CN106566388A - Long-acting antibacterial anti-scraping protection film and preparation method thereof - Google Patents
Long-acting antibacterial anti-scraping protection film and preparation method thereof Download PDFInfo
- Publication number
- CN106566388A CN106566388A CN201610974120.0A CN201610974120A CN106566388A CN 106566388 A CN106566388 A CN 106566388A CN 201610974120 A CN201610974120 A CN 201610974120A CN 106566388 A CN106566388 A CN 106566388A
- Authority
- CN
- China
- Prior art keywords
- protecting film
- long acting
- scratch resistant
- base material
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a long-acting antibacterial anti-scraping protection film which comprises an antibacterial protection layer smeared to the surface of a base material. The antibacterial protection layer is prepared from 5 g to 7 g of UV resin, 8 g to 9 g of butanone, 5 g to 6 g of methylbenzene, 0.5 g to 1.5 g of photoinitiator and 0.03 g to 0.3 g of nano-silver ion antibacterial agent. The long-acting antibacterial anti-scraping protection film adheres to the surface of a pasted object, and can achieve a long-acting antibacterial effect. A preparation method of the long-acting antibacterial anti-scraping protection film comprises the following steps that 1, the UV resin is weighed, butanone and methylbenzene are weighed, and the materials are stirred to be uniform; 2, the photoinitiator is added, and the materials are stirred to be uniform; 3, the nano-silver ion antibacterial agent is added, and the materials are stirred to be uniform; 4, glue liquid formed in the step 3 is evenly smeared to the surface of the base material; 5, heating treatment is carried out; and 6, UV light treatment is carried out, and the long-acting antibacterial anti-scraping protection film is prepared after cooling. The preparation method of the long-acting antibacterial anti-scraping protection film is simple and easy to operate.
Description
Technical field
The present invention relates to protecting film field, more particularly to a kind of scratch resistant protecting film of long acting antibiotic and preparation method thereof.
Background technology
With becoming increasingly popular for intelligent terminal, the usage frequency in daily life of the electronic equipment with display screen
More and more higher.In order to avoid colliding with or scraping the damage to electronic equipment display screen, usual people paste one layer in display screen surface
Protecting film, in order to reach the effect for taking into account anti scuffing, can add one layer of stiffening layer with the surface in protecting film, and such scheme is very
Good solves the shortcoming that display screen is easy to scratch.But, Recent study finds, the high usage frequency meeting of electronic product can not
The Adherent bacteria for avoiding, especially has some antibacterials to be with Infective, such as staphylococcus aureuses；Electronic equipment is not
Can clean, prolonged accumulation only can make antibacterial cumulative；In addition, meeting spontaneous heating when electronic equipment is used, carries with
Electronic equipment such as mobile phone or wrist-watch temperature are more constant, and for bacterial reproduction suitable temperature and environment are provided.
Although existing antibacterial and protective film can reach the effect of antibacterial, more than its antibacterial effect after the regular hour
Have a greatly reduced quality, it is impossible to realize long acting antibiotic.
The content of the invention
It is an object of the invention to propose scratch resistant protecting film of a kind of long acting antibiotic and preparation method thereof, the long acting antibiotic is scratch resistant
Protecting film is attached at the surface of affixed object, can reach the effect of long acting antibiotic.
It is that, up to this purpose, the present invention is employed the following technical solutions：
A kind of scratch resistant protecting film of long acting antibiotic, including：Base material and be coated on the base material surface antibacterial and protective layer；Institute
Stating the component of antibacterial and protective layer includes：The UV resins of 5g～7g, the butanone of 8g～9g, the toluene of 5g～6g, 0.5g～1.5g
The nano silver ion antibiotic agent of light trigger and 0.03g～0.3g.
Preferably, the content of the UV resins is 5g, 5.5g, 6g, 6.5g or 7g.
Preferably, the content of the butanone be 8g, 8.1g, 8.2g, 8.3g, 8.4g, 8.5g, 8.6g, 8.7g, 8.8g,
8.9g or 9g.
Preferably, the content of the toluene be 5g, 5.1g, 5.2g, 5.3g, 5.4g, 5.5g, 5.6g, 5.7g, 5.8g,
5.9g or 6g.
Preferably, the content of the light trigger be 0.5g, 0.6g, 0.7g, 0.8g, 0.9g, 1.0g, 1.1g, 1.2g,
1.3g, 1.4g or 1.5g.
Preferably, the content of the nano silver ion antibiotic agent be 0.03g, 0.05g, 0.08g, 0.1g, 0.13g,
0.15g, 0.18g, 0.2g, 0.23g, 0.25g, 0.28g or 0.3g.
Wherein, the UV resins be UV epoxy acrylates, UV epoxy acrylates, UV urethane acrylates, UV gather
Ester acrylate, one or more of UV epoxy resin of mixture.
Wherein, argent simple substance is contained in the nano silver ion antibiotic agent, the particle diameter of the argent simple substance is 23nm
～26nm.
Wherein, the thickness of the antibacterial and protective layer is 3 μm～12 μm.
A kind of preparation method of the above-mentioned scratch resistant protecting film of long acting antibiotic, comprises the following steps：
1) UV resins are weighed, butanone and toluene is added, is stirred under room temperature；
2) to the step 1) add and stirred under light trigger, room temperature in the glue that formed；
3) to the step 2) formed glue in add nano silver ion antibiotic agent, stir under room temperature；
4) by the step 3) glue that formed is evenly applied to the surface of the base material；
5) by the step 4 described in) process after base material carry out heat treated；
6) by the step 5 described in) process after base material carry out UV photo-irradiation treatment, long acting antibiotic scratch resistant protection is obtained after cooling
Film.
Wherein, the step 5) in heating-up temperature be 70 DEG C～160 DEG C, heat time heating time be 20s～120s.
Wherein, the step 6) in UV illumination temperatures be 120 DEG C～160 DEG C, UV light application times be 15s～60s.
Beneficial effects of the present invention are：A kind of scratch resistant protecting film of long acting antibiotic proposed by the present invention, including：Base material and coating
In the antibacterial and protective layer on the surface of the base material；The component of the antibacterial and protective layer includes：The UV resins of 5g～7g, 8g～9g
The nano silver ion antibiotic agent of butanone, the toluene of 5g～6g, the light trigger of 0.5g～1.5g and 0.03g～0.3g.This is long-acting
The scratch resistant protecting film of antibacterial is attached at the surface of affixed object, can reach the effect of long acting antibiotic.One kind proposed by the present invention is long-acting anti-
The preparation method of the scratch resistant protecting film of bacterium, comprises the following steps：1) UV resins are weighed, butanone and toluene is added, stirs equal under room temperature
It is even；2) to the step 1) add and stirred under light trigger, room temperature in the glue that formed；3) to the step 2) formed
Nano silver ion antibiotic agent is added in glue, is stirred under room temperature；4) by the step 3) formed glue be evenly applied to
The surface of the base material；5) by the step 4 described in) process after base material carry out heat treated；6) by step 5 described in Jing) process
Base material afterwards carries out UV photo-irradiation treatment, and the scratch resistant protecting film of long acting antibiotic is obtained after cooling.The system of the scratch resistant protecting film of the long acting antibiotic
Preparation Method is simple, it is easy to operate.
Specific embodiment
Technical scheme is further illustrated below by specific embodiment.
Embodiment 1
The scratch resistant protecting film of long acting antibiotic includes：Base material and be coated on base material surface antibacterial and protective layer；Wherein, antibacterial is prevented
The component of sheath includes：The UV epoxy acrylates of 5g, the butanone of 8g, the toluene of 5g, the light trigger of 0.5g and 0.03g's
Nano silver ion antibiotic agent.Wherein, the particle diameter containing argent simple substance is 23nm in nano silver ion antibiotic agent.Antibacterial and protective
The thickness of layer is 3 μm.
The preparation method of the scratch resistant protecting film of above-mentioned long acting antibiotic, comprises the following steps：
1) UV epoxy acrylates are weighed, butanone and toluene is added, is stirred under room temperature；
2) to step 1) add and stirred under light trigger, room temperature in the glue that formed；
3) to step 2) formed glue in add nano silver ion antibiotic agent, stir under room temperature；
4) by step 3) glue that formed is evenly applied to the surface of base material；
5) by Jing step 4) process after base material carry out heat treated；80 DEG C of heating-up temperature, heat time heating time is 120s；
6) by Jing step 5) process after base material carry out UV photo-irradiation treatment, UV illumination temperatures are 120 DEG C, and UV light application times are
60s, is obtained the scratch resistant protecting film of long acting antibiotic after cooling.
Embodiment 2
The scratch resistant protecting film of long acting antibiotic includes：Base material and be coated on base material surface antibacterial and protective layer；Wherein, antibacterial is prevented
The component of sheath includes：The UV epoxy acrylates of 6g, the butanone of 8.4g, the toluene of 5.6g, the light trigger of 1g and 0.1g's
Nano silver ion antibiotic agent.Wherein, the particle diameter containing argent simple substance is 25nm in nano silver ion antibiotic agent.Antibacterial and protective layer
Thickness be 8 μm.
The preparation method of the scratch resistant protecting film of above-mentioned long acting antibiotic, comprises the following steps：
1) UV epoxy acrylates are weighed, butanone and toluene is added, is stirred under room temperature；
2) to step 1) add and stirred under light trigger, room temperature in the glue that formed；
3) to step 2) formed glue in add nano silver ion antibiotic agent, stir under room temperature；
4) by step 3) glue that formed is evenly applied to the surface of base material；
5) by Jing step 4) process after base material carry out heat treated；100 DEG C of heating-up temperature, heat time heating time is 80s；
6) by Jing step 5) process after base material carry out UV photo-irradiation treatment, UV illumination temperatures are 100 DEG C, UV light application times
For 40s, the scratch resistant protecting film of long acting antibiotic is obtained after cooling.
Embodiment 3
The scratch resistant protecting film of long acting antibiotic includes：Base material and be coated on base material surface antibacterial and protective layer；Wherein, antibacterial is prevented
The component of sheath includes：The UV polyester acrylates of 7g, the butanone of 9g, the toluene of 6g, the light trigger of 1.5g and 0.3g's receives
Nano silver ion antibacterial.Wherein, the particle diameter containing argent simple substance is 26nm in nano silver ion antibiotic agent.Antibacterial and protective layer
Thickness is 12 μm.
The preparation method of the scratch resistant protecting film of above-mentioned long acting antibiotic, comprises the following steps：
1) UV polyester acrylates are weighed, butanone and toluene is added, is stirred under room temperature；
2) to step 1) add and stirred under light trigger, room temperature in the glue that formed；
3) to step 2) formed glue in add nano silver ion antibiotic agent, stir under room temperature；
4) by step 3) glue that formed is evenly applied to the surface of base material；
5) by Jing step 4) process after base material carry out heat treated；150 DEG C of heating-up temperature, heat time heating time is 30s；
6) by Jing step 5) process after base material carry out UV photo-irradiation treatment, UV illumination temperatures are 150 DEG C, and UV light application times are
20s, is obtained the scratch resistant protecting film of long acting antibiotic after cooling.
The testing result of the scratch resistant protecting film of long acting antibiotic in above-described embodiment 1 to 3 see the table below 1.
The testing result of the scratch resistant protecting film of the long acting antibiotic of table 1
A kind of scratch resistant protecting film of long acting antibiotic proposed by the present invention can be seen that by upper table 1, antibacterial effect is notable.
The know-why of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's
Principle, and can not by any way be construed to limiting the scope of the invention.Based on explanation herein, the technology of this area
Personnel associate other specific embodiments of the present invention by need not paying performing creative labour, these modes fall within
Within protection scope of the present invention.
Claims (7)
1. the scratch resistant protecting film of a kind of long acting antibiotic, it is characterised in that include：Base material and be coated on the base material surface antibacterial
Overcoat；The component of the antibacterial and protective layer includes：The UV resins of 5g～7g, the butanone of 8g～9g, the toluene of 5g～6g, 0.5g
The light trigger of～1.5g and the nano silver ion antibiotic agent of 0.03g～0.3g.
2. the scratch resistant protecting film of a kind of long acting antibiotic according to claim 1, it is characterised in that the UV resins are UV epoxies
Acrylate, UV epoxy acrylates, UV urethane acrylates, UV polyester acrylates, one kind of UV epoxy resin or many
The mixture planted.
3. a kind of scratch resistant protecting film of long acting antibiotic according to claim 1, it is characterised in that the nano silver ion antibiotic
Contain argent simple substance in agent, the particle diameter of the argent simple substance is 23nm～26nm.
4. a kind of scratch resistant protecting film of long acting antibiotic according to claim 1, it is characterised in that the thickness of the antibacterial and protective layer
Spend for 3 μm～12 μm.
5. the preparation method of the scratch resistant protecting film of a kind of long acting antibiotic any one of Claims 1-4, it is characterised in that
Comprise the following steps：
1) UV resins are weighed, butanone and toluene is added, is stirred under room temperature；
2) to the step 1) add and stirred under light trigger, room temperature in the glue that formed；
3) to the step 2) formed glue in add nano silver ion antibiotic agent, stir under room temperature；
4) by the step 3) glue that formed is evenly applied to the surface of the base material；
5) by the step 4 described in) process after base material carry out heat treated；
6) by the step 5 described in) process after base material carry out UV photo-irradiation treatment, long acting antibiotic scratch resistant protecting film is obtained after cooling.
6. a kind of preparation method of the scratch resistant protecting film of long acting antibiotic according to claim 5, it is characterised in that the step
5) heating-up temperature in is 70 DEG C～160 DEG C, and heat time heating time is 20s～120s.
7. a kind of preparation method of the scratch resistant protecting film of long acting antibiotic according to claim 5, it is characterised in that the step
6) the UV illumination temperatures in are 120 DEG C～160 DEG C, and UV light application times are 15s～60s.