CN106634307B - 一种多彩生物工程墙面涂料 - Google Patents

一种多彩生物工程墙面涂料 Download PDF

Info

Publication number
CN106634307B
CN106634307B CN201611213869.XA CN201611213869A CN106634307B CN 106634307 B CN106634307 B CN 106634307B CN 201611213869 A CN201611213869 A CN 201611213869A CN 106634307 B CN106634307 B CN 106634307B
Authority
CN
China
Prior art keywords
parts
bioengineering
colorful
agent
wall covering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201611213869.XA
Other languages
English (en)
Other versions
CN106634307A (zh
Inventor
郑玉斌
周之运
黄琼戎
吴美玲
黄林林
刘畅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU RESEARCH INSTITUTE OF DLUT Co Ltd
Original Assignee
CHANGSHU RESEARCH INSTITUTE OF DLUT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU RESEARCH INSTITUTE OF DLUT Co Ltd filed Critical CHANGSHU RESEARCH INSTITUTE OF DLUT Co Ltd
Priority to CN201611213869.XA priority Critical patent/CN106634307B/zh
Publication of CN106634307A publication Critical patent/CN106634307A/zh
Application granted granted Critical
Publication of CN106634307B publication Critical patent/CN106634307B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种多彩生物工程墙面涂料，包括以下组分：羟基丙烯酸乳液、填充剂、防沉剂、中和剂、分散剂、消泡剂、耐水剂、促进剂和水，所述填充剂为空心玻璃微珠和玻璃短纤维，所述空心玻璃微珠内部分填充有可逆性变色漆。通过上述方式，本发明所述的多彩生物工程墙面涂料，利用空心玻璃微珠对可逆性变色漆进行包裹，避免可逆性变色漆对空气环境的污染，并在温度变化时进行颜色的变化，再利用玻璃短纤维进行光线的传递，使得涂料表面星光闪烁并展现出颜色的变化，充分利用了可逆性变色漆的工作原理，涂料的施工便利，耐用性好。

Description

一种多彩生物工程墙面涂料
技术领域
本发明涉及生物工程涂料领域，特别是涉及一种多彩生物工程墙面涂料。
背景技术
涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、油或乳液为主涂料。
为了减少环境污染，越来越多的墙面涂料采用了水性涂料，制成的涂料在施工中可用水来稀释，颜色深度调节比较便利，降低成本，但是普通的墙面涂料颜色比较单一，无法随温度进行变化，而如果采用可逆性变色漆进行墙面的涂刷，又容易污染环境，而且成本高。
发明内容
本发明主要解决的技术问题是提供一种多彩生物工程墙面涂料，实现颜色随温度的变化，避免环境的污染，降低成本。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种多彩生物工程墙面涂料，包括以下重量份的组分：
羟基丙烯酸乳液 400~450份
填充剂 65~70份
防沉剂 0.5~1份
中和剂 5~6份
分散剂 0.5~1.2份
消泡剂 0.4~0.6份
耐水剂 55~65份
促进剂 50~60份
水 100~300份
所述填充剂为空心玻璃微珠和玻璃短纤维，所述空心玻璃微珠内部分填充有可逆性变色漆。
在本发明一个较佳实施例中，所述空心玻璃微珠在填充剂中所占的比重为50%~60%，所述玻璃短纤维在填充剂中所占的比重为40%~50%。
在本发明一个较佳实施例中，所述多彩生物工程墙面涂料中各组分的重量份为：
羟基丙烯酸乳液 450份
填充剂 70份
防沉剂 1份
中和剂 6份
分散剂 1.2份
消泡剂 0.6份
耐水剂 65份
促进剂 60份
水 300份。
在本发明一个较佳实施例中，所述防沉剂为钛酸酯偶联剂。
在本发明一个较佳实施例中，所述中和剂为氢氧化钾。
在本发明一个较佳实施例中，所述分散剂为聚乙烯蜡。
在本发明一个较佳实施例中，所述消泡剂为聚二甲基硅氧烷。
在本发明一个较佳实施例中，所述耐水剂为三聚磷酸铝。
在本发明一个较佳实施例中，所述促进剂为三乙醇胺。
在本发明一个较佳实施例中，所述多彩生物工程墙面涂料中还含有增韧剂，所述增韧剂为环氧树脂。
本发明的有益效果是：本发明指出的一种多彩生物工程墙面涂料，利用空心玻璃微珠对可逆性变色漆进行包裹，避免可逆性变色漆对空气环境的污染，并在温度变化时进行颜色的变化，再利用玻璃短纤维进行光线的传递，使得涂料表面星光闪烁并展现出颜色的变化，充分利用了可逆性变色漆的工作原理，涂料的施工便利，耐用性好。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
一种多彩生物工程墙面涂料，包括以下重量份的组分：
羟基丙烯酸乳液 400~450份
填充剂 65~70份
防沉剂 0.5~1份
中和剂 5~6份
分散剂 0.5~1.2份
消泡剂 0.4~0.6份
耐水剂 55~65份
促进剂 50~60份
水 100~300份
所述填充剂为空心玻璃微珠和玻璃短纤维，所述空心玻璃微珠内部分填充有可逆性变色漆，可逆性变色漆被空心玻璃微珠包裹，避免了泄漏和污染，降低了使用量和成本，再利用玻璃短纤维与空心玻璃微珠的接触，进行光线在涂料内的传播，实现涂料表面色彩随温度的变化。
所述防沉剂为钛酸酯偶联剂，提升涂料的防流挂能力和防沉降能力，特别是提升涂料的施工便利性和使用稳定性。所述中和剂为氢氧化钾，进行pH值调整，提升结构的稳定性，特别是方便涂料的存储和高温下的安全使用。所述分散剂为聚乙烯蜡，增加去除杂质颗粒的能力，所述消泡剂为聚二甲基硅氧烷，消除溶液中的气泡。所述耐水剂为三聚磷酸铝，提升涂料在墙面使用后的耐水效果。所述促进剂为三乙醇胺，促进涂料的混合，使得性能更加稳定，还具有一定的防腐性，减少墙体表面受潮后的霉变问题。
所述多彩生物工程墙面涂料中还含有增韧剂，所述增韧剂为环氧树脂。羟基丙烯酸乳液在墙面上干固后比较脆，时间长了在墙面上容易起皮，添加环氧树脂增加整体的柔韧性，特别是与墙面的连接牢度，不易起皮，抗震性好。
实施例1：
取如下重量份的各组分：
羟基丙烯酸乳液 400份
填充剂 65份
防沉剂 0.5份
中和剂 5份
分散剂 0.5份
消泡剂 0.4份
耐水剂 55份
促进剂 50份
水 100份
混合后进行搅拌，搅拌均匀后分装到密封桶中，进行保存。
实施例2：
取如下重量份的各组分：
羟基丙烯酸乳液 450份
填充剂 70份
防沉剂 1份
中和剂 6份
分散剂 1.2份
消泡剂 0.6份
耐水剂 65份
促进剂 60份
水 300份
混合后进行搅拌，搅拌均匀后分装到密封桶中，进行保存。
实施例3：
取如下重量份的各组分：
羟基丙烯酸乳液 420份
填充剂 68份
防沉剂 0.8份
中和剂 5.5份
分散剂 1份
消泡剂 0.5份
耐水剂 60份
促进剂 58份
水 200份
混合后进行搅拌，搅拌均匀后分装到密封桶中，进行保存。
综上所述，本发明指出的一种多彩生物工程墙面涂料，充分利用了可逆性变色漆的工作原理，随着温度变化而改变颜色，减少了可逆性变色漆的添加量，降低了成本，涂料的施工便利，与墙面的结合性好，经久耐用。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (9)

1.一种多彩生物工程墙面涂料，其特征在于，包括以下重量份的组分：
羟基丙烯酸乳液 400~450份
填充剂 65~70份
防沉剂 0.5~1份
中和剂 5~6份
分散剂 0.5~1.2份
消泡剂 0.4~0.6份
耐水剂 55~65份
促进剂 50~60份
水 100~300份
所述填充剂为空心玻璃微珠和玻璃短纤维，所述空心玻璃微珠内部分填充有可逆性变色漆，所述空心玻璃微珠在填充剂中所占的比重为50%~60%，所述玻璃短纤维在填充剂中所占的比重为40%~50%。
2.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述多彩生物工程墙面涂料中各组分的重量份为：
羟基丙烯酸乳液 450份
填充剂 70份
防沉剂 1份
中和剂 6份
分散剂 1.2份
消泡剂 0.6份
耐水剂 65份
促进剂 60份
水 300份。
3.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述防沉剂为钛酸酯偶联剂。
4.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述中和剂为氢氧化钾。
5.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述分散剂为聚乙烯蜡。
6.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述消泡剂为聚二甲基硅氧烷。
7.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述耐水剂为三聚磷酸铝。
8.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述促进剂为三乙醇胺。
9.根据权利要求1所述的多彩生物工程墙面涂料，其特征在于，所述多彩生物工程墙面涂料中还含有增韧剂，所述增韧剂为环氧树脂。
CN201611213869.XA 2016-12-26 2016-12-26 一种多彩生物工程墙面涂料 Active CN106634307B (zh)