CN106634260A - 一种高层建筑用电梯门板阻燃涂层 - Google Patents
一种高层建筑用电梯门板阻燃涂层 Download PDFInfo
- Publication number
- CN106634260A CN106634260A CN201611151163.5A CN201611151163A CN106634260A CN 106634260 A CN106634260 A CN 106634260A CN 201611151163 A CN201611151163 A CN 201611151163A CN 106634260 A CN106634260 A CN 106634260A
- Authority
- CN
- China
- Prior art keywords
- parts
- mesh
- flame retardant
- retardant coating
- phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高层建筑用电梯门板阻燃涂层，由以下组分组成：聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5‑氨基苯并咪唑酮、磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖、月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基。本发明产品具有较为优越的阻燃、耐酸碱、防霉变抗菌性能，改善了产品性能。
Description
技术领域
本发明涉及一种高层建筑用电梯门板阻燃涂层，属于建筑电梯技术领域。
背景技术
电梯是一种以电动机为动力的垂直升降机，装有箱状吊舱，用于多层建筑乘人或载运货物的运输工具。也有台阶式，踏步板装在履带上连续运行，俗称自动扶梯或自动人行道。服务于规定楼层的固定式升降设备。垂直升降电梯具有一个轿厢，运行在至少两列垂直的或倾斜角小于15°的刚性导轨之间。轿厢尺寸与结构形式便于乘客出入或装卸货物。习惯上不论其驱动方式如何，将电梯作为建筑物内垂直交通运输工具的总称。这些电梯在使用过程中，有必要针对电梯门板采用合适的方式予以处理，以便增强其门板使用效果，便于使用。
发明内容
本发明的目的在于提供一种高层建筑用电梯门板阻燃涂层，以便更好地实现高层建筑用电梯门板阻燃涂层的使用功能，使产品具有阻燃、耐酸碱、防霉变抗菌性能，改善产品使用性能。
为了实现上述目的，本发明的技术方案如下。
一种高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯24～28份、脲醛树脂22～26份、聚氨酯热塑性弹性体22～26份、四氯化碳20～24份、聚乙烯蜡乳液22～26份、氢化大豆油22～26份、乙酸丁酯20～24份、烯丙基硫醚22～26份、单氟磷酸钠22～26份、十二烷基乙氧基磺基甜菜碱20～24份、二苯并呋喃20～24份、乙酸铵20～24份、氯化亚铜22～26份、偏钛酸20～24份、富马酸二甲酯18～22份、二硫化四甲基秋兰姆22～26份、脱氢醋酸钠20～24份、玻璃纤维粉18～22份、甘油松香酯20～24份、5-氨基苯并咪唑酮18～22份、磷酸三(丁氧基乙基)酯18～22份、六溴环十二烷18～22份、三氯乙基磷酸酯16～20份、磷酸脒基脲12～16份、普鲁兰多糖10～14份、月桂醇硫酸钠10～14份、过氧苯甲酰10～14份、过氧化二苯甲酰10～14份、过氧化苯甲酰10～14份、过氧化氢叔丁基10～14份。
进一步地，上述高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯24份、脲醛树脂22份、聚氨酯热塑性弹性体22份、四氯化碳20份、聚乙烯蜡乳液22份、氢化大豆油22份、乙酸丁酯20份、烯丙基硫醚22份、单氟磷酸钠22份、十二烷基乙氧基磺基甜菜碱20份、二苯并呋喃20份、乙酸铵20份、氯化亚铜22份、偏钛酸20份、富马酸二甲酯18份、二硫化四甲基秋兰姆22份、脱氢醋酸钠20份、玻璃纤维粉18份、甘油松香酯20份、5-氨基苯并咪唑酮18份、磷酸三(丁氧基乙基)酯18份、六溴环十二烷18份、三氯乙基磷酸酯16份、磷酸脒基脲12份、普鲁兰多糖10份、月桂醇硫酸钠10份、过氧苯甲酰10份、过氧化二苯甲酰10份、过氧化苯甲酰10份、过氧化氢叔丁基10份。
进一步地，上述高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯26份、脲醛树脂24份、聚氨酯热塑性弹性体24份、四氯化碳22份、聚乙烯蜡乳液24份、氢化大豆油24份、乙酸丁酯22份、烯丙基硫醚24份、单氟磷酸钠24份、十二烷基乙氧基磺基甜菜碱22份、二苯并呋喃22份、乙酸铵22份、氯化亚铜24份、偏钛酸22份、富马酸二甲酯20份、二硫化四甲基秋兰姆24份、脱氢醋酸钠22份、玻璃纤维粉20份、甘油松香酯22份、5-氨基苯并咪唑酮20份、磷酸三(丁氧基乙基)酯20份、六溴环十二烷20份、三氯乙基磷酸酯18份、磷酸脒基脲14份、普鲁兰多糖12份、月桂醇硫酸钠12份、过氧苯甲酰12份、过氧化二苯甲酰12份、过氧化苯甲酰12份、过氧化氢叔丁基12份。
进一步地，上述高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯28份、脲醛树脂26份、聚氨酯热塑性弹性体26份、四氯化碳24份、聚乙烯蜡乳液26份、氢化大豆油26份、乙酸丁酯24份、烯丙基硫醚26份、单氟磷酸钠26份、十二烷基乙氧基磺基甜菜碱24份、二苯并呋喃24份、乙酸铵24份、氯化亚铜26份、偏钛酸24份、富马酸二甲酯22份、二硫化四甲基秋兰姆26份、脱氢醋酸钠24份、玻璃纤维粉22份、甘油松香酯24份、5-氨基苯并咪唑酮22份、磷酸三(丁氧基乙基)酯22份、六溴环十二烷22份、三氯乙基磷酸酯20份、磷酸脒基脲16份、普鲁兰多糖14份、月桂醇硫酸钠14份、过氧苯甲酰14份、过氧化二苯甲酰14份、过氧化苯甲酰14份、过氧化氢叔丁基14份。
进一步地，所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶4～8∶1。
进一步地，所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶2～10∶1。
进一步地，所述三氯乙基磷酸酯的粘度在25℃为120～140mpa.s。
进一步地，所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2～4∶3～5∶1。
进一步地，所述聚乙烯蜡乳液的粘度在25℃为80～100mpa.s。
进一步地，上述高层建筑用电梯门板阻燃涂层制备方法步骤如下：
(1)将所述质量份数的聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮予以混合，超声高速分散，超声波频率为20～40KHz，分散速度5000～5400r/min左右，分散时间为30～60min；
(2)加入所述质量份数的磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖，超声高速分散，超声波频率为20～35KHz，分散速度4800～5200r/min左右，分散时间为30～50min；
(3)加入所述质量份数的月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基，超声高速分散，超声波频率为20～30KHz，分散速度4600～4800r/min左右，分散时间为20～40min；混合均匀后制得本品。
该发明的有益效果在于：本发明中的高层建筑用电梯门板阻燃涂层，由以下组分组成：聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮、磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖、月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基。本发明产品具有较为优越的阻燃、耐酸碱、防霉变抗菌性能，改善了产品性能。
具体实施方式
本发明中的高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯24～28份、脲醛树脂22～26份、聚氨酯热塑性弹性体22～26份、四氯化碳20～24份、聚乙烯蜡乳液22～26份、氢化大豆油22～26份、乙酸丁酯20～24份、烯丙基硫醚22～26份、单氟磷酸钠22～26份、十二烷基乙氧基磺基甜菜碱20～24份、二苯并呋喃20～24份、乙酸铵20～24份、氯化亚铜22～26份、偏钛酸20～24份、富马酸二甲酯18～22份、二硫化四甲基秋兰姆22～26份、脱氢醋酸钠20～24份、玻璃纤维粉18～22份、甘油松香酯20～24份、5-氨基苯并咪唑酮18～22份、磷酸三(丁氧基乙基)酯18～22份、六溴环十二烷18～22份、三氯乙基磷酸酯16～20份、磷酸脒基脲12～16份、普鲁兰多糖10～14份、月桂醇硫酸钠10～14份、过氧苯甲酰10～14份、过氧化二苯甲酰10～14份、过氧化苯甲酰10～14份、过氧化氢叔丁基10～14份。
所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶4～8∶1。
所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶2～10∶1。
所述三氯乙基磷酸酯的粘度在25℃为120～140mpa.s。
所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2～4∶3～5∶1。
所述聚乙烯蜡乳液的粘度在25℃为80～100mpa.s。
下面结合实施例对本发明的具体实施方式进行描述，以便更好的理解本发明。
实施例1
本实施例中的高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯24份、脲醛树脂22份、聚氨酯热塑性弹性体22份、四氯化碳20份、聚乙烯蜡乳液22份、氢化大豆油22份、乙酸丁酯20份、烯丙基硫醚22份、单氟磷酸钠22份、十二烷基乙氧基磺基甜菜碱20份、二苯并呋喃20份、乙酸铵20份、氯化亚铜22份、偏钛酸20份、富马酸二甲酯18份、二硫化四甲基秋兰姆22份、脱氢醋酸钠20份、玻璃纤维粉18份、甘油松香酯20份、5-氨基苯并咪唑酮18份、磷酸三(丁氧基乙基)酯18份、六溴环十二烷18份、三氯乙基磷酸酯16份、磷酸脒基脲12份、普鲁兰多糖10份、月桂醇硫酸钠10份、过氧苯甲酰10份、过氧化二苯甲酰10份、过氧化苯甲酰10份、过氧化氢叔丁基10份。
所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3∶4∶1。
所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3∶2∶1。
所述三氯乙基磷酸酯的粘度在25℃为120mpa.s。
所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2∶3∶1。
所述聚乙烯蜡乳液的粘度在25℃为80mpa.s。
上述高层建筑用电梯门板阻燃涂层制备方法步骤如下：
(1)将所述质量份数的聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮予以混合，超声高速分散，超声波频率为20kHz，分散速度5400r/min左右，分散时间为60min；
(2)加入所述质量份数的磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖，超声高速分散，超声波频率为20kHz，分散速度5200r/min左右，分散时间为50min；
(3)加入所述质量份数的月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基，超声高速分散，超声波频率为20kHz，分散速度4800r/min左右，分散时间为40min；混合均匀后制得本品。
实施例2
本实施例中的高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯26份、脲醛树脂24份、聚氨酯热塑性弹性体24份、四氯化碳22份、聚乙烯蜡乳液24份、氢化大豆油24份、乙酸丁酯22份、烯丙基硫醚24份、单氟磷酸钠24份、十二烷基乙氧基磺基甜菜碱22份、二苯并呋喃22份、乙酸铵22份、氯化亚铜24份、偏钛酸22份、富马酸二甲酯20份、二硫化四甲基秋兰姆24份、脱氢醋酸钠22份、玻璃纤维粉20份、甘油松香酯22份、5-氨基苯并咪唑酮20份、磷酸三(丁氧基乙基)酯20份、六溴环十二烷20份、三氯乙基磷酸酯18份、磷酸脒基脲14份、普鲁兰多糖12份、月桂醇硫酸钠12份、过氧苯甲酰12份、过氧化二苯甲酰12份、过氧化苯甲酰12份、过氧化氢叔丁基12份。
所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为4∶6∶1。
所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为4∶6∶1。
所述三氯乙基磷酸酯的粘度在25℃为130mpa.s。
所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为3∶4∶1。
所述聚乙烯蜡乳液的粘度在25℃为90mpa.s。
上述高层建筑用电梯门板阻燃涂层制备方法步骤如下：
(1)将所述质量份数的聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮予以混合，超声高速分散，超声波频率为30kHz，分散速度5200r/min左右，分散时间为45min；
(2)加入所述质量份数的磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖，超声高速分散，超声波频率为27kHz，分散速度5000r/min左右，分散时间为40min；
(3)加入所述质量份数的月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基，超声高速分散，超声波频率为25kHz，分散速度4700r/min左右，分散时间为30min；混合均匀后制得本品。
实施例3
本实施例中的高层建筑用电梯门板阻燃涂层，由以下质量份数的组分组成：聚氯乙烯28份、脲醛树脂26份、聚氨酯热塑性弹性体26份、四氯化碳24份、聚乙烯蜡乳液26份、氢化大豆油26份、乙酸丁酯24份、烯丙基硫醚26份、单氟磷酸钠26份、十二烷基乙氧基磺基甜菜碱24份、二苯并呋喃24份、乙酸铵24份、氯化亚铜26份、偏钛酸24份、富马酸二甲酯22份、二硫化四甲基秋兰姆26份、脱氢醋酸钠24份、玻璃纤维粉22份、甘油松香酯24份、5-氨基苯并咪唑酮22份、磷酸三(丁氧基乙基)酯22份、六溴环十二烷22份、三氯乙基磷酸酯20份、磷酸脒基脲16份、普鲁兰多糖14份、月桂醇硫酸钠14份、过氧苯甲酰14份、过氧化二苯甲酰14份、过氧化苯甲酰14份、过氧化氢叔丁基14份。
所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为5∶8∶1。
所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为5∶10∶1。
所述三氯乙基磷酸酯的粘度在25℃为140mpa.s。
所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为4∶5∶1。
所述聚乙烯蜡乳液的粘度在25℃为100mpa.s。
上述高层建筑用电梯门板阻燃涂层制备方法步骤如下：
(1)将所述质量份数的聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮予以混合，超声高速分散，超声波频率为40kHz，分散速度5000r/min，分散时间为30min；
(2)加入所述质量份数的磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖，超声高速分散，超声波频率为35kHz，分散速度4800r/min，分散时间为30min；
(3)加入所述质量份数的月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基，超声高速分散，超声波频率为30kHz，分散速度4600r/min左右，分散时间为20min；混合均匀后制得本品。
针对实施例1、实施例2和实施例3中的产品和某市售产品进行性能测量，所测得的数据如表1所示。防火阻燃等级测试采用UL94标准。
表1性能测试结果
可见，本发明产品具有较好的耐腐蚀、防火阻燃、防霉变、抗菌性能。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。
Claims (10)
1.一种高层建筑用电梯门板阻燃涂层，其特征在于：由以下质量份数的组分组成：聚氯乙烯24～28份、脲醛树脂22～26份、聚氨酯热塑性弹性体22～26份、四氯化碳20～24份、聚乙烯蜡乳液22～26份、氢化大豆油22～26份、乙酸丁酯20～24份、烯丙基硫醚22～26份、单氟磷酸钠22～26份、十二烷基乙氧基磺基甜菜碱20～24份、二苯并呋喃20～24份、乙酸铵20～24份、氯化亚铜22～26份、偏钛酸20～24份、富马酸二甲酯18～22份、二硫化四甲基秋兰姆22～26份、脱氢醋酸钠20～24份、玻璃纤维粉18～22份、甘油松香酯20～24份、5-氨基苯并咪唑酮18～22份、磷酸三(丁氧基乙基)酯18～22份、六溴环十二烷18～22份、三氯乙基磷酸酯16～20份、磷酸脒基脲12～16份、普鲁兰多糖10～14份、月桂醇硫酸钠10～14份、过氧苯甲酰10～14份、过氧化二苯甲酰10～14份、过氧化苯甲酰10～14份、过氧化氢叔丁基10～14份。
2.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述高层建筑用电梯门板阻燃涂层由以下质量份数的组分组成：聚氯乙烯24份、脲醛树脂22份、聚氨酯热塑性弹性体22份、四氯化碳20份、聚乙烯蜡乳液22份、氢化大豆油22份、乙酸丁酯20份、烯丙基硫醚22份、单氟磷酸钠22份、十二烷基乙氧基磺基甜菜碱20份、二苯并呋喃20份、乙酸铵20份、氯化亚铜22份、偏钛酸20份、富马酸二甲酯18份、二硫化四甲基秋兰姆22份、脱氢醋酸钠20份、玻璃纤维粉18份、甘油松香酯20份、5-氨基苯并咪唑酮18份、磷酸三(丁氧基乙基)酯18份、六溴环十二烷18份、三氯乙基磷酸酯16份、磷酸脒基脲12份、普鲁兰多糖10份、月桂醇硫酸钠10份、过氧苯甲酰10份、过氧化二苯甲酰10份、过氧化苯甲酰10份、过氧化氢叔丁基10份。
3.根据权利要求1至2所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述高层建筑用电梯门板阻燃涂层由以下质量份数的组分组成：聚氯乙烯26份、脲醛树脂24份、聚氨酯热塑性弹性体24份、四氯化碳22份、聚乙烯蜡乳液24份、氢化大豆油24份、乙酸丁酯22份、烯丙基硫醚24份、单氟磷酸钠24份、十二烷基乙氧基磺基甜菜碱22份、二苯并呋喃22份、乙酸铵22份、氯化亚铜24份、偏钛酸22份、富马酸二甲酯20份、二硫化四甲基秋兰姆24份、脱氢醋酸钠22份、玻璃纤维粉20份、甘油松香酯22份、5-氨基苯并咪唑酮20份、磷酸三(丁氧基乙基)酯20份、六溴环十二烷20份、三氯乙基磷酸酯18份、磷酸脒基脲14份、普鲁兰多糖12份、月桂醇硫酸钠12份、过氧苯甲酰12份、过氧化二苯甲酰12份、过氧化苯甲酰12份、过氧化氢叔丁基12份。
4.根据权利要求1至3所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述高层建筑用电梯门板阻燃涂层由以下质量份数的组分组成：聚氯乙烯28份、脲醛树脂26份、聚氨酯热塑性弹性体26份、四氯化碳24份、聚乙烯蜡乳液26份、氢化大豆油26份、乙酸丁酯24份、烯丙基硫醚26份、单氟磷酸钠26份、十二烷基乙氧基磺基甜菜碱24份、二苯并呋喃24份、乙酸铵24份、氯化亚铜26份、偏钛酸24份、富马酸二甲酯22份、二硫化四甲基秋兰姆26份、脱氢醋酸钠24份、玻璃纤维粉22份、甘油松香酯24份、5-氨基苯并咪唑酮22份、磷酸三(丁氧基乙基)酯22份、六溴环十二烷22份、三氯乙基磷酸酯20份、磷酸脒基脲16份、普鲁兰多糖14份、月桂醇硫酸钠14份、过氧苯甲酰14份、过氧化二苯甲酰14份、过氧化苯甲酰14份、过氧化氢叔丁基14份。
5.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述玻璃纤维粉由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶4～8∶1。
6.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述氯化亚铜由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～5∶2～10∶1。
7.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述三氯乙基磷酸酯的粘度在25℃为120～140mpa.s。
8.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述月桂醇硫酸钠由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2～4∶3～5∶1。
9.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述聚乙烯蜡乳液的粘度在25℃为80～100mpa.s。
10.根据权利要求1所述的高层建筑用电梯门板阻燃涂层，其特征在于：所述高层建筑用电梯门板阻燃涂层制备方法步骤如下：
(1)将所述质量份数的聚氯乙烯、脲醛树脂、聚氨酯热塑性弹性体、四氯化碳、聚乙烯蜡乳液、氢化大豆油、乙酸丁酯、烯丙基硫醚、单氟磷酸钠、十二烷基乙氧基磺基甜菜碱、二苯并呋喃、乙酸铵、氯化亚铜、偏钛酸、富马酸二甲酯、二硫化四甲基秋兰姆、脱氢醋酸钠、玻璃纤维粉、甘油松香酯、5-氨基苯并咪唑酮予以混合，超声高速分散，超声波频率为20～40KHz，分散速度约5000～5400r/min，分散时间为30～60min左右；
(2)加入所述质量份数的磷酸三(丁氧基乙基)酯、六溴环十二烷、三氯乙基磷酸酯、磷酸脒基脲、普鲁兰多糖，超声高速分散，超声波频率为20～35KHz，分散速度为约4800～5200r/min，分散时间为30～50min左右；
(3)加入所述质量份数的月桂醇硫酸钠、过氧苯甲酰、过氧化二苯甲酰、过氧化苯甲酰、过氧化氢叔丁基，超声高速分散，超声波频率为20～30KHz，分散速度为约4600～4800r/min，分散时间为20～40min左右；混合均匀后制得本品。