CN106591752A - 一种2060合金均匀化方法 - Google Patents

一种2060合金均匀化方法 Download PDF

Info

Publication number
CN106591752A
CN106591752A CN201611265183.5A CN201611265183A CN106591752A CN 106591752 A CN106591752 A CN 106591752A CN 201611265183 A CN201611265183 A CN 201611265183A CN 106591752 A CN106591752 A CN 106591752A
Authority
CN
China
Prior art keywords
alloy
temperature
homogenization method
heating furnace
drilling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611265183.5A
Other languages
English (en)
Inventor
张敏
游文
杜荣
姚勇
呙永林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Southwest Aluminum Group Co Ltd
Original Assignee
Southwest Aluminum Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Southwest Aluminum Group Co Ltd filed Critical Southwest Aluminum Group Co Ltd
Priority to CN201611265183.5A priority Critical patent/CN106591752A/zh
Publication of CN106591752A publication Critical patent/CN106591752A/zh
Pending legal-status Critical Current

Abstract

本发明所提供的一种2060合金均匀化方法，通过将2060合金预热、两次退火均匀化处理以及冷却处理，从而避免了2060合金严重的元素偏析，保证了合金化学成分充分均匀化。

Description

一种2060合金均匀化方法
技术领域
本发明属于消除合金铸锭结晶相的均匀化热处理方法技术领域，特别涉及一种2060合金均匀化方法。
背景技术
2060系合金属于能获得最高时效强化效果的一类变形合金，具有密度低、强度高、加工性能好等特点。该系合金主要含有Mn、Mg、Ag、Zr和Cu等元素，然而由于2060系合金化程度较高，在凝固过程中Cu元素易在晶界处富集，存在着严重枝晶偏析、晶内和晶界化学成分及组织分布的不均匀，这些都会严重降低合金的塑性、恶化热加工性能，使合金制品强度和塑性降低，各向异性和腐蚀敏感性增加。因此为了消除合金组织缺陷对合金后续加工性能的影响，合金热变形前必须进行合理的均匀化热处理。
均匀化热处理是合金制备和应用的一个极其重要的工艺过程。然而目前针对2060系合金还没有适合的均匀化热处理工艺。因此，提供一种对2060系合金热加工过程中避免严重的元素偏析，是本领域技术人员亟待解决的问题。
发明内容
本发明提供了一种2060合金均匀化方法，避免了严重的元素偏析，保证了合金化学成分充分均匀化。
为解决上述技术问题，本发明提供了一种2060合金均匀化方法，包括以下步骤：
第一步：当加热炉的温度为275℃-285℃以下时所述2060合金装入所述加热炉中；
第二步：所述加热炉的温度设定为T1：450℃-475℃，测得所述2060合金的温度达到设定温度T1后，保温7.5h-8.5h；
第三步：所述加热炉的温度设定为T2：480℃-505℃，测得所述2060合金的温度达到设定温度T2后，保温23.5h-24.5h；
第四步：出炉后对所述2060合金风冷。
优选地，在上述2060合金均匀化方法中，所述加热炉为均热炉。
优选地，在上述2060合金均匀化方法中，所述均热炉的控温精度为±5℃。
优选地，在上述2060合金均匀化方法中，所述2060合金两端各放置用于测量所述2060合金温度的热电偶。
优选地，在上述2060合金均匀化方法中，所述2060合金上开设有放置所述热电偶的钻孔，所述钻孔的直径为5mm-10mm、深度为30mm-50mm。
优选地，在上述2060合金均匀化方法中，所述钻孔与所述热电偶连接处之间的缝隙用硅毡棉堵塞密封。
相对于背景技术，本发明所提供的一种2060合金均匀化方法，通过将2060合金预热、两次退火均匀化处理以及冷却处理，从而避免了2060合金严重的元素偏析，保证了合金化学成分充分均匀化。
具体实施方式
本发明的核心是提供一种2060合金均匀化方法，避免了严重的元素偏析，保证了合金化学成分充分均匀化。
为了使本领域的技术人员更好地理解本发明提供的技术方案，下面将结合具体实施例对本发明作进一步的详细说明。
本发明所提供的一种2060合金均匀化方法，包括以下步骤：
第一步：当加热炉的温度为275℃-285℃以下时2060合金装入加热炉中，进行装炉。
第二步：加热炉的温度设定为T1：450℃-475℃，测得2060合金的温度达到设定温度T1后或设定温度T1上下5℃范围内，保温7.5h-8.5h；
第三步：加热炉的温度设定为T2：480℃-505℃，测得2060合金的温度均达到设定温度T2后或设定温度T2上下5℃范围内，保温23.5h-24.5h。进行均匀化退火时，合金中的元素进行固态扩散，可以消除或减轻晶内偏析，从而改善铸锭或铸件的性能。为了加速原子扩散，缩短退火时间，均匀化退火温度一般都很高。
第四步：出炉后对2060合金风冷进行冷却。
本方案提供的一种2060合金均匀化方法，通过将2060合金预热、两次退火均匀化处理以及冷却处理，从而避免了2060合金严重的元素偏析，保证了合金化学成分充分均匀化。
进一步，加热炉为均热炉。均热炉能够均衡控制炉温，控制回路响应速度相对于普通工业炉的响应速度快。均热炉的控温精度为±5℃，在一定的幅度范围下使得均热炉控制精度更加精准。
进一步，2060合金两端各放置用于测量2060合金温度的热电偶。2060合金上开设有放置热电偶的钻孔，钻孔的直径为5mm-10mm、深度为30mm-50mm。钻孔与热电偶连接处之间的缝隙用硅毡棉堵塞密封，将电热偶紧固在钻孔内。
本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。

Claims (6)

1.一种2060合金均匀化方法，其特征在于，包括以下步骤：
第一步：当加热炉的温度为275℃-285℃以下时所述2060合金装入所述加热炉中；
第二步：所述加热炉的温度设定为T1：450℃-475℃，测得所述2060合金的温度达到设定温度T1后，保温7.5h-8.5h；
第三步：所述加热炉的温度设定为T2：480℃-505℃，测得所述2060合金的温度达到设定温度T2后，保温23.5h-24.5h；
第四步：出炉后对所述2060合金风冷。
2.根据权利要求1所述的2060合金均匀化方法，其特征在于，所述加热炉为均热炉。
3.根据权利要求2所述的2060合金均匀化方法，其特征在于，所述均热炉的控温精度为±5℃。
4.根据权利要求1所述的2060合金均匀化方法，其特征在于，所述2060合金两端各放置用于测量所述2060合金温度的热电偶。
5.根据权利要求4所述的2060合金均匀化方法，其特征在于，所述2060合金上开设有放置所述热电偶的钻孔，所述钻孔的直径为5mm-10mm、深度为30mm-50mm。
6.根据权利要求5所述的2060合金均匀化方法，其特征在于，所述钻孔与所述热电偶连接处之间的缝隙用硅毡棉堵塞密封。
CN201611265183.5A 2016-12-30 2016-12-30 一种2060合金均匀化方法 Pending CN106591752A (zh)