CN106630907A - 一种加固材料及其制备方法 - Google Patents
一种加固材料及其制备方法 Download PDFInfo
- Publication number
- CN106630907A CN106630907A CN201611100957.9A CN201611100957A CN106630907A CN 106630907 A CN106630907 A CN 106630907A CN 201611100957 A CN201611100957 A CN 201611100957A CN 106630907 A CN106630907 A CN 106630907A
- Authority
- CN
- China
- Prior art keywords
- parts
- portland cement
- cement
- powder
- carclazyte
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种加固材料及其制备方法,由以下质量份数配方成分组成:水玻璃5‑15份、白土5‑7份、硅酸盐水泥6‑8份、普通硅酸盐水泥5‑7份、岩粉15‑25份、丁苯胶乳2‑4份、白水泥6‑8份、钢渣微粉2‑4份、滑石粉10‑20份、减水剂2‑4份、纤维素醚3‑5份、消泡剂4‑6份、调凝剂4‑6份,本发明可保持长时间输送不泌水、施工简单、操作方便。该材料与煤岩体有良好的粘结能力、加固煤岩体具有合适的强度、浆液无毒、价格低廉,可广泛用于各类破碎煤岩体的加固。
Description
技术领域
本发明涉及材料领域,具体而言涉及一种加固材料及其制备方法。
背景技术
煤炭在我国一次能源生产和消费结构中始终占70%左右。随着煤矿开采深度的增加煤质破碎变软。矿井开采过程中片帮、冒顶事故不断增加,给工作面的开采带来了严重影响。因此,确保煤岩体的稳定,防止工作面发生片帮冒顶,实现稳产高产及安全生产,是采煤过程中必须解决的问题之一。煤岩体注浆加固材料是解决这一问题的有效手段,它能将原来裂隙发育的破碎煤岩体固结成为完整性较好的煤岩体,可有效地防止片帮冒顶事故的发生。
为了减小片帮和冒顶的危险向松软和破碎的煤体中注入注浆材料,提高煤体强度,使破碎的煤岩体能发展成为一个整体,增加阻碍煤与瓦斯突出的阻力。目前用于注浆的材料主要分为以下三类:化学浆液类;水泥类;复合浆材类。化学浆液属于真溶液型,配成的浆液不易出现颗粒的离析,一般粘度较低,易于进入细小裂隙或孔隙之中,浆液注入能力较强,但由于其造价一般都很高,浆液成分中一般都有含量不等的有害化合物,处理不好常会造成不同程度的环境污染,很难大范围应用于井下注浆工程。水泥浆材由于较差的析水性和稳定性以及颗粒粒径本身的限制,水泥类浆材对较小裂隙注浆体的注浆表现出局限性。复合浆材类,其主要是在水泥材料的基础上添加各种聚合物化学浆液,将水泥浆材和化学浆材的优点结合起来,使水泥浆材的性能得到改善,以达到不同注浆环境下的应用目的。正是因为复合浆材的优点目前受到广泛的关注和研究。由于井下煤体注浆的特殊环境,我们选择水泥基聚合物复合浆材来进行研究。
发明内容
本发明提供了一种加固材料及其制备方法,本发明可保持长时间输送不泌水、施工简单、操作方便。该材料与煤岩体有良好的粘结能力、加固煤岩体具有合适的强度、浆液无毒、价格低廉,可广泛用于各类破碎煤岩体的加固。
为实现上述目的,本发明提供如下技术方案:
一种加固材料及其制备方法,由以下质量份数配方成分组成:水玻璃5-15份、白土5-7份、硅酸盐水泥6-8份、普通硅酸盐水泥5-7份、岩粉15-25份、丁苯胶乳2-4份、白水泥6-8份、钢渣微粉2-4份、滑石粉10-20份、减水剂2-4份、纤维素醚3-5份、消泡剂4-6份、调凝剂4-6份。
进一步:由以下质量份数配方成分组成:水玻璃5份、白土5份、硅酸盐水泥6份、普通硅酸盐水泥5份、岩粉15份、丁苯胶乳2份、白水泥6份、钢渣微粉2份、滑石粉10份、减水剂2份、纤维素醚3份、消泡剂4份、调凝剂4份。
进一步:由以下质量份数配方成分组成:水玻璃10份、白土6份、硅酸盐水泥7份、普通硅酸盐水泥6份、岩粉20份、丁苯胶乳3份、白水泥7份、钢渣微粉3份、滑石粉15份、减水剂3份、纤维素醚4份、消泡剂5份、调凝剂5份。
进一步:由以下质量份数配方成分组成:水玻璃15份、白土7份、硅酸盐水泥8份、普通硅酸盐水泥7份、岩粉25份、丁苯胶乳4份、白水泥8份、钢渣微粉4份、滑石粉20份、减水剂4份、纤维素醚5份、消泡剂6份、调凝剂6份。
进一步:本发明制备方法具有如下步骤:
步骤一、选取粒度筛选合适的普通硅酸盐水泥;
步骤二、按照配方将普通硅酸盐水泥、奈系减水剂等粉料称量好进行预混,将水、消泡剂、三乙醇胺按等其余原料照配方加入搅拌机中与粉料一起进行搅拌。
步骤三、最后加入合适比例的调凝剂,混合搅拌均匀既得成品。
本发明的有益效果是:
1、本发明可保持长时间输送不泌水、施工简单、操作方便;
2、该材料与煤岩体有良好的粘结能力、加固煤岩体具有合适的强度、浆液无毒、价格低廉;
3、可广泛用于各类破碎煤岩体的加固。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例一:
一种加固材料由以下质量份数配方成分组成:水玻璃5-15份、白土5-7份、硅酸盐水泥6-8份、普通硅酸盐水泥5-7份、岩粉15-25份、丁苯胶乳2-4份、白水泥6-8份、钢渣微粉2-4份、滑石粉10-20份、减水剂2-4份、纤维素醚3-5份、消泡剂4-6份、调凝剂4-6份。
实施例二:
一种加固材料由以下质量份数配方成分组成:水玻璃5份、白土5份、硅酸盐水泥6份、普通硅酸盐水泥5份、岩粉15份、丁苯胶乳2份、白水泥6份、钢渣微粉2份、滑石粉10份、减水剂2份、纤维素醚3份、消泡剂4份、调凝剂4份。
实施例三:
一种加固材料由以下质量份数配方成分组成:水玻璃10份、白土6份、硅酸盐水泥7份、普通硅酸盐水泥6份、岩粉20份、丁苯胶乳3份、白水泥7份、钢渣微粉3份、滑石粉15份、减水剂3份、纤维素醚4份、消泡剂5份、调凝剂5份。
实施例四:
一种加固材料由以下质量份数配方成分组成:水玻璃15份、白土7份、硅酸盐水泥8份、普通硅酸盐水泥7份、岩粉25份、丁苯胶乳4份、白水泥8份、钢渣微粉4份、滑石粉20份、减水剂4份、纤维素醚5份、消泡剂6份、调凝剂6份。
实施例五:
一种加固材料的制备方法制备方法包括如下步骤:
步骤一、选取粒度筛选合适的普通硅酸盐水泥;
步骤二、按照配方将普通硅酸盐水泥、奈系减水剂等粉料称量好进行预混,将水、消泡剂、三乙醇胺按等其余原料照配方加入搅拌机中与粉料一起进行搅拌。
步骤三、最后加入合适比例的调凝剂,混合搅拌均匀既得成品。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种加固材料,其特征在于:由以下质量份数配方成分组成:
水玻璃5-15份、白土5-7份、硅酸盐水泥6-8份、普通硅酸盐水泥5-7份、岩粉15-25份、丁苯胶乳2-4份、白水泥6-8份、钢渣微粉2-4份、滑石粉10-20份、减水剂2-4份、纤维素醚3-5份、消泡剂4-6份、调凝剂4-6份。
2.根据权利要求1所述的一种加固材料,其特征在于:由以下质量份数配方成分组成:
水玻璃5份、白土5份、硅酸盐水泥6份、普通硅酸盐水泥5份、岩粉15份、丁苯胶乳2份、白水泥6份、钢渣微粉2份、滑石粉10份、减水剂2份、纤维素醚3份、消泡剂4份、调凝剂4份。
3.根据权利要求1所述的一种加固材料,其特征在于:由以下质量份数配方成分组成:
水玻璃10份、白土6份、硅酸盐水泥7份、普通硅酸盐水泥6份、岩粉20份、丁苯胶乳3份、白水泥7份、钢渣微粉3份、滑石粉15份、减水剂3份、纤维素醚4份、消泡剂5份、调凝剂5份。
4.根据权利要求1所述的一种加固材料,其特征在于:由以下质量份数配方成分组成:
水玻璃15份、白土7份、硅酸盐水泥8份、普通硅酸盐水泥7份、岩粉25份、丁苯胶乳4份、白水泥8份、钢渣微粉4份、滑石粉20份、减水剂4份、纤维素醚5份、消泡剂6份、调凝剂6份。
5.一种根据权利要求1所述的一种加固材料的制备方法,其特征在于:包括如下步骤:
步骤一、选取粒度筛选合适的普通硅酸盐水泥;
步骤二、按照配方将普通硅酸盐水泥、奈系减水剂等粉料称量好进行预混,将水、消泡剂、三乙醇胺按等其余原料照配方加入搅拌机中与粉料一起进行搅拌。
步骤三、最后加入合适比例的调凝剂,混合搅拌均匀既得成品。