CN106587749B - A kind of environment friendly light decorative material - Google Patents
A kind of environment friendly light decorative material Download PDFInfo
- Publication number
- CN106587749B CN106587749B CN201611068029.9A CN201611068029A CN106587749B CN 106587749 B CN106587749 B CN 106587749B CN 201611068029 A CN201611068029 A CN 201611068029A CN 106587749 B CN106587749 B CN 106587749B
- Authority
- CN
- China
- Prior art keywords
- wattle
- charcoal
- hide fiber
- jianization
- environment friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to decorative materials technologies, and in particular to a kind of environment friendly light decorative material is made of following raw material：Calcium-base bentonite, sepiolite powder, charcoal, monocline tobermorite powder, algin, Jianization wattle hide fiber, dimethyl fumarate, dialkyl ferrocene, polyethylene terephthalate, cumyl peroxide, triethylenediamine.The present invention has the following advantages compared with prior art：Ornament materials Environmental Safety in the present invention; it being capable of effective protection wall; appearance looks elegant; it being capable of insulation; the charcoal and Jianization added wattle hide fiber can adsorb radiation far infrared in the material, there is negative ion effect, preparation process is simple; bacteriostasis rate reaches 92% or more, meets the modern requirement environmentally protective to ornament materials.
Description
Technical field
The invention belongs to decorative materials technologies, and in particular to a kind of environment friendly light decorative material.
Background technology
As the improvement of people's living standards, while being increasingly particular about to quality of the life, people decorate living environment
The requirement of quality is higher and higher, and the environmental protection of ornament materials whether affects the health of user, at the same with rhythm of life plus
Soon, in ornament materials in use, whether will produce pernicious gas, harmful ion or harmful radiation compares care as consumer
Problem, therefore, environmental protection and public nuisance free is easy to be mounted to the research direction for Novel environment-friendlymaterial material.
Invention content
The purpose of the present invention is for existing problem, provide a kind of environment friendly light decorative material.
The present invention is achieved by the following technical solutions：A kind of environment friendly light decorative material, by following parts by weight
Raw material is made：Calcium-base bentonite 28-32, sepiolite powder 12-16, charcoal 8-15, monocline tobermorite powder 12-14, seaweed
Glue 6-10, Jianization wattle hide fiber 15-18, dimethyl fumarate 2-6, dialkyl ferrocene 1-2, poly terephthalic acid second two
Alcohol ester 3-7, cumyl peroxide 0.8-1.5, triethylenediamine 3-7；
Wherein, Jianization wattle hide fiber preparation method it is as follows：Jiang wattle hide fiber, be put into temperature be 26-30 DEG C
Buck in impregnate 3.5-4 hours, buck is the sodium hydroxide solution that mass percent is 4.5%, is rinsed with clear water after taking-up,
It is 12-16% to be dried to moisture with infrared-ray dryer after draining away the water, and 200 mesh of pulverizing sieve to obtain the final product.
As further improvement of these options, the charcoal is pig manure charcoal, cracks and obtains at 700 DEG C.
As further improvement of these options, preparation method is：After raw material high-speed stirred, addition is equivalent to total
The water of its weight 30%, at room temperature shelving obtain after mixture the extrusion forming under the pressure of 65-70MPa, according to a conventional method
Processing, obtains finished product.
The present invention has the following advantages compared with prior art：Ornament materials Environmental Safety in the present invention, being capable of effective protection
Wall, appearance looks elegant, can insulation, the charcoal and Jianization added wattle hide fiber can adsorb spoke in the material
Far infrared is penetrated, there is negative ion effect, preparation process is simple, and bacteriostasis rate reaches 92% or more, meets modern to ornament materials green
The requirement of environmental protection.
Specific implementation mode
Embodiment 1
A kind of environment friendly light decorative material, is made of the raw material of following parts by weight：Calcium-base bentonite 28, sepiolite powder
16, charcoal 8-15, monocline tobermorite powder 11, algin 10, Jianization wattle hide fiber 18, dimethyl fumarate 2, two
Alkyl ferrocene 1, polyethylene terephthalate 7, cumyl peroxide 1.5, triethylenediamine 4；
Wherein, Jianization wattle hide fiber preparation method it is as follows：Jiang wattle hide fiber, it is 30 DEG C of alkali to be put into temperature
It is impregnated 4 hours in water, buck is the sodium hydroxide solution that mass percent is 4.5%, is rinsed with clear water after taking-up, is drained away the water
It is 16% to be dried to moisture with infrared-ray dryer afterwards, and 200 mesh of pulverizing sieve to obtain the final product.
Wherein, the charcoal is pig manure charcoal, cracks and obtains at 700 DEG C；Preparation method is：By raw material high-speed stirred
Afterwards, the water for being equivalent to its total weight 30% is added, shelving, is squeezed into after obtaining mixture under the pressure of 68MPa at room temperature
Type is handled according to a conventional method, obtains finished product.
The compression strength of ornament materials reaches 9.0MPa in the present embodiment, and bending strength reaches 4.9MPa, be unlikely to deform or
It cracks, thermal coefficient is low, is 0.42W/mK, far infrared transmissivity 86.8%, anion burst size is 3.2 × 103
A/cm3.
Embodiment 2
A kind of environment friendly light decorative material, is made of the raw material of following parts by weight：Calcium-base bentonite 32, sepiolite powder
12, charcoal 15, monocline tobermorite powder 12, algin 10, Jianization wattle hide fiber 15, dimethyl fumarate 2, two hydrocarbon
Base ferrocene 1, polyethylene terephthalate 3, cumyl peroxide 0.8, triethylenediamine 6；
Wherein, Jianization wattle hide fiber preparation method it is as follows：Jiang wattle hide fiber, it is 26 DEG C of alkali to be put into temperature
It is impregnated 3.5 hours in water, buck is the sodium hydroxide solution that mass percent is 4.5%, is rinsed with clear water after taking-up, is drained the water
It is 15% to be dried to moisture with infrared-ray dryer after point, and 200 mesh of pulverizing sieve to obtain the final product.
Preparation method is in the same manner as in Example 1.
The compression strength of ornament materials reaches 8.5MPa in the present embodiment, and bending strength reaches 4.6MPa, be unlikely to deform or
It cracks, thermal coefficient is low, is 0.47W/mK, far infrared transmissivity 88.2%, anion burst size is 3.4 × 103
A/cm3.
Embodiment 3
A kind of environment friendly light decorative material, is made of the raw material of following parts by weight：Calcium-base bentonite 30, sepiolite powder
14, charcoal 12, monocline tobermorite powder 13, algin 8, Jianization wattle hide fiber 16, dimethyl fumarate 4, two hydrocarbon
Base ferrocene 2, polyethylene terephthalate 5, cumyl peroxide 1.2, triethylenediamine 5；
Wherein, Jianization wattle hide fiber preparation method it is as follows：Jiang wattle hide fiber, it is 30 DEG C of alkali to be put into temperature
It is impregnated 3.5 hours in water, buck is the sodium hydroxide solution that mass percent is 4.5%, is rinsed with clear water after taking-up, is drained the water
It is 16% to be dried to moisture with infrared-ray dryer after point, and 200 mesh of pulverizing sieve to obtain the final product.
Preparation method is in the same manner as in Example 1.
The compression strength of ornament materials reaches 8.2MPa in the present embodiment, and bending strength reaches 4.5MPa, be unlikely to deform or
It cracks, thermal coefficient is low, is 0.44W/mK, far infrared transmissivity 87.2%, anion burst size is 3.6 × 103
A/cm3.
Claims (1)
1. a kind of environment friendly light decorative material, which is characterized in that be made of the raw material of following parts by weight：Calcium-base bentonite 28-
32, sepiolite powder 12-16, charcoal 8-15, monocline tobermorite powder 12-14, algin 6-10, Jianization wattle hide fiber
15-18, dimethyl fumarate 2-6, dialkyl ferrocene 1-2, polyethylene terephthalate 3-7, cumyl peroxide
0.8-1.5, triethylenediamine 3-7；
Wherein, Jianization wattle hide fiber preparation method it is as follows：Jiang wattle hide fiber, it is 26-30 DEG C of alkali to be put into temperature
It is impregnated 3.5-4 hours in water, buck is the sodium hydroxide solution that mass percent is 4.5%, is rinsed with clear water after taking-up, is drained
It is 12-16% to be dried to moisture with infrared-ray dryer after moisture, and 200 mesh of pulverizing sieve to obtain the final product；
Wherein, the charcoal is pig manure charcoal, cracks and obtains at 700 DEG C；
Environment friendly light decorative material, preparation method are：After raw material high-speed stirred, the water for being equivalent to its total weight 30% is added,
Shelving at room temperature obtains after mixture the extrusion forming under the pressure of 65-70MPa, handles according to a conventional method, obtain finished product.