CN106541649B - 一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法 - Google Patents

一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法 Download PDF

Info

Publication number
CN106541649B
CN106541649B CN201611113347.2A CN201611113347A CN106541649B CN 106541649 B CN106541649 B CN 106541649B CN 201611113347 A CN201611113347 A CN 201611113347A CN 106541649 B CN106541649 B CN 106541649B
Authority
CN
China
Prior art keywords
far
layer
fibre
nano
ion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201611113347.2A
Other languages
English (en)
Other versions
CN106541649A (zh
Inventor
刘惠峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maya Forest (Beijing) International Technology Co., Ltd.
Original Assignee
Taicang Datang Chemical Fiber Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Datang Chemical Fiber Factory filed Critical Taicang Datang Chemical Fiber Factory
Priority to CN201611113347.2A priority Critical patent/CN106541649B/zh
Publication of CN106541649A publication Critical patent/CN106541649A/zh
Application granted granted Critical
Publication of CN106541649B publication Critical patent/CN106541649B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种纤维，特别涉及一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法。本发明所述的一种远红外负离子抗静电纤维，基层纤维层中含有纳米抗静电母粒，抗静电效果稳定持久，让人们远离静电的困扰和伤害；负离子纤维层释放负离子；远红外纤维层释放远红外线，从而促进人体血液循环，杀菌，健肤美肤，促进人体新陈代谢，纳米抗静电母粒的制备方法简单，成本低。

Description

一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法
技术领域
本发明涉及一种纤维，特别涉及一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法。
背景技术
人们在日常生活中经常会受到静电的困扰，静电对人体的危害有：可能引起心率异常、心脏早博；聚集灰尘中的细菌影响人体健康；产生皮肤病；持续静电会产生心情烦燥不安、头晕胸闷和喉鼻不适等。因此人们对日常生活中的各类纤维织物的抗静电功能性要求越来越高。
发明内容
发明的目的：本发明公开了一种远红外负离子抗静电纤维，具有美肤健肤、减少呼吸道疾病、改善睡眠质量、改善心肌营养，有效降低三高，促进血液循环，还可以净化空气、杀菌和除臭作用，同时含有纳米抗静电母粒，抗静电效果持久稳定。
技术方案：为了实现以上目的，本发明公开了一种远红外负离子抗静电纤维，包括第一基层纤维层、抗菌纤维层、远红外纤维层、负离子纤维层和第二基层纤维层，所述第一基层纤维层和第二基层纤维层为聚酯纤维层，所述第一基层纤维层的上端交叉搭接设有抗菌纤维层，所述抗菌纤维层的上端设有远红外纤维层，所述远红外纤维层的上端设有负离子纤维层，所述负离子纤维层的上端设有第二基层纤维层，所述第一基层纤维层和第二基层纤维层中含有纳米抗静电母粒。
进一步的，上述一种远红外负离子抗静电纤维，所述抗菌纤维层为竹纤维。竹纤维具有天然抗菌、抑菌、除螨、防臭和抗紫外功能，同时还具有良好的透气性、瞬间吸水性和较强的耐磨性能。
进一步的，上述一种远红外负离子抗静电纤维，所述抗菌纤维层还设有载锌抗菌母粒。可以提供人体所需微量元素，改善人体微循环，增强细胞免疫力，并能起到预防和治疗多种皮肤病的作用。
进一步的，上述一种远红外负离子抗静电纤维，所述的远红外纤维层为远红外锦纶纤维，锦纶纤维具有耐磨性能好和弹性及弹性恢复性极好，吸湿性较好同时还具有良好的耐蛀、耐腐蚀性。
进一步的，上述一种远红外负离子驱蚊纤维，所述远红外锦纶纤维包括锦纶纤维和远红外母粒，所述锦纶纤维截面成四叶草形且有空腔，所述远红外母粒分布在锦纶纤维内表面；提高了远红外负离子抗静电纤维的弹性和透气性。
进一步的，上述一种远红外负离子抗静电纤维，所述的负离子纤维层为负离子涤纶纤维制成，负离子纤维具有美肤健肤、减少呼吸道疾病、改善睡眠质量、改善心肌营养，有效降低三高，促进血液循环，还可以净化空气、杀菌和除臭作用。
进一步的，上述一种远红外负离子抗静电纤维，所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体40-60份、纳米竹碳粉10-15份、纳米抗静电剂 10-12份、抗氧化剂1010 2-4份、硬脂酸锌1-2份。抗静电效果稳定持久。
进一步的，上述一种远红外负离子抗静电纤维，所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体50份、纳米竹碳粉12份、纳米抗静电剂 11份、抗氧化剂1010 3份、硬脂酸锌2份。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法：包括以下步骤：
（1）将聚酯载体冷冻粉碎至20目；
（2）称取配方重量份的聚酯载体，纳米竹炭粉、纳米抗静电剂、抗氧化剂和硬脂酸锌，加入到高混机中搅拌混合均匀；
（3）将混合好后的混料加入到双螺杆挤出机中挤出造粒；
（4）造粒好后过振动筛即得所述纳米抗静电母粒。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法，所述步骤（2）中高混机搅拌混匀温度为120℃-130℃。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法，所述步骤（2）中高混机搅拌混匀温度为125℃。
上述技术方案可以看出，本发明具有如下有益效果：本发明所述的一种远红外负离子抗静电纤维，基层纤维层中含有纳米抗静电母粒，抗静电效果稳定持久，让人们远离静电的困扰和伤害；负离子纤维层释放负离子；远红外纤维层释放远红外线，从而促进人体血液循环，杀菌，健肤美肤，促进人体新陈代谢。
附图说明
图1为本发明的结构示意图；
图2为远红外纤维层截面结构图；
图中：1-第一基层纤维层，2-抗菌纤维层，3-远红外纤维层，31-锦纶纤维，32-远红外母粒，33-空腔，4-负离子纤维层，5-第二基层纤维层，6-纳米抗静电母粒，7-载锌抗菌母粒。
具体实施方式
下面结合附图，对本发明具体实施方式进行详细的描述。
实施例1-3所述的一种远红外负离子抗静电纤维，如图1所示，包括第一基层纤维层1、抗菌纤维层2、远红外纤维层3、负离子纤维层4和第二基层纤维层5，所述第一基层纤维层1和第二基层纤维层5为聚酯纤维层，所述第一基层纤维层1的上端交叉搭接设有抗菌纤维层2，所述抗菌纤维层2的上端设有远红外纤维层3，所述远红外纤维层3的上端设有负离子纤维层4，所述负离子纤维层4的上端设有第二基层纤维层5，所述第一基层纤维层1和第二基层纤维层5中含有纳米抗静电母粒6。
进一步的，上述一种远红外负离子抗静电纤维，所述抗菌纤维层2为竹纤维。竹纤维具有天然抗菌、抑菌、除螨、防臭和抗紫外功能，同时还具有良好的透气性、瞬间吸水性和较强的耐磨性能。
进一步的，上述一种远红外负离子抗静电纤维，所述抗菌纤维层2还设有载锌抗菌母粒7。可以提供人体所需微量元素，改善人体微循环，增强细胞免疫力，并能起到预防和治疗多种皮肤病的作用。
进一步的，上述一种远红外负离子抗静电纤维，所述的远红外纤维层3为远红外锦纶纤维，锦纶纤维具有耐磨性能好和弹性及弹性恢复性极好，吸湿性较好同时还具有良好的耐蛀、耐腐蚀性能，如图2所示，所述远红外锦纶纤维3包括锦纶纤维31和远红外母粒32，所述锦纶纤维31截面成四叶草形且有空腔33，所述远红外母粒32分布在锦纶纤维31内表面；提高了远红外负离子抗静电纤维的弹性和透气性。
进一步的，上述一种远红外负离子抗静电纤维，所述的负离子纤维层4为负离子涤纶纤维，负离子纤维具有美肤健肤、减少呼吸道疾病、改善睡眠质量、改善心肌营养，有效降低三高，促进血液循环，还可以净化空气、杀菌和除臭作用。
实施例1
上述一种远红外负离子抗静电纤维，所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体40份、纳米竹碳粉10份、纳米抗静电剂 10份、抗氧化剂1010 2份、硬脂酸锌1份。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法：包括以下步骤：
（1）将聚酯载体冷冻粉碎至20目；
（2）称取配方重量份的聚酯载体，纳米竹炭粉、纳米抗静电剂、抗氧化剂和硬脂酸锌，加入到高混机中混合均匀；
（3）将混合好后的混料加入到双螺杆挤出机中挤出造粒；
（4）造粒好后过振动筛即得所述纳米抗静电母粒。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法，所述步骤（2）中高混机搅拌混匀温度为120℃。
实施例2
上述一种远红外负离子抗静电纤维，所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体60份、纳米竹碳粉15份、纳米抗静电剂 12份、抗氧化剂1010 4份、硬脂酸锌2份。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法：包括以下步骤：
（1）将聚酯载体冷冻粉碎至20目；
（2）称取配方重量份的聚酯载体，纳米竹炭粉、纳米抗静电剂、抗氧化剂和硬脂酸锌，加入到高混机中混合均匀；
（3）将混合好后的混料加入到双螺杆挤出机中挤出造粒；
（4）造粒好后过振动筛即得所述纳米抗静电母粒。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法，所述步骤（2）中高混机搅拌混匀温度为130℃。
实施例3
上述一种远红外负离子抗静电纤维，所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体50份、纳米竹碳粉12份、纳米抗静电剂 11份、抗氧化剂1010 3份、硬脂酸锌2份。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法：包括以下步骤：
（1）将聚酯载体冷冻粉碎至20目；
（2）称取配方重量份的聚酯载体，纳米竹炭粉、纳米抗静电剂、抗氧化剂和硬脂酸锌，加入到高混机中混合均匀；
（3）将混合好后的混料加入到双螺杆挤出机中挤出造粒；
（4）造粒好后过振动筛即得所述纳米抗静电母粒。
进一步的，上述一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法，所述步骤（2）中高混机搅拌混匀温度为125℃。
上述实施例1-3所述的一种远红外负离子抗静电纤维的纳米抗静电母粒的制备方法所得的纳米抗静电母粒抗静电效果稳定持久。
上述技术方案可以看出，本发明具有如下有益效果：本发明所述的一种远红外负离子抗静电纤维，基层纤维层中含有纳米抗静电母粒，抗静电效果稳定持久，让人们远离静电的困扰和伤害；负离子纤维层释放负离子；远红外纤维层释放远红外线，从而促进人体血液循环，杀菌，健肤美肤。
以上所述仅是本发明的优选实施方式，应指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进，这些改进也应视为本发明的保护范围。

Claims (6)

1.一种远红外负离子抗静电的纤维层叠体，其特征在于：包括第一基层纤维层、抗菌纤维层、远红外纤维层、负离子纤维层和第二基层纤维层，所述第一基层纤维层和第二基层纤维层为聚酯纤维层，所述第一基层纤维层的上端交叉搭接设有抗菌纤维层，所述抗菌纤维层的上端设有远红外纤维层，所述远红外纤维层的上端设有负离子纤维层，所述负离子纤维层的上端设有第二基层纤维层，所述第一基层纤维层和第二基层纤维层中含有纳米抗静电母粒；所述抗菌纤维层还设有载锌抗菌母粒；所述的远红外纤维层为远红外锦纶纤维，所述远红外锦纶纤维包括锦纶纤维和远红外母粒，所述锦纶纤维内有空腔，并且空腔的截面成四叶草形，所述远红外母粒分布在锦纶纤维内表面；所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体40-60份、纳米竹碳粉10-15份、纳米抗静电剂 10-12份、抗氧化剂1010 2-4份、硬脂酸锌1-2份；
一种远红外负离子抗静电的纤维层叠体的纳米抗静电母粒的制备方法，包括以下步骤：
（1）将聚酯载体冷冻粉碎至20目；
（2）称取配方重量份的聚酯载体，纳米竹炭粉、纳米抗静电剂、抗氧化剂和硬脂酸锌，加入到高混机中搅拌混合均匀；
（3）将混合好后的混料加入到双螺杆挤出机中挤出造粒；
（4）造粒好后过振动筛即得所述纳米抗静电母粒。
2.根据权利要求1所述的一种远红外负离子抗静电的纤维层叠体，其特征在于：所述抗菌纤维层为竹纤维。
3.根据权利要求1所述的一种远红外负离子抗静电的纤维层叠体，其特征在于：所述的负离子纤维层为负离子涤纶纤维。
4.根据权利要求1所述的一种远红外负离子抗静电的纤维层叠体，其特征在于：所述的纳米抗静电母粒包括以下重量份的组成成分：聚酯载体50份、纳米竹碳粉12份、纳米抗静电剂11份、抗氧化剂1010 3份、硬脂酸锌2份。
5.根据权利要求1所述的一种远红外负离子抗静电的纤维层叠体，其特征在于：所述步骤（2）中高混机搅拌混匀温度为120℃-130℃。
6.根据权利要求1所述的一种远红外负离子抗静电的纤维层叠体，其特征在于：所述步骤（2）中高混机搅拌混匀温度为125℃。
CN201611113347.2A 2016-12-06 2016-12-06 一种远红外负离子抗静电纤维及纳米抗静电母粒制备方法 Active CN106541649B (zh)