CN106541639A - A kind of insulation ultrathin type decorating board - Google Patents
A kind of insulation ultrathin type decorating board Download PDFInfo
- Publication number
- CN106541639A CN106541639A CN201610979244.8A CN201610979244A CN106541639A CN 106541639 A CN106541639 A CN 106541639A CN 201610979244 A CN201610979244 A CN 201610979244A CN 106541639 A CN106541639 A CN 106541639A
- Authority
- CN
- China
- Prior art keywords
- decorating board
- water
- insulation
- ultrathin type
- type decorating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of insulation ultrathin type decorating board, is made up of surface layer, core and cementing layer;Surface layer is any one in cementitious coating felt or alkali-free glass fibre felt;Core is without any one in glue or impregnation alkali-free glass fibre grid;Cementing layer is mixed by inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change microcapsule and auxiliary aid.The ultrathin decorating board thickness prepared using the present invention arbitrarily can be controlled, and 3mm plates heat conductivity is less than 0.07W/mK.Various dalles made by all kinds of coating of surface spraying, true mineral varnish in this substrate etc. have excellent thermal and insulating performance, eliminate heat-insulation mortar bed compared to traditional " thermal insulation mortar coating ornamental surface system ", and it is simple to construct, and cost performance is projected.
Description
Technical field
The present invention relates to a kind of insulation ultrathin type decorating board, more particularly to a kind of to be used for high-rise outer wall, abnormal shape
The ornamental decorative heat preservation integrated board in the positions such as face, belongs to building thermal insulation material field.
Background technology
With the every field of the society that deepens continuously of energy-saving and emission-reduction theory, building heat preservation also becomes heat at present naturally
Point, and the conventional mode of building heat preservation is three layers of insulation construction using " heat-insulation layer-screed-coat-decorative layer " at present, this guarantor
Warm structure needs at least three road working procedures, long construction period, high cost, and the conventional organic heat-insulating plate of wall thermal insulating at present,
The heat of such as EPS, XPS, polyurethane sheet etc., these materials and the levelling screed of wall inorganic material, especially insulation layer surface
The situation for metope cracking is deposited during expansion coefficient difference is larger, therefore the summer is recycled for a long time in the winter, even coming off, service life have
Limit;Although and the integrated plate for heat insulation currently promoted overcomes organic layer-inorganic layer coefficient of thermal expansion differences to a certain extent
Different big problem, but higher cost, heat-insulation layer are exposed that its service life and product promotion are still govern the shortcomings of outer.
The content of the invention
For the problems referred to above, the invention discloses a kind of insulation ultrathin type decorating board, by surface layer, core and gluing
Layer composition, it is characterised in that:
Described surface layer is:Any one in cementitious coating felt or alkali-free glass fibre felt;
Described core is:Without any one in glue or impregnation alkali-free glass fibre grid, more specifically, grammes per square metre be 60~
160g/m2;
Described cementing layer is:By inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change microcapsule
And auxiliary aid is mixed, more specifically, each component percentage by weight is:1:(0.1-0.3):(0.2-0.5):
(0.005-0.01):(0.01-0.05):(0.017-0.095);
Described inorganic gel materials are:Mixed by portland cement, Gypsum Fibrosum, flyash, fire retardant, more specifically, respectively
Weight percentages are:1:(0.1~0.3):(0.5-1.5):(0.05-0.2);
Described auxiliary aid is:Formed by water reducer, Propylene Glycol, early strength agent compounding, more specifically, each component percentage by weight
For:1:(3.5-5):(1.5-2).
Described water-based emulsion is alkaline-resisting pure-acrylic emulsion, alkaline-resisting styrene-acrylic emulsion, any one in alkaline-resisting acetate emulsion
Plant or several.
Described hollow beads are organosilicon ceramic fine bead of the particle diameter between 30-150um, silicone glass microballon, powder
One or more in coal ash hollow beads.
The acrylate wax phase change Microcapsules Size be 30-150um, paraffin content>70%.
Described fire retardant is aluminium hydroxide, magnesium hydroxide, water-soluble poly ammonium phosphate, one or more in red phosphorus.
A kind of insulation ultrathin type decorating board disclosed by the invention, adds hollow beads and paraffin microcapsule in formula
Material, hollow beads have the effect for intercepting external heat conduction, reducing material thermal conductivity, and paraffin microcapsule can on a small quantity
Penetrate into the heat absorption of sheet material, it is to avoid excessive accumulation of heat heat conduction temperature rises so as to reduce the heat-insulated effect of hollow beads inside sheet material
Really, the two cooperates, and plays good heat-blocking action, Jing actual tests, thin plate its heat conductivity of 3mm<0.07 W/m·
K, it is suitable with 1cm thermal insulation mortar effects, with excellent heat insulation effect.
Description of the drawings
Fig. 1 is a kind of insulation ultrathin type decorating board structural representation disclosed in this invention.
Reference:1- surface layers, 2- cores, 3- cementing layers, 4- hollow minute particle, 5- acrylate wax phase change microcapsules.
Specific embodiment
In order that the purpose of the present invention, technical scheme become more apparent, below in conjunction with specific embodiment, invention is carried out
Further describe.
Embodiment 1.
It is surface layer from cementitious coating felt.
It is core from impregnation alkali-free glass fibre grid, grammes per square metre is 60g/m2。
Gel rubber material:Prepared from P.O32.5 cement, Gypsum Fibrosum, one-level flyash and aluminium hydrate powder, four weight ratios
Example be:1:0.2:0.8:0.1.
Auxiliary aid:Prepared from water reducer, Propylene Glycol and early strength agent, three's part by weight is:1:3.5:1.5.
Cementing layer:From gel rubber material, alkaline-resisting pure-acrylic emulsion, water, ceramic fine bead, acrylate paraffin microcapsule and supporting
Auxiliary agent, percentage by weight is:1:0.2:0.3:0.005:0.01:0.017.
By above-mentioned material Jing 2mm forming machine molding, you can obtain the insulation ultrathin type decorating board that thickness is 2mm.
Embodiment 2.
It is surface layer from cementitious coating felt.
From being core without glue alkali-free glass fibre grid, grammes per square metre is 80g/m2。
Gel rubber material:Prepared from P.O42.5 cement, Gypsum Fibrosum, one-level flyash and water-soluble poly ammonium phosphate, four weights
Amount ratio is:1:0.15:0.9:0.05.
Auxiliary aid:Prepared from water reducer, Propylene Glycol and early strength agent, three's part by weight is:1:3:2.
Cementing layer:From gel rubber material, alkaline-resisting styrene-acrylic emulsion, water, glass microballoon, acrylate paraffin microcapsule and supporting
Auxiliary agent, percentage by weight is:1:0.2:0.4:0.01:0.03:0.04.
By above-mentioned material Jing 3mm forming machine molding, you can obtain the insulation ultrathin type decorating board that thickness is 3mm.
Embodiment 3.
Inorfil glass felt is selected to be surface layer.
It is core from impregnation alkali-free glass fibre grid, grammes per square metre is 100g/m2。
Gel rubber material:Prepared from P.O42.5 cement, Gypsum Fibrosum, one-level flyash and magnesium hydroxide powder, four weight ratios
Example be:1:0.3:1.4:0.15.
Auxiliary aid:Prepared from water reducer, Propylene Glycol and early strength agent, three's part by weight is:1:4:2.
Cementing layer:From gel rubber material, alkaline-resisting acetate emulsion, water, glass microballoon, acrylate paraffin microcapsule and
Auxiliary aid, percentage by weight is:1:0.3:0.5:0.01:0.05:0.095.
By above-mentioned material Jing 4mm forming machine molding, you can obtain the insulation ultrathin type decorating board that thickness is 4mm.
Above example is only the preferable embodiment of the present invention, but and be not used to the constraint present invention, but in order to easy
Understand implementation of the present invention.The technical staff in any building thermal insulation material field, is being taken off without departing from the present invention
Under the premise of the spirit shown, equivalent variations that part details is made, replace, within the scope of protection of the invention.
Claims (5)
1. a kind of insulation ultrathin type decorating board, is made up of surface layer, core and cementing layer, it is characterised in that:
Described surface layer is:Any one in cementitious coating felt or alkali-free glass fibre felt;
Described core is:Without any one in glue or impregnation alkali-free glass fibre grid, more specifically, grammes per square metre be 60~
160g/m2;
Described cementing layer is:By inorganic gel materials, water-based emulsion, water, hollow beads, acrylate wax phase change microcapsule
And auxiliary aid is mixed, more specifically, each component percentage by weight is:1:(0.1-0.3):(0.2-0.5):
(0.005-0.01):(0.01-0.05):(0.017-0.095);
Described inorganic gel materials are:Mixed by portland cement, Gypsum Fibrosum, flyash, fire retardant, more specifically, respectively
Weight percentages are:1:(0.1~0.3):(0.5-1.5):(0.05-0.2);
Described auxiliary aid is:Formed by water reducer, Propylene Glycol, early strength agent compounding, more specifically, each component percentage by weight
For:1:(3.5-5):(1.5-2).
2. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that:Described water-based emulsion
For any one or a few in alkaline-resisting pure-acrylic emulsion, alkaline-resisting styrene-acrylic emulsion, alkaline-resisting acetate emulsion.
3. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that:Described hollow beads
One kind in the organosilicon ceramic fine bead for being particle diameter between 30-150um, silicone glass microballon, flyash hollow beads or
It is several.
4. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that:The acrylate stone
Wax phase-change microcapsule particle diameter be 30-150um, paraffin content>70%.
5. a kind of insulation ultrathin type decorating board according to claim 1, it is characterised in that:Described fire retardant is
One or more in aluminium hydroxide, magnesium hydroxide, water-soluble poly ammonium phosphate, red phosphorus.