CN106543700A - 用于汽车顶棚的发泡材料 - Google Patents

用于汽车顶棚的发泡材料 Download PDF

Info

Publication number
CN106543700A
CN106543700A CN201610928724.1A CN201610928724A CN106543700A CN 106543700 A CN106543700 A CN 106543700A CN 201610928724 A CN201610928724 A CN 201610928724A CN 106543700 A CN106543700 A CN 106543700A
Authority
CN
China
Prior art keywords
parts
agent
roof
expanded material
bbp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610928724.1A
Other languages
English (en)
Inventor
顾鹏程
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Hao Sheng Plastic Technology Co Ltd
Original Assignee
Jiangsu Hao Sheng Plastic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Hao Sheng Plastic Technology Co Ltd filed Critical Jiangsu Hao Sheng Plastic Technology Co Ltd
Priority to CN201610928724.1A priority Critical patent/CN106543700A/zh
Publication of CN106543700A publication Critical patent/CN106543700A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于汽车顶棚的发泡材料，包括下列重量份的组份：芳香族异氰酸酯30~40份、聚氧化丙烯二醇30~40份、棕榈油2~6份、无规聚丙烯2~5份、有机硅油泡沫稳定剂3~5份、复配交联剂3~5份、纤维素3~5份、邻苯二甲酸丁苄酯2~6份、第二含氮发泡剂2~4份、SOLSPERSE系列超分散助剂1~4份、三（2‑氯乙基）磷酸酯1~3份、二甲基亚砜1~3份和密胺聚磷酸盐1~3份。通过上述方式，本发明强度高，具有较好的抗弯性和保温性。

Description

用于汽车顶棚的发泡材料
技术领域
本发明涉及发泡材料技术领域，特别是涉及一种用于汽车顶棚的发泡材料。
背景技术
随着社会经济的飞速发展，人们的生活水平越来越高，拥有私家车的家庭也越来越多。人们在购买汽车时，不懂行的人对汽车的关注点主要集中在汽车动力性、外观美观度、燃油经济性、功能多样性等方面，懂行的人还会关注汽车制动性、操控稳定性、平顺性以及通过性等方面，其中，汽车内饰方面现在越来越受到人们的关注，汽车内饰件许多由发泡材料制成，现有的这种发泡材料还有待改进。
发明内容
本发明主要解决的技术问题是提供一种用于汽车顶棚的发泡材料，强度高，具有较好的抗弯性和保温性。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种用于汽车顶棚的发泡材料，包括下列重量份的组份：芳香族异氰酸酯30~40份、聚氧化丙烯二醇30~40份、棕榈油2~6份、无规聚丙烯2~5份、有机硅油泡沫稳定剂3~5份、复配交联剂3~5份、纤维素3~5份、邻苯二甲酸丁苄酯2~6份、第二含氮发泡剂2~4份、SOLSPERSE系列超分散助剂1~4份、三（2-氯乙基）磷酸酯1~3份、二甲基亚砜1~3份和密胺聚磷酸盐1~3份。
在本发明一个较佳实施例中，包括下列重量份的组份：芳香族异氰酸酯30份、聚氧化丙烯二醇30份、棕榈油2份、无规聚丙烯2份、有机硅油泡沫稳定剂3份、复配交联剂3份、纤维素3份、邻苯二甲酸丁苄酯2份、第二含氮发泡剂2份、SOLSPERSE系列超分散助剂1份、三（2-氯乙基）磷酸酯1份、二甲基亚砜1份和密胺聚磷酸盐1份。
在本发明一个较佳实施例中，包括下列重量份的组份：芳香族异氰酸酯33份、聚氧化丙烯二醇36份、棕榈油4份、无规聚丙烯3份、有机硅油泡沫稳定剂4份、复配交联剂4份、纤维素4份、邻苯二甲酸丁苄酯5份、第二含氮发泡剂3份、SOLSPERSE系列超分散助剂2份、三（2-氯乙基）磷酸酯2份、二甲基亚砜2份和密胺聚磷酸盐2份。
在本发明一个较佳实施例中，包括下列重量份的组份：芳香族异氰酸酯40份、聚氧化丙烯二醇40份、棕榈油6份、无规聚丙烯5份、有机硅油泡沫稳定剂5份、复配交联剂5份、纤维素5份、邻苯二甲酸丁苄酯6份、第二含氮发泡剂4份、SOLSPERSE系列超分散助剂4份、三（2-氯乙基）磷酸酯3份、二甲基亚砜3份和密胺聚磷酸盐3份。
本发明的有益效果是：本发明用于汽车顶棚的发泡材料，强度高，具有较好的抗弯性和保温性。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
实施例一：
一种用于汽车顶棚的发泡材料，包括下列重量份的组份：芳香族异氰酸酯30份、聚氧化丙烯二醇30份、棕榈油2份、无规聚丙烯2份、有机硅油泡沫稳定剂3份、复配交联剂3份、纤维素3份、邻苯二甲酸丁苄酯2份、第二含氮发泡剂2份、SOLSPERSE系列超分散助剂1份、三（2-氯乙基）磷酸酯1份、二甲基亚砜1份和密胺聚磷酸盐1份。
实施例二：
一种用于汽车顶棚的发泡材料，包括下列重量份的组份：芳香族异氰酸酯33份、聚氧化丙烯二醇36份、棕榈油4份、无规聚丙烯3份、有机硅油泡沫稳定剂4份、复配交联剂4份、纤维素4份、邻苯二甲酸丁苄酯5份、第二含氮发泡剂3份、SOLSPERSE系列超分散助剂2份、三（2-氯乙基）磷酸酯2份、二甲基亚砜2份和密胺聚磷酸盐2份。
实施例三：
一种用于汽车顶棚的发泡材料，包括下列重量份的组份：芳香族异氰酸酯40份、聚氧化丙烯二醇40份、棕榈油6份、无规聚丙烯5份、有机硅油泡沫稳定剂5份、复配交联剂5份、纤维素5份、邻苯二甲酸丁苄酯6份、第二含氮发泡剂4份、SOLSPERSE系列超分散助剂4份、三（2-氯乙基）磷酸酯3份、二甲基亚砜3份和密胺聚磷酸盐3份。
本发明的有益效果是：本发明用于汽车顶棚的发泡材料，强度高，具有较好的抗弯性和保温性。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种用于汽车顶棚的发泡材料，其特征在于，包括下列重量份的组份：芳香族异氰酸酯30~40份、聚氧化丙烯二醇30~40份、棕榈油2~6份、无规聚丙烯2~5份、有机硅油泡沫稳定剂3~5份、复配交联剂3~5份、纤维素3~5份、邻苯二甲酸丁苄酯2~6份、第二含氮发泡剂2~4份、SOLSPERSE系列超分散助剂1~4份、三（2-氯乙基）磷酸酯1~3份、二甲基亚砜1~3份和密胺聚磷酸盐1~3份。
2.根据权利要求1所述的用于汽车顶棚的发泡材料，其特征在于，包括下列重量份的组份：芳香族异氰酸酯30份、聚氧化丙烯二醇30份、棕榈油2份、无规聚丙烯2份、有机硅油泡沫稳定剂3份、复配交联剂3份、纤维素3份、邻苯二甲酸丁苄酯2份、第二含氮发泡剂2份、SOLSPERSE系列超分散助剂1份、三（2-氯乙基）磷酸酯1份、二甲基亚砜1份和密胺聚磷酸盐1份。
3.根据权利要求1所述的用于汽车顶棚的发泡材料，其特征在于，包括下列重量份的组份：芳香族异氰酸酯33份、聚氧化丙烯二醇36份、棕榈油4份、无规聚丙烯3份、有机硅油泡沫稳定剂4份、复配交联剂4份、纤维素4份、邻苯二甲酸丁苄酯5份、第二含氮发泡剂3份、SOLSPERSE系列超分散助剂2份、三（2-氯乙基）磷酸酯2份、二甲基亚砜2份和密胺聚磷酸盐2份。
4.根据权利要求1所述的用于汽车顶棚的发泡材料，其特征在于，包括下列重量份的组份：芳香族异氰酸酯40份、聚氧化丙烯二醇40份、棕榈油6份、无规聚丙烯5份、有机硅油泡沫稳定剂5份、复配交联剂5份、纤维素5份、邻苯二甲酸丁苄酯6份、第二含氮发泡剂4份、SOLSPERSE系列超分散助剂4份、三（2-氯乙基）磷酸酯3份、二甲基亚砜3份和密胺聚磷酸盐3份。
CN201610928724.1A 2016-10-31 2016-10-31 用于汽车顶棚的发泡材料 Pending CN106543700A (zh)