CN106543802A - A kind of film printing water color ink and preparation method thereof - Google Patents
A kind of film printing water color ink and preparation method thereof Download PDFInfo
- Publication number
- CN106543802A CN106543802A CN201611049605.5A CN201611049605A CN106543802A CN 106543802 A CN106543802 A CN 106543802A CN 201611049605 A CN201611049605 A CN 201611049605A CN 106543802 A CN106543802 A CN 106543802A
- Authority
- CN
- China
- Prior art keywords
- parts
- color ink
- water color
- film printing
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of film printing water color ink and preparation method thereof, is made up of the raw material of following weight portion:28 35 parts of acrylic resin, 10 20 parts of epoxy resin, 12 20 parts of pigment, 6 12 parts of wollastonite in powder, 27 parts of nano-bentonite, 49 parts of biocide mildewcide, 0.5 3 parts of epoxy soybean oil, 14 parts of polyurethane, 0.5 2 parts of surfactant, 0.5 2 parts of silane, 26 38 parts of deionized water;The water color ink of the present invention, can improve the wearability and resistance to blocking of ink by adding wollastonite in powder;The biocide mildewcide of addition is prepared with Chinese medicine ingredients, and safety and environmental protection is harmless to health;The ink performance of the present invention is stable, and with good glossiness and dispersibility, rate of drying is fast;During use, ink do not fall off, not fall the effect of ink, and printing effect is lasting.
Description
Technical field
The present invention relates to printing-ink, and in particular to a kind of film printing water color ink and preparation method thereof.
Background technology
At present, plastic sheeting miscellaneous is widely used in printing and packaging industry.These thin film print in many cases
There is writings and image, in order that printing quality meets use requirement, need have certain understanding to the preparation of printing-ink.It is common
Printing-ink be divided into solvent type ink, water color ink and light-curable ink three types.With global environmental pollution and life
Life, concern for the environment and the development of the mankind are increasingly paid close attention in the aggravation of state environmental disruption degree, people, improve production and using green
Color product.Water color ink is widely used in printing and packaging industry.
The uniform slurry like material that water color ink is mainly made up of coloring agent and binder, with not firing, it is not quick-fried, nontoxic,
The characteristic such as have no irritating odor.The effect of coloring agent is that image function is provided on base material, and gives latex film light resistance and light
Pool.But at present, generally in dispersibility, glossiness, water-resistance, performance is not enough for water color ink, and hardening time is long, reduces use
Efficiency, increased cost.Therefore, it is necessary to existing printing-ink is improved, it is many with low cost, function so as to produce
Unitization, high temperature resistant, the printing-ink of wear-resisting, good environmental protection.
The content of the invention
It is an object of the invention to provide a kind of film printing water color ink, stable performance, antibacterial and mouldproof, with good light
Damp degree and wearability.
In order to realize the purpose of the present invention, adopt the following technical scheme that:
A kind of film printing water color ink, is made up of the raw material of following weight portion:
Preferably, it is made up of the raw material of following weight portion:
Preferably, it is made up of the raw material of following weight portion:
Preferably, pigment is the one kind in phthalocyanine blue, titanium dioxide or permanent bordeaux.
Preferably, surfactant is sulfuric ester.
Further, the preparation method of biocide mildewcide is:By Herba Menthae 15-22 parts, Radix Sophorae Flavescentiss 12-20 parts, Flos Caryophylli 8-15 parts,
Remonstrate with skin 6-12 parts, Flos Lonicerae 14-18 part of Radix Arnebiae (Radix Lithospermi) 10-15 parts, Rhizoma Coptidis 5-10 parts, Camphora 9-13 parts, hardship is added to 2-5 times of weight portion
Water in, decoct 3 times, each 40-60min, filter, three filtrate is merged, cooling, concentration obtain final product biocide mildewcide.
Further, a kind of preparation method of film printing water color ink, comprises the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 650-800 DEG C, and roasting time is 45-70min,
Cooling, ground 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing high-speed stirred
Machine mixing and stirring, mixing speed are 80-120r/min, and heating-up temperature is 60-75 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for up to preliminary dispersion, then ultrasound
Ripple vibrates 20-30min, and compound B is obtained;
(5) compound B is ground on three-roller and is obtained final product.
Beneficial effects of the present invention:
The water color ink of the present invention, can improve the wearability and resistance to blocking of ink by adding wollastonite in powder;Addition
Biocide mildewcide prepared with Chinese medicine ingredients, safety and environmental protection is harmless to health;The ink performance of the present invention is stable, tool
There are good glossiness and dispersibility, rate of drying is fast;During use, ink do not fall off, not fall the effect of ink, and printing effect is held
Long.
Specific embodiment
Below embodiments of the invention are elaborated, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following enforcements
Example.
Embodiment 1
A kind of film printing water color ink, is made up of the raw material of following weight portion:28 parts of acrylic resin, epoxy resin 10
Part, 12 parts of pigment, 6 parts of wollastonite in powder, 2 parts of nano-bentonite, 4 parts of biocide mildewcide, 0.5 part of epoxy soybean oil, polyurethane 1
Part, 0.5 part of surfactant, 0.5 part of silane, 26 parts of deionized water;During wherein pigment is phthalocyanine blue, titanium dioxide or permanent bordeaux
It is a kind of;Surfactant is sulfuric ester.
Wherein, the preparation method of biocide mildewcide is:By 15 parts of Herba Menthae, 12 parts of Radix Sophorae Flavescentiss, 8 parts of Flos Caryophylli, 10 parts of Radix Arnebiae (Radix Lithospermi), Rhizoma Coptidis
5 parts, 9 parts of Camphora, remonstrate with 6 parts of skin, 14 parts of Flos Lonicerae of hardship be added in the water of 2 times of weight portions, decoct 3 times, each 40min, filter,
Three filtrate merging, cooling, concentrations are obtained final product into biocide mildewcide.
A kind of preparation method of film printing water color ink, comprises the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 650 DEG C, and roasting time is 50min, cooling is ground
Honed 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing high-speed stirred
Machine mixing and stirring, mixing speed are 80r/min, and heating-up temperature is 60 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for up to preliminary dispersion, then ultrasound
Ripple vibrates 20min, and compound B is obtained;
(5) compound B is ground on three-roller and is obtained final product.
Embodiment 2
A kind of film printing water color ink, is made up of the raw material of following weight portion:35 parts of acrylic resin, epoxy resin 20
Part, 20 parts of pigment, 12 parts of wollastonite in powder, 7 parts of nano-bentonite, 9 parts of biocide mildewcide, 3 parts of epoxy soybean oil, 4 parts of polyurethane,
2 parts of surfactant, 2 parts of silane, 38 parts of deionized water;Wherein pigment is the one kind in phthalocyanine blue, titanium dioxide or permanent bordeaux;Table
Face activating agent is sulfuric ester.
Wherein, the preparation method of biocide mildewcide is:By 22 parts of Herba Menthae, 20 parts of Radix Sophorae Flavescentiss, 15 parts of Flos Caryophylli, 15 parts of Radix Arnebiae (Radix Lithospermi), Huang
10 parts of company, 13 parts of Camphora, bitter remonstrate with 12 parts of skin, 18 parts of Flos Lonicerae are added in the water of 3 times of weight portions, are decocted 3 times, each 50min,
Filter, three filtrate merging, cooling, concentrations are obtained final product into biocide mildewcide.
A kind of preparation method of film printing water color ink, comprises the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 700 DEG C, and roasting time is 60min, cooling is ground
Honed 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing high-speed stirred
Machine mixing and stirring, mixing speed are 90r/min, and heating-up temperature is 65 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for up to preliminary dispersion, then ultrasound
Ripple vibrates 25min, and compound B is obtained;
(5) compound B is ground on three-roller and is obtained final product.
Embodiment 3
A kind of film printing water color ink, is made up of the raw material of following weight portion:30 parts of acrylic resin, epoxy resin 14
Part, 15 parts of pigment, 8 parts of wollastonite in powder, 4 parts of nano-bentonite, 5 parts of biocide mildewcide, 1 part of epoxy soybean oil, 2 parts of polyurethane,
1 part of surfactant, 1 part of silane, 32 parts of deionized water;Wherein pigment is the one kind in phthalocyanine blue, titanium dioxide or permanent bordeaux;Table
Face activating agent is sulfuric ester.
Wherein, the preparation method of biocide mildewcide is:By 18 parts of Herba Menthae, 15 parts of Radix Sophorae Flavescentiss, 10 parts of Flos Caryophylli, 12 parts of Radix Arnebiae (Radix Lithospermi), Huang
8 parts of company, 10 parts of Camphora, bitter remonstrate with 8 parts of skin, 15 parts of Flos Lonicerae are added in the water of 3 times of weight portions, are decocted 3 times, each 55min, mistake
Three filtrate merging, cooling, concentrations are obtained final product biocide mildewcide by filter.
A kind of preparation method of film printing water color ink, comprises the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 750 DEG C, and roasting time is 60min, cooling is ground
Honed 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing high-speed stirred
Machine mixing and stirring, mixing speed are 100r/min, and heating-up temperature is 70 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for up to preliminary dispersion, then ultrasound
Ripple vibrates 25min, and compound B is obtained;
(5) compound B is ground on three-roller and is obtained final product.
Embodiment 4
A kind of film printing water color ink, is made up of the raw material of following weight portion:32 parts of acrylic resin, epoxy resin 18
Part, 17 parts of pigment, 10 parts of wollastonite in powder, 5 parts of nano-bentonite, 7 parts of biocide mildewcide, 2 parts of epoxy soybean oil, 3 parts of polyurethane,
1.5 parts of surfactant, 1.5 parts of silane, 35 parts of deionized water;Wherein pigment is in phthalocyanine blue, titanium dioxide or permanent bordeaux
Kind;Surfactant is sulfuric ester.
Wherein, the preparation method of biocide mildewcide is:By 20 parts of Herba Menthae, 18 parts of Radix Sophorae Flavescentiss, 12 parts of Flos Caryophylli, 12 parts of Radix Arnebiae (Radix Lithospermi), Huang
8 parts of company, 11 parts of Camphora, bitter remonstrate with 10 parts of skin, 16 parts of Flos Lonicerae are added in the water of 4 times of weight portions, are decocted 3 times, each 55min,
Filter, three filtrate merging, cooling, concentrations are obtained final product into biocide mildewcide.
A kind of preparation method of film printing water color ink, comprises the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 750 DEG C, and roasting time is 65min, cooling is ground
Honed 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing high-speed stirred
Machine mixing and stirring, mixing speed are 115r/min, and heating-up temperature is 65 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for up to preliminary dispersion, then ultrasound
Ripple vibrates 30min, and compound B is obtained;
(5) compound B is ground on three-roller and is obtained final product.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all essences in the present invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (7)
1. a kind of film printing water color ink, it is characterised in that be made up of the raw material of following weight portion:
2. a kind of film printing water color ink according to claim 1, it is characterised in that by the raw material group of following weight portion
Into:
3. a kind of film printing water color ink according to claim 1, it is characterised in that by the raw material group of following weight portion
Into:
4. a kind of film printing water color ink according to claim 1, it is characterised in that pigment is phthalocyanine blue, titanium dioxide
Or the one kind in permanent bordeaux.
5. a kind of film printing water color ink according to claim 1, it is characterised in that surfactant is sulfuric ester.
6. a kind of film printing water color ink according to claim 1, it is characterised in that the preparation method of biocide mildewcide
For:By Herba Menthae 15-22 parts, Radix Sophorae Flavescentiss 12-20 parts, Flos Caryophylli 8-15 parts, Radix Arnebiae (Radix Lithospermi) 10-15 parts, Rhizoma Coptidis 5-10 parts, Camphora 9-13 parts, hardship
Remonstrate with skin 6-12 parts, Flos Lonicerae 14-18 part is added in the water of 2-5 times of weight portion, is decocted 3 times, each 40-60min, is filtered, will
Three filtrate merging, cooling, concentrations obtain final product biocide mildewcide.
7. a kind of preparation method of film printing water color ink, it is characterised in that comprise the following steps:
(1) each raw material of corresponding weight portion is weighed respectively;
(2) wollastonite in powder is placed in into roasting in Muffle furnace, sintering temperature is 650-800 DEG C, and roasting time is 45-70min, cold
But, ground 350 mesh standard sieve;
(3) wollastonite in powder after acrylic resin, epoxy resin and roasting is added in deionized water, Jing homogenizers are mixed
Conjunction stirs, and mixing speed is 80-120r/min, and heating-up temperature is 60-75 DEG C, obtains compound A;
(4) remaining raw material is added in the compound A that step (3) is obtained, is sufficiently stirred for until preliminary disperse, then ultrasound wave shakes
Dynamic 20-30min, is obtained compound B;
(5) compound B is ground on three-roller and is obtained final product.