CN106565986A - 一种表面改性的纳米碳酸钙 - Google Patents
一种表面改性的纳米碳酸钙 Download PDFInfo
- Publication number
- CN106565986A CN106565986A CN201610995731.3A CN201610995731A CN106565986A CN 106565986 A CN106565986 A CN 106565986A CN 201610995731 A CN201610995731 A CN 201610995731A CN 106565986 A CN106565986 A CN 106565986A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- nano
- sodium
- anhydrous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种表面改性的纳米碳酸钙，由以下质量份数的组分组成：500‑550份纳米碳酸钙基料、4‑5份焦磷酸钾、2‑3份衣康酸、5‑6份碱式碳酸镁、4‑5份无水氯化钙、3‑4份五氧化二磷、2‑4份无水亚硫酸钠、1‑2份氨基酸、2‑3份氨基磺酸、2‑4份乙二胺四乙酸二钠、1‑2份丙氨酸、2‑3份邻苯二甲酰亚胺、1‑2份山梨糖醇、2‑3份六偏磷酸钠、3‑4份苯甲酸钠、4‑5份十二烷基二甲基甜菜碱、4‑5份十二烷基二羟乙基甜菜碱、4‑5份月桂酰胺基丙基甜菜碱、1‑2份脯氨酸、3‑5份烯丙基聚氧乙烯醚。该表面改性的纳米碳酸钙采用全新的表面改性剂制成，通过添加不同组分比例的表面改性剂，解决了纳米碳酸钙在压延膜及封边条中应用时难以着色的问题，达到容易吸墨的效果。
Description
技术领域
本发明涉及一种纳米碳酸钙的技术领域，尤其涉及一种通过表面改性的表面改性的纳米碳酸钙。
背景技术
碳酸钙是一种重要的无机化工产品，作为填充剂，被广泛应用于橡胶、塑料、造纸、涂料、油墨、医药等领域。纳米碳酸钙是工业碳酸钙中极为重要的一种，其主要特点是粒径小、比表面积大，性能远远优于微米级碳酸钙，在高分子材料填充应用中，往往体现出显著的补强、增韧效果。
目前，由于纳米碳酸钙粒径较小，表面能大，在干燥和应用过程中都容易出现硬团聚。这种硬团聚在橡胶加工过程中不易被解聚，形成应力集中点，降低制品力学强度，还会影响制品外观。解决硬团聚问题的主要手段是对纳米碳酸钙进行有机化表面处理，选用的表面处理剂通常为脂肪酸或其盐。这类表面处理剂虽然可以有效改善粉体分散性，但处理剂与橡胶体系间作用力较弱，补强效果不明显，而且加工性能欠佳，橡胶的焦烧时间缩短。
另外，采用传统的表面改性剂如硬脂酸等制成的纳米碳酸钙用于压延膜及封边条时，由于采用传统的改性剂而令产品的进吸墨性差，印刷时难以着色。
发明内容
本发明的目的是为了克服上述现有技术的缺点，提供一种表面改性的纳米碳酸钙，该表面改性的纳米碳酸钙采用全新的表面改性剂制成，通过添加不同组分比例的表面改性剂，解决了传统的纳米碳酸钙在压延膜及封边条中应用时难以着色的问题，达到容易吸墨的效果，具有高补强、易加工、高分散性和高稳定性的特点，也具有良好相容性，能显著提高填充橡胶制品等的力学性能和改善橡胶等的加工性能。
本发明解决其技术问题所采用的技术方案是：一种表面改性的纳米碳酸钙，由以下质量份数的组分组成：500-550份纳米碳酸钙基料、4-5份焦磷酸钾、2-3份衣康酸、5-6份碱式碳酸镁、4-5份无水氯化钙、3-4份五氧化二磷、2-4份无水亚硫酸钠、1-2份氨基酸、2-3份氨基磺酸、2-4份乙二胺四乙酸二钠、1-2份丙氨酸、2-3份邻苯二甲酰亚胺、1-2份山梨糖醇、2-3份六偏磷酸钠、3-4份苯甲酸钠、4-5份十二烷基二甲基甜菜碱、4-5份十二烷基二羟乙基甜菜碱、4-5份月桂酰胺基丙基甜菜碱、1-2份脯氨酸、3-5份烯丙基聚氧乙烯醚。
进一步的，该表面改性的纳米碳酸钙，由以下质量份数的组分组成：500份纳米碳酸钙基料、4份焦磷酸钾、2份衣康酸、5份碱式碳酸镁、4份无水氯化钙、3份五氧化二磷、2份无水亚硫酸钠、1份氨基酸、2份氨基磺酸、2份乙二胺四乙酸二钠、1份丙氨酸、2份邻苯二甲酰亚胺、1份山梨糖醇、2份六偏磷酸钠、3份苯甲酸钠、4份十二烷基二甲基甜菜碱、4份十二烷基二羟乙基甜菜碱、4份月桂酰胺基丙基甜菜碱、1份脯氨酸、3份烯丙基聚氧乙烯醚。
或者是，该表面改性的纳米碳酸钙由以下质量份数的组分组成：550份纳米碳酸钙基料、5份焦磷酸钾、3份衣康酸、6份碱式碳酸镁、5份无水氯化钙、4份五氧化二磷、4份无水亚硫酸钠、2份氨基酸、3份氨基磺酸、4份乙二胺四乙酸二钠、2份丙氨酸、3份邻苯二甲酰亚胺、2份山梨糖醇、3份六偏磷酸钠、3-4份苯甲酸钠、5份十二烷基二甲基甜菜碱、5份十二烷基二羟乙基甜菜碱、5份月桂酰胺基丙基甜菜碱、2份脯氨酸、5份烯丙基聚氧乙烯醚。
综上所述，本发明的表面改性的纳米碳酸钙采用全新的表面改性剂制成，通过添加不同组分比例的表面改性剂，解决了传统的纳米碳酸钙在压延膜及封边条中应用时难以着色的问题，达到容易吸墨的效果，具有高补强、易加工、高分散性和高稳定性的特点，也具有良好相容性，能显著提高填充橡胶制品等的力学性能和改善橡胶等的加工性能。
具体实施方式
实施例1
本实施例1所描述的一种表面改性的纳米碳酸钙，由以下质量份数的组分组成：500份纳米碳酸钙基料、4份焦磷酸钾、2份衣康酸、5份碱式碳酸镁、4份无水氯化钙、3份五氧化二磷、2份无水亚硫酸钠、1份氨基酸、2份氨基磺酸、2份乙二胺四乙酸二钠、1份丙氨酸、2份邻苯二甲酰亚胺、1份山梨糖醇、2份六偏磷酸钠、3份苯甲酸钠、4份十二烷基二甲基甜菜碱、4份十二烷基二羟乙基甜菜碱、4份月桂酰胺基丙基甜菜碱、1份脯氨酸、3份烯丙基聚氧乙烯醚。
实施例2
本实施例2所描述的一种表面改性的纳米碳酸钙由以下质量份数的组分组成：550份纳米碳酸钙基料、5份焦磷酸钾、3份衣康酸、6份碱式碳酸镁、5份无水氯化钙、4份五氧化二磷、4份无水亚硫酸钠、2份氨基酸、3份氨基磺酸、4份乙二胺四乙酸二钠、2份丙氨酸、3份邻苯二甲酰亚胺、2份山梨糖醇、3份六偏磷酸钠、3-4份苯甲酸钠、5份十二烷基二甲基甜菜碱、5份十二烷基二羟乙基甜菜碱、5份月桂酰胺基丙基甜菜碱、2份脯氨酸、5份烯丙基聚氧乙烯醚。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明的技术方案的范围内。
Claims (3)
1.一种表面改性的纳米碳酸钙，其特征在于，由以下质量份数的组分组成：500-550份纳米碳酸钙基料、4-5份焦磷酸钾、2-3份衣康酸、5-6份碱式碳酸镁、4-5份无水氯化钙、3-4份五氧化二磷、2-4份无水亚硫酸钠、1-2份氨基酸、2-3份氨基磺酸、2-4份乙二胺四乙酸二钠、1-2份丙氨酸、2-3份邻苯二甲酰亚胺、1-2份山梨糖醇、2-3份六偏磷酸钠、3-4份苯甲酸钠、4-5份十二烷基二甲基甜菜碱、4-5份十二烷基二羟乙基甜菜碱、4-5份月桂酰胺基丙基甜菜碱、1-2份脯氨酸、3-5份烯丙基聚氧乙烯醚。
2.根据权利要求1所述的一种表面改性的纳米碳酸钙，其特征在于，由以下质量份数的组分组成：500份纳米碳酸钙基料、4份焦磷酸钾、2份衣康酸、5份碱式碳酸镁、4份无水氯化钙、3份五氧化二磷、2份无水亚硫酸钠、1份氨基酸、2份氨基磺酸、2份乙二胺四乙酸二钠、1份丙氨酸、2份邻苯二甲酰亚胺、1份山梨糖醇、2份六偏磷酸钠、3份苯甲酸钠、4份十二烷基二甲基甜菜碱、4份十二烷基二羟乙基甜菜碱、4份月桂酰胺基丙基甜菜碱、1份脯氨酸、3份烯丙基聚氧乙烯醚。
3.根据权利要求1所述的一种表面改性的纳米碳酸钙，其特征在于，由以下质量份数的组分组成：550份纳米碳酸钙基料、5份焦磷酸钾、3份衣康酸、6份碱式碳酸镁、5份无水氯化钙、4份五氧化二磷、4份无水亚硫酸钠、2份氨基酸、3份氨基磺酸、4份乙二胺四乙酸二钠、2份丙氨酸、3份邻苯二甲酰亚胺、2份山梨糖醇、3份六偏磷酸钠、3-4份苯甲酸钠、5份十二烷基二甲基甜菜碱、5份十二烷基二羟乙基甜菜碱、5份月桂酰胺基丙基甜菜碱、2份脯氨酸、5份烯丙基聚氧乙烯醚。