CN106589817A - Heat conducting plate and preparation method thereof - Google Patents
Heat conducting plate and preparation method thereof Download PDFInfo
- Publication number
- CN106589817A CN106589817A CN201611114772.3A CN201611114772A CN106589817A CN 106589817 A CN106589817 A CN 106589817A CN 201611114772 A CN201611114772 A CN 201611114772A CN 106589817 A CN106589817 A CN 106589817A
- Authority
- CN
- China
- Prior art keywords
- heat
- powder
- conducting plate
- heat conducting
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat conducting plate. The heat conducting plate is characterized by being prepared from, by weight, 30-40% of 2000-mesh metal powder, 15-25% of puffed microbeads, 25-35% of heat conducting resin, 8-12% of macromolecular heat conducting powder and 3-6% of infiltration agent, wherein the heat conducting resin is epoxy resin and/or isocyanate resin, and the macromolecular heat conducting powder is reinforced carbon fiber powder. The heat conducting resin is stirred with the metal powder and the macromolecular heat conducting powder in air, then the infiltration agent and the puffed microbeads are added, vacuumizing is performed, then the mixture is put in a mold, and the mold is put in a levelling machine to perform pressure casting for forming. The heat conducting plate has the advantages of being uniform in heat conduction, high in heat conduction efficiency and low in cost.
Description
Technical field
The present invention relates to technical field of composite materials, specifically relates to heat-conducting plate and preparation method thereof.
Background technology
The heat-conducting plate of prior art is usually to be made using metal material, and is mostly to realize that heat conduction is imitated by structure
Really, such as entitled heat-conducting plate and its plate body production method, application publication number are CN105865242A, Shen Qing Publication day is
2016.08.17, application number:2016102306434 application for a patent for invention, the heat-conducting plate includes integrally formed plate body, institute
Plate body is stated including front surface and the plate body inside is taken shape in and for some capillary cavities of heat exchange medium flowing, each institute
Capillary cavity is stated along the first direction extension parallel to the front surface and its inwall is provided with micro- toothing, the heat exchange is situated between
Matter can flow in the capillary cavity along the first direction.The uniformity that the heat-conducting plate of said structure has heat conduction is not good
Problem, heat transfer efficiency still needs further raising.
The content of the invention
The purpose of the present invention is exactly that a kind of heat conduction provided to solve the deficiency of prior art is uniform, heat conduction efficiency
Height, and heat-conducting plate of cost and preparation method thereof can be substantially reduced.
The present invention is to realize above-mentioned purpose using following technical solution:
A kind of heat-conducting plate, it is characterised in that the heat-conducting plate is made up of (by weight proportion) following component:
, using epoxy resin and/or isocyanate resin, macromolecule heat transfer powder is using enhancing carbon for the thermal conductive resin
It is also coupling agent that fiber powder oozes profit agent;The metal powder can be using high metal powders of heat conduction efficiency such as copper powder, aluminium powders.
A kind of heat-conducting plate preparation method, it is characterised in that it is by the thermal conductive resin of aforementioned proportion and metal powder, strengthens
Carbon fiber powder is stirred in a vacuum, and afterwards input is oozed profit agent, expanded microballon, vacuumized again, then puts into mould and is put into leveling machine pressure
Casting is molded.
The present invention is using the above-mentioned technical solution beneficial effect to be reached:
, as a result of the absorption releasing effect of expanded microballon, using the metal powder of 2000 mesh, its metal powder is complete for the present invention
Entirely can in the surface of expanded microballon, obtain the heat-conduction effect with more than 3 times of virgin metal sheet material, heat conduction efficiency is high;Simultaneously
Sheet material global density reduces by more than 3 times;The uniformity of heat transfer is significantly larger than conventional metals sheet material, greatly reduces cost.Can
In being widely used in the equipment such as baking oven, oven.
Specific embodiment
The technical program is explained in detail below in conjunction with specific embodiment.
Embodiment
A kind of heat-conducting plate preparation method, by weight, it be by upper epoxy resin and/or isocyanate resin 30% with
The metal powder 35% of 2000 mesh, the high carbon fiber powder 10% that strengthens are stirred in the air, put into afterwards coupling agent 5%, expanded microballon 20%,
Vacuumize again, then put into mould Jing leveling machine die casting and be molded.
, using epoxy resin and isocyanate resin, macromolecule heat transfer powder is using enhancing carbon fiber for the thermal conductive resin
It is also coupling agent that powder oozes profit agent;The metal powder can be using high metal powders of heat conduction efficiency such as copper powder, aluminium powders.
Metal powder described in the present embodiment can be 30-40%, expanded microballon 15-25%, macromolecule heat transfer powder 8-
12% oozes profit agent 3-6%, and coupling agent is the commercially available conventional coupling agent in current city, and here of the present invention will not be discussed further.
Above-described is only the preferred embodiment of the present invention, it is noted that for one of ordinary skill in the art
For, without departing from the concept of the premise of the invention, some deformations and improvement can also be made, these belong to the present invention
Protection domain.
Claims (4)
1. a kind of heat-conducting plate, it is characterised in that the heat-conducting plate is made up of following component, by weight proportion:
2. heat-conducting plate according to claim 1, it is characterised in that the thermal conductive resin is using epoxy resin and/or different
Cyanate ester resin, macromolecule heat transfer powder is using enhancing carbon fiber powder.
3. heat-conducting plate according to claim 1 and 2, it is characterised in that the metal powder can be passed using the heat such as copper powder, aluminium powder
Lead the metal powder of efficiency high.
4. heat-conducting plate preparation method described in any one of claim 1-3 is adopted, it is characterised in that it is to pass above-mentioned very cool heat
Lead resin to stir in the air with metal powder, enhancing carbon fiber powder, afterwards input is oozed profit agent, expanded microballon, vacuumized again, then puts into
Mould is put into leveling machine die casting and is molded.