CN106590897A - 一种高渗透环保切削液及其制备方法 - Google Patents

一种高渗透环保切削液及其制备方法 Download PDF

Info

Publication number
CN106590897A
CN106590897A CN201611114193.9A CN201611114193A CN106590897A CN 106590897 A CN106590897 A CN 106590897A CN 201611114193 A CN201611114193 A CN 201611114193A CN 106590897 A CN106590897 A CN 106590897A
Authority
CN
China
Prior art keywords
parts
stirring
cutting liquid
water
rev
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201611114193.9A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Deyang Li Long Yun Intellectual Property Operation Co Ltd
Original Assignee
Deyang Li Long Yun Intellectual Property Operation Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Deyang Li Long Yun Intellectual Property Operation Co Ltd filed Critical Deyang Li Long Yun Intellectual Property Operation Co Ltd
Priority to CN201611114193.9A priority Critical patent/CN106590897A/zh
Publication of CN106590897A publication Critical patent/CN106590897A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种高渗透环保切削液，由下列重量份的原料制成：藻酸丙二醇酯2‑3、纳米金刚石粉4‑6、聚醚改性聚二甲基硅氧烷1‑3、海藻酸钠4‑7、硫化脂肪酸皂3‑5、土耳其红油2‑4、季戊四醇1‑3、烷基丁二酸酯磺酸钠1‑2、助剂9‑12、水120‑150。本发明添加的助剂增强了切削液的分散、润滑、成膜性能，同时提高了切削液的渗透性和冷却性能，本发明的切削液具有分散性好、稳定性高、冷却效果好的优点，提高了加工质量，同时其成本低廉，对环境友好、对人体无毒无害并且生物降解性好。

Description

一种高渗透环保切削液及其制备方法
技术领域
本发明涉及切削液领域，特别涉及一种高渗透环保切削液及其制备方法。
背景技术
环境资源问题是当前人类面临的一个重要问题。对于绿色制造而言，就是实现资源利用最大化和环境影响最小化。切削液在制造加严重后果；亚硝酸钠和磷酸钠等添加剂对环境和人体危害非常大。因此，在满足加工性能的工当中起着至关重要的作用，尽管干式切削技术在某些加工工艺当中得到成功应用，但由于冷却性能较差及所应用工艺的限制，切削液的运用仍不可或缺。在切削加工过程当中，为了减少摩擦带来的能量消耗，保证工件质量以及提高刀具寿命，切削液必须具有良好使用性能。切削液广泛使用给我们带来巨大的经济效益的同时，也威胁着生态环境和人体健康：未经处理的切削液当中，由于防锈剂磷酸钠的累积，会导致水质富营养化进而引发赤潮；杀菌剂苯酚的生物降解性较差，对水生物具有很大的危害；一些表面活性剂会使人体皮肤脱脂、红肿，甚至出现开裂、化脓的条件下，研究和开发性能优越、对环境友好、对人体无毒无害并且生物降解性好的环保切削液具有非常重要的现实意义。
发明内容
本发明的目的在于克服现有技术中所存在的上述不足，提供一种高渗透环保切削液及其制备方法
为了实现上述发明目的，本发明提供了以下技术方案：
一种高渗透环保切削液，由下列重量份的原料制成：藻酸丙二醇酯2-3、纳米金刚石粉4-6、聚醚改性聚二甲基硅氧烷1-3、海藻酸钠4-7、硫化脂肪酸皂3-5、土耳其红油2-4、季戊四醇1-3、烷基丁二酸酯磺酸钠1-2、助剂9-12、水120-150；
所述助剂是由下列重量份的原料制成：松香甘油酯聚氧乙烯醚1-3、偏硼酸钾1-2、硫化烯烃棉籽油5-8、异噻唑啉酮1-2、纤维素羟乙基醚1-2、椰子油烷醇酰胺3-6、聚乙二醇十六烷基醚3-6、月桂醇聚氧乙烯醚硫酸钠1-2、消泡剂0.1-0.3、水40-50；制备方法是(1)将纤维素羟乙基醚、聚乙二醇十六烷基醚、硫化烯烃棉籽油、月桂醇聚氧乙烯醚硫酸钠加到水中，加热至55-65℃，搅拌均匀后加入消泡剂备用；(2)将松香甘油酯聚氧乙烯醚、椰子油烷醇酰胺混合加热至60-70℃，搅拌均匀后将步骤(1)中的产物缓慢加入，以300-400转/分的转速搅拌，加料结束后加热至75-85℃，并在2000-3000转/分下高速搅拌15-30分钟，再加入其余剩余物质继续搅拌5-10分钟即可。
本发明的另一目的在于提供上述水基切削液的制备方法，包括以下步骤：
(1)将土耳其红油、聚醚改性聚二甲基硅氧烷和藻酸丙二醇酯混合，加热至55-65℃，搅拌反应30-40分钟后得到混合物A；
(2)将水煮沸后迅速冷却至60-70℃，再加入烷基丁二酸酯磺酸钠和季戊四醇搅拌均匀，搅拌均匀后加入助剂以1000-1400转/分下搅拌反应20-30分钟，得到混合物B；
(3)将混合物B边搅拌边缓慢的加入混合物A中，将温度控制在65-75℃，搅拌均匀后加入其余剩余成分，在1500-2000转/分下高速搅拌20-30分钟后过滤即可。
与现有技术相比，本发明的有益效果：
本发明添加的助剂增强了切削液的分散、润滑、成膜性能，同时提高了切削液的渗透性和冷却性能，本发明的切削液具有分散性好、稳定性高、冷却效果好的优点，提高了加工质量，同时其成本低廉，对环境友好、对人体无毒无害并且生物降解性好。
具体实施方式
下面结合试验例及具体实施方式对本发明作进一步的详细描述。但不应将此理解为本发明上述主题的范围仅限于以下的实施例，凡基于本发明内容所实现的技术均属于本发明的范围。
实施例1
一种高渗透环保切削液，由下列重量份的原料制成：藻酸丙二醇酯3、纳米金刚石粉5、聚醚改性聚二甲基硅氧烷2、海藻酸钠6、硫化脂肪酸皂4、土耳其红油3、季戊四醇2、烷基丁二酸酯磺酸钠1、助剂10、水140；
所述助剂是由下列重量份的原料制成：松香甘油酯聚氧乙烯醚2、偏硼酸钾1、硫化烯烃棉籽油7、异噻唑啉酮1、纤维素羟乙基醚2、椰子油烷醇酰胺5、聚乙二醇十六烷基醚4、月桂醇聚氧乙烯醚硫酸钠2、消泡剂0.2、水45；制备方法是(1)将纤维素羟乙基醚、聚乙二醇十六烷基醚、硫化烯烃棉籽油、月桂醇聚氧乙烯醚硫酸钠加到水中，加热至60℃，搅拌均匀后加入消泡剂备用；(2)将松香甘油酯聚氧乙烯醚、椰子油烷醇酰胺混合加热至65℃，搅拌均匀后将步骤(1)中的产物缓慢加入，以360转/分的转速搅拌，加料结束后加热至80℃，并在2300转/分下高速搅拌20分钟，再加入其余剩余物质继续搅拌8分钟即可。
上述高渗透环保切削液的制备方法，包括以下步骤：
(1)将土耳其红油、聚醚改性聚二甲基硅氧烷和藻酸丙二醇酯混合，加热至62℃，搅拌反应32分钟后得到混合物A；
(2)将水煮沸后迅速冷却至67℃，再加入烷基丁二酸酯磺酸钠和季戊四醇搅拌均匀，搅拌均匀后加入助剂以1200转/分下搅拌反应25分钟，得到混合物B；
(3)将混合物B边搅拌边缓慢的加入混合物A中，将温度控制在70℃，搅拌均匀后加入其余剩余成分，在1600转/分下高速搅拌25分钟后过滤即可。

Claims (2)

1.一种高渗透环保切削液，其特征在于，由下列重量份的原料制成：藻酸丙二醇酯2-3、纳米金刚石粉4-6、聚醚改性聚二甲基硅氧烷1-3、海藻酸钠4-7、硫化脂肪酸皂3-5、土耳其红油2-4、季戊四醇1-3、烷基丁二酸酯磺酸钠1-2、助剂9-12、水120-150；
所述助剂是由下列重量份的原料制成：松香甘油酯聚氧乙烯醚1-3、偏硼酸钾1-2、硫化烯烃棉籽油5-8、异噻唑啉酮1-2、纤维素羟乙基醚1-2、椰子油烷醇酰胺3-6、聚乙二醇十六烷基醚3-6、月桂醇聚氧乙烯醚硫酸钠1-2、消泡剂0.1-0.3、水40-50；制备方法是(1)将纤维素羟乙基醚、聚乙二醇十六烷基醚、硫化烯烃棉籽油、月桂醇聚氧乙烯醚硫酸钠加到水中，加热至55-65℃，搅拌均匀后加入消泡剂备用；(2)将松香甘油酯聚氧乙烯醚、椰子油烷醇酰胺混合加热至60-70℃，搅拌均匀后将步骤(1)中的产物缓慢加入，以300-400转/分的转速搅拌，加料结束后加热至75-85℃，并在2000-3000转/分下高速搅拌15-30分钟，再加入其余剩余物质继续搅拌5-10分钟即可。
2.根据权利要求1所述一种高渗透环保切削液，其特征在于，由以下具体步骤制成：
(1)将土耳其红油、聚醚改性聚二甲基硅氧烷和藻酸丙二醇酯混合，加热至55-65℃，搅拌反应30-40分钟后得到混合物A；
(2)将水煮沸后迅速冷却至60-70℃，再加入烷基丁二酸酯磺酸钠和季戊四醇搅拌均匀，搅拌均匀后加入助剂以1000-1400转/分下搅拌反应20-30分钟，得到混合物B；
(3)将混合物B边搅拌边缓慢的加入混合物A中，将温度控制在65-75℃，搅拌均匀后加入其余剩余成分，在1500-2000转/分下高速搅拌20-30分钟后过滤即可。
CN201611114193.9A 2016-12-07 2016-12-07 一种高渗透环保切削液及其制备方法 Withdrawn CN106590897A (zh)