal liquor, Lauryl Alcohol ester
1.5-2, ultrafine kaolin 8-10, PPG 3-4, epoxy resin 2-3, epoxy resin latex 7-8, BFEE 1-
2。
2. the enhanced elastic exterior wall paint of a kind of composite epoxy resin emulsion antiseptic property according to claims 1, its
It is characterised by, is prepared from by following concrete grammar:
(1)OP-10 is dissolved in the 35-30 times of deionized water measured, is stirred to after being completely dissolved with 200-300 rev/min of speed
Methyl methacrylate, butyl acrylate are slowly added to, to be warming up to 80-85 after 800 revs/min of speed stirring 20-30 minutes
DEG C insulation 15-20 minutes, ammonium persulfate is added, hexafluorobutyl acrylate and the ethoxy of vinyl three are slowly added dropwise after stirring
The mixed liquor of base silane, time for adding is controlled in 2.5-3 hours, after dripping off, at 80-85 DEG C 60-90 minutes is incubated, and is cooled to
40 DEG C, it is 7-8 to adjust pH with ammoniacal liquor, then crosses 200 mesh sieves, obtains fluorinated silicone modified acrylic elastic emulsion;
(2)PPG is mixed with epoxy resin, 80-85 DEG C is heated to until both fully dissolvings, are subsequently adding trifluoro
Change borate ether, under nitrogen protection, be heated to 100 DEG C, after stirring reaction 5-6 hour emulsifying agent is obtained;By epoxy resin latex with
Mentioned emulsifier mixes, and with 600-800 rev/min of speed 60-90 minutes are stirred, and obtains composite epoxy resin emulsion;
(3)By step(1)(2)The product mixing for obtaining, adds appropriate amount of deionized water and remaining residual components, controls solid content
For 68-70%, ball milling 40-60 minutes in ball mill are put into after stirring 15-20 minutes with 300-400 rev/min of speed, finally mistake
200 mesh sieves are obtained final product.