CN106630676A - Spray-colored glass as well as production process and application - Google Patents
Spray-colored glass as well as production process and application Download PDFInfo
- Publication number
- CN106630676A CN106630676A CN201611155672.5A CN201611155672A CN106630676A CN 106630676 A CN106630676 A CN 106630676A CN 201611155672 A CN201611155672 A CN 201611155672A CN 106630676 A CN106630676 A CN 106630676A
- Authority
- CN
- China
- Prior art keywords
- ink
- glass
- spray
- layer
- glass body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses spray-colored glass as well as a production process and application. The spray-colored glass comprises a tempered glass body, an ink sprayed layer, a covering ink layer and an ink protection layer, wherein the low-temperature glass screen printed ink sprayed layer is arranged on one surface of the tempered glass body; the covering ink layer is arranged on the low-temperature glass screen printed ink sprayed layer; the ink protection layer is abutted on the covering ink layer. The spray-colored glass has the beneficial effect that the strength of the spray-colored glass is 3 to 5 times of that of an ordinary glass door panel. The breakage rate in the processes of transportation, mounting and use is greatly decreased. In addition, as tempered glass belongs to safety glass, the tempered glass cannot cause an injury to a human body even though being crushed; meanwhile, the attractiveness degree is increased; the cost is reduced; the purchase cost of a consumer is decreased.
Description
Technical field
The present invention relates to glass technology field, more particularly to a kind of spray colouration glass and production technology and application.
Background technology
Popular coloured glass on market again in recent years, coloured glass because color it is beautiful, environmentally friendly, it is easy to clean the features such as receive deeply
Consumer's likes, prior art is all, with the plate glass of 2-5 millimeters, to carry out cutting edging and then root after colouring using silk-screen
Finished product is made according to demand to use.
But, these products all have the shortcomings that one it is common, what is used is all ordinary plate glass, it is easy to ruptured,
And human body can be damaged after rupturing.The People's Republic of China (PRC) lives to build portion JGJ113-2015《Building glass application technology is advised
Journey》In to different-thickness ordinary plate glass maximum usable floor area have strict regulation.
The maximum usable floor area of plate glass, ultra-white float glass and vacuum glass:
Although safety glass is safer, simple glass is all to be cut after screen printing, if safety glass
Cut, because the characteristic of safety glass will all go to sticks and staves, become glass particle, so to glass in industry both at home and abroad
Color is all to adopt simple glass, security of the our company to increase coloured glass, is coloured using safety glass, and have developed one is
The technological process of row.
The content of the invention
For the deficiency in structure in prior art, it is an object of the invention to provide a kind of spray colouration glass and production
Technique and application, the security applicable for meeting coloured glass, colour to safety glass.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of spray colouration glass includes:Safety glass body, low temperature glass screen printing ink sprayed coating, covering ink
Layer and ink protective layer;Wherein,
The low temperature glass screen printing ink sprayed coating is arranged on the one side of the safety glass body, the covering oil
Layer of ink is arranged on above the low temperature glass screen printing ink sprayed coating, and the ink protective layer fits in the covering oil
Above layer of ink.
A kind of spray colouration process of glass flow process is:
A. select simple glass body, on demand size first cut then edging after carry out tempering again so as to indices
Reach the requirement of GB15763.2-2005 national standards;
B. ink is allocated, selects to use low temperature glass screen printing ink, made by every square metre of glass according to shade
With 80~120 grams of ink;
C. according to the recipe requirements addition curing agent using low temperature glass screen printing ink, and diluent is added, ink
It is 1 with the proportioning of diluent:2 are diluted to the viscosity of ink more than 1 centipoise less than 4000 centipoises, can use spray gun spraying,
After stirring, stand more than half an hour, ink is fully dissolved;
D. by safety glass body surface wiped clean;
E., the ink that step C is modulated is sprayed on the one side of the simple glass body of the tempering that step A is obtained with spray gun
On;
The glass body of the tempering for having sprayed ink that F. step E is obtained carries out constant temperature baking;
The glass body of the tempering of the coloring that G. baking that step F is obtained is completed applies one layer of grey on the surface of ink layer
Or white covers ink;
H. the product for step G being obtained pastes again last layer Boeing film outside covering ink layer.
A kind of application of spray colouration glass:
The spray colouration glass is used with backing material plate assembling and is applied to:Kitchen sliding door, cupboard door, toilet sliding door, window
Family, TV cabinet door, bookcase door, glass curtain wall and building decoration.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the spray colouration glass is provided with the aluminum alloy frame of a circle at its edge.
Further, the operating condition of spraying process described in step E is less than for indoor spraying, relative humidity
70%, temperature is not less than 5 DEG C.
Further, the temperature toasted in step F is 160 DEG C -220 DEG C.
Further, the time of the baking of constant temperature described in step F is 7-12 minutes.
The invention has the beneficial effects as follows:Its intensity is 3-5 times of simple glass door-plate.Greatly reduce transport, install,
Breakage rate during use.In addition because safety glass is belonging to safety glass, even if broken also will not cause wound to human body
Evil, while and increased aesthetics, cost is reduced, reduce the purchase cost of consumer.
Description of the drawings
Fig. 1 is the decomposition texture schematic diagram of the spray colouration glass of the present invention;
Fig. 2 is the brief process chart of the spray colouration glass of the present invention;
In FIG, the list of designations represented by each label is as follows:
1 safety glass body
2 ink sprayed coatings
3 cover ink layer
4 ink protective layers
Specific embodiment
The principle and feature of the present invention are described below in conjunction with accompanying drawing, example is served only for explaining the present invention, and
It is non-for limiting the scope of the present invention.
Please also refer to shown in Fig. 1, it is the decomposition texture schematic diagram of the spray colouration glass of the present invention.The spray colouration
Glass includes:Safety glass body 1, ink sprayed coating 2, covering ink layer 3 and ink protective layer 4;Wherein,
The ink sprayed coating 2 is arranged on the one side of the safety glass body 1 and adopts spray gun spraying, institute's ink sprayed coating
2 thickness is 0.1mm, and the ink sprayed coating 2 can not be too thin, and too thin easily show-through, color saturation is bad;Can not spray
Excessively, ink is excessively wasted, the covering ink layer 3 is arranged on above the ink sprayed coating 2, the covering ink layer 3
Color be grey or white, the colour rendering for increasing ink also acts as certain protective effect simultaneously;The ink protective layer 4
Fit in above the covering ink layer 3, the ink protective layer 4 is Boeing film, the cheap energy of the Boeing film
Enough prevent ink from being scratched when in use.
The ink sprayed coating 2 is low temperature glass screen printing ink sprayed coating.
Please also refer to shown in Fig. 2, it is the brief process chart of the spray colouration glass of the present invention;
The technological process of production of spray colouration glass of the present invention is:
A. select simple glass body, on demand size first cut then edging after carry out tempering again so as to indices
Reach the requirement of GB15763.2-2005 national standards;
B. ink is allocated, selects to use low temperature glass screen printing ink, made by every square metre of glass according to shade
With 80~120 grams of ink;
C. according to the recipe requirements addition curing agent using low temperature glass screen printing ink, and diluent is added, ink
It is 1 with the proportioning of diluent:2 are diluted to the viscosity of ink more than 1 centipoise less than 4000 centipoises, can use spray gun spraying,
After stirring, stand more than half an hour, ink is fully dissolved;
D. by safety glass body surface wiped clean;
E., the ink that step C is modulated is sprayed on the one side of the simple glass body of the tempering that step A is obtained with spray gun
On;Relative humidity is sprayed on less than 70%, temperature is not less than 5 DEG C of indoor spraying.
The glass body of the tempering for having sprayed ink that F. step E is obtained carries out constant temperature baking;The temperature of constant temperature baking
For 160 DEG C -220 DEG C, the time of constant temperature baking is 7-12 minutes
The glass body of the tempering of the coloring that G. baking that step F is obtained is completed applies one layer of grey on the surface of ink layer
Or white covers ink;
H. the product for step G being obtained pastes again last layer Boeing film outside covering ink layer.
The application of the spray colouration glass of the present invention:
The spray colouration glass is used with backing material plate assembling and is applied to:Kitchen sliding door, cupboard door, toilet sliding door, window
Family, TV cabinet door, bookcase door, glass curtain wall and building decoration.
The application of the spray colouration glass, the spray colouration glass is provided with the aluminum alloy frame of a circle at its edge
Frame, using in door, window and cut-off.
The foregoing is only presently preferred embodiments of the present invention, not to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (7)
1. a kind of spray colouration glass, it is characterised in that include:Safety glass body, ink sprayed coating, cover ink layer and
Ink protective layer;Wherein,
The ink sprayed coating is arranged on the one side of the safety glass body, and the covering ink layer is arranged on the ink spray
Above coating, the ink protective layer is fitted in above the covering ink layer.
2. according to the spray colouration glass described in claim 1, it is characterised in that the spray colouration glass sets at its edge
It is equipped with the aluminum alloy frame of a circle.
3. according to the spray colouration glass described in claim 1 in kitchen sliding door, cupboard door, toilet sliding door, window, TV
Application in cabinet door, bookcase door, glass curtain wall and building decoration.
4. a kind of spray colouration process of glass flow process, it is characterised in that:
A. select simple glass body, on demand size first cut then edging after carry out tempering again so as to indices reach
GB15763.2-2005 national standards are required;
B. ink is allocated, selects to use low temperature glass screen printing ink, oil is used by every square metre of glass according to shade
80~120 grams of ink;
C. according to the recipe requirements addition curing agent using low temperature glass screen printing ink, and add diluent, ink with it is dilute
The proportioning for releasing agent is 1:2 are diluted to the viscosity of ink more than 1 centipoise less than 4000 centipoises, can use spray gun spraying, stirring
After uniform, stand more than half an hour, ink is fully dissolved;
D. by safety glass body surface wiped clean;
E. the ink that step C is modulated is sprayed in the one side of simple glass body of the tempering that step A is obtained with spray gun;
The glass body of the tempering for having sprayed ink that F. step E is obtained carries out constant temperature baking;
The glass body of the tempering of the coloring that G. baking that step F is obtained is completed ink layer surface apply one layer of grey or
White covers ink;
H. the product for step G being obtained pastes again last layer Boeing film outside covering ink layer.
5. spray colouration process of glass flow process according to claim 4, it is characterised in that described in step E
The operating condition of spraying process is less than 70% for indoor spraying, relative humidity, and temperature is not less than 5 DEG C.
6. spray colouration process of glass flow process according to claim 4, it is characterised in that toast in step F
Temperature be 160 DEG C -220 DEG C.
7. spray colouration process of glass flow process according to claim 4, it is characterised in that described in step F
The time of constant temperature baking is 7-12 minutes.