CN106541639B - A kind of insulation ultrathin type decorating board - Google Patents
A kind of insulation ultrathin type decorating board Download PDFInfo
- Publication number
- CN106541639B CN106541639B CN201610979244.8A CN201610979244A CN106541639B CN 106541639 B CN106541639 B CN 106541639B CN 201610979244 A CN201610979244 A CN 201610979244A CN 106541639 B CN106541639 B CN 106541639B
- Authority
- CN
- China
- Prior art keywords
- water
- insulation
- decorating board
- ultrathin type
- type decorating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of insulation ultrathin type decorating boards, are made of face layer, core material and cementing layer；Face layer is any one in cementitious coating felt or alkali-free glass fibre felt；Core material is any one in no glue or impregnation alkali-free glass fibre grid；Cementing layer is mixed by inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change microcapsules and auxiliary aid.The ultrathin decorating board thickness prepared using the present invention can be controlled arbitrarily, and 3mm plate thermal coefficients are less than 0.07W/mK.The various dalles made of all kinds of coating of surface spraying of this substrate, lacquer etc. have excellent thermal and insulating performance, are eliminated compared to traditional " thermal insulation mortar coating ornamental surface system " heat-insulation mortar bed, and construction is simple, cost performance protrude.
Description
Technical field
The present invention relates to a kind of insulation ultrathin type decorating boards, more particularly to one kind for high-rise outer wall, abnormal shape
The ornamental decorative heat preservation integrated board in the positions such as face, belongs to building thermal insulation material field.
Background technology
With the every field of the society that deepens continuously of energy-saving and emission-reduction theory, building heat preservation also becomes hot at present naturally
Point, and the common mode of building heat preservation is three layers of insulation construction using " insulating layer-screed-coat-decorative layer " at present, this guarantor
Warm structure needs at least three working procedures, long construction period, of high cost, and wall thermal insulating often uses organic heat-insulating plate at present,
Such as EPS, XPS, polyurethane sheet, the heat of these materials and the levelling screed of wall inorganic material, especially insulation layer surface
The case where depositing metope cracking during expansion coefficient difference is larger, therefore the summer is recycled for a long time in the winter, even falling off, service life has
Limit；Although and the integrated plate for heat insulation currently promoted overcomes organic layer-inorganic layer coefficient of thermal expansion differences to a certain extent
Different big problem, but higher cost, insulating layer are exposed still restricts its service life and product promotion the shortcomings of outer.
Invention content
In view of the above-mentioned problems, the invention discloses a kind of insulation ultrathin type decorating board, by face layer, core material and gluing
Layer composition, it is characterised in that：
The face layer is：Any one in cementitious coating felt or alkali-free glass fibre felt；
The core material is：Without any one in glue or impregnation alkali-free glass fibre grid, more specifically, grammes per square metre 60
~160g/m2；
The cementing layer is：It is micro- by inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change
Capsule and auxiliary aid mix, and more specifically, each component weight percent is：1:(0.1-0.3):(0.2-0.5):
(0.005-0.01):(0.01-0.05):(0.017-0.095)；
The inorganic gel materials are：It is mixed by portland cement, gypsum, flyash, fire retardant, more specifically
, each component weight percent is：1:(0.1~0.3):(0.5-1.5):(0.05-0.2)；
The auxiliary aid is：It is compounded by water-reducing agent, propylene glycol, early strength agent, more specifically, each component weight hundred
Point ratio is：1:(3.5-5):(1.5-2).
The water-based emulsion is any one in alkaline-resisting pure-acrylic emulsion, alkaline-resisting styrene-acrylic emulsion, alkaline-resisting acetate emulsion
Kind is several.
The hollow beads are organosilicon ceramic microsphere of the grain size between 30-150um, silicone glass microballon, powder
One or more of coal ash hollow beads.
The acrylate wax phase change Microcapsules Size is 30-150um, paraffin content>70%.
The fire retardant is one or more of aluminium hydroxide, magnesium hydroxide, water-soluble poly ammonium phosphate, red phosphorus.
A kind of insulation ultrathin type decorating board disclosed by the invention, addition hollow beads and paraffin microcapsule in formula
Material, hollow beads have the function of obstructing external heat conduction, reduce material thermal conductivity, and paraffin microcapsule energy will be a small amount of
The heat absorption for penetrating into plank avoids the excessive accumulation of heat heat conduction temperature rise in plank inside to reduce the heat-insulated effect of hollow beads
Fruit, the two cooperate, and good heat-blocking action are played, through actual test, its thermal coefficient of the thin plate of 3mm<0.07 W/m·
K, it is suitable with 1cm thermal insulation mortar effects, there is excellent heat insulation effect.
Description of the drawings
Fig. 1 is a kind of insulation ultrathin type decorating board structural schematic diagram disclosed in this invention.
Reference numeral：The faces 1- layer, 2- core materials, 3- cementing layers, 4- hollow minute particles, 5- acrylate wax phase change microcapsules.
Specific embodiment
In order to make the purpose of the present invention, technical solution be more clearly understood, below in conjunction with specific embodiment, invention is carried out
It is further described.
Embodiment 1.
It is face layer to select cementitious coating felt.
Selection impregnation alkali-free glass fibre grid is core material, grammes per square metre 60g/m2。
Gel rubber material：P.O32.5 cement, gypsum, level-one flyash and aluminium hydrate powder is selected to prepare, four weight ratios
Example be：1:0.2:0.8:0.1.
Auxiliary aid：Water-reducing agent, propylene glycol and early strength agent is selected to prepare, three's weight ratio is：1:3.5:1.5.
Cementing layer：Select gel rubber material, alkaline-resisting pure-acrylic emulsion, water, ceramic microsphere, acrylate paraffin microcapsule and mating
Auxiliary agent, weight percent are：1:0.2:0.3:0.005:0.01:0.017.
Above-mentioned material is molded through 2mm molding machines, you can obtain the insulation ultrathin type decorating board that thickness is 2mm.
Embodiment 2.
It is face layer to select cementitious coating felt.
It is core material, grammes per square metre 80g/m to select without glue alkali-free glass fibre grid2。
Gel rubber material：P.O42.5 cement, gypsum, level-one flyash and water-soluble poly ammonium phosphate is selected to prepare, four weights
Amount ratio is：1:0.15:0.9:0.05.
Auxiliary aid：Water-reducing agent, propylene glycol and early strength agent is selected to prepare, three's weight ratio is：1:3:2.
Cementing layer：Select gel rubber material, alkaline-resisting styrene-acrylic emulsion, water, glass microballoon, acrylate paraffin microcapsule and mating
Auxiliary agent, weight percent are：1:0.2:0.4:0.01:0.03:0.04.
Above-mentioned material is molded through 3mm molding machines, you can obtain the insulation ultrathin type decorating board that thickness is 3mm.
Embodiment 3.
Select inorfil glass felt for face layer.
Selection impregnation alkali-free glass fibre grid is core material, grammes per square metre 100g/m2。
Gel rubber material：P.O42.5 cement, gypsum, level-one flyash and magnesium hydroxide powder is selected to prepare, four weight ratios
Example be：1:0.3:1.4:0.15.
Auxiliary aid：Water-reducing agent, propylene glycol and early strength agent is selected to prepare, three's weight ratio is：1:4:2.
Cementing layer：Select gel rubber material, alkaline-resisting acetate emulsion, water, glass microballoon, acrylate paraffin microcapsule and
Auxiliary aid, weight percent are：1:0.3:0.5:0.01:0.05:0.095.
Above-mentioned material is molded through 4mm molding machines, you can obtain the insulation ultrathin type decorating board that thickness is 4mm.
Above example is only the preferable embodiment of the present invention, but not to constrain the present invention, but in order to be easy
Understand implementation of the present invention.The technical staff in any building thermal insulation material field is taken off not departing from the present invention
Under the premise of the spirit shown, the equivalent variations made to part details are replaced, within the scope of protection of the invention.
Claims (5)
1. a kind of insulation ultrathin type decorating board is made of face layer, core material and cementing layer, it is characterised in that：
The face layer is：Any one in cementitious coating felt or alkali-free glass fibre felt；
The core material is：Without any one in glue or impregnation alkali-free glass fibre grid, more specifically, grammes per square metre be 60~
160g/m2；
The cementing layer is：By inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change microcapsules
And auxiliary aid mixes, more specifically, each component weight percent is：1:(0.1-0.3):(0.2-0.5):
(0.005-0.01):(0.01-0.05):(0.017-0.095)；
The inorganic gel materials are：It is mixed by portland cement, gypsum, flyash, fire retardant, more specifically, respectively
Weight percentages are：1:(0.1~0.3):(0.5-1.5):(0.05-0.2)；
The auxiliary aid is：It is compounded by water-reducing agent, propylene glycol, early strength agent, more specifically, each component weight percent
For：1:(3.5-5):(1.5-2).
2. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that：The water-based emulsion
For any one or a few in alkaline-resisting pure-acrylic emulsion, alkaline-resisting styrene-acrylic emulsion, alkaline-resisting acetate emulsion.
3. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that：The hollow beads
For grain size between 30-150 μm organosilicon ceramic microsphere, silicone glass microballon, one kind in flyash hollow beads or
It is several.
4. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that：The acrylate stone
Wax phase-change microcapsule grain size is 30-150 μm, paraffin content>70%.
5. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that：The fire retardant is
One or more of aluminium hydroxide, magnesium hydroxide, water-soluble poly ammonium phosphate, red phosphorus.