CN106590206A - Method of using aqueous multicolor paint and solvent-free epoxy terrace paint in matched manner - Google Patents
Method of using aqueous multicolor paint and solvent-free epoxy terrace paint in matched manner Download PDFInfo
- Publication number
- CN106590206A CN106590206A CN201611239806.1A CN201611239806A CN106590206A CN 106590206 A CN106590206 A CN 106590206A CN 201611239806 A CN201611239806 A CN 201611239806A CN 106590206 A CN106590206 A CN 106590206A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- water
- rpms
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to the technical field of paint, in particular to a method of using aqueous multicolor paint and solvent-free epoxy terrace paint in a matched manner. According to the method of using the aqueous multicolor paint and the solvent-free epoxy terrace paint in a matched manner, during construction, firstly a base layer surface needing to spray is treated, so that the base layer surface is level and free from cracks, and the PH value of the treated base layer surface is 8-10. According to the method disclosed by the invention, the aqueous multicolor paint and the solvent-free epoxy terrace paint are combined, so that the color diversity of the aqueous multicolor paint is utilized, the uniqueness of the solvent-free epoxy terrace paint is also fully utilized, during coating and brushing, diversified designs and colors of decorative coatings can be realized, the decoration effects obtained by using the method can be equivalent to the decoration effects of terraces of places of homes, schools, bazaars and the like using ceramic tiles and marble, and the decoration cost is saved; and besides, the solvent-free epoxy terrace paint has the characteristics of being high in curing speed, self-leveling, good in mechanical properties, acid-resistant, alkali-resistant, salt water resistant and the like, and can also be used for enterprise workshops with adverse environment.
Description
Technical field
The present invention relates to technical field of coatings, a kind of water-soluble colorful coating is engaged with non-solvent epoxy floor coatings
Using method.Background technology
The decoration in the places such as family, school, market can adopt ceramic tile, marble, but, marble or/and ceramic tile are frangible
And it is expensive.At present useful water-soluble colorful coating replaces marble or/and ceramic tile decoration with non-solvent epoxy floor coatings
, although pattern can be with arbitrary selection, but usage is limited, relatively simple；Non-solvent epoxy floor coatings also can only be with monochrome
Form is used, such as bottle green, light gray, grey, white etc., also relatively simple just because of color, so also can only use
In the decoration on the ground such as factory, enterprise, and it is used in commonly fitting up.
The content of the invention
The invention provides the using method that a kind of water-soluble colorful coating is engaged with non-solvent epoxy floor coatings, overcomes
The deficiency of above-mentioned prior art, it can the current water-soluble colorful coating of effectively solving and non-solvent epoxy floor coatings usage list
First, marble and ceramic tile is frangible and expensive problem.
The technical scheme is that by following measures to realize：A kind of water-soluble colorful coating and non-solvent epoxy
The using method that floor coatings are engaged, during construction, is first processed the substrate surface for needing to be sprayed, and makes substrate surface
It is 8% to 10% that smooth free from flaw, PH values are 8 to 10, moisture content, then needs the aqueous colorful of color to apply basic unit's spraying
Material, after water-soluble colorful coating to be sprayed is parched completely, then sprays non-solvent epoxy floor coatings.
The further optimization and/or improvements to foregoing invention technical scheme are presented herein below：
Above-mentioned water-soluble colorful coating used can be obtained by following preparation methods：
The first step, another name of scoring by weight take 980 parts to 990 parts water, 5 parts to 10 parts hydroxypropyl celluloses, 5 parts
To 10 parts of preservatives, 0.5 part to 2 parts defoamer and 1 part to 3 parts AMP-95, add water to into Scattered Kettle, unlatching is stirred
Mix, under conditions of stir speed (S.S.) is for 500 rpms to 700 rpms, add hydroxypropyl fine in Scattered Kettle successively
Dimension element, preservative, defoamer and AMP-95, dispersed with stirring obtains Protection glue to transparent；
Second step, another name of scoring by weight take 750 parts to 800 parts water, 28 parts to 32 parts granulating agent A, 1 part to 4
Part granulating agent B, 2 parts to 6 parts granulating agent C and 450 parts of slurries to 500 parts of required colors, first add in stirred tank
Water, opens stirring, under conditions of stir speed (S.S.) is for 100 rpms to 300 rpms, three points is added in stirred tank
One of weight portion granulating agent A and the slurry of 1/2nd weight portions, add the granulating agent A and two of 1/3rd weight portions
The slurry of/mono- weight portion, is subsequently added into the granulating agent A of 1/3rd weight portions, and stirring stands 5 after 5 minutes to 10 minutes
Minute, to 10 minutes, opens stirring, and under conditions of stir speed (S.S.) is for 100 rpms to 300 rpms, addition is made
Granula B and granulating agent C, add AMP-95 that 40 mesh are crossed after solution pH value is adjusted to into 8.5 to 9 and obtain institute to 80 mesh sieves
Need the color point liquid of color；
3rd step, by weight meter weigh 200 parts to 250 parts Protection glues and 750 parts of coloured silks to 800 parts of required colors
Point liquid, the color point liquid of required color is added to paint mixing kettle, opens stirring, is 80 rpms to 100 turns in stir speed (S.S.)
Add Protection glue to be uniformly mixing to obtain the net particle of required color into paint mixing kettle under conditions of per minute, repeat the first step to the
Three steps are obtained the net particle of different colours；
4th step, another name of scoring by weight take 220 parts to 230 parts water, 5 parts to 9 portions preservatives, 1 part to 3 parts
Defoamer, 15 parts to 25 parts ethylene glycol, 35 parts to 40 parts coalescents, 5.5 parts to 6.5 parts association thickeners, 1
Part adds styrene-acrylic emulsion in paint mixing kettle to 3 parts of TT-935 thickeners and 710 parts to 720 parts styrene-acrylic emulsions, and unlatching is stirred
Mix, under conditions of stir speed (S.S.) is for 120 rpms to 150 rpms, add water, anti-corrosion into paint mixing kettle successively
Agent, defoamer, ethylene glycol and coalescents, after stirring, are subsequently added into association thickener and the adjustment of TT-935 thickeners
Viscosity to 90KU to 100KU obtains base paint；
5th step, counts by weight, 250 parts to 300 parts of base paint is weighed respectively and with according to floral designs effect requirements institute
Need 750 parts to 800 parts of the net particle of color, net particle put in paint mixing kettle, stir speed (S.S.) be 80 rpms extremely
Base paint is added to be uniformly mixing to obtain water-soluble colorful coating into paint mixing kettle under conditions of 100 rpms.
In above-mentioned water-soluble colorful coating：Preservative is the preservative of the code name for HF of Sol company production；Or/and,
Coalescents are the coalescents of model OE500 of Rhom and Hass's production；Or/and, association thickener is Nuo Puke
The association thickener of model SN-612 of company's production；Or/and, defoamer is the model 7005 of this production of hamming
Defoamer；Or/and, the slurry of granulating agent A, granulating agent B, granulating agent C and required color is the beautiful company's life of Beijing Saden
The product of product.
Above-mentioned non-solvent epoxy floor coatings used can be obtained by following preparation methods：Another name of scoring by weight takes
85 parts to 85.5 parts of epoxy resin, 11.77 parts to 11.87 parts of reactive diluent, 0.93 part to 1.03 parts of levelling agent, disappear
I 1.1 parts to 1.2 parts of infusion, II 0.15 parts to 0.25 part and KH550 of defoamer 0.45 part of silane coupler extremely
0.55 part；By the silane coupler of epoxy resin, reactive diluent, levelling agent, defoamer I, defoamer II and KH550 by suitable
Sequence is added to feeding intake in kettle, and 30 minutes are stirred under conditions of stir speed (S.S.) is for 950 rpms to 1050 rpms extremely
Obtain first component within 40 minutes, weigh parts by weight be first component parts by weight 1/2nd 1689 resins as component B, make
Used time, first component and component B are stirred the non-solvent epoxy floor coatings that obtain.
Epoxy resin used, reactive diluent and 1689 resins are Jiangsu in above-mentioned non-solvent epoxy floor coatings
The epoxy resin of model 618, the reactive diluent of model 660A and 1689 resins that three wood are produced；Or/and, levelling
Agent and defoamer I are the levelling agent of model BYK306 of Bick chemical production and the defoamer I of model BYK066；
Or/and, defoamer II is the defoamer II of model BZ403 that the good open-birth of TaiWan, China is produced.
During above-mentioned construction, the environment temperature of construction can be 45% to 75% for 30 DEG C to 40 DEG C, relative air humidity.
Water-soluble colorful coating make use of in combination with non-solvent epoxy floor coatings, both the present invention water-soluble colorful coating face
Color diversity, also sufficiently utilizes very the uniqueness of non-solvent epoxy floor coatings, and decoration can be realized when brushing
Paint pattern is various, and the decoration in the places such as family, school, market can be used for equivalent to ceramic tile, marble, saves and is decorated
This, while non-solvent epoxy floor coatings have, curing rate is fast, Self-leveling, good mechanical property, acidproof, alkaline-resisting, salt water resistance etc.
Characteristic, it can also be used to the working shop of enterprise of bad environments.
Specific embodiment
The present invention is not limited by following embodiments, can technology according to the present invention scheme and actual conditions determining specifically
Embodiment.
Embodiment 1, when the using method that the water-soluble colorful coating is engaged with non-solvent epoxy floor coatings is constructed, first will
The substrate surface that needs are sprayed is processed, and it is 8% to make the smooth free from flaw of substrate surface, PH values for 8 to 10, moisture content
To 10%, the water-soluble colorful coating of color is then needed to basic unit's spraying, after water-soluble colorful coating to be sprayed is parched completely, then
Spraying non-solvent epoxy floor coatings.
Embodiment 2, the using method that the water-soluble colorful coating is engaged with non-solvent epoxy floor coatings, during construction, first
The substrate surface for needing to be sprayed is processed, it is 8 to make the smooth free from flaw of substrate surface, PH values or 10, moisture content is
8% or 10%, the water-soluble colorful coating of color is then needed to basic unit's spraying, after water-soluble colorful coating to be sprayed is parched completely,
Non-solvent epoxy floor coatings are sprayed again.
Embodiment 3, used as the preferred of above-described embodiment, water-soluble colorful coating used is obtained by following preparation methods：
The first step, another name of scoring by weight take 980 parts to 990 parts water, 5 parts to 10 parts hydroxypropyl celluloses, 5 parts
To 10 parts of preservatives, 0.5 part to 2 parts defoamer and 1 part to 3 parts AMP-95, add water to into Scattered Kettle, unlatching is stirred
Mix, under conditions of stir speed (S.S.) is for 500 rpms to 700 rpms, add hydroxypropyl fine in Scattered Kettle successively
Dimension element, preservative, defoamer and AMP-95, dispersed with stirring obtains Protection glue to transparent；
Second step, another name of scoring by weight take 750 parts to 800 parts water, 28 parts to 32 parts granulating agent A, 1 part to 4
Part granulating agent B, 2 parts to 6 parts granulating agent C and 450 parts of slurries to 500 parts of required colors, first add in stirred tank
Water, opens stirring, under conditions of stir speed (S.S.) is for 100 rpms to 300 rpms, three points is added in stirred tank
One of weight portion granulating agent A and the slurry of 1/2nd weight portions, add the granulating agent A and two of 1/3rd weight portions
The slurry of/mono- weight portion, is subsequently added into the granulating agent A of 1/3rd weight portions, and stirring stands 5 after 5 minutes to 10 minutes
Minute, to 10 minutes, opens stirring, and under conditions of stir speed (S.S.) is for 100 rpms to 300 rpms, addition is made
Granula B and granulating agent C, add AMP-95 that 40 mesh are crossed after solution pH value is adjusted to into 8.5 to 9 and obtain institute to 80 mesh sieves
Need the color point liquid of color；
3rd step, by weight meter weigh 200 parts to 250 parts Protection glues and 750 parts of coloured silks to 800 parts of required colors
Point liquid, the color point liquid of required color is added to paint mixing kettle, opens stirring, is 80 rpms to 100 turns in stir speed (S.S.)
Add Protection glue to be uniformly mixing to obtain the net particle of required color into paint mixing kettle under conditions of per minute, repeat the first step to the
Three steps are obtained the net particle of different colours；
4th step, another name of scoring by weight take 220 parts to 230 parts water, 5 parts to 9 portions preservatives, 1 part to 3 parts
Defoamer, 15 parts to 25 parts ethylene glycol, 35 parts to 40 parts coalescents, 5.5 parts to 6.5 parts association thickeners, 1
Part adds styrene-acrylic emulsion in paint mixing kettle to 3 parts of TT-935 thickeners and 710 parts to 720 parts styrene-acrylic emulsions, and unlatching is stirred
Mix, under conditions of stir speed (S.S.) is for 120 rpms to 150 rpms, add water, anti-corrosion into paint mixing kettle successively
Agent, defoamer, ethylene glycol and coalescents, after stirring, are subsequently added into association thickener and the adjustment of TT-935 thickeners
Viscosity to 90KU to 100KU obtains base paint；
5th step, counts by weight, 250 parts to 300 parts of base paint is weighed respectively and with according to floral designs effect requirements institute
Need 750 parts to 800 parts of the net particle of color, net particle put in paint mixing kettle, stir speed (S.S.) be 80 rpms extremely
Base paint is added to be uniformly mixing to obtain water-soluble colorful coating into paint mixing kettle under conditions of 100 rpms.
Embodiment 4, as the preferred of above-described embodiment, in above-mentioned water-soluble colorful coating：Preservative is the life of Sol company
The code name of product is the preservative of HF；Or/and, coalescents are that the film forming of model OE500 of Rhom and Hass's production is helped
Agent；Or/and, association thickener is the association thickener of model SN-612 of Nuo Puke companies production；Or/and, disappear
Infusion is the defoamer of this model 7005 for producing of hamming；Or/and, granulating agent A, granulating agent B, granulating agent C and required face
The slurry of color is the product of the beautiful company's production of Beijing Saden.Hydroxypropyl cellulose, TT-935 thickenings employed in the present invention
Agent, AMP-95 are the products of existing public offering on market.
Embodiment 5, used as the preferred of above-described embodiment, non-solvent epoxy floor coatings used press following preparation methods
Obtain：By weight score another name 85 parts to 85.5 parts of extracting epoxy resin, 11.77 parts to 11.87 parts of reactive diluent,
0.93 part to 1.03 parts of levelling agent, I 1.1 parts to 1.2 parts of defoamer, II 0.15 parts to 0.25 part of defoamer and
0.45 part to 0.55 part of the silane coupler of KH550；By epoxy resin, reactive diluent, levelling agent, defoamer I, defoamer
II and KH550 silane coupler is sequentially added into feeding intake in kettle, is 950 rpms to 1050 turns in stir speed (S.S.)
Stirring under conditions of per minute obtains first component in 30 minutes to 40 minutes, weighs parts by weight for two points of first component parts by weight
One of 1689 resins as component B, when using, first component and component B are stirred the non-solvent epoxy terrace that obtain
Coating.
Embodiment 6, as the preferred of above-described embodiment, epoxy resin used, activity in non-solvent epoxy floor coatings
Diluent and 1689 resins are the activity dilution of the epoxy resin of the model 618 of the wood production of Jiangsu three, model 660A
Agent and 1689 resins；Or/and, levelling agent and defoamer I be the levelling agent of model BYK306 of Bick chemical production and
The defoamer I of model BYK066；Or/and, defoamer II is the froth breaking of model BZ403 that the good open-birth of TaiWan, China is produced
Agent II.The silane coupler of the KH550 employed in the present invention is the product of existing public offering on market.
Embodiment 7, used as the preferred of above-described embodiment, during construction, the environment temperature of construction is 30 DEG C to 40 DEG C, air phase
It is 45% to 75% to humidity.
The decorative paint color come is brushed as stated above generous attractive in appearance, potentially acting as the conduct such as marble, ceramic tile is used for
The decoration in the places such as family, school, market, can effectively reduce trimming cost, while non-solvent epoxy floor coatings have admittedly
Change speed is fast, Self-leveling, good mechanical property, the characteristic such as acidproof, alkaline-resisting, salt water resistance, it can also be used to the working shop of enterprise of bad environments.
Lacquer painting after method brushing according to above-described embodiment is detected：
Lacquer painting is detected according to test method GB/T1720-1979, the adhesive force of lacquer painting is 2 grades, is illustrated according to above-mentioned
The lacquer painting adhesive ability of embodiment brushing is excellent；Lacquer painting is detected according to test method GB/T1731-1993, lacquer painting is soft
Toughness is 1mm, illustrates that the pliability of lacquer painting is very good, if being painted on processing component surface, when processing component bends, and Bu Huifa
Raw depainting phenomenon；Lacquer painting is detected according to test method GB/T1732-1993, the impact strength of lacquer painting is 50kg.cm,
Illustrate that the anti-strike capability of lacquer painting is stronger；Lacquer painting is detected according to test method GB/T1730, pencil hardness is 3 H, is said
Bright lacquer painting should not trace, stay print, the hardness of lacquer painting is preferable；Lacquer painting is detected according to test method GB/T1768,
Under 250g, 1000 turns of testing conditions, wearability is less than or equal to 0.01, illustrates that the wearability of lacquer painting is preferable；According to test method
GB9274-88 is detected to lacquer painting, is 20% H2SO4 in the case where environment temperature is 25 degrees celsius, with volumetric concentration
Carry out smearing lacquer painting 30 days, be that 20% NaOH carries out smearing lacquer painting 30 days with volumetric concentration, carried out smearing lacquer painting with machine oil
30 days, lacquer painting was not any change, and illustrated that the corrosion resistance of lacquer painting is good.
Claims (3)
1. the using method that a kind of water-soluble colorful coating is engaged with non-solvent epoxy floor coatings, it is characterised in that during construction,
First the substrate surface for needing to be sprayed is processed, the smooth free from flaw of substrate surface, PH values is made for 8 to 10, moisture content
For 8% to 10%, the water-soluble colorful coating of color, water-soluble colorful coating to be sprayed is then needed to parch completely to basic unit's spraying
Afterwards, then non-solvent epoxy floor coatings are sprayed；Wherein：Non-solvent epoxy floor coatings used are obtained by following preparation methods：
By weight score another name 85 parts to 85.5 parts of extracting epoxy resin, 11.77 parts to 11.87 parts of reactive diluent, levelling
0.93 part to 1.03 parts of agent, I 1.1 parts to 1.2 parts of defoamer, II 0.15 parts to 0.25 part and KH550 of defoamer
0.45 part to 0.55 part of silane coupler；By epoxy resin, reactive diluent, levelling agent, defoamer I, the and of defoamer II
The silane coupler of KH550 is sequentially added into feeding intake in kettle, is 950 rpms to 1050 rpms in stir speed (S.S.)
Under conditions of stirring obtain first component within 30 minutes to 40 minutes, weigh parts by weight for first component parts by weight 1/2nd
1689 resins when using, first component and component B are stirred the non-solvent epoxy floor coatings that obtain as component B.
2. the using method that the water-soluble colorful coating according to claim 1 is engaged with non-solvent epoxy floor coatings, its
It is characterised by that water-soluble colorful coating used is obtained by following preparation methods：The first step, another name of scoring by weight takes 980
Part is to 990 parts of water, 5 parts to 10 parts hydroxypropyl celluloses, 5 parts to 10 parts preservatives, 0.5 part to 2 parts defoamers and 1
Part is added water to into Scattered Kettle to 3 parts of AMP-95, and it is 500 rpms to 700 turns every to open stirring in stir speed (S.S.)
Under conditions of minute, hydroxypropyl cellulose, preservative, defoamer and AMP-95 are added in Scattered Kettle successively, dispersed with stirring is extremely
It is transparent to obtain Protection glue；Second step, another name of scoring by weight takes 750 parts to 800 parts water, 28 parts to 32 parts granulating agents
A, 1 part to 4 parts granulating agent B, 2 parts to 6 parts granulating agent C and 450 parts of slurries to 500 parts of required colors, first to stirring
Water is added in kettle, stirring is opened, under conditions of stir speed (S.S.) is for 100 rpms to 300 rpms, in stirred tank
The granulating agent A of 1/3rd weight portions and the slurry of 1/2nd weight portions are added, the granulation of 1/3rd weight portions is added
The slurry of agent A and 1/2nd weight portions, is subsequently added into the granulating agent A of 1/3rd weight portions, stirs 5 minutes to 10 points
5 minutes to 10 minutes are stood after clock, stirring is opened, in the condition that stir speed (S.S.) is 100 rpms to 300 rpms
Under, granulating agent B and granulating agent C is added, add AMP-95 that 40 mesh are crossed after solution pH value is adjusted to into 8.5 to 9 to 80 mesh
Sieve obtains the color point liquid of required color；3rd step, by weight meter weigh 200 parts to 250 parts Protection glues and 750 parts extremely
The color point liquid of 800 parts of required colors, the color point liquid of required color is added to paint mixing kettle, opens stirring, is in stir speed (S.S.)
Protection glue is added to be uniformly mixing to obtain the net of required color into paint mixing kettle under conditions of 80 rpms to 100 rpms
Particle, repeats the net particle that the first step to the 3rd step is obtained different colours；4th step, another name of scoring by weight takes
220 parts to 230 parts water, 5 parts to 9 portions preservatives, 1 part to 3 parts defoamer, 15 parts to 25 parts ethylene glycol, 35 parts extremely
40 parts of coalescents, 5.5 parts to 6.5 parts association thickeners, 1 part to 3 parts TT-935 thickener and 710 parts to 720
Part styrene-acrylic emulsion, styrene-acrylic emulsion is added in paint mixing kettle, opens stirring, is 120 rpms to 150 turns every in stir speed (S.S.)
Under conditions of minute, water, preservative, defoamer, ethylene glycol and coalescents are added into paint mixing kettle successively, after stirring,
It is subsequently added into association thickener and TT-935 thickeners adjustment viscosity obtains base paint to 90KU to 100KU；5th step,
Count by weight, 250 parts to 300 parts of base paint is weighed respectively and with the net grain according to floral designs effect requirements required color
750 parts to 800 parts of son, net particle is put in paint mixing kettle, is 80 rpms to 100 rpms in stir speed (S.S.)
Under conditions of into paint mixing kettle add base paint be uniformly mixing to obtain water-soluble colorful coating.
3. the using method that the water-soluble colorful coating according to claim 2 is engaged with non-solvent epoxy floor coatings,
It is characterized in that preservative is the preservative of the code name for HF of Sol company production.