CN106625910A - Bamboo, wood and vine compound plywood and preparation method thereof - Google Patents
Bamboo, wood and vine compound plywood and preparation method thereof Download PDFInfo
- Publication number
- CN106625910A CN106625910A CN201611171631.5A CN201611171631A CN106625910A CN 106625910 A CN106625910 A CN 106625910A CN 201611171631 A CN201611171631 A CN 201611171631A CN 106625910 A CN106625910 A CN 106625910A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo
- wood
- rattan
- naoh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bamboo, wood and vine compound plywood and a preparation method thereof. The bamboo, wood and vine compound plywood is composed of the following components, by mass, 20-30 parts of bamboos, 6-10 parts of sodium hydroxide, 5-9 parts of butyl acrylate, 20-30 parts of woods, 6-8 parts of sodium silicate, 11-13 parts of polyketoamine, 20-30 parts of vines, 5-7 parts of sodium hydroxide, 7-11 parts of calcium oxide, 10-20 parts of natural resin, 9-11 parts of polyethyleneimine and 60-80 parts of water. According to the bamboo, wood and vine compound plywood disclosed by the invention, the application range of a raw material is expanded, and the production cost is lowered; the problem that the raw material of a container soleplate is short can be solved, development of containers can be further accelerated, and development of other floors for cases and household panels are further accelerated. A lot of high-quality woods can be saved, the forests are protected, and the ecological environment is protected.
Description
Technical field
The present invention relates to glued board technical field, in particular to a kind of bamboo and wood, cane combined glued board and its preparation side
Method.
Background technology
Need with the fast development of China's economy, container bottom board and for the glued board of building slab and board for furniture
The amount of asking is increasing.Only with timber and bamboo wood manufacture container floor far from meeting demand.And substantial amounts of use timber
Also consume substantial amounts of forest and destroy ecological environment simultaneously.
The content of the invention
The invention provides a kind of bamboo and wood, cane combined glued board and preparation method thereof, bamboo and wood, the cane combined glue of the present invention
Plywood, expands the range of application of raw material, and reduces production cost, not only can solve container bottom board raw material tight
Scarce problem, and the development of container can also be promoted, also promote the development of other case floors and family expenses sheet material.Can save
Substantial amounts of high-quality timber is saved, forest is protected, ecological environment is protected.
For achieving the above object, the present invention provides following technical scheme：
A kind of bamboo and wood, cane combined glued board and preparation method thereof, are made up of following mass fraction formula components：Bamboo 20-30
Part, NaOH 6-10 parts, butyl acrylate 5-9 parts, wood 20-30 parts, sodium metasilicate 6-8 parts, polyketone amine 11-13 parts, rattan 20-30
Part, NaOH 5-7 parts, calcium oxide 7-11 parts, natural resin 10-20 parts, polyethyleneimine 9-11 parts, water 60-80 parts.
Further：It is made up of following mass fraction formula components：20 parts of bamboo, 6 parts of NaOH, 5 parts of butyl acrylate, wood
20 parts, 6 parts of sodium metasilicate, 11 parts of polyketone amine, 20 parts of rattan, 5 parts of NaOH, 7 parts of calcium oxide, 10 parts of natural resin, polyethyleneimine
9 parts of amine, 60 parts of water.
Further：It is made up of following mass fraction formula components：25 parts of bamboo, 8 parts of NaOH, 7 parts of butyl acrylate, wood
25 parts, 7 parts of sodium metasilicate, 12 parts of polyketone amine, 25 parts of rattan, 6 parts of NaOH, 9 parts of calcium oxide, 15 parts of natural resin, polyethyleneimine
10 parts of amine, 70 parts of water.
Further：It is made up of following mass fraction formula components：30 parts of bamboo, 10 parts of NaOH, 9 parts of butyl acrylate,
30 parts of wood, 8 parts of sodium metasilicate, 13 parts of polyketone amine, 30 parts of rattan, 7 parts of NaOH, 11 parts of calcium oxide, 20 parts of natural resin, polyethylene
11 parts of imines, 80 parts of water.
Further：Preparation method of the present invention has following steps：
Step one, bamboo and wood, rattan are carried out into heating disinfection with 100 DEG C of boiling water；
Step 2, with bamboo and wood, rattan difference it is accommodating plate-shaped standby；
Step 3, surplus stock is merged after 80～100 DEG C of heating-up temperature, 10～15min, cooling down after mixing both must be crosslinked
Agent；
Step 4, bamboo and wood, rattan mid portion are touched into respectively upper crosslinking agent, after being suppressed both finished product.
The invention has the beneficial effects as follows：
1st, of the invention bamboo and wood, cane combined glued board, expand the range of application of raw material, and reduce and produce into
This, not only can solve the problems, such as that container bottom board raw material are in short supply, and can also promote the development of container, also promote it
Its case floor and the development of family expenses sheet material；
2nd, substantial amounts of high-quality timber can be saved, forest is protected, ecological environment is protected.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of bamboo and wood, cane combined glued board are made up of following mass fraction formula components：Bamboo 20-30 parts, NaOH 6-
10 parts, butyl acrylate 5-9 parts, wood 20-30 parts, sodium metasilicate 6-8 parts, polyketone amine 11-13 parts, rattan 20-30 parts, NaOH 5-
7 parts, calcium oxide 7-11 parts, natural resin 10-20 parts, polyethyleneimine 9-11 parts, water 60-80 parts.
Embodiment two：
A kind of bamboo and wood, cane combined glued board are made up of following mass fraction formula components：20 parts of bamboo, 6 parts of NaOH,
5 parts of butyl acrylate, 20 parts of wood, 6 parts of sodium metasilicate, 11 parts of polyketone amine, 20 parts of rattan, 5 parts of NaOH, 7 parts of calcium oxide, natural tree
10 parts of fat, 9 parts of polyethyleneimine, 60 parts of water.
Embodiment three：
A kind of bamboo and wood, cane combined glued board are made up of following mass fraction formula components：25 parts of bamboo, 8 parts of NaOH,
7 parts of butyl acrylate, 25 parts of wood, 7 parts of sodium metasilicate, 12 parts of polyketone amine, 25 parts of rattan, 6 parts of NaOH, 9 parts of calcium oxide, natural tree
15 parts of fat, 10 parts of polyethyleneimine, 70 parts of water.
Example IV：
A kind of bamboo and wood, cane combined glued board are made up of following mass fraction formula components：30 parts of bamboo, 10 parts of NaOH,
It is 9 parts of butyl acrylate, 30 parts of wood, 8 parts of sodium metasilicate, 13 parts of polyketone amine, 30 parts of rattan, 7 parts of NaOH, 11 parts of calcium oxide, natural
20 parts of resin, 11 parts of polyethyleneimine, 80 parts of water.
Embodiment five：
A kind of bamboo and wood, the preparation method preparation method of cane combined glued board comprise the steps：
Step one, bamboo and wood, rattan are carried out into heating disinfection with 100 DEG C of boiling water；
Step 2, with bamboo and wood, rattan difference it is accommodating plate-shaped standby；
Step 3, surplus stock is merged after 80～100 DEG C of heating-up temperature, 10～15min, cooling down after mixing both must be crosslinked
Agent；
Step 4, bamboo and wood, rattan mid portion are touched into respectively upper crosslinking agent, after being suppressed both finished product.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity those skilled in the art should
Using specification as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (5)
1. a kind of bamboo and wood, cane combined glued board, it is characterised in that：It is made up of following mass fraction formula components：
Bamboo 20-30 parts, NaOH 6-10 parts, butyl acrylate 5-9 parts, wood 20-30 parts, sodium metasilicate 6-8 parts, polyketone amine 11-
13 parts, rattan 20-30 parts, NaOH 5-7 parts, calcium oxide 7-11 parts, natural resin 10-20 parts, polyethyleneimine 9-11 parts, water
60-80 parts.
2. a kind of bamboo and wood according to claim 1, cane combined glued board, it is characterised in that：Filled a prescription by following mass fraction
Into being grouped into：
20 parts of bamboo, 6 parts of NaOH, 5 parts of butyl acrylate, 20 parts of wood, 6 parts of sodium metasilicate, 11 parts of polyketone amine, 20 parts of rattan, hydrogen-oxygen
Change 5 parts of sodium, 7 parts of calcium oxide, 10 parts of natural resin, 9 parts of polyethyleneimine, 60 parts of water.
3. a kind of bamboo and wood according to claim 1, cane combined glued board, it is characterised in that：Filled a prescription by following mass fraction
Into being grouped into：
25 parts of bamboo, 8 parts of NaOH, 7 parts of butyl acrylate, 25 parts of wood, 7 parts of sodium metasilicate, 12 parts of polyketone amine, 25 parts of rattan, hydrogen-oxygen
Change 6 parts of sodium, 9 parts of calcium oxide, 15 parts of natural resin, 10 parts of polyethyleneimine, 70 parts of water.
4. a kind of bamboo and wood according to claim 1, cane combined glued board, it is characterised in that：Filled a prescription by following mass fraction
Into being grouped into：
30 parts of bamboo, 10 parts of NaOH, 9 parts of butyl acrylate, 30 parts of wood, 8 parts of sodium metasilicate, 13 parts of polyketone amine, 30 parts of rattan, hydrogen-oxygen
Change 7 parts of sodium, 11 parts of calcium oxide, 20 parts of natural resin, 11 parts of polyethyleneimine, 80 parts of water.
5. a kind of a kind of bamboo and wood according to claim 1, the preparation method of cane combined glued board, it is characterised in that：Including
Following steps：
Step one, bamboo and wood, rattan are carried out into heating disinfection with 100 DEG C of boiling water；
Step 2, with bamboo and wood, rattan difference it is accommodating plate-shaped standby；
Step 3, surplus stock is merged after 80～100 DEG C of heating-up temperature, 10～15min, cool down after mixing both crosslinking agent；
Step 4, bamboo and wood, rattan mid portion are touched into respectively upper crosslinking agent, after being suppressed both finished product.