CN106554092A - 一种马来酸酐共聚物阻垢分散剂及其制备方法 - Google Patents
一种马来酸酐共聚物阻垢分散剂及其制备方法 Download PDFInfo
- Publication number
- CN106554092A CN106554092A CN201510631117.4A CN201510631117A CN106554092A CN 106554092 A CN106554092 A CN 106554092A CN 201510631117 A CN201510631117 A CN 201510631117A CN 106554092 A CN106554092 A CN 106554092A
- Authority
- CN
- China
- Prior art keywords
- maleic anhydride
- phosphate
- scale
- mass percent
- anhydride copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种马来酸酐共聚物阻垢分散剂及其制备方法，该阻垢分散剂包括马来酸酐、不饱和羧酸、磷酸盐、引发剂和去离子水，各组分的质量百分数为：马来酸酐，15％-20％；不饱和羧酸，10％-20％；磷酸盐，15％-20％；引发剂，4％-5％；去离子水，余量。该阻垢分散剂的制备方法，包括如下步骤：称取质量百分数为15％-20％的马来酸酐溶于去离子水中，加入质量百分数为10％-20％不饱和羧酸和质量百分数为4％-5％的引发剂，升温至40℃-70℃，恒温反应1-4h，冷却即得马来酸酐与不饱和酸的共聚物；在共聚物中加入质量分数为15％-20％的磷酸盐，搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。本发明制得的阻垢分散剂具有稳定和分散成垢物质的双重阻垢效应，阻垢性能稳定持久。
Description
技术领域
本发明涉及一种阻垢分散剂及其制备方法，具体涉及一种马来酸酐共聚物阻垢分散剂及其制备方法，属于水处理技术领域。
背景技术
阻垢剂是指能分散水中的难溶性无机盐，阻止或干扰难溶性无机盐在金属表面的沉淀、结垢，维持金属设备具有良好的传热效果的一类化学品。
常用的阻垢剂有无机磷酸盐、有机磷酸盐和聚合物三类。
无机磷酸盐，也就是聚磷酸盐，如三聚磷酸钠、六偏磷酸钠等，其价格便宜，虽然分散能力较差，但它能使晶格畸变，是最早使用的阻垢剂。有机磷酸盐如氨基亚甲基磷酸盐或羟基亚乙基膦酸盐，作用与有机磷酸盐相似，是非常强的阻垢剂。
但是，磷酸盐的缺点在于，易水解生成正磷酸盐，与二价金属阳离子Ca2+、Mg2+等反应而结垢，在高温和高pH值下尤甚。
聚马来酸酐，是马来酸酐与丙烯酸、磺化苯乙烯、醋酸乙烯等的共聚物，同时兼有晶格畸变和阀值效应两种作用，还有分三磷酸钙微晶的效能，在高pH值条件下，仍能防止磷酸钙形成，生成的垢比较松软，易被流水冲掉并自身有较高的热稳定性等优点。
发明内容
发明目的：本发明的第一目的是提供一种具有稳定和分散成垢物质双重阻垢效应的马来酸酐共聚物阻垢分散剂，本发明的第二目的是提供该阻垢分散剂的制备方法。
技术方案：本发明所述的一种马来酸酐共聚物阻垢分散剂，包括马来酸酐、不饱和羧酸、磷酸盐、引发剂和去离子水，各组分的质量百分数如下：
马来酸酐：15％-20％；
不饱和羧酸：10％-20％；
磷酸盐：15％-20％；
引发剂：4％-5％；
去离子水：余量。
优选的，马来酸酐的质量百分数为18％-20％，不饱和羧酸的质量百分数为10％-15％，磷酸盐的质量百分数为15％-18％。
优选的，不饱和羧酸为丙烯酸或甲基丙烯酸。
优选的，磷酸盐为无机磷酸盐或有机磷酸盐。
优选的，引发剂为过硫酸铵或过硫酸钾。
本发明所述的一种马来酸酐共聚物阻垢分散剂的制备方法，包括如下步骤：称取马来酸酐充分溶于去离子水中，在搅拌下加入不饱和羧酸和引发剂，升温至40℃-70℃，恒温反应1-4h，冷却即得马来酸酐与不饱和酸酸的共聚物；在上述共聚物中加入磷酸盐，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。
有益效果：本发明与现有技术相比，具有以下优点：
(1)将聚马来酸酐与磷酸盐混合使用，由于共聚物中含有羧基官能团，避免了磷酸盐与Ca2+、Mg2+等的结垢，使阻垢分散剂不仅具有优良的阻CaSO4垢功能，还有一定的分散氧化铁的性能，同时受水质中Fe2+、Ba2+浓度的影响较小，具有稳定持久的阻垢性能；
(2)本发明的制备方法简单，工艺易于控制，原料成本较低，简单易得，可广泛应用于工业循环水处理。
具体实施方式
下面对本发明的技术方案作进一步说明。
实施例1
称取15g马来酸酐充分溶于去离子水中，在搅拌下加入10g丙烯酸和4g过硫酸铵，升温至50℃，恒温反应2h，冷却即得马来酸酐与丙烯酸的共聚物；在上述共聚物中加入15g三聚磷酸钠，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。
实施例2
称取18g马来酸酐充分溶于去离子水中，在搅拌下加入20g丙烯酸和4g过硫酸钾，升温至40℃，恒温反应4h，冷却即得马来酸酐与丙烯酸的共聚物；在上述共聚物中加入15g羟基亚乙基膦酸盐，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。
实施例3
称取20g马来酸酐充分溶于去离子水中，在搅拌下加入15g甲基丙烯酸和5g过硫酸钾，升温至70℃，恒温反应1h，冷却即得马来酸酐与甲基丙烯酸的共聚物；在上述共聚物中加入18g六偏磷酸钠，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。
实施例4
称取16g马来酸酐充分溶于去离子水中，在搅拌下加入18g甲基丙烯酸和4.5g过硫酸铵，升温至60℃，恒温反应3h，冷却即得马来酸酐与甲基丙烯酸的共聚物；在上述共聚物中加入20g的氨基亚甲基磷酸盐，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。
Claims (6)
1.一种马来酸酐共聚物阻垢分散剂，其特征在于，包括马来酸酐、不饱和羧酸、磷酸盐、引发剂和去离子水，各组分的质量百分数如下：
马来酸酐：15％-20％；
不饱和羧酸：10％-20％；
磷酸盐：15％-20％；
引发剂：4％-5％；
去离子水：余量。
2.根据权利要求1所述的马来酸酐共聚物阻垢分散剂，其特征在于，所述马来酸酐的质量百分数为18％-20％，所述不饱和羧酸的质量百分数为10％-15％，所述磷酸盐的质量百分数为15％-18％。
3.根据权利要求1所述的马来酸酐共聚物阻垢分散剂，其特征在于，所述不饱和羧酸为丙烯酸或甲基丙烯酸。
4.根据权利要求1所述的马来酸酐共聚物阻垢分散剂，其特征在于，所述磷酸盐为无机磷酸盐或有机磷酸盐。
5.根据权利要求1所述的马来酸酐共聚物阻垢分散剂，其特征在于，所述引发剂为过硫酸铵或过硫酸钾。
6.一种权利要求1所述的马来酸酐共聚物阻垢分散剂的制备方法，其特征在于，包括如下步骤：称取马来酸酐充分溶于去离子水中，在搅拌下加入不饱和羧酸和引发剂，升温至40℃-70℃，恒温反应1-4h，冷却即得马来酸酐与不饱和酸酸的共聚物；在上述共聚物中加入磷酸盐，常温下搅拌、溶解，即得马来酸酐共聚物阻垢分散剂。