CN106592922A - Damp-proof aluminum foil composite floor for container - Google Patents

Damp-proof aluminum foil composite floor for container Download PDF

Info

Publication number
CN106592922A
CN106592922A CN201611028875.8A CN201611028875A CN106592922A CN 106592922 A CN106592922 A CN 106592922A CN 201611028875 A CN201611028875 A CN 201611028875A CN 106592922 A CN106592922 A CN 106592922A
Authority
CN
China
Prior art keywords
layer
composite floor
waterproof
aluminium foil
foil composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611028875.8A
Other languages
Chinese (zh)
Inventor
葛庭洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhangjiagang Shenggang Environment Fireproof Construction Material Co Ltd
Original Assignee
Zhangjiagang Shenggang Environment Fireproof Construction Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang Shenggang Environment Fireproof Construction Material Co Ltd filed Critical Zhangjiagang Shenggang Environment Fireproof Construction Material Co Ltd
Priority to CN201611028875.8A priority Critical patent/CN106592922A/en
Publication of CN106592922A publication Critical patent/CN106592922A/en
Pending legal-status Critical Current

Abstract

The invention discloses a damp-proof aluminum foil composite floor for a container. The damp-proof aluminum foil composite floor comprises a surface pulp layer and a middle material layer, a platinum cloth layer is arranged between the middle material layer and the surface pulp layer, a waterproof layer is arranged on the middle material layer, and an aluminum foil layer is further arranged on the waterproof layer. The composite light floor made from various materials not only is light in weight and convenient to install but also can provide good waterproof and damp-proof performance. Common composite floors achieve the waterproof effect by means of the waterproof performance of floor materials, some board materials are poor in waterproof effect, and moisture is likely to invade into floors and consequently leads to the situation that floors warp. However, the damp-proof aluminum foil composite floor is provided with the waterproof layer independently, and thus the waterproof and damp-proof effects of the floor can be improved to the greatest extent, and moisture permeation is prevented.

Description

A kind of moistureproof aluminium foil composite floor board for container
Technical field
The present invention relates to indoor set Material Field, specifically refers to a kind of moistureproof aluminium foil composite floor board for container.
Background technology
At present, in order to meet the demand that expressway around city develops, substantial amounts of work personnel pour in city, these work personnel's More liquid, in order to solve the problems, such as lodging, cheap container house becomes first-selected；Live for convenience and use, collect The inside in vanning house is all also equipped with floor.Existing container is mostly container made of steel, aluminium alloy container and glass Glass steel container.Container made of steel intensity height, good weldability, sound construction, watertightness are good, but its heat conductivity is stronger, easily Internal material is caused to burn；Aluminium alloy container is although lightweight, specious, anticorrosion, easy to process and processing cost And repair cost is low, but its cost height, welding performance are poor；Although fibreglass reinforced plastic container strength rigid is big, heat-insulated anti- Rotten, easy cleaning is repaired, but intensity is relatively low at its easily aging, stubborn bolt.Therefore, existing container all can not be directly as collection Vanning house is used, and is required for laying the floor of a layer function in container, but now one kind can not make up Container heat conductivity is strong, the defect for easily causing internal-combustion and water proofing property poor.
Notification number is a kind of container house aluminum foil special composite floor board and its manufacture method of CN104328892A, and it is public The technical scheme of cloth is, using multiple field composite construction, to combine various material and then play fire-resistant waterproof by reasonable Arrangement Purpose, and being wherein not only added with aluminium foil layer can improve the fire resistance of whole sheet material, also in the side face edge of whole sheet material Edge is coated with the waterproof sealing layer for waterproof, but whole floor is simply provided with one layer of waterproofing agent in the side surface of surrounding to be applied Layer, causes the water-proof function on whole floor poor, easily occur being oozed under steam, floor corrosion expansion the problems such as.
The content of the invention
It is an object of the invention to provide a kind of for portable container house floor, with higher waterproof and dampproof Performance and a kind of container floor of self flame retardance fireproof.
The present invention is achieved through the following technical solutions：A kind of moistureproof aluminium foil composite floor board for container, including starch adhesive Layer and the middle bed of material, are provided with platinum layer of cloth between the middle bed of material and starch adhesive layer, the middle bed of material top is provided with waterproof layer, described anti- Water layer top is additionally provided with aluminium foil layer.The present invention is the floor material for providing a kind of waterproof heat-insulating for container, general packaging Case adopts two-layer stratigraphic structure, and up and down the bottom in the middle of two-layer can adopt composite floor, not only provide certain support Property, relatively low weight is also kept as far as possible to mitigate the load of whole container, it is easy to mobile and assembles.The present invention is by more Composite light floor made by planting material, is not only easily installed with lighter quality, it is also possible to provides preferable waterproof and prevents Damp performance.General compound floor is the effect that waterproof is reached using the water proofing property of flooring material itself, some sheet materials Material waterproofing effect it is poor, aqueous vapor easily invades the situation for causing floor seesaw occur in floor, and the present invention is by independent One layer of waterproof layer is provided with, the waterproof moisture-proof effect on floor can be to greatest extent improved, waterproof aqueous vapor is penetrated into.
Further, the material of the platinum layer of cloth is alkali-free glass fiber platinum cloth.The alkali-free glass fiber platinum layer of cloth is to adopt The one layer of reinforcement structure laid as main material with alkali-free glass fiber cloth, and described alkali-free glass fiber cloth be extensive utilization with A kind of geosynthetics of civil engineering, mainly by glass fibre with it is chopped fiber needle-punched it is non-woven fabric compounded form, with higher Tensile strength, effectively prevent floor from ftractureing, for there is reinforcement effect on floor and reproducible, save trouble and labor, green ring Protect.
Further, it is additionally provided with nonwoven layer between the platinum layer of cloth dough-making powder pulp layer.Nonwoven layer be by orienting or Random fiber and constitute, be environment-friendly materials of new generation, with moistureproof, ventilative, flexible, light weight, not combustion-supporting, easy decomposition, nothing Malicious nonirritant, rich color, it is cheap, recyclable the features such as.And its Main Function reduces product surface porosity, Facilitate vacuum cup product offline.
Further, it is additionally provided with carbon fiber mesh fabric between the waterproof layer and the middle bed of material.Carbon fiber mesh fabric is also known as carbon Cellulose fiber cloth, carbon fiber cloth, carbon fiber woven cloth etc., carbon fiber mesh fabric has intensity high, and density is little, and thickness of thin does not increase substantially Plus the features such as strenthening member deadweight and sectional dimension, various fields are widely used at present.And have additional carbon fiber mesh fabric The anti-seismic performance on floor can be improved, plays a part of reinforcing, being prevented from container load increases and caused malformation, Also there is higher corrosion-resistant and durability.
Further, the starch adhesive layer outer surface is provided with layer of PVC.The Main Ingredients and Appearance of the layer of PVC is polrvinyl chloride, and is added The other compositions for entering are strengthening its thermostability, toughness, ductility etc..The superiors of this skin covering of the surface are paints, it is middle it is main into It is polrvinyl chloride to divide, and orlop is back of the body coating adhesive.And directly lay to form polyvinyl chloride layer and attached using Corvic And show in PVC starch adhesive layers, so as to improve the aesthetics and oxidation resistance of whole plate body.
Further, the middle bed of material material is magnesium oxychloride cementing material.The middle bed of material material is chlorine oxygen magnesium gelling material Material.Magnesium oxychloride cementing material is a kind of special kinds cement, is mainly forged with the light burnt powder or low temperature obtained by calcined magnesite stone Ashes (main component is MgO) obtained by calcined dolomite is cementing agent, with magnesium chloride hexahydrate (MgCL2The water soluble magnesium such as 6H2O) Salt is blender, adds the hardening of cement body that water is formed.The hardenite main component that magnesium oxychloride cementing material is formed is 5Mg(OH)2·MgCL28H2O and 3Mg (OH)2·MgCL2Magnesium oxide-magnesium chloride-water that 8H2O crystalline phases are constituted is ternary Compound crystalline phase double salt, in addition, some Mg (OH)2Gel.Magnesia oxychloride cement can quickly at normal temperatures and pressures Hardening, forms the fragility artificial stone very higher than larger and hardness.Using its this hardening gelling, can be processed into various The construction material and ornament materials of various kinds, has broad application prospects.And wherein according to MgO, MgCl of different materials2No Same content, is converted, to adjust formula.And MgO：MgCl2Mol ratio should rest in 6-8:Between 1, conventional mol ratio exists 6.5-7.5:Between 1.
Further, the starch adhesive layer material is magnesium oxysulfide Binder Materials.Magnesium oxysulfide Binder Materials are the one of magnesia cement Kind, it is active MgO and certain density MgSO4A kind of MgO-MgSO of solution composition4- H2O ternary gelling systems, magnesium oxysulfide The maximum difference of Binder Materials and magnesium oxychloride cementing material is that the acid group of mix solution used is different, so two kinds of magnesio gellings The property of material, such as fire line, heat insulating ability, durability and the feature of environmental protection are substantially the same.Magnesium oxysulfide Binder Materials remain chlorine oxygen Magnesium Binder Materials above-mentioned performance, it is to avoid manufacturer is the hidden danger that magnesium oxychloride cementing material damp suction surface halide accumulation is checked, and magnesium oxysulfide Binder Materials also have the shortcomings that the relatively low poor water resistance of intensity, so PVC starch adhesives layer sulfur magnesium Binder Materials, and the gelling of centre Layer adopts magnesium oxychloride cementing material, using having complementary functions so as to improve the water proofing property of whole plate body between two kinds of different materials Energy.
Further, the waterproof layer is organic silicon water-proofing layer.The material of described organic silicon water-proofing layer is magnesite gelling Material, and the proportioning raw materials of waterproof layer are：The magnesium oxide of 30-35%, the magnesium sulfate solution of 40-60%, and wherein magnesium oxide In the waterproofing agent of organosilicon containing 1-3%.
Further, the layer of PVC thickness is 1.5-2.4mm.The THICKNESS CONTROL of layer of PVC is prevented within the specific limits The excessively thin easy abrasion exposed surface pulp layer of layer of PVC, and if too thick not only increase manufacturing cost, also increase manufacture difficulty.It is logical Cross experiment can layer of PVC thickness and more than 2.4mm after the decorative effect that reached can decrease, and the weight of plate body Also weight can be become, so having optimal cost effectiveness in the range of 1.5～2.4mm thickness.
Further, dyestuff is provided with the starch adhesive layer, the dyestuff is iron oxide red or iron oxide black.Described polychlorostyrene Pvdf layer is water white protective layer, and dyestuff is added with starch adhesive layer so as to further increase its decorative effect, also can Enough avoid causing the problem of color fade to occur because polyvinyl chloride layer is worn.
Its manufacture method is：
(1) the injection face pulp layer raw material in basic unit's mould, solidify to form starch adhesive layer as basic unit；
(2) upper surface in starch adhesive layer lays platinum cloth of the one layer of specification for 6x4, as platinum layer of cloth, and is squeezed with cylinder Pressure；
(3) upper surface in platinum layer of cloth is layed in the non-woven fabrics of the equal size of starch adhesive layer, as nonwoven layers, and uses cylinder Extruding；
(4) upper surface in platinum layer of cloth lays grid cloth of the one layer of specification for 5x5, as clathrum, and is squeezed with cylinder Pressure；
(5) bed of material raw material in adding in middle bed of material mould, solidify to form the middle bed of material；The middle bed of material is placed on into the upper of clathrum Side, and use drum extrusion；
(6) prepare organosilicon waterproof layer mould, be added thereto to organic silicon water-proofing raw material slip, and be stirred for uniformly, Until as organic silicon water-proofing layer after solidification, and organic silicon water-proofing layer is placed on into middle bed of material top；
(7) upper surface in waterproof layer is layed in the aluminium foil of the equal size of clathrum, as aluminium foil layer, and is squeezed with cylinder Pressure；
(8) tabular mould is removed, to overall hot pressing is carried out, and carry out deburring.
Wherein：Middle bed of material raw material is made up of magnesium oxide, magnesium chloride, wood flour, leftover pieces and dyestuff；Magnesium oxide belongs to gelling Material, can by each constituent be gelled together, and it is nonpoisonous and tasteless, with extremely fireproof insulating properties；Magnesium chloride, wood flour And leftover pieces are all filled as inserts.
Starch adhesive layer raw material is made up of magnesium oxide, magnesium sulfide, Pulvis Talci, flyash, silica flour and dyestuff；Magnesium oxide belongs to Binder Materials, can by each constituent be gelled together, and it is nonpoisonous and tasteless, with extremely fireproof insulating properties；Pulvis Talci With excellent fire resistance and acid-resisting；Flyash can improve the workability of silica flour and other components；Silica flour is used as filling out Material.
The present invention compared with prior art, with advantages below and beneficial effect：
(1) present invention is not only easily installed by composite light floor made by multiple material with lighter quality, Preferable waterproof and dampproof performance also can be provided；
(2) present invention is equipped with alkali-free glass fiber platinum layer of cloth so that floor has higher tensile strength, and can have The floor that prevents of effect is ftractureed, for there is reinforcement effect on floor and reproducible, save trouble and labor, environmental protection；
(3) present invention is additionally provided with nonwoven layer, and by nonwoven layer Main Function product surface porosity is reduced, convenient true Suction disk product is offline；
(4) present invention is provided with carbon fiber mesh fabric can improve the anti-seismic performance on floor, play a part of reinforcing, Neng Goufang Only container load increases and caused malformation, also with higher corrosion-resistant and durability；
(5) present invention is provided with layer of PVC and can not only be provided with preferable waterproof effect in outermost layer, it is also possible to protect starch adhesive Layer, prevents from causing starch adhesive layer frayed because of direct contact surface pulp layer and fading；
(6) the middle bed of material of the invention can be hardened quickly at normal temperatures and pressures using magnesium oxychloride cementing material, be formed crisp The property artificial stone very higher than larger and hardness, using its this hardening gelling, can be processed into various buildings Material and ornament materials, with higher intensity, preferable anti-flammability, durability and the feature of environmental protection；
(7) starch adhesive layer of the invention can remain magnesium oxychloride cementing material performance using magnesium oxysulfide Binder Materials, while The hidden danger of magnesium oxychloride cementing material damp suction surface halide accumulation is avoided, and magnesium oxysulfide Binder Materials are also scarce with the relatively low poor water resistance of intensity Point, so using having complementary functions so as to improve the water resistance of whole plate body between two kinds of different materials；
(8) present invention can further improve the waterproof effect on whole floor, waterproof by the organic silicon water-proofing layer being provided with Layer can effectively suppress moisture to enter in substrate, produce waterproof, anti-Cl-, anti-ultraviolet performance and with breathability, improve The service life of whole container；
(9) THICKNESS CONTROL of layer of PVC is within the specific limits to prevent the excessively thin easy abrasion of layer of PVC from exposing starch adhesive by the present invention Top layer, has optimal cost effectiveness in the range of 1.5～3mm thickness；
(10) present invention is added with dyestuff so as to further increase its decorative effect in starch adhesive layer, it is also possible to avoid because poly- Pvdc layer is worn causes the problem of color fade to occur.
Description of the drawings
The detailed description by reading non-limiting example made with reference to the following drawings, other features of the present invention, Objects and advantages will become apparent：
Fig. 1 is the structural representation of the present invention；
Fig. 2 is the board house application schematic diagram of the present invention.
Wherein：1-starch adhesive layer, the 2-middle bed of material, 3-platinum layer of cloth, 4-waterproof layer, 5-aluminium foil layer.
Specific embodiment
Embodiments of the invention are described below in detail, the example of the embodiment is shown in the drawings, wherein from start to finish Same or similar label represents same or similar element or the element with same or like function.Below with reference to attached The embodiment of figure description is exemplary, is only used for explaining the present invention, and is not considered as limiting the invention.
In describing the invention, it is to be understood that term " " center ", " longitudinal direction ", " horizontal ", " on ", D score, The orientation or position relationship of the instruction such as "front", "rear", "left", "right", " vertical ", " level ", " top ", " bottom ", " interior ", " outward " is Based on orientation shown in the drawings or position relationship, it is for only for ease of the description present invention and simplifies description, rather than indicates or dark Showing the device or element of indication must have specific orientation, with specific azimuth configuration and operation therefore it is not intended that right The restriction of the present invention.
Embodiment 1：
A kind of moistureproof aluminium foil composite floor board for container of the present embodiment, as depicted in figs. 1 and 2, including starch adhesive layer 1 With the middle bed of material 2, platinum layer of cloth 3 is provided between the middle bed of material 2 and starch adhesive layer 1, the top of the middle bed of material 2 is provided with waterproof layer 4, institute State the top of waterproof layer 4 and be additionally provided with aluminium foil layer 5.The present invention by composite light floor made by multiple material, not only with compared with Light quality is easily installed, it is also possible to provide preferably waterproof and dampproof performance.General compound floor is to utilize flooring board Expect the water proofing property of itself to reach the effect of waterproof, the material waterproofing effect of some sheet materials is poor, and aqueous vapor is easily invaded in floor Floor is caused the situation of seesaw occur, and the present invention can improve ground to greatest extent by being separately provided with one layer of waterproof layer 4 The waterproof moisture-proof effect of plate, waterproof aqueous vapor is penetrated into.
Embodiment 2：
The present embodiment is on the basis of above-described embodiment, further to limit, and the material of the platinum layer of cloth 3 is alkali-free Glass platinum cloth.The alkali-free glass fiber platinum layer of cloth is strengthened as one layer that main material is laid using alkali-free glass fiber cloth Structure, and described alkali-free glass fiber cloth is a kind of geosynthetics of extensive utilization and civil engineering, mainly by glass fibers Dimension with it is chopped fiber needle-punched it is non-woven fabric compounded form, with higher tensile strength, effectively prevent floor from ftractureing, floor is had plus Gu effect, and reproducible, save trouble and labor, environmental protection.The other parts of the present embodiment are same as the previously described embodiments, no longer Repeat.
Embodiment 3：
The present embodiment is on the basis of above-described embodiment, further to limit, the dough-making powder pulp layer 1 of the platinum layer of cloth 3 it Between be additionally provided with nonwoven layer.Nonwoven layer is made up of fiber orient or random, is environment-friendly materials of new generation, with anti- Damp, ventilative, flexible, light weight, not combustion-supporting, easy decomposition, nontoxic nonirritant, rich color, cheap, recyclable etc. Feature.And its Main Function reduces product surface porosity, facilitate vacuum cup product offline.The other parts of the present embodiment with Above-described embodiment is identical, repeats no more.
Embodiment 4：
The present embodiment is on the basis of above-described embodiment, further to limit, between the waterproof layer 4 and the middle bed of material 2 It is additionally provided with carbon fiber mesh fabric.Carbon fiber mesh fabric is also known as carbon fiber sheet, carbon fiber cloth, carbon fiber woven cloth etc., carbon fibre web Ge Bu has intensity high, and density is little, thickness of thin, wide at present the features such as do not increase strenthening member deadweight and sectional dimension substantially It is general to be applied to various fields.And having additional carbon fiber mesh fabric can improve the anti-seismic performance on floor, play a part of reinforcing, energy Enough prevent container load from increasing and caused malformation, also with higher corrosion-resistant and durability.The present embodiment its His part is same as the previously described embodiments, repeats no more.
Embodiment 5：
The present embodiment is on the basis of above-described embodiment, further to limit, and the outer surface of starch adhesive layer 1 is provided with PVC Layer.The Main Ingredients and Appearance of the layer of PVC is polrvinyl chloride, and the other compositions for adding to be strengthening its thermostability, toughness, ductility Deng.The superiors of this skin covering of the surface are paints, and middle main component is polrvinyl chloride, and orlop is back of the body coating adhesive.And utilize Corvic directly is laid to form polyvinyl chloride layer and be attached to PVC starch adhesive layers and is shown, so as to improve U.S. of whole plate body Sight degree and oxidation resistance.The other parts of the present embodiment are same as the previously described embodiments, repeat no more.
Embodiment 6：
The present embodiment is on the basis of above-described embodiment, further to limit, and the material of the middle bed of material 2 is chlorine oxygen magnesium glue Gel material.And the constituent of the raw material of the middle bed of material 2 and mass percent shared by each composition are：Magnesium oxide：31-35%, Magnesium chloride：28-37%, wood flour：13-16%, leftover pieces：14-17%, dyestuff：0.3-1.8%.The other parts of the present embodiment It is same as the previously described embodiments, repeat no more.
Embodiment 7：
The present embodiment is on the basis of above-described embodiment, further to limit, and the described material of starch adhesive layer 1 is magnesium oxysulfide Binder Materials.The constituent of starch adhesive raw material and mass percent shared by each composition are：Magnesium oxide：22-27%, magnesium sulfide： 55-71%, Pulvis Talci：8-11%, flyash：1.8-2.7%, silica flour：1.8-3.2%, dyestuff：0.7-1.4%.This enforcement The other parts of example are same as the previously described embodiments, repeat no more.
Embodiment 8：
The present embodiment is on the basis of above-described embodiment, further to limit, and the waterproof layer 4 is organic silicon water-proofing Layer.The material of described organic silicon water-proofing layer is magnesite binding material, and the proportioning raw materials of waterproof layer 4 are：The oxidation of 30-35% The magnesium sulfate solution of magnesium, 40-60%, and the waterproofing agent of organosilicon containing 1-3% wherein in magnesium oxide.The present embodiment other Part is same as the previously described embodiments, repeats no more.
Embodiment 9：
The present embodiment is on the basis of above-described embodiment, further to limit, and the layer of PVC thickness is 1.5-2.4mm. By the THICKNESS CONTROL of layer of PVC be within the specific limits prevent layer of PVC excessively it is thin it is easy abrasion exposed surface pulp layer, and if too it is thick not only Manufacturing cost is increased, manufacture difficulty is also increased.By experiment can layer of PVC thickness and more than 2.4mm after reached Decorative effect can decrease, and the weight of plate body also can become weight, so in the range of 1.5～2.4mm thickness have most Good cost effectiveness.The other parts of the present embodiment are same as the previously described embodiments, repeat no more.
Embodiment 10：
The present embodiment is on the basis of above-described embodiment, further to limit, and is provided with dyestuff in the starch adhesive layer 1, institute Dyestuff is stated for iron oxide red or iron oxide black.Described polyvinyl chloride layer is water white protective layer, and is added in starch adhesive layer 1 Added with dyestuff so as to further increasing its decorative effect, it is also possible to avoid causing asking for color fade because polyvinyl chloride layer is worn Topic occurs.The other parts of the present embodiment are same as the previously described embodiments, repeat no more.
Although an embodiment of the present invention has been shown and described, it will be understood by those skilled in the art that：Not These embodiments can be carried out with various changes, modification, replacement and modification under the principle and objective that depart from the present invention, it is of the invention Scope is limited by claim and its equivalent.

Claims (10)

1. a kind of moistureproof aluminium foil composite floor board for container, it is characterised in that：Including starch adhesive layer (1) and the middle bed of material (2), institute State and platinum layer of cloth (3) is provided between the bed of material (2) and starch adhesive layer (1), the middle bed of material (2) top is provided with waterproof layer (4), described Waterproof layer (4) top is additionally provided with aluminium foil layer (5).
2. a kind of moistureproof aluminium foil composite floor board for container according to claim 1, it is characterised in that：The platinum The material of layer of cloth (3) is alkali-free glass fiber platinum cloth.
3. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Nonwoven layer is additionally provided between platinum layer of cloth (3) dough-making powder pulp layer (1).
4. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Carbon fiber mesh fabric is additionally provided between waterproof layer (3) and the middle bed of material (2).
5. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Starch adhesive layer (1) outer surface is provided with layer of PVC.
6. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described The middle bed of material (1) material is magnesium oxychloride cementing material.
7. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Starch adhesive layer (1) material is magnesium oxysulfide Binder Materials.
8. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Waterproof layer (4) is organic silicon water-proofing layer.
9. a kind of moistureproof aluminium foil composite floor board for container according to claim 5, it is characterised in that：The PVC Thickness degree is 1.5-2.4mm.
10. a kind of moistureproof aluminium foil composite floor board for container according to claim 1 and 2, it is characterised in that：It is described Dyestuff is provided with starch adhesive layer, the dyestuff is iron oxide red or iron oxide black.
CN201611028875.8A 2016-11-19 2016-11-19 Damp-proof aluminum foil composite floor for container Pending CN106592922A (en)