CN106592790A - Outer wall outer heat preservation system - Google Patents
Outer wall outer heat preservation system Download PDFInfo
- Publication number
- CN106592790A CN106592790A CN201611091407.5A CN201611091407A CN106592790A CN 106592790 A CN106592790 A CN 106592790A CN 201611091407 A CN201611091407 A CN 201611091407A CN 106592790 A CN106592790 A CN 106592790A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- thermal insulation
- insulation system
- external thermal
- heat preservation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an outer wall outer heat preservation system. The outer wall outer heat preservation system comprises a binding agent, a fireproof heat preservation plate and a facing layer which are fixedly connected in sequence from a wall base body to the outside. The fireproof heat preservation plate is a three-dimensional fiber reinforcement body formed through the steps that three-dimensional fibers are impregnated with glue solutions, then glue extruding is conducted, and curing is conducted at the temperature of 180 DEG C-200 DEG C and under the curing pressure of 0.2-0.8 MPa. The outer wall outer heat preservation system has excellent heat preservation and insulation performance, flame retardancy and water repellency.
Description
Technical field
The present invention relates to a kind of heat-insulation system, particularly a kind of to be used for external thermal insulation system.
Background technology
The heat insulating material for external of popularization and application mainly has polystyrene block, squeezes on China's construction insulated fire infrastructure market
Modeling styrofoam (XPS plate), polyurethane, rock cotton board, alumina silicate hardboard, block of glass wool, phenolic foam plate, foam cement, alumina silicate
Fiberboard etc..Wherein heat-insulating property preferably has polystyrene block, extruded polystyrene board (XPS plate), polyurethane etc., but these materials
Belong to low side B levels fire-retardant, and there is foam cement, alumina silicate hardboard, the aluminosilicate fiberboard of the relatively low A level fire resistances of heatproof
It is poor etc. heat-insulating property.Heat-insulating property and fire resistance can be taken into account, the A level flame-retardant thermal insulation materials of high temperature fire protection field are especially met
It is still blank.
The existing external wall outer insulation facility system of existing market can not be while having insulation concurrently, preventing due to the fire proofing material for using
Fire, water repellency, cause many problems of generally existing:Come off using the easy moisture crazing of rock wool material and heat insulating ability is poor;Use
Organic insulation material such as XPS, polyurethane etc., belong to B levels fire-retardant, it is impossible to meet public building or high-storey fire protection requirement;
In surface coating inorganic material, core remains combustible material to an also class, and this material tests report is fire-retardant in A levels, but one
Jing is used, and when building is on fire, will form wind field passage at core position, and aggravation burning leads to tragedy.By this exterior wall
Using and promoting for external thermal insulation facility system, has taken into account fire prevention and has been incubated, and can effectively reduce and be made because heat insulating material for external burns
Into tragedy.
The content of the invention
The present invention technology solve problem be:Overcome the deficiencies in the prior art, there is provided a kind of existing excellent insulation
Performance, has the external thermal insulation system of fire resistance and water repellency concurrently again.
The present invention technical solution be:A kind of external thermal insulation system, by wall base body fixed successively company is outwards included
Binding agent, fireproof heated board and the finish coat for connecing;The fireproof heated board be by three-dimensional fiber dipping glue after plastic squeeze and
180 DEG C -200 DEG C, the three-dimensional fiber reinforcement solidified under 0.2-0.8MPa solidifying pressures.
Further, the binding agent, fireproof heated board and finish coat are strengthened fixing by buckle and expansion bolt, described
Buckle is arranged in the finish coat, the expansion bolt through the buckle centre bore after, sequentially pass through fireproof heated board,
Binding agent is fixedly connected with wall base body.
Further, the binding agent is the magnesium chloride solution that the concentration of 1.4 weight portions is 25%, the end of 0.2 weight portion
Hydroxyl polybutadiene, the stearic acid sodium of 1 weight portion, the silane coupler of 0.1 weight portion, the ethylene glycol solution of 1 weight portion it is mixed
Compound.
Further, the glue is consisted of:The water soluble phenol resin of 3-36 weight portions, the accelerator of 1 weight portion
With the water of 63-96 weight portions;The accelerator consists of:The rosin foaming agent of 0.27 weight portion, the sulfuric acid of 0.23 weight portion
The sodium tripolyphosphate of the magnesium aqueous solution, the methylsiloxane of 0.06 weight portion, the oxalic acid of 0.2 weight portion and 0.24 weight portion.
Further, the three-dimensional fiber is glass fibre, high silica fiber or quartz fibre.
Further, the finish coat is stone material, imitative stone material, calcium silicate board with microporous or water resistant coating.
Further, packing material is filled with the piece between multiple fireproof heated boards, and in packing material surface brush
Fire resistant coating.
Further, the packing material is fireproof heat insulating lath.
Present invention advantage compared with prior art is:
External thermal insulation system of the present invention, it is existing excellent by the fireproof heated board using three-dimensional fiber reinforcement
Different thermal and insulating performance, has fire resistance and water repellency concurrently again, effectively reduce existing other external thermal insulation systems because
Splice and the stress concentration for occurring and then the probability for crack occur, the probability aging so as to reduce further moisture absorption, so that
External wall insulating layer effectively prevent fires, be incubated, cracking resistance, protection against the tide, accomplish and build same life-span.
Description of the drawings
Fig. 1 is the structural representation of external thermal insulation system of the present invention.
Fig. 2 is the external structure schematic diagram of external thermal insulation system of the present invention.
Fig. 3 is the zoomed-in view in A portions in Fig. 2.
Fig. 4 is the structural representation of the buckle of external thermal insulation system of the present invention.
Specific embodiment
As Figure 1-4, a kind of external thermal insulation system, the binding agent for outwards including being fixedly connected sequentially by wall base body 1
2nd, fireproof heated board 3 and finish coat 6;The fireproof heated board 3 be by three-dimensional fiber dipping glue after plastic squeeze and 180 DEG C-
200 DEG C, the three-dimensional fiber reinforcement solidified under 0.2-0.8MPa solidifying pressures.
The binding agent 2, fireproof heated board 3 and finish coat 6 are strengthened fixing by buckle 5 and expansion bolt 4, the buckle
5 are arranged in the finish coat 6, and the expansion bolt 4 sequentially passes through fireproof heated board through after the centre bore of the buckle 5
3rd, binding agent 2 is fixedly connected with wall base body 1.
The binding agent 2 is the magnesium chloride solution that the concentration of 1.4 weight portions is 25%, the poly- fourth of terminal hydroxy group of 0.2 weight portion
Diene, the stearic acid sodium of 1 weight portion, the silane coupler of 0.1 weight portion, the mixture of the ethylene glycol solution of 1 weight portion.
The glue is consisted of:The water soluble phenol resin of 3-36 weight portions, the accelerator of 1 weight portion and 63-96 weights
The water of amount part;The accelerator consists of:The rosin foaming agent of 0.27 weight portion, the magnesium sulfate solution of 0.23 weight portion,
The sodium tripolyphosphate of the methylsiloxane of 0.06 weight portion, the oxalic acid of 0.2 weight portion and 0.24 weight portion.
Preferably, the three-dimensional fiber is glass fibre, high silica fiber or quartz fibre.
Preferably, the finish coat 6 is stone material, imitative stone material, calcium silicate board with microporous or water resistant coating.
Preferably, between multiple fireproof heated boards 3 fireproof heat insulating lath 8 is filled with piece 7, and in fireproof heated board
The surface brush fire resistant coating 9 of bar 8.
The content not described in detail in description of the invention belongs to the known technology of professional and technical personnel in the field.
Claims (8)
1. a kind of external thermal insulation system, it is characterised in that:The binding agent for outwards including being fixedly connected sequentially by wall base body (1)
(2), fireproof heated board (3) and finish coat (6);The fireproof heated board (3) be by three-dimensional fiber dipping glue after plastic squeeze and
180 DEG C -200 DEG C, the three-dimensional fiber reinforcement solidified under 0.2-0.8MPa solidifying pressures.
2. external thermal insulation system according to claim 1, it is characterised in that:The binding agent (2), fireproof heated board
(3) fixed by buckle (5) and expansion bolt (4) reinforcement with finish coat (6), the buckle (5) is arranged on the finish coat (6)
It is interior, the expansion bolt (4) through after the centre bore of the buckle (5), sequentially pass through fireproof heated board (3), binding agent (2) with
Wall base body (1) is fixedly connected.
3. external thermal insulation system according to claim 1, it is characterised in that:The binding agent (2) is 1.4 weight portions
Concentration is 25% magnesium chloride solution, the end hydroxy butadiene of 0.2 weight portion, the stearic acid sodium of 1 weight portion, 0.1 weight portion
Silane coupler, the mixture of the ethylene glycol solution of 1 weight portion.
4. external thermal insulation system according to claim 1, it is characterised in that:The glue is consisted of:3-36 weight
The water soluble phenol resin of part, the accelerator of 1 weight portion and the water of 63-96 weight portions;The accelerator consists of:0.27 weight
The rosin foaming agent of amount part, the magnesium sulfate solution of 0.23 weight portion, the methylsiloxane of 0.06 weight portion, 0.2 weight portion
The sodium tripolyphosphate of oxalic acid and 0.24 weight portion.
5. external thermal insulation system according to claim 1, it is characterised in that:The three-dimensional fiber is glass fibre, height
Silica fiber or quartz fibre.
6. external thermal insulation system according to claim 1, it is characterised in that:The finish coat (6) is stone material, imitative stone
Material, calcium silicate board with microporous or water resistant coating.
7. external thermal insulation system according to claim 1, it is characterised in that:Spelling between multiple fireproof heated boards (3)
Packing material (8) is filled with seam (7), and on packing material (8) surface brush fire resistant coating (9).
8. external thermal insulation system according to claim 7, it is characterised in that:The packing material (8) is fireproof heat insulating
Lath.