CN106590343A - Crossbeam-type shelf - Google Patents
Crossbeam-type shelf Download PDFInfo
- Publication number
- CN106590343A CN106590343A CN201611158188.8A CN201611158188A CN106590343A CN 106590343 A CN106590343 A CN 106590343A CN 201611158188 A CN201611158188 A CN 201611158188A CN 106590343 A CN106590343 A CN 106590343A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- protective layer
- necked flask
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a crossbeam-type shelf. The crossbeam-type shelf is characterized in that the outer surface of a shelf body is coated with a protective layer, wherein the protective layer comprises the following components in parts by mass: 10-15 parts of epoxy resin, 10-20 parts of acrylic resin, 10-15 parts of a butanol phosphate antistatic agent, 8-10 parts of silicon carbide micropowder, 20-25 parts of a coupling agent, 20-50 parts of a curing agent, 2-8 parts of a defoamer, 2-8 parts of a leveling agent and 10-15 parts of isopropyl alcohol. The crossbeam-type shelf has excellent abrasion resistance in use and is long in service life.
Description
Technical field
The present invention relates to a kind of shelf, and in particular to a kind of cross beam type shelf.
Background technology
Storage rack is storage device, and it based on packaging, transport, handling, sorting, information management is the six big basic of logistics to be
Function.With the continuous development of 2014 storage rack industries, increasing industry and enterprise have applied to storage rack, more next
More enterprises enter storage sector.Serve various circles of society friend.And shelf are one of key facilities of storage, can be with
Say, shelf are modern industry warehouse, logistics center, the requisite part of home-delivery center.
The content of the invention
The technical problem to be solved is, for the shortcoming that above prior art is present, proposes a kind of cross beam type
Shelf, the shelf have when in use fine wearability, long service life.
The present invention solves the technical scheme of above technical problem：
A kind of cross beam type shelf, the outer surface coating layer protective layer of shelf, protective layer presses mass fraction including following components：
Epoxy resin：10-15 parts, acrylic resin：10-20 parts, butanol phosphate antistatic additive：10-15 parts, carborundum is micro-
Powder：8-10 parts, coupling agent：20-25 parts；Curing agent：20-50 parts, defoamer：2-8 parts, levelling agent：2-8 parts, isopropanol：10-
15 parts；
Wherein, the coupling agent is gamma-aminopropyl-triethoxy-silane；Described curing agent be m-phenylene diamine (MPD), diethylenetriamine,
One kind in polyamide；Described defoamer is the one kind in dimethicone, organosilicon, polyvinyl acetate；Described stream
Flat agent is the one kind in dimethyl silicone polymer, PSI or acrylic acid.
Further technical scheme is the present invention：
Aforementioned cross beam type shelf, protective layer presses mass fraction including following components：
Epoxy resin：10 parts, acrylic resin：10 parts, butanol phosphate antistatic additive：10 parts, silicon carbide micro-powder：8 parts, it is coupled
Agent：20 parts；Curing agent：20 parts, defoamer：2 parts, levelling agent：2 parts, isopropanol：10 parts.
Aforementioned cross beam type shelf, protective layer presses mass fraction including following components：
Epoxy resin：15 parts, acrylic resin：20 parts, butanol phosphate antistatic additive：15 parts, silicon carbide micro-powder：It is 10 parts, even
Connection agent：25 parts；Curing agent：50 parts, defoamer：8 parts, levelling agent：8 parts, isopropanol：15 parts.
Aforementioned cross beam type shelf, protective layer presses mass fraction including following components：
Epoxy resin：13 parts, acrylic resin：15 parts, butanol phosphate antistatic additive：13 parts, silicon carbide micro-powder：9 parts, it is coupled
Agent：22 parts；Curing agent：40 parts, defoamer：6 parts, levelling agent：6 parts, isopropanol：13 parts.
Aforementioned cross beam type shelf, the preparation method of protective layer is specific as follows：
（1）The preparation of butanol phosphate antistatic additive
A is added to n-butanol in clean there-necked flask, is subsequently adding phosphorus pentoxide, and with spoon n-butanol has slowly been put into
There-necked flask in, there-necked flask is placed in the large beaker equipped with cold water, with control in adition process its temperature be less than 50
℃；
B has been finished, and is sealed with plug, the plug with thermometer, by there-necked flask respectively, and there-necked flask is fixed on into electric mixing
Mix on device, and be put into and be adjusted in 70 DEG C of thermostat water bath, timing is started when thermometer registration is 70 DEG C, use after reaction 4h
Pipette accurately pipettes deionized water and adds there-necked flask to be hydrolyzed, and hydrolysis time is 2-3h, and after reaction terminates, cooling is taken out
Product, that is, obtain butanol phosphate antistatic additive；
（2）Epoxy resin and acrylic resin are melted at certain 150-200 DEG C, isopropanol heating stirring is subsequently adding, is treated
After resin is solvent, coupling agent is added, continue to stir 10-15min, add silicon carbide micro-powder and butanol phosphate antistatic additive, filled
Divide stirring, add curing agent, defoamer and levelling agent to disperse 5-10min using ultrasonic wave, you can to obtain coating, coating is coated
Protective layer is formed on shelf.
The invention has the beneficial effects as follows：
The present invention by add silicon carbide micro-powder, carborundum differential is a kind of ceramic material, tool have good wearability, it is excellent
Heat endurance, silicon carbide micro-powder is evenly dispersed in coating so that the coating has good abrasion resistant effect.
With epoxy resin as bonding agent, polyamide is curing agent to the present invention, and silicon carbide micro-powder is wear resistant filler, using chemistry
Gluing method is prepared for a kind of wear-resistant paint, and compared with using thermal spraying and vapour deposition process coating is prepared, and the glutinous method of chemistry prepares wear-resisting painting
Material has the advantages that process is simple, energy-conservation.
Specific embodiment
Embodiment 1
The present embodiment provides a kind of cross beam type shelf, and the outer surface coating layer protective layer of shelf, protective layer presses mass fraction bag
Include following components：
Epoxy resin：10 parts, acrylic resin：10 parts, butanol phosphate antistatic additive：10 parts, silicon carbide micro-powder：8 parts, it is coupled
Agent：20 parts；Curing agent：20 parts, defoamer：2 parts, levelling agent：2 parts, isopropanol：10 parts.
Wherein, coupling agent is gamma-aminopropyl-triethoxy-silane；Curing agent is m-phenylene diamine (MPD), diethylenetriamine, polyamide
In one kind；Defoamer is the one kind in dimethicone, organosilicon, polyvinyl acetate；Levelling agent is polydimethylsiloxanes
One kind in alkane, PSI or acrylic acid.
The preparation method of protective layer is specific as follows：
（1）The preparation of butanol phosphate antistatic additive
A is added to n-butanol in clean there-necked flask, is subsequently adding phosphorus pentoxide, and with spoon n-butanol has slowly been put into
There-necked flask in, there-necked flask is placed in the large beaker equipped with cold water, with control in adition process its temperature be less than 50
℃；
B has been finished, and is sealed with plug, the plug with thermometer, by there-necked flask respectively, and there-necked flask is fixed on into electric mixing
Mix on device, and be put into and be adjusted in 70 DEG C of thermostat water bath, timing is started when thermometer registration is 70 DEG C, use after reaction 4h
Pipette accurately pipettes deionized water and adds there-necked flask to be hydrolyzed, and hydrolysis time is 2-3h, and after reaction terminates, cooling is taken out
Product, that is, obtain butanol phosphate antistatic additive；
（2）Epoxy resin and acrylic resin are melted at certain 150-200 DEG C, isopropanol heating stirring is subsequently adding, is treated
After resin is solvent, coupling agent is added, continue to stir 10-15min, add silicon carbide micro-powder and butanol phosphate antistatic additive, filled
Divide stirring, add curing agent, defoamer and levelling agent to disperse 5-10min using ultrasonic wave, you can to obtain coating, coating is coated
Protective layer is formed on shelf.
Embodiment 2
The present embodiment provides a kind of cross beam type shelf, and the outer surface coating layer protective layer of shelf, protective layer presses mass fraction bag
Include following components：
Epoxy resin：15 parts, acrylic resin：20 parts, butanol phosphate antistatic additive：15 parts, silicon carbide micro-powder：It is 10 parts, even
Connection agent：25 parts；Curing agent：50 parts, defoamer：8 parts, levelling agent：8 parts, isopropanol：15 parts.
Wherein, coupling agent is gamma-aminopropyl-triethoxy-silane；Curing agent is m-phenylene diamine (MPD), diethylenetriamine, polyamide
In one kind；Defoamer is the one kind in dimethicone, organosilicon, polyvinyl acetate；Levelling agent is polydimethylsiloxanes
One kind in alkane, PSI or acrylic acid.
The preparation method of protective layer is specific as follows：
（1）The preparation of butanol phosphate antistatic additive
A is added to n-butanol in clean there-necked flask, is subsequently adding phosphorus pentoxide, and with spoon n-butanol has slowly been put into
There-necked flask in, there-necked flask is placed in the large beaker equipped with cold water, with control in adition process its temperature be less than 50
℃；
B has been finished, and is sealed with plug, the plug with thermometer, by there-necked flask respectively, and there-necked flask is fixed on into electric mixing
Mix on device, and be put into and be adjusted in 70 DEG C of thermostat water bath, timing is started when thermometer registration is 70 DEG C, use after reaction 4h
Pipette accurately pipettes deionized water and adds there-necked flask to be hydrolyzed, and hydrolysis time is 2-3h, and after reaction terminates, cooling is taken out
Product, that is, obtain butanol phosphate antistatic additive；
（2）Epoxy resin and acrylic resin are melted at certain 150-200 DEG C, isopropanol heating stirring is subsequently adding, is treated
After resin is solvent, coupling agent is added, continue to stir 10-15min, add silicon carbide micro-powder and butanol phosphate antistatic additive, filled
Divide stirring, add curing agent, defoamer and levelling agent to disperse 5-10min using ultrasonic wave, you can to obtain coating, coating is coated
Protective layer is formed on shelf.
Embodiment 3
The present embodiment provides a kind of cross beam type shelf, and the outer surface coating layer protective layer of shelf, protective layer presses mass fraction bag
Include following components：
Epoxy resin：13 parts, acrylic resin：15 parts, butanol phosphate antistatic additive：13 parts, silicon carbide micro-powder：9 parts, it is coupled
Agent：22 parts；Curing agent：40 parts, defoamer：6 parts, levelling agent：6 parts, isopropanol：13 parts.
Wherein, coupling agent is gamma-aminopropyl-triethoxy-silane；Curing agent is m-phenylene diamine (MPD), diethylenetriamine, polyamide
In one kind；Defoamer is the one kind in dimethicone, organosilicon, polyvinyl acetate；Levelling agent is polydimethylsiloxanes
One kind in alkane, PSI or acrylic acid.
The preparation method of protective layer is specific as follows：
（1）The preparation of butanol phosphate antistatic additive
A is added to n-butanol in clean there-necked flask, is subsequently adding phosphorus pentoxide, and with spoon n-butanol has slowly been put into
There-necked flask in, there-necked flask is placed in the large beaker equipped with cold water, with control in adition process its temperature be less than 50
℃；
B has been finished, and is sealed with plug, the plug with thermometer, by there-necked flask respectively, and there-necked flask is fixed on into electric mixing
Mix on device, and be put into and be adjusted in 70 DEG C of thermostat water bath, timing is started when thermometer registration is 70 DEG C, use after reaction 4h
Pipette accurately pipettes deionized water and adds there-necked flask to be hydrolyzed, and hydrolysis time is 2-3h, and after reaction terminates, cooling is taken out
Product, that is, obtain butanol phosphate antistatic additive；
（2）Epoxy resin and acrylic resin are melted at certain 150-200 DEG C, isopropanol heating stirring is subsequently adding, is treated
After resin is solvent, coupling agent is added, continue to stir 10-15min, add silicon carbide micro-powder and butanol phosphate antistatic additive, filled
Divide stirring, add curing agent, defoamer and levelling agent to disperse 5-10min using ultrasonic wave, you can to obtain coating, coating is coated
Protective layer is formed on shelf.
In addition to the implementation, the present invention can also have other embodiment.All employing equivalents or equivalent transformation shape
Into technical scheme, all fall within the protection domain of application claims.
Claims (5)
1. a kind of cross beam type shelf, it is characterised in that：The outer surface coating layer protective layer of the shelf, described protective layer is pressed
Mass fraction includes following components：
Epoxy resin：10-15 parts, acrylic resin：10-20 parts, butanol phosphate antistatic additive：10-15 parts, carborundum is micro-
Powder：8-10 parts, coupling agent：20-25 parts；Curing agent：20-50 parts, defoamer：2-8 parts, levelling agent：2-8 parts, isopropanol：10-
15 parts；
Wherein, the coupling agent is gamma-aminopropyl-triethoxy-silane；Described curing agent be m-phenylene diamine (MPD), diethylenetriamine,
One kind in polyamide；Described defoamer is the one kind in dimethicone, organosilicon, polyvinyl acetate；Described stream
Flat agent is the one kind in dimethyl silicone polymer, PSI or acrylic acid.
2. cross beam type shelf according to claim 1, it is characterised in that：The protective layer is included with the following group by mass fraction
Point：
Epoxy resin：10 parts, acrylic resin：10 parts, butanol phosphate antistatic additive：10 parts, silicon carbide micro-powder：8 parts, it is coupled
Agent：20 parts；Curing agent：20 parts, defoamer：2 parts, levelling agent：2 parts, isopropanol：10 parts.
3. cross beam type shelf according to claim 1, it is characterised in that：The protective layer is included with the following group by mass fraction
Point：
Epoxy resin：15 parts, acrylic resin：20 parts, butanol phosphate antistatic additive：15 parts, silicon carbide micro-powder：It is 10 parts, even
Connection agent：25 parts；Curing agent：50 parts, defoamer：8 parts, levelling agent：8 parts, isopropanol：15 parts.
4. cross beam type shelf according to claim 1, it is characterised in that：The protective layer is included with the following group by mass fraction
Point：
Epoxy resin：13 parts, acrylic resin：15 parts, butanol phosphate antistatic additive：13 parts, silicon carbide micro-powder：9 parts, it is coupled
Agent：22 parts；Curing agent：40 parts, defoamer：6 parts, levelling agent：6 parts, isopropanol：13 parts.
5. cross beam type shelf as claimed in claim 1, it is characterised in that：The preparation method of the protective layer is specific as follows：
（1）The preparation of butanol phosphate antistatic additive
A is added to n-butanol in clean there-necked flask, is subsequently adding phosphorus pentoxide, and with spoon n-butanol has slowly been put into
There-necked flask in, there-necked flask is placed in the large beaker equipped with cold water, with control in adition process its temperature be less than 50
℃；
B has been finished, and is sealed with plug, the plug with thermometer, by there-necked flask respectively, and there-necked flask is fixed on into electric mixing
Mix on device, and be put into and be adjusted in 70 DEG C of thermostat water bath, timing is started when thermometer registration is 70 DEG C, use after reaction 4h
Pipette accurately pipettes deionized water and adds there-necked flask to be hydrolyzed, and hydrolysis time is 2-3h, and after reaction terminates, cooling is taken out
Product, that is, obtain butanol phosphate antistatic additive；
（2）Epoxy resin and acrylic resin are melted at certain 150-200 DEG C, isopropanol heating stirring is subsequently adding, is treated
After resin is solvent, coupling agent is added, continue to stir 10-15min, add silicon carbide micro-powder and butanol phosphate antistatic additive, filled
Divide stirring, add curing agent, defoamer and levelling agent to disperse 5-10min using ultrasonic wave, you can to obtain coating, coating is coated
Protective layer is formed on shelf.