CN106626935A - High-temperature preparing method of metallic color effect embosses capable of overlaying gold and metallic color effect embosses - Google Patents
High-temperature preparing method of metallic color effect embosses capable of overlaying gold and metallic color effect embosses Download PDFInfo
- Publication number
- CN106626935A CN106626935A CN201610878307.0A CN201610878307A CN106626935A CN 106626935 A CN106626935 A CN 106626935A CN 201610878307 A CN201610878307 A CN 201610878307A CN 106626935 A CN106626935 A CN 106626935A
- Authority
- CN
- China
- Prior art keywords
- embossment
- golden
- marble paper
- glaze
- metallochrome
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a high-temperature preparing method of metallic color effect embosses capable of overlaying gold and metallic color effect embosses. The preparing method comprises the ratio of colored embosses, the ratio of metallic color effect glaze, the ratio of colored glaze for stained paper and the ratio of the metallic color effect glaze in the metallic color effect embosses. The high-temperature preparing method of the metallic color effect embosses capable of overlaying gold and metallic color effect embosses comprises the following steps: S1, screening raw materials; S2, stirring; S3, grinding; S4, cleaning the materials; S5, printing a gold film; S6, printing the metallic color effect embosses capable of overlaying gold, printing the colored embosses or printing colored glaze; S7, overlapping metal color glaze; S8, sintering; and S9, preparing a finished product. The gold content of the gold film is not limited, and the gold film can be changed into a photoelectric film or the metallic effect glaze. When being sintered, the metallic color effect embosses capable of overlapping the gold and the metallic color effect embosses show pearlescent flickering metallic luster at a low temperature and show mirror flickering metallic luster at a high temperature. The preparing formula and technology are very energy-saving and environment-friendly.
Description
Technical field
The present invention relates to the field of ceramics, enamel or glass decoration metallochrome effect embossment and metallochrome effect, especially relates to
And a kind of high temperature can fold the product of golden metallochrome effect embossment and the product of metallochrome effect.
Background technology
The present invention be directed to the class for consuming gold process and metallic luster technique and researching and developing in the decoration such as ceramics, enamel, glass
Metallike effect alternative；Plane gold and anaglyph of the present invention in for glass, ceramic product is (disposable with gold
Embossment is golden, Secondary embossment is golden) alternative of similar Gold production effect well is provided, and present there is provided more
Effect, except the golden yellow metallochrome effect for substituting gold and the imitative argentine of golden yellow metallochrome effect embossment and replacement platinum
Outside color effect and imitative silver metallic effect embossment, the metallochrome effect and metallochrome effect that can be made into shades of colour is floated
Carving, the such as metallochrome effect and metallochrome effect embossment of the bluish-green black and white color of reddish yellow, due to side property embossment it is golden and Secondary
Embossment gold is first to do one layer of golden film of embossment bonnet, thus it is higher to the requirement of golden film gold content, typically require gold content in 8%-
More than 12%, so causing a large amount of consumption of gold, fold after golden film because the metallochrome effect embossment of the present invention can first do
Embossment, so not limiting the gold content of golden film, and can change electric light film or imitative metallochrome into, so as to reduce golden film
Whether consumption to gold or not gold, for this purpose, we have proposed a kind of high temperature can fold golden metallochrome effect embossment and metal
The preparation method of color effect.
The content of the invention
The invention aims to the shortcomings of there is a large amount of consumption of gold in prior art is solved, and the one kind for proposing
High temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method.
To achieve these goals, present invention employs following technical scheme：A kind of high temperature can fold golden metallochrome effect and float
Carving and metallochrome effect preparation method, the high temperature can fold the dispensing percentage by weight of golden metallochrome effect embossment and metallochrome effect
Than as follows：
The proportioning of color embossment：
Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；
Marble paper is with transparent embossment glaze：25%；
Marble paper varnish：40%；
Golden metallochrome effect embossment proportioning can be folded：
Pearl mica powder pigment：10%；
Low temperature oil plant：40%；
Marble paper varnish：50%；
The proportioning of marble paper coloured glaze：
Marble paper coloured glaze：65%；
Marble paper varnish：35%；
The proportioning of metallochrome effect glaze：
Pearl mica powder pigment：12.5%；
Low temperature oil plant：20%；
Marble paper coloured glaze：12.5%；
Marble paper varnish：55%.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the high temperature
Golden metallochrome effect embossment can be folded and metallochrome effect preparation method comprises the steps：
S1：Raw material screening：Percentage by above-mentioned formula is constituted is equipped with the proportioning of color embossment：Pearl mica powder pigment：
10%；Marble paper coloured glaze：30%；Marble paper is with transparent embossment glaze：25%；Marble paper varnish：40%；Golden metallochrome effect can be folded
Fruit embossment proportioning：Pearl mica powder pigment：10%；Low temperature oil plant：40%；Marble paper varnish：50%；Marble paper coloured glaze
Proportioning：Marble paper coloured glaze：65%；Marble paper varnish：35%；The proportioning of metallochrome effect glaze：Pearl mica powder pigment：
12.5%；Low temperature oil plant：20%；Marble paper coloured glaze：12.5%；Marble paper varnish：55%；
S2：Stirring：Each group dispensing in above-mentioned steps S1 is put into respectively in ready stirred autoclave and is fully stirred
Mix to pasty state, for future use；
S3：Grinding：The dispensing that is stirred will be grouped in above-mentioned steps S2 puts in lapping device respectively and be ground, directly
To printing performance requirement is reached, being obtained can fold golden metallochrome effect embossment, color embossment, metallochrome effect glaze and coloured glaze, with
Standby rear use；
S4：Cleaning material：The material cleaning such as ceramics, enamel or glass of glazing will be prepared clean；
S5：Bronze printing film：300-400 mesh is used in the materials such as clean ceramics, enamel or glass by cleaning in above-mentioned steps S4
One layer of marble paper gold paste of serigraphy, is obtained golden film；
S6：Print can fold golden metallochrome effect embossment/print color embossment/print coloured glaze：By it is obtained in above-mentioned steps S3 can
Folded gold metallochrome effect embossment 200-120 mesh silk screen double exposures float obtained color in above-mentioned steps S3 3-8 time in golden film
Carving is folded obtained coloured glaze in above-mentioned steps S3 with 200-120 mesh silk screens with 3-8 time in 200-120 mesh silk screen double exposure golden films
It is imprinted on 1 time in golden film；
S7：Folded metallochrome effect glaze：Obtained metallochrome effect glaze in above-mentioned steps S3 is floated can fold golden metal effect
With 200-120 mesh serigraphy 1-2 time on carving, color embossment and coloured glaze, then dry, semi-finished product are obtained.
S8：Fire：Semi-finished product after drying in above-mentioned steps S7 are put in high-temperature cellar stove, 520-800 DEG C is warming up to, are protected
Warm 5-15 minutes.
S9：Finished product：Material after firing in above-mentioned steps S8 is taken out, room temperature, finished product is cooled to.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the step
The type of cooling in rapid S9 is natural cooling.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the step
Stirred autoclave in rapid S2 is ball grinder.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the step
The mode printed in rapid S6 directly prints or water transfer pictures for glazing, Freehandhand-drawing, silk screen.
A kind of high temperature that the present invention is provided can fold golden metallochrome effect embossment and metallochrome effect preparation method, for glass
Plane gold and anaglyph in glass, ceramic product gold (disposable embossment is golden, Secondary embossment is golden) provides good
The alternative of similar Gold production effect, and effect is presented there is provided more, except the golden yellow metallochrome effect for substituting gold
Outside the imitative silver metallic effect and imitative silver metallic effect embossment of fruit and golden yellow metallochrome effect embossment and replacement platinum,
Can be made into the metallochrome effect and metallochrome effect embossment of shades of colour, such as the metallochrome effect of the bluish-green black and white color of reddish yellow
Fruit and metallochrome effect embossment, fold after golden film embossment, so to golden film because the metallochrome effect embossment of the present invention can first do
Gold content do not limit, and golden film can be changed into electric light film or imitative metallochrome, so as to reduce the consumption to gold
Or gold is not consumed, and environmental protection and the energy conservation characteristic of the material have been fully demonstrated, while firing temperature is low, making formula and technique are all
Very energy-conserving and environment-protective.
Description of the drawings
Fig. 1 is manufacturing process flow diagram of the present invention.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that specific embodiment described herein is only to explain the present invention, not
For limiting the present invention.
Embodiment one
A kind of high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, and the high temperature can fold golden metallochrome effect
The dispensing of fruit embossment and metallochrome effect is as follows by weight percentage：
The proportioning of color embossment：
Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；
Marble paper is with transparent embossment glaze：25%；
Marble paper varnish：40%；
Golden metallochrome effect embossment proportioning can be folded：
Pearl mica powder pigment：10%；
Low temperature oil plant：40%；
Marble paper varnish：50%；
The proportioning of marble paper coloured glaze：
Marble paper coloured glaze：65%；
Marble paper varnish：35%；
The proportioning of metallochrome effect glaze：
Pearl mica powder pigment：12.5%；
Low temperature oil plant：20%；
Marble paper coloured glaze：12.5%；
Marble paper varnish：55%.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the high temperature
Golden metallochrome effect embossment can be folded and metallochrome effect preparation method comprises the steps：
S1：Raw material screening：Percentage by above-mentioned formula is constituted is equipped with the proportioning of color embossment：Pearl mica powder pigment：
10%；Marble paper coloured glaze：30%；Marble paper is with transparent embossment glaze：25%；Marble paper varnish：40%；Golden metallochrome effect can be folded
Fruit embossment proportioning：Pearl mica powder pigment：10%；Low temperature oil plant：40%；Marble paper varnish：50%；Marble paper coloured glaze
Proportioning：Marble paper coloured glaze：65%；Marble paper varnish：35%；The proportioning of metallochrome effect glaze：Pearl mica powder pigment：
12.5%；Low temperature oil plant：20%；Marble paper coloured glaze：12.5%；Marble paper varnish：55%；
S2：Stirring：Each group dispensing in above-mentioned steps S1 is put into respectively in ready stirred autoclave and is fully stirred
Mix to pasty state, for future use, stirred autoclave is ball grinder；
S3：Grinding：The dispensing that is stirred will be grouped in above-mentioned steps S2 puts in lapping device respectively and be ground, directly
To printing performance requirement is reached, being obtained can fold golden metallochrome effect embossment, color embossment, metallochrome effect glaze and coloured glaze, with
Standby rear use；
S4：Cleaning material：The material cleaning such as ceramics, enamel or glass of glazing will be prepared clean；
S5：Bronze printing film：300-400 mesh is used in the materials such as clean ceramics, enamel or glass by cleaning in above-mentioned steps S4
One layer of marble paper gold paste of serigraphy, is obtained golden film；
S6：Print can fold golden metallochrome effect embossment/print color embossment/print coloured glaze：By it is obtained in above-mentioned steps S3 can
Gold metallochrome effect embossment 200-120 mesh silk screen double exposures are folded 3 times in golden film, by obtained color embossment in above-mentioned steps S3
With 3 times in 200-120 mesh silk screen double exposure golden films, obtained coloured glaze in above-mentioned steps S3 is existed with 200-120 mesh silk screen double exposures
1 time in golden film, the mode of printing directly prints or water transfer pictures for glazing, Freehandhand-drawing, silk screen；
S7：Folded metallochrome effect glaze：Obtained metallochrome effect glaze in above-mentioned steps S3 is floated can fold golden metal effect
With 200-120 mesh serigraphy 1-2 time on carving, color embossment and coloured glaze, then dry, semi-finished product are obtained.
S8：Fire：Semi-finished product after drying in above-mentioned steps S7 are put in high-temperature cellar stove, 520 DEG C is warming up to, insulation 5
Minute.
S9：Finished product：Material after firing in above-mentioned steps S8 is taken out, room temperature, finished product, cooling side is cooled to
Formula is natural cooling.
Embodiment two
A kind of high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, and the high temperature can fold golden metallochrome effect
The dispensing of fruit embossment and metallochrome effect is as follows by weight percentage：
The proportioning of color embossment：
Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；
Marble paper is with transparent embossment glaze：25%；
Marble paper varnish：40%；
Golden metallochrome effect embossment proportioning can be folded：
Pearl mica powder pigment：10%；
Low temperature oil plant：40%；
Marble paper varnish：50%；
The proportioning of marble paper coloured glaze：
Marble paper coloured glaze：65%；
Marble paper varnish：35%；
The proportioning of metallochrome effect glaze：
Pearl mica powder pigment：12.5%；
Low temperature oil plant：20%；
Marble paper coloured glaze：12.5%；
Marble paper varnish：55%.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the high temperature
Golden metallochrome effect embossment can be folded and metallochrome effect preparation method comprises the steps：
S1：Raw material screening：Percentage by above-mentioned formula is constituted is equipped with the proportioning of color embossment：Pearl mica powder pigment：
10%；Marble paper coloured glaze：30%；Marble paper is with transparent embossment glaze：25%；Marble paper varnish：40%；Golden metallochrome effect can be folded
Fruit embossment proportioning：Pearl mica powder pigment：10%；Low temperature oil plant：40%；Marble paper varnish：50%；Marble paper coloured glaze
Proportioning：Marble paper coloured glaze：65%；Marble paper varnish：35%；The proportioning of metallochrome effect glaze：Pearl mica powder pigment：
12.5%；Low temperature oil plant：20%；Marble paper coloured glaze：12.5%；Marble paper varnish：55%；
S2：Stirring：Each group dispensing in above-mentioned steps S1 is put into respectively in ready stirred autoclave and is fully stirred
Mix to pasty state, for future use, stirred autoclave is ball grinder；
S3：Grinding：The dispensing that is stirred will be grouped in above-mentioned steps S2 puts in lapping device respectively and be ground, directly
To printing performance requirement is reached, being obtained can fold golden metallochrome effect embossment, color embossment, metallochrome effect glaze and coloured glaze, with
Standby rear use；
S4：Cleaning material：The material cleaning such as ceramics, enamel or glass of glazing will be prepared clean；
S5：Bronze printing film：300-400 mesh is used in the materials such as clean ceramics, enamel or glass by cleaning in above-mentioned steps S4
One layer of marble paper gold paste of serigraphy, is obtained golden film；
S6：Print can fold golden metallochrome effect embossment/print color embossment/print coloured glaze：By it is obtained in above-mentioned steps S3 can
Gold metallochrome effect embossment 200-120 mesh silk screen double exposures are folded 8 times in golden film, by obtained color embossment in above-mentioned steps S3
With 8 times in 200-120 mesh silk screen double exposure golden films, obtained coloured glaze in above-mentioned steps S3 is existed with 200-120 mesh silk screen double exposures
1 time in golden film, the mode of printing directly prints or water transfer pictures for glazing, Freehandhand-drawing, silk screen；
S7：Folded metallochrome effect glaze：Obtained metallochrome effect glaze in above-mentioned steps S3 is floated can fold golden metal effect
With 200-120 mesh serigraphy 1-2 time on carving, color embossment and coloured glaze, then dry, semi-finished product are obtained.
S8：Fire：Semi-finished product after drying in above-mentioned steps S7 are put in high-temperature cellar stove, 800 DEG C is warming up to, insulation 15
Minute.
S9：Finished product：Material after firing in above-mentioned steps S8 is taken out, room temperature, finished product, cooling side is cooled to
Formula is natural cooling.
Comprehensive above example, the present invention provides a preferable real-time proposals：
A kind of high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, and the high temperature can fold golden metallochrome effect
The dispensing of fruit embossment and metallochrome effect is as follows by weight percentage：
The proportioning of color embossment：
Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；
Marble paper is with transparent embossment glaze：25%；
Marble paper varnish：40%；
Golden metallochrome effect embossment proportioning can be folded：
Pearl mica powder pigment：10%；
Low temperature oil plant：40%；
Marble paper varnish：50%；
The proportioning of marble paper coloured glaze：
Marble paper coloured glaze：65%；
Marble paper varnish：35%；
The proportioning of metallochrome effect glaze：
Pearl mica powder pigment：12.5%；
Low temperature oil plant：20%；
Marble paper coloured glaze：12.5%；
Marble paper varnish：55%.
Preferably, a kind of described high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, the high temperature
Golden metallochrome effect embossment can be folded and metallochrome effect preparation method comprises the steps：
S1：Raw material screening：Percentage by above-mentioned formula is constituted is equipped with the proportioning of color embossment：Pearl mica powder pigment：
10%；Marble paper coloured glaze：30%；Marble paper is with transparent embossment glaze：25%；Marble paper varnish：40%；Golden metallochrome effect can be folded
Fruit embossment proportioning：Pearl mica powder pigment：10%；Low temperature oil plant：40%；Marble paper varnish：50%；Marble paper coloured glaze
Proportioning：Marble paper coloured glaze：65%；Marble paper varnish：35%；The proportioning of metallochrome effect glaze：Pearl mica powder pigment：
12.5%；Low temperature oil plant：20%；Marble paper coloured glaze：12.5%；Marble paper varnish：55%；
S2：Stirring：Each group dispensing in above-mentioned steps S1 is put into respectively in ready stirred autoclave and is fully stirred
Mix to pasty state, for future use, stirred autoclave is ball grinder；
S3：Grinding：The dispensing that is stirred will be grouped in above-mentioned steps S2 puts in lapping device respectively and be ground, directly
To printing performance requirement is reached, being obtained can fold golden metallochrome effect embossment, color embossment, metallochrome effect glaze and coloured glaze, with
Standby rear use；
S4：Cleaning material：The material cleaning such as ceramics, enamel or glass of glazing will be prepared clean；
S5：Bronze printing film：300-400 mesh is used in the materials such as clean ceramics, enamel or glass by cleaning in above-mentioned steps S4
One layer of marble paper gold paste of serigraphy, is obtained golden film；
S6：Print can fold golden metallochrome effect embossment/print color embossment/print coloured glaze：By it is obtained in above-mentioned steps S3 can
Gold metallochrome effect embossment 200-120 mesh silk screen double exposures are folded 5 times in golden film, by obtained color embossment in above-mentioned steps S3
With 5 times in 200-120 mesh silk screen double exposure golden films, obtained coloured glaze in above-mentioned steps S3 is existed with 200-120 mesh silk screen double exposures
1 time in golden film, the mode of printing directly prints or water transfer pictures for glazing, Freehandhand-drawing, silk screen；
S7：Folded metallochrome effect glaze：Obtained metallochrome effect glaze in above-mentioned steps S3 is floated can fold golden metal effect
With 200-120 mesh serigraphy 1-2 time on carving, color embossment and coloured glaze, then dry, semi-finished product are obtained.
S8：Fire：Semi-finished product after drying in above-mentioned steps S7 are put in high-temperature cellar stove, 750 DEG C is warming up to, insulation 10
Minute.
S9：Finished product：Material after firing in above-mentioned steps S8 is taken out, room temperature, finished product, cooling side is cooled to
Formula is natural cooling.
Claims (5)
1. a kind of high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method, it is characterised in that：The high temperature can be folded
The dispensing of golden metallochrome effect embossment and metallochrome effect is as follows by weight percentage：
The proportioning of color embossment：
Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；
Marble paper is with transparent embossment glaze：25%；
Marble paper varnish：40%；
Golden metallochrome effect embossment proportioning can be folded：
Pearl mica powder pigment：10%；
Low temperature oil plant：40%；
Marble paper varnish：50%；
The proportioning of marble paper coloured glaze：
Marble paper coloured glaze：65%；
Marble paper varnish：35%；
The proportioning of metallochrome effect glaze：
Pearl mica powder pigment：12.5%；
Low temperature oil plant：20%；
Marble paper coloured glaze：12.5%；
Marble paper varnish：55%.
2. a kind of high temperature according to claim 1 can fold golden metallochrome effect embossment and metallochrome effect preparation method, its
It is characterised by：The high temperature can fold golden metallochrome effect embossment and metallochrome effect preparation method comprises the steps：
S1：Raw material screening：Percentage by above-mentioned formula is constituted is equipped with the proportioning of color embossment：Pearl mica powder pigment：10%；
Marble paper coloured glaze：30%；Marble paper is with transparent embossment glaze：25%；Marble paper varnish：40%；Golden metallochrome effect can be folded to float
Carving proportioning：Pearl mica powder pigment：10%；Low temperature oil plant：40%；Marble paper varnish：50%；Marble paper coloured glaze is matched somebody with somebody
Than：Marble paper coloured glaze：65%；Marble paper varnish：35%；The proportioning of metallochrome effect glaze：Pearl mica powder pigment：
12.5%；Low temperature oil plant：20%；Marble paper coloured glaze：12.5%；Marble paper varnish：55%；
S2：Stirring：Each group dispensing in above-mentioned steps S1 is put into respectively in ready stirred autoclave and is stirred well to
Pasty state, for future use；
S3：Grinding：The dispensing that is stirred will be grouped in above-mentioned steps S2 puts in lapping device respectively and be ground, until reaching
Require to printing performance, being obtained can fold golden metallochrome effect embossment, color embossment, metallochrome effect glaze and coloured glaze, in case after
With；
S4：Cleaning material：The material cleaning such as ceramics, enamel or glass of glazing will be prepared clean；
S5：Bronze printing film：To clean in above-mentioned steps S4 and use in the materials such as clean ceramics, enamel or glass 300-400 mesh silk screens
One layer of marble paper gold paste of printing, is obtained golden film；
S6：Print can fold golden metallochrome effect embossment/print color embossment/print coloured glaze：Gold is folded by obtained in above-mentioned steps S3
Metallochrome effect embossment 200-120 mesh silk screen double exposures use on obtained color embossment in above-mentioned steps S3 3-8 time in golden film
3-8 time in 200-120 mesh silk screen double exposure golden films, obtained coloured glaze in above-mentioned steps S3 is existed with 200-120 mesh silk screen double exposures
1 time in golden film；
S7：Folded metallochrome effect glaze：Obtained metallochrome effect glaze in above-mentioned steps S3 can folded into golden metal effect embossment, face
With 200-120 mesh serigraphy 1-2 time on color embossment and coloured glaze, then dry, semi-finished product are obtained；
S8：Fire：Semi-finished product after drying in above-mentioned steps S7 are put in high-temperature cellar stove, 520-800 DEG C is warming up to, 5- is incubated
15 minutes；
S9：Finished product：Material after firing in above-mentioned steps S8 is taken out, room temperature, finished product is cooled to.
3. a kind of high temperature according to claim 2 can fold golden metallochrome effect embossment and metallochrome effect preparation method, its
It is characterised by：The type of cooling in step S9 is natural cooling.
4. a kind of high temperature according to claim 2 can fold golden metallochrome effect embossment and metallochrome effect preparation method, its
It is characterised by：Stirred autoclave in step S2 is ball grinder.
5. a kind of high temperature according to claim 2 can fold golden metallochrome effect embossment and metallochrome effect preparation method, its
It is characterised by：The mode printed in step S6 directly prints or water transfer pictures for glazing, Freehandhand-drawing, silk screen.