CN106630864A - A caulking compound used for tiles - Google Patents
A caulking compound used for tiles Download PDFInfo
- Publication number
- CN106630864A CN106630864A CN201510714718.1A CN201510714718A CN106630864A CN 106630864 A CN106630864 A CN 106630864A CN 201510714718 A CN201510714718 A CN 201510714718A CN 106630864 A CN106630864 A CN 106630864A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- tiles
- agent
- gap filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a caulking compound used for tiles, and belongs to the technical field of building materials. The caulking compound is characterized by being prepared from, by weight, 20-50 parts of quartz sand, 4-6 parts of calcium carbonate, 8-12 parts of calcium sulfoaluminate cement, 1-3 parts of an antioxidant, 0.2-0.6 part of cellulose ether, 1-3 parts of a mildew inhibitor, 1-3 parts of an inorganic aluminium salt waterproof agent, 20-30 parts of silicone emulsion, 20-30 parts of acrylic acid emulsion, 1-2 parts of a bactericide, 1-2 parts of a defoamer and 2-3 parts of a thickening agent. The caulking compound is characterized by being alkali-resistant, mildew-resistant, waterproof, weather-proof, and the like, and can be used for tiles at dry and wet positions, effects are durable, influences of the environment are few, and the service lifetime of the tiles can be effectively prolonged.
Description
Technical field
The present invention relates to a kind of ceramic tile gap filler, belongs to building material technical field.
Background technology
The paving of ceramic tile becomes a kind of universal decoration in daily life, from household to hotel and other public places, from ground to metope, the decorative effect that ceramic tile brings can't neglect, but during paving, the joint filling between fragment of brick and fragment of brick is needed through special handling, all it is generally filling gap filler, present gap filler water proofing property, thermostability are all bad, are easily caused ceramic tile and come off, and affect attractive in appearance and use.
The content of the invention
It is an object of the invention to solve the deficiency of above-mentioned gap filler, there is provided a kind of resistance to water and heat-resist, use time length and dedicated for the gap filler of ceramic tile.
A kind of ceramic tile of the present invention is achieved through the following technical solutions with gap filler：
A kind of ceramic tile gap filler, is made using the raw material of following weight portion：
Quartz sand 20-50 parts, Calcium Carbonate 4-6 part, sulphate aluminium cement 8-12 parts, antioxidant 1-3 parts, cellulose ether 0.2-0.6 parts, antifungus agent 1-3 parts, inorganic aluminate water-proof agent 1-3 parts, organic silicon emulsion 20-30 parts, acrylic emulsion 20-30 parts, antibacterial 1-2 parts, defoamer 1-2 parts, thickening agent 2-3 parts；
Wherein, the solid content of the acrylic emulsion is 52%～55%；
Preferably, 40 parts of quartz sand, 5 parts of Calcium Carbonate, 10 parts of sulphate aluminium cement, 2 parts of antioxidant, 0.5 part of cellulose ether, antifungus agent 2
Part, 2 parts of inorganic aluminate water-proof agent, 25 parts of organic silicon emulsion, 25 parts of acrylic emulsion, 2 parts of antibacterial, 2 parts of defoamer, 2 parts of thickening agent.
The ceramic tile gap filler of the present invention, with alkali resistant, anti-mildew, waterproof, it is weather-proof the features such as, can be widely used for being dried and moist position ceramic tile, effect is persistently, affected by environment little, effectively extends the service life of ceramic tile.
Specific embodiment
Form by the following examples, the above of the present invention is described in further detail again, but this scope for being interpreted as above-mentioned theme of the invention should not be only limitted to Examples below, all technologies realized based on the above of the present invention belong to the scope of the present invention.
Embodiment 1：A kind of ceramic tile gap filler, is made using the raw material of following weight portion：
20 parts of quartz sand, 4 parts of Calcium Carbonate, 8 parts of sulphate aluminium cement, 1 part of antioxidant, cellulose ether
0.2 part, 1 part of antifungus agent, 1 part of inorganic aluminate water-proof agent, 20 parts of organic silicon emulsion, 20 parts of acrylic emulsion, 1 part of antibacterial, 1 part of defoamer, thickening agent 2
Part；
Wherein, the solid content of the acrylic emulsion is 52%.
Embodiment 2：A kind of ceramic tile gap filler, is made using the raw material of following weight portion：
40 parts of quartz sand, 5 parts of Calcium Carbonate, 10 parts of sulphate aluminium cement, 2 parts of antioxidant, 0.5 part of cellulose ether, antifungus agent 2
Part, 2 parts of inorganic aluminate water-proof agent, 25 parts of organic silicon emulsion, 25 parts of acrylic emulsion, 2 parts of antibacterial, 2 parts of defoamer, 2 parts of thickening agent.
Wherein, the solid content of the acrylic emulsion is 53%～55%.
Embodiment 3：A kind of ceramic tile gap filler, is made using the raw material of following weight portion：
50 parts of quartz sand, 6 parts of Calcium Carbonate, 12 parts of sulphate aluminium cement, 3 parts of antioxidant, 0.6 part of cellulose ether, 3 parts of antifungus agent, 3 parts of inorganic aluminate water-proof agent, 30 parts of organic silicon emulsion, 30 parts of acrylic emulsion, 2 parts of antibacterial, 2 parts of defoamer, 3 parts of thickening agent；
Wherein, the solid content of the acrylic emulsion is 55%.
Claims (3)
1. a kind of ceramic tile gap filler, it is characterised in that：Made using the raw material of following weight portion：
Quartz sand 20-50 parts, Calcium Carbonate 4-6 part, sulphate aluminium cement 8-12 parts, antioxidant 1-3
Part, cellulose ether 0.2-0.6 parts, antifungus agent 1-3 parts, inorganic aluminate water-proof agent 1-3 parts, organic silicon emulsion 20-30 parts, acrylic emulsion 20-30 parts, antibacterial 1-2 parts, defoamer 1-2
Part, thickening agent 2-3 parts.
2. a kind of ceramic tile gap filler according to claim 1, it is characterised in that：The solid content of the acrylic emulsion is 52%～55%.
3. a kind of ceramic tile gap filler according to claim 1 or claim 2, it is characterised in that：The ceramic tile gap filler, is made using the raw material of following weight portion：40 parts of quartz sand, 5 parts of Calcium Carbonate, 10 parts of sulphate aluminium cement, 2 parts of antioxidant, 0.5 part of cellulose ether, 2 parts of antifungus agent, 2 parts of inorganic aluminate water-proof agent, 25 parts of organic silicon emulsion, 25 parts of acrylic emulsion, 2 parts of antibacterial, 2 parts of defoamer, 2 parts of thickening agent.