CN106634315A - Formula for high-brightness varnish used for woodenware - Google Patents
Formula for high-brightness varnish used for woodenware Download PDFInfo
- Publication number
- CN106634315A CN106634315A CN201710014655.8A CN201710014655A CN106634315A CN 106634315 A CN106634315 A CN 106634315A CN 201710014655 A CN201710014655 A CN 201710014655A CN 106634315 A CN106634315 A CN 106634315A
- Authority
- CN
- China
- Prior art keywords
- parts
- dsx
- brightness
- varnish
- woodenware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula for a high-brightness varnish used for woodenware. The formula comprises 78 parts of Viacryl VSC 6295W, 12.2 parts of water, 8.0 parts of ethylene glycol monobutyl ether, 0.4 part of Hydropalat 140, 0.6 part of FoamStar A34, 0.4 part of DSX-2000 and 0.4 part of DSX-1550. According to the invention, the raw materials are simple and easily available; cost is low; production process is simple; the varnish is convenient to use and suitable for industrial production; and the high-brightness varnish has solid content of 32.8%, surface drying time of 15 min, pencil hardness of HB-1H and adhesion of grade 1, and the viscosity of the high-brightness varnish is in the grade of 35 s in testing with a Ford cup No. 4.
Description
Technical field
The present invention relates to woodwork coating technical field, the highlighted lacquer formulation of specifically a kind of woodenware.
Background technology
Paint is of many uses in the life of people and industrial production, plays a part of protection, decoration, and high lac varnish has color
Damp light, the features such as reflective strong.Bloom panel construction used by existing interior decoration is：In the surface patch wood of wooden facing substrate layer
After cortex, brush high lac varnish and be made.But because the specification of some high lac varnish wood veneers is larger, base layer template local is not
Flat, there is surface irregularity in the high lac varnish wood veneer after shaping.The uneven phenomenon of refractive power and warpage, it is impossible to meet it is attractive in appearance and
Esthetic requirement.
The content of the invention
The technical assignment of the present invention is to solve the deficiencies in the prior art, there is provided a kind of highlighted lacquer formulation of woodenware.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of highlighted lacquer formulation of woodenware, including following components and each component weight fraction ratio be： Viacryl VSC 6295W
76-79 parts；Water 12-13 parts；Butyl glycol ether 7-9 parts；The 0.2-0.7 parts of Hydropalat 140； FoamStar A34
0.3-0.8 parts；DSX-2000 0.2-0.6 parts；DSX-1550 0.3-0.6 parts.
Preferably, 78 parts of Viacryl VSC 6295W；12.2 parts of water；8.0 parts of butyl glycol ether； Hydropalat 140
0.4 part；0.6 part of FoamStar A34；0.4 part of DSX-2000；0.4 part of DSX-1550.
A kind of produced compared with prior art beneficial effect of the highlighted lacquer formulation of woodenware of the present invention is：
Raw material used in the present invention are simple to be obtained, and with low cost, simple production process is easy to use, is adapted to industrialized production,
The performance of the highlighted varnish be solid content 32.8%, viscosity（Apply 4 glasss）35 seconds, surface drying time 15min, pencil hardness HB-1H were attached
Put forth effort 1 grade.
Specific embodiment
The present invention is described in detail with reference to specific embodiment.
By 78 parts of Viacryl VSC 6295W；12.2 parts of water；8.0 parts of butyl glycol ether； Hydropalat 140
0.4 part；0.6 part of FoamStar A34；0.4 part of DSX-2000；0.4 part of DSX-1550.
78 parts of precise component Viacryl VSC 6295W add the water after premix under 600rpm stirring conditions
12.2 parts and 8.0 parts of butyl glycol ether；Then 140 0.4 parts of Hydropalat, 0.6 part of FoamStar A34 are sequentially added
With 0.4 part of DSX-2000,60min is stirred in 2000rpm/min, then rotating speed is adjusted to into 600rpm and add DSX-1550 0.4
Part adjustment viscosity and at a slow speed froth breaking 10 minutes.
Embodiment 2：
By 78.3 parts of Viacryl VSC 6295W；12.4 parts of water；7.8 parts of butyl glycol ether；Hydropalat 140 0.4
Part；0.5 part of FoamStar A34；0.3 part of DSX-2000；0.3 part of DSX-1550.
78.3 parts of precise component Viacryl VSC 6295W add the water after premix under 600rpm stirring conditions
12.4 parts and 7.8 parts of butyl glycol ether；Then 140 0.4 parts of Hydropalat, 0.5 part of FoamStar A34 are sequentially added
With 0.3 part of DSX-2000,60min is stirred in 2000rpm/min, then rotating speed is adjusted to into 600rpm and add DSX-1550 0.3
Part adjustment viscosity and at a slow speed froth breaking 10 minutes.
Embodiment 3：
By 77.7 parts of Viacryl VSC 6295W；12.0 parts of water；8.2 parts of butyl glycol ether；Hydropalat 140 0.5
Part；0.7 part of FoamStar A34；0.4 part of DSX-2000；0.5 part of DSX-1550.
77.7 parts of precise component Viacryl VSC 6295W add the water after premix under 600rpm stirring conditions
12.0 parts and 8.2 parts of butyl glycol ether；Then 140 0.5 parts of Hydropalat, 0.7 part of FoamStar A34 are sequentially added
With 0.4 part of DSX-2000,60min is stirred in 2000rpm/min, then rotating speed is adjusted to into 600rpm and add DSX-1550 0.5
Part adjustment viscosity and at a slow speed froth breaking 10 minutes.
By above component it is standby enter tank in, under 800 turns of rotating speed dispersion 20 minutes can transparent priming.
It should be noted that above content is only to illustrate technical scheme, rather than the limit to the scope of the present invention
System, although the specific embodiment part has been made to explain to the present invention, it will be understood by those within the art that,
Technical scheme can be modified or equivalent, without deviating from the essence and model of technical solution of the present invention
Enclose.
Claims (2)
1. the highlighted lacquer formulation of a kind of woodenware, it is characterised in that including following components and each component weight fraction ratio is：
Viacryl VSC 6295W 76-79 parts；Water 12-13 parts；Butyl glycol ether 7-9 parts；Hydropalat 140 0.2-
0.7 part；FoamStar A34 0.3-0.8 parts；DSX-2000 0.2-0.6 parts；DSX-1550 0.3-0.6 parts.
2. the highlighted lacquer formulation of a kind of woodenware according to claim 1, it is characterised in that including following components and each component weight
Measuring score ratio is：
78 parts of Viacryl VSC 6295W；12.2 parts of water；8.0 parts of butyl glycol ether；140 0.4 parts of Hydropalat；
0.6 part of FoamStar A34；0.4 part of DSX-2000；0.4 part of DSX-1550.