CN107265929A - A kind of corrosion-resistant environment friendly decorative material and preparation method thereof - Google Patents
A kind of corrosion-resistant environment friendly decorative material and preparation method thereof Download PDFInfo
- Publication number
- CN107265929A CN107265929A CN201710479317.1A CN201710479317A CN107265929A CN 107265929 A CN107265929 A CN 107265929A CN 201710479317 A CN201710479317 A CN 201710479317A CN 107265929 A CN107265929 A CN 107265929A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- environment friendly
- resistant environment
- decorative material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of corrosion-resistant environment friendly decorative material, it is made up of the raw material of following parts by weight：28 ~ 38 parts of calcium-base bentonite, 10 ~ 30 parts of polyvinyl chloride, 5 ~ 10 parts of modification infusorial earth, 2 ~ 8 parts of dimethyl fumarate, 12 ~ 16 parts of dimethyl maleate, 5 ~ 15 parts of charcoal, 3 ~ 9 parts of ethyl acetate, 12 ~ 16 parts of monocline tobermorite powder, 6 ~ 10 parts of algin, Jianization 15 ~ 25 parts of wattle hide fiber, 1 ~ 5 part of dialkyl ferrocene, 0.8 ~ 1.5 part of cumyl peroxide, 3 ~ 8 parts of polyethylene terephthalate, 3 ~ 7 parts of bishydroxyethyl terephthalate, 2 ~ 4 parts of fire retardant, 5 ~ 8 parts of thickener.A kind of corrosion-resistant environment friendly decorative material provided by the present invention, Environmental Safety can effectively protect wall; appearance looks elegant, can insulation, the charcoal added and monocline tobermorite powder can adsorb radiation far infrared in the material; with negative ion effect, preparation technology is simple.
Description
Technical field
The invention belongs to decoration material field, and in particular to a kind of corrosion-resistant environment friendly decorative material and preparation method thereof.
Background technology
As the improvement of people's living standards, while being increasingly particular about to quality of the life, people decorate to living environment
The requirement more and more higher of quality, the whether environmentally friendly health for affecting user of ornament materials, while adding with rhythm of life
It hurry up, in ornament materials in use, pernicious gas, harmful ion or harmful radiation whether can be produced is compared care as consumer
Problem, therefore, environmental protection and public nuisance free, the easy research direction being mounted to for Novel environment-friendlymaterial material.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of corrosion-resistant environment friendly decorative material and its system
Preparation Method.
To achieve the above object, the technical scheme is that：A kind of corrosion-resistant environment friendly decorative material, by following parts by weight
Raw material be made：28 ~ 38 parts of calcium-base bentonite, 10 ~ 30 parts of polyvinyl chloride, 5 ~ 10 parts of modification infusorial earth, dimethyl fumarate 2 ~ 8
Part, 12 ~ 16 parts of dimethyl maleate, 5 ~ 15 parts of charcoal, 3 ~ 9 parts of ethyl acetate, 12 ~ 16 parts of monocline tobermorite powder, sea
6 ~ 10 parts of phycocolloid, Jianization 15 ~ 25 parts of wattle hide fiber, 1 ~ 5 part of dialkyl ferrocene, 0.8 ~ 1.5 part of cumyl peroxide,
3 ~ 8 parts of polyethylene terephthalate, 3 ~ 7 parts of bishydroxyethyl terephthalate, 2 ~ 4 parts of fire retardant, 5 ~ 8 parts of thickener.
Further, it is made up of the raw material of following parts by weight：28 parts of calcium-base bentonite, 10 parts of polyvinyl chloride, modified diatom
5 parts of soil, 2 parts of dimethyl fumarate, 12 parts of dimethyl maleate, 5 parts of charcoal, 3 parts of ethyl acetate, monocline tobermorite powder
12 parts, 6 parts of algin, Jianization 15 parts of wattle hide fiber, 1 part of dialkyl ferrocene, 0.8 part of cumyl peroxide, poly- pair
3 parts of PET, 3 parts of bishydroxyethyl terephthalate, 2 parts of fire retardant, 5 parts of thickener.
Further, the thickener be sodium bentonite, organobentonite, diatomite, attapulgite soil, molecular sieve,
Silica hydrogel, methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, hydroxyethyl cellulose, starch, gelatin, marine alga
One or more in sour sodium, casein, guar gum and chitosan.
Further, the charcoal is cow dung charcoal, cracks and obtains under 500 ~ 700 DEG C of temperature conditionss.
Further, the fire retardant is selected from alundum (Al2O3), magnesia or antimony oxide.
A kind of preparation method of corrosion-resistant environment friendly decorative material, is mainly included the following steps that：
Step 1：Prepare material requested according to formula as below parts by weight：28 ~ 38 parts of calcium-base bentonite, 10 ~ 30 parts of polyvinyl chloride, change
5 ~ 10 parts of diatomite of property, 2 ~ 8 parts of dimethyl fumarate, 12 ~ 16 parts of dimethyl maleate, 5 ~ 15 parts of charcoal, ethyl acetate 3 ~ 9
Part, 12 ~ 16 parts of monocline tobermorite powder, 6 ~ 10 parts of algin, Jianization 15 ~ 25 parts of wattle hide fiber, dialkyl ferrocene 1
~ 5 parts, 0.8 ~ 1.5 part of cumyl peroxide, 3 ~ 8 parts of polyethylene terephthalate, bishydroxyethyl terephthalate 3 ~ 7
Part, 2 ~ 4 parts of fire retardant, 5 ~ 8 parts of thickener；
Step 2：By calcium-base bentonite, polyvinyl chloride, modification infusorial earth, dimethyl fumarate, dimethyl maleate, charcoal,
Ethyl acetate is added after batch mixer, to be operated under 300 ~ 450 revs/min of rotating speed 15 ~ 20 minutes, then adds monocline Tuo Beimo
Come stone flour, algin, Jianization wattle hide fiber, dialkyl ferrocene, cumyl peroxide, polyethylene terephthalate
Ester, bishydroxyethyl terephthalate, by rotational speed regulation to 2400 ~ 2600 revs/min；
Step 3：By temperature adjustment to 65 ~ 70 DEG C, fire retardant and thickener are added, it is cold in cold mixer after operating 1.5 ~ 2 hours
But to 30 DEG C, discharging；
Step 4：Sheet material is prepared in extruder by expecting on above-mentioned resulting material, it is fixed that sheet material is cooled down by Vacuum shaping mould
Type, then cuts into blank and produces corrosion-resistant environment friendly decorative material as needed.
Further, the temperature control of the Vacuum shaping mould cooling water is at 20 ~ 25 DEG C.
Further, the premixing machine is V-type premixing machine.
The beneficial effects of the present invention are：A kind of corrosion-resistant environment friendly decorative material provided by the present invention, Environmental Safety, energy
Enough effectively protection walls, appearance looks elegant, can insulation, the charcoal added and monocline tobermorite powder are in the material
Radiation far infrared can be adsorbed, with negative ion effect, preparation technology is simple, and bacteriostasis rate reaches more than 99%, meet modern to dress
The requirement of exterior material environmental protection；Effectively prevent ornament materials during long-time use because the environmental factors such as light, water are led
The phenomenons such as jaundice, cracking are caused, weatherability is strong, extends the service life of ornament materials.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, do not limit
The fixed present invention.
Embodiment 1
A kind of corrosion-resistant environment friendly decorative material, is made up of the raw material of following parts by weight：28 parts of calcium-base bentonite, polyvinyl chloride 10
Part, 5 parts of modification infusorial earth, 2 parts of dimethyl fumarate, 12 parts of dimethyl maleate, 5 parts of charcoal, 3 parts of ethyl acetate, monocline
12 parts of tobermorite powder, 6 parts of algin, Jianization 15 parts of wattle hide fiber, 1 part of dialkyl ferrocene, peroxidating diisopropyl
0.8 part of benzene, 3 parts of polyethylene terephthalate, 3 parts of bishydroxyethyl terephthalate, 2 parts of fire retardant, 5 parts of thickener.
Wherein, the thickener be sodium bentonite, organobentonite, diatomite, attapulgite soil, molecular sieve, silicon coagulate
Glue, methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, hydroxyethyl cellulose, starch, gelatin, alginic acid
One or more in sodium, casein, guar gum and chitosan.
Wherein, the charcoal is cow dung charcoal, cracks and obtains under 500 DEG C of temperature conditionss.
Wherein, the fire retardant is selected from alundum (Al2O3), magnesia or antimony oxide.
A kind of preparation method of corrosion-resistant environment friendly decorative material, is mainly included the following steps that：
Step 1：Prepare material requested according to formula as below parts by weight：28 parts of calcium-base bentonite, 10 parts of polyvinyl chloride, modified diatom
5 parts of soil, 2 parts of dimethyl fumarate, 12 parts of dimethyl maleate, 5 parts of charcoal, 3 parts of ethyl acetate, monocline tobermorite powder
12 parts, 6 parts of algin, Jianization 15 parts of wattle hide fiber, 1 part of dialkyl ferrocene, 0.8 part of cumyl peroxide, poly- pair
3 parts of PET, 3 parts of bishydroxyethyl terephthalate, 2 parts of fire retardant, 5 parts of thickener；
Step 2：By calcium-base bentonite, polyvinyl chloride, modification infusorial earth, dimethyl fumarate, dimethyl maleate, charcoal,
Ethyl acetate is added after batch mixer, to be operated under 300 revs/min of rotating speed 15 minutes, then add monocline tobermorite powder,
Algin, Jianization wattle hide fiber, dialkyl ferrocene, cumyl peroxide, polyethylene terephthalate, to benzene
The double hydroxyl ethyl esters of dioctyl phthalate, by rotational speed regulation to 2400 revs/min；
Step 3：By temperature adjustment to 65 DEG C, fire retardant and thickener are added, operating is cooled to 30 after 1.5 hours in cold mixer
DEG C, discharging；
Step 4：Sheet material is prepared in extruder by expecting on above-mentioned resulting material, it is fixed that sheet material is cooled down by Vacuum shaping mould
Type, then cuts into blank and produces corrosion-resistant environment friendly decorative material as needed.
Wherein, the temperature control of the Vacuum shaping mould cooling water is at 20 DEG C.
Wherein, the premixing machine is V-type premixing machine.
Embodiment 2
A kind of corrosion-resistant environment friendly decorative material, is made up of the raw material of following parts by weight：35 parts of calcium-base bentonite, polyvinyl chloride 20
Part, 8 parts of modification infusorial earth, 5 parts of dimethyl fumarate, 14 parts of dimethyl maleate, 10 parts of charcoal, 6 parts of ethyl acetate, monocline
14 parts of tobermorite powder, 8 parts of algin, Jianization 20 parts of wattle hide fiber, 3 parts of dialkyl ferrocene, peroxidating diisopropyl
1.2 parts of benzene, 5 parts of polyethylene terephthalate, 6 parts of bishydroxyethyl terephthalate, 3 parts of fire retardant, 7 parts of thickener.
Wherein, the thickener be sodium bentonite, organobentonite, diatomite, attapulgite soil, molecular sieve, silicon coagulate
Glue, methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, hydroxyethyl cellulose, starch, gelatin, alginic acid
One or more in sodium, casein, guar gum and chitosan.
Wherein, the charcoal is cow dung charcoal, cracks and obtains under 600 DEG C of temperature conditionss.
Wherein, the fire retardant is selected from alundum (Al2O3), magnesia or antimony oxide.
A kind of preparation method of corrosion-resistant environment friendly decorative material, is mainly included the following steps that：
Step 1：Prepare material requested according to formula as below parts by weight：35 parts of calcium-base bentonite, 20 parts of polyvinyl chloride, modified diatom
8 parts of soil, 5 parts of dimethyl fumarate, 14 parts of dimethyl maleate, 10 parts of charcoal, 6 parts of ethyl acetate, monocline tobermorite
14 parts of powder, 8 parts of algin, Jianization 20 parts of wattle hide fiber, 3 parts of dialkyl ferrocene, 1.2 parts of cumyl peroxide, poly-
5 parts of ethylene glycol terephthalate, 6 parts of bishydroxyethyl terephthalate, 3 parts of fire retardant, 7 parts of thickener；
Step 2：By calcium-base bentonite, polyvinyl chloride, modification infusorial earth, dimethyl fumarate, dimethyl maleate, charcoal,
Ethyl acetate is added after batch mixer, to be operated under 400 revs/min of rotating speed 18 minutes, then add monocline tobermorite powder,
Algin, Jianization wattle hide fiber, dialkyl ferrocene, cumyl peroxide, polyethylene terephthalate, to benzene
The double hydroxyl ethyl esters of dioctyl phthalate, by rotational speed regulation to 2500 revs/min；
Step 3：By temperature adjustment to 68 DEG C, fire retardant and thickener are added, operating is cooled to 30 after 1.5 hours in cold mixer
DEG C, discharging；
Step 4：Sheet material is prepared in extruder by expecting on above-mentioned resulting material, it is fixed that sheet material is cooled down by Vacuum shaping mould
Type, then cuts into blank and produces corrosion-resistant environment friendly decorative material as needed.
Wherein, the temperature control of the Vacuum shaping mould cooling water is at 22 DEG C.
Wherein, the premixing machine is V-type premixing machine.
Embodiment 3
A kind of corrosion-resistant environment friendly decorative material, is made up of the raw material of following parts by weight：38 parts of calcium-base bentonite, polyvinyl chloride 30
Part, 10 parts of modification infusorial earth, 8 parts of dimethyl fumarate, 16 parts of dimethyl maleate, 15 parts of charcoal, 9 parts of ethyl acetate, list
Oblique 16 parts of tobermorite powder, 10 parts of algin, Jianization 25 parts of wattle hide fiber, 5 parts of dialkyl ferrocene, peroxidating two it is different
1.5 parts of propyl benzene, 8 parts of polyethylene terephthalate, 7 parts of bishydroxyethyl terephthalate, 4 parts of fire retardant, 8 parts of thickener.
Wherein, the thickener be sodium bentonite, organobentonite, diatomite, attapulgite soil, molecular sieve, silicon coagulate
Glue, methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, hydroxyethyl cellulose, starch, gelatin, alginic acid
One or more in sodium, casein, guar gum and chitosan.
Wherein, the charcoal is cow dung charcoal, cracks and obtains under 700 DEG C of temperature conditionss.
Wherein, the fire retardant is selected from alundum (Al2O3), magnesia or antimony oxide.
A kind of preparation method of corrosion-resistant environment friendly decorative material, is mainly included the following steps that：
Step 1：Prepare material requested according to formula as below parts by weight：38 parts of calcium-base bentonite, 30 parts of polyvinyl chloride, modified diatom
10 parts of soil, 8 parts of dimethyl fumarate, 16 parts of dimethyl maleate, 15 parts of charcoal, 9 parts of ethyl acetate, monocline tobermorite
16 parts of powder, 10 parts of algin, Jianization 25 parts of wattle hide fiber, 5 parts of dialkyl ferrocene, 1.5 parts of cumyl peroxide, poly-
8 parts of ethylene glycol terephthalate, 7 parts of bishydroxyethyl terephthalate, 4 parts of fire retardant, 8 parts of thickener；
Step 2：By calcium-base bentonite, polyvinyl chloride, modification infusorial earth, dimethyl fumarate, dimethyl maleate, charcoal,
Ethyl acetate is added after batch mixer, to be operated under 450 revs/min of rotating speed 20 minutes, then add monocline tobermorite powder,
Algin, Jianization wattle hide fiber, dialkyl ferrocene, cumyl peroxide, polyethylene terephthalate, to benzene
The double hydroxyl ethyl esters of dioctyl phthalate, by rotational speed regulation to 2600 revs/min；
Step 3：By temperature adjustment to 70 DEG C, fire retardant and thickener are added, operating is cooled to 30 after 2 hours in cold mixer
DEG C, discharging；
Step 4：Sheet material is prepared in extruder by expecting on above-mentioned resulting material, it is fixed that sheet material is cooled down by Vacuum shaping mould
Type, then cuts into blank and produces corrosion-resistant environment friendly decorative material as needed.
Wherein, the temperature control of the Vacuum shaping mould cooling water is at 25 DEG C.
Wherein, the premixing machine is V-type premixing machine.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of corrosion-resistant environment friendly decorative material, it is characterised in that be made up of the raw material of following parts by weight：Calcium-base bentonite 28 ~
38 parts, 10 ~ 30 parts of polyvinyl chloride, 5 ~ 10 parts of modification infusorial earth, 2 ~ 8 parts of dimethyl fumarate, 12 ~ 16 parts of dimethyl maleate,
5 ~ 15 parts of charcoal, 3 ~ 9 parts of ethyl acetate, 12 ~ 16 parts of monocline tobermorite powder, 6 ~ 10 parts of algin, Jianization wattle skin
15 ~ 25 parts of fiber, 1 ~ 5 part of dialkyl ferrocene, 0.8 ~ 1.5 part of cumyl peroxide, polyethylene terephthalate 3 ~ 8
Part, 3 ~ 7 parts of bishydroxyethyl terephthalate, 2 ~ 4 parts of fire retardant, 5 ~ 8 parts of thickener.
2. a kind of corrosion-resistant environment friendly decorative material according to claim 1, it is characterised in that by the raw material of following parts by weight
It is made：28 parts of calcium-base bentonite, 10 parts of polyvinyl chloride, 5 parts of modification infusorial earth, 2 parts of dimethyl fumarate, dimethyl maleate 12
Part, 5 parts of charcoal, 3 parts of ethyl acetate, 12 parts of monocline tobermorite powder, 6 parts of algin, Jianization 15 parts of wattle hide fiber,
The double hydroxyl second of 1 part of dialkyl ferrocene, 0.8 part of cumyl peroxide, 3 parts of polyethylene terephthalate, terephthalic acid (TPA)
3 parts of ester, 2 parts of fire retardant, 5 parts of thickener.
3. a kind of corrosion-resistant environment friendly decorative material according to claim 1, it is characterised in that the thickener is that sodium base is swollen
Moisten soil, organobentonite, diatomite, attapulgite soil, molecular sieve, Silica hydrogel, methylcellulose, hydroxypropyl methyl cellulose,
One kind in sodium carboxymethylcellulose, hydroxyethyl cellulose, starch, gelatin, sodium alginate, casein, guar gum and chitosan
Or it is a variety of.
4. a kind of corrosion-resistant environment friendly decorative material according to claim 1, it is characterised in that the charcoal is cow dung
Charcoal, cracks and obtains under 500 ~ 700 DEG C of temperature conditionss.
5. a kind of corrosion-resistant environment friendly decorative material according to claim 1, it is characterised in that the fire retardant is selected from three oxygen
Change two aluminium, magnesia or antimony oxide.
6. a kind of preparation method of corrosion-resistant environment friendly decorative material, it is characterised in that mainly include the following steps that：
Step 1：Prepare material requested according to formula as below parts by weight：28 ~ 38 parts of calcium-base bentonite, 10 ~ 30 parts of polyvinyl chloride, change
5 ~ 10 parts of diatomite of property, 2 ~ 8 parts of dimethyl fumarate, 12 ~ 16 parts of dimethyl maleate, 5 ~ 15 parts of charcoal, ethyl acetate 3 ~ 9
Part, 12 ~ 16 parts of monocline tobermorite powder, 6 ~ 10 parts of algin, Jianization 15 ~ 25 parts of wattle hide fiber, dialkyl ferrocene 1
~ 5 parts, 0.8 ~ 1.5 part of cumyl peroxide, 3 ~ 8 parts of polyethylene terephthalate, bishydroxyethyl terephthalate 3 ~ 7
Part, 2 ~ 4 parts of fire retardant, 5 ~ 8 parts of thickener；
Step 2：By calcium-base bentonite, polyvinyl chloride, modification infusorial earth, dimethyl fumarate, dimethyl maleate, charcoal,
Ethyl acetate is added after batch mixer, to be operated under 300 ~ 450 revs/min of rotating speed 15 ~ 20 minutes, then adds monocline Tuo Beimo
Come stone flour, algin, Jianization wattle hide fiber, dialkyl ferrocene, cumyl peroxide, polyethylene terephthalate
Ester, bishydroxyethyl terephthalate, by rotational speed regulation to 2400 ~ 2600 revs/min；
Step 3：By temperature adjustment to 65 ~ 70 DEG C, fire retardant and thickener are added, it is cold in cold mixer after operating 1.5 ~ 2 hours
But to 30 DEG C, discharging；
Step 4：Sheet material is prepared in extruder by expecting on above-mentioned resulting material, it is fixed that sheet material is cooled down by Vacuum shaping mould
Type, then cuts into blank and produces corrosion-resistant environment friendly decorative material as needed.
7. a kind of corrosion-resistant environment friendly decorative material according to claim 6, it is characterised in that the Vacuum shaping mould cooling
The temperature control of water is at 20 ~ 25 DEG C.
8. a kind of corrosion-resistant environment friendly decorative material according to claim 6, it is characterised in that the premixing machine is that V-type is pre-
Mixed machine.