CN106541005A - For the cavity filling device and its using method of hollow aluminium section bar bending process - Google Patents
For the cavity filling device and its using method of hollow aluminium section bar bending process Download PDFInfo
- Publication number
- CN106541005A CN106541005A CN201610891337.5A CN201610891337A CN106541005A CN 106541005 A CN106541005 A CN 106541005A CN 201610891337 A CN201610891337 A CN 201610891337A CN 106541005 A CN106541005 A CN 106541005A
- Authority
- CN
- China
- Prior art keywords
- aluminium sheet
- aluminium
- section bar
- hollow
- short
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Cavity filling device for hollow aluminium section bar bending process belongs to the hollow forming aluminium section implant of rail vehicle big cross section and its using method field, which is made up of the short aluminium sheet of the long aluminium sheet and polylith rectangle of two pieces of rectangles, and the thickness of two block length aluminium sheets is thicker than short aluminium sheet;The length of short aluminium sheet with the equal length for being filled aluminium section bar, the thickness of short aluminium sheet is identical;The width of long aluminium sheet and short aluminium sheet is equal with the width of hollow molded cavity, and the gross thickness that two block length aluminium sheets and the short aluminium sheet of polylith are stacked together jointly is highly equal with hollow molded cavity;The deformation coefficient of two block length aluminium sheets and the short aluminium sheet of polylith is identical with the deformation coefficient for being filled aluminium section bar.The present invention can be ensured in Forging Process, the flow performance of cavity filling device is always consistent with the hollow aluminium section bar of big cross section, and then cause the overall dimensions and interior cavity shape variable of the hollow aluminium section bar of big cross section after bent into shape effectively optimization and control, and make workpiece global formation quality be significantly improved.
Description
Technical field
The invention belongs to the hollow forming aluminium section implant of rail vehicle big cross section and its using method field, and in particular to
A kind of cavity filling device and its using method for hollow aluminium section bar bending process.
Background technology
As shown in Figure 1 to Figure 3, which includes the hollow molded cavity 1-1 of rectangle and many to the initiating structure of the hollow aluminium section bar of big cross section 1
Individual skirt border structure 1-2, hollow aluminium section bar 1 are needed through machining of bending, and are bent into the curved shape shown in Fig. 4 to Fig. 5.
To ensure that hollow molded cavity 1-1 keeps the cross-sectional outling of its rectangle in press bending process, need to fill to the inside of which
Molding implant.
At present, the hollow forming aluminium section implant of big cross section mostly is fluid corundum, using fluid corundum as filling
During thing, need hollow molded cavity 1-1 one end is closed using welding manner, corundum is inserted from the other end of hollow molded cavity 1-1, gold
Wedged the end of hollow molded cavity 1-1 after emery end-of-fill by operator with timber wedge so as to form near closed hollow ring, prevent Buddha's warrior attendant
Sand flow goes out, and timber wedge is pulled out after terminating by molding, then corundum is poured out.
However, one end that sealing is soldered on hollow molded cavity 1-1 need to also be beaten after press-bending by said method again again
Open, this process wastes time and energy, and be easily caused the welding deformation of 1 workpiece of hollow aluminium section bar.Additionally, by the experience of operator
Judge that the method for the wedging depth of timber wedge is difficult to accurately weigh the density of corundum implant in hollow molded cavity 1-1, to operator
Experience and skill set requirements are high, and personal error is larger, cause the packed density of corundum filling to be difficult to obtain reliable guarantee, and then
Cause the press-bending difficult quality precise control of sky aluminium section bar, defect rate and scrappage high.
The content of the invention
In order to solve the existing section bar bending process using fluid corundum as the hollow forming aluminium section implant of big cross section
Die cavity need to be sealed bending, and be opened die cavity sealed end time after press-bending terminates again by method, and its process steps is numerous
It is trivial, waste time and energy, and easily make the generation welding deformation of hollow aluminium section bar.And by operator experience to filling up Buddha's warrior attendant
In the die cavity of sand, the method personal error of the wedging depth of timber wedge is larger, and causing the packed density of corundum filling to be difficult to obtain can
By ensureing, the press-bending difficult quality precise control of sky aluminium section bar is in turn resulted in, the high technical problem of defect rate and scrappage, this
It is bright that a kind of cavity filling device and its using method for hollow aluminium section bar bending process is provided.
The technical scheme taken by present invention solution technical problem is as follows:
For the cavity filling device of hollow aluminium section bar bending process, its long aluminium sheet and polylith rectangle by two pieces of rectangles
Short aluminium sheet composition, the thickness of this two block lengths aluminium sheet are thicker than the thickness of short aluminium sheet;The length of short aluminium sheet be filled aluminium section bar
Equal length, the thickness of short aluminium sheet are identical;The width of the long aluminium sheet and short aluminium sheet with the hollow molded cavity for being filled aluminium section bar
Width it is equal, two block length aluminium sheets and the short aluminium sheet of the polylith gross thickness being stacked together jointly and the hollow type for being filled aluminium section bar
Chamber it is highly equal;The deformation coefficient of two block length aluminium sheets and the short aluminium sheet of polylith is identical with the deformation coefficient for being filled aluminium section bar.
The length of the two block lengths aluminium sheet is 1.05~1.1 times of short aluminium sheet length, and the thickness of this two block lengths aluminium sheet is short
1.2~1.5 times of aluminium plate thickness.
The two block lengths aluminium sheet includes that left side extends aluminium sheet and right side extends aluminium sheet, and left side extends the two ends of aluminium sheet and is equipped with
Dog hole, the structure that right side extends aluminium sheet are identical with the structure that left side extends aluminium sheet;Two block length aluminium sheets and the short aluminium sheet of polylith
Stacked position relation is:Together with left side prolongation aluminium sheet is stacked on one another with right side prolongation aluminium sheet, other length identical polyliths are short
Aluminium sheet is divided into two groups of A, B, and the short aluminium sheet of A groups of wherein lower floor is overlayed above long aluminium sheet, and the short aluminium sheet of B groups on upper strata overlays the right side
Side extends below aluminium sheet.
Align with the two ends of the hollow molded cavity for being filled aluminium section bar at the two ends of the short aluminium sheet;Left side extends the right side of aluminium sheet
The right alignment with the hollow molded cavity for being filled aluminium section bar, left side is held to extend the left end of aluminium sheet from the hollow type for being filled aluminium section bar
Stretch out in the left end in chamber and hanging;Right side extends the left end of aluminium sheet and the left alignment of the hollow molded cavity for being filled aluminium section bar, right
Side extends the right-hand member of aluminium sheet and stretches out from the right-hand member of hollow molded cavity for being filled aluminium section bar and hanging.
For the using method of the cavity filling device of hollow aluminium section bar bending process, which comprises the steps:
Step one, before hollow aluminium section bar is installed to bender, first the short aluminium sheet of A groups of lower floor is inserted one by one and is filled
In the hollow molded cavity of aluminium section bar, and be laminated on the lower surface inside hollow molded cavity, and make the two ends of the short aluminium sheet of lower floor's A groups with
Align respectively at the two ends of hollow molded cavity;
Step 2, the top insertion hollow type that the lower surface that left side extends aluminium sheet right-hand member is laminated in the short aluminium sheet of lower floor's A groups
Intracavity, and make left side extend aluminium sheet right-hand member alignd with the right-hand member in hollow molded cavity respectively, make left side prolongation aluminium sheet left end from
Stretch out in hollow molded cavity and hanging;
Step 3, the top insertion hollow molded cavity that the lower surface that right side extends aluminium sheet left end is laminated in left side prolongation aluminium sheet
It is interior, and make the left end that right side extends aluminium sheet be alignd with the left end in hollow molded cavity respectively, make the right-hand member of right side prolongation aluminium sheet therefrom
Stretch out in casement chamber and hanging;
Step 4, the short aluminium sheet of B groups on upper strata is inserted in hollow molded cavity one by one and is laminated in right side extend aluminium sheet upper surface
Top, make the short aluminium sheet of B groups on upper strata fill up remaining gap in hollow molded cavity, and make the two ends of the short aluminium sheet of B groups on upper strata equal
Alignd with the two ends in hollow molded cavity respectively, complete the lumen loading operation of hollow aluminium section bar;
Step 5, the hollow aluminium section bar that step 4 has filled aluminium sheet is hung on the operating platform of bender using crane,
Bending and molding is carried out using cavity filling device of the bender according to the actual requirements to hollow aluminium section bar together with its inside, in
After empty forming aluminium section, two operator stand the two ends of hollow aluminium section bar after shaping respectively, operator's sled
Thick stick insertion left side extends the dog hole of aluminium sheet left end, and extraction left side extends aluminium sheet in hollow molded cavity, and another operator prizes
Thick stick insertion right side extends the dog hole of aluminium sheet right-hand member, and promotes right side to extend aluminium sheet to the left, and two operator make a concerted effort left side
Extend aluminium sheet and right side extends aluminium sheet and synchronously extracts out from hollow type intracavity;
Step 6, the short aluminium sheet of remaining polylith rectangle in hollow molded cavity is taken out one by one by two operator, so it is complete
Into the taking-up operation of hollow aluminium section bar lumen loading thing.
The invention has the beneficial effects as follows:The cavity filling device for being used for hollow aluminium section bar bending process is adopted and hollow aluminum
The identical multilamellar aluminum layer poststack of deformation coefficient of section bar collectively forms the molding implant of hollow molded cavity, so as to ensure
In Forging Process, the mechanical performance such as flow of the cavity filling device is always consistent with the hollow aluminium section bar of big cross section, enters
And cause bent into shape after the hollow aluminium section bar of big cross section overall dimensions and interior cavity shape variable effectively optimization and control, and
Workpiece global formation quality is made to be significantly improved.
Contribute to the Stress Release during bending between each layer aluminium sheet in the form of multilamellar aluminum layer is stacked and put,
The taking-up one by one of the multilamellar aluminium sheet therefrom casement intracavity after being conducive to bending.Left side with dog hole extends aluminium sheet and right side extends
Aluminium sheet extends and is suspended on outside hollow molded cavity, and the dismounting for being cavity filling device both which from die cavity provides extra
Force so that dismounting operation is more facilitated.After each piece of deformation, aluminium sheet can recover rectangular flat by deformation correction again
Plate, and recycle, its deformation correcting process simple and fast, it is easy to control, therefore production cost can be saved, increase the benefit.
The cavity filling device of the present invention can effectively overcome that old corundum fill process Forming Quality is poor, production efficiency
The technological deficiencies such as low, easily to make hollow aluminium section bar generation welding deformation, press-bending difficult quality precise control, the cavity filling are filled
The using method flow process put is succinct, time saving and energy saving, it is easy to accomplish, and substantially reduce can the probability of generation personal error, so as to
It is precisely controlled can the press-bending quality of sky aluminium section bar, reduction in the numbers of seconds and scrappage.
In addition this be used for cavity filling device of hollow aluminium section bar bending process also have filling and the good manufacturability taken out,
It is simple and practical, it is easy to operate, it is with low cost, it is easy to the advantages of popularizing.
Description of the drawings
Fig. 1 is the axonometric chart before the hollow aluminium section bar bending of big cross section;
Fig. 2 is the front view of Fig. 1;
Fig. 3 is the right view of Fig. 2;
Fig. 4 is the axonometric chart after the hollow aluminium section bar bending of big cross section;
Fig. 5 is the front view of Fig. 4;
Fig. 6 is schematic perspective view of the present invention for the cavity filling device of hollow aluminium section bar bending process;
Fig. 7 is the exploded perspective view of Fig. 6;
Fig. 8 is the partial enlarged drawing of the middle I parts of Fig. 6;
Fig. 9 is application schematic diagram of the present invention for the cavity filling device of hollow aluminium section bar bending process;
Figure 10 is the B-B generalized sections in Fig. 9;
Figure 11 is the left view in Fig. 9;
Figure 12 is the B-B generalized sections in Figure 11.
Specific embodiment
Below in conjunction with the accompanying drawings the present invention is described in further details.
As shown in Figure 6 to 8, the present invention is used for the cavity filling device 2 of hollow aluminium section bar bending process by two pieces of rectangles
Long aluminium sheet 2-1 and polylith rectangle short aluminium sheet 2-2 composition, the thickness of the thickness of this two block length aluminium sheet 2-1 than short aluminium sheet 2-2
It is thick.The length of short aluminium sheet 2-2 with the equal length for being filled aluminium section bar, the thickness of short aluminium sheet 2-2 is identical.The long aluminium sheet 2-
1 and short aluminium sheet 2-2 width is equal with the width of the hollow molded cavity for being filled aluminium section bar, two block length aluminium sheet 2-1 and eight pieces short
The gross thickness that aluminium sheet 2-2 is stacked together jointly is highly equal with the hollow molded cavity for being filled aluminium section bar.Two block length aluminium sheet 2-1
It is identical with the deformation coefficient for being filled aluminium section bar with the deformation coefficient of eight pieces short aluminium sheet 2-2, so as to ensure in Forging Process,
The mechanical performances such as the flow of the cavity filling device 2 are always consistent with the hollow aluminium section bar 1 of big cross section, and then cause to bend
After molding the overall dimensions and interior cavity shape variable of the hollow aluminium section bar of big cross section 1 effectively optimize and control, and make workpiece whole
Body formed quality is significantly improved.
The length of two block length aluminium sheet 2-1 is 1.1 times of short aluminium sheet length, and the thickness of this two block length aluminium sheet 2-1 is short aluminium sheet
1.5 times of 2-2 thickness.
Two block length aluminium sheet 2-1 include that left side extends aluminium sheet 2-1-1 and right side extends aluminium sheet 2-1-2, and left side extends aluminium sheet 2-
The two ends of 1-1 are equipped with dog hole, and the structure that right side extends aluminium sheet 2-1-2 is identical with the structure that left side extends aluminium sheet 2-1-1.
The stacked position relation of two block length aluminium sheet 2-1 and eight pieces short aluminium sheet 2-2 is:Left side extends aluminium sheet 2-1-1 and right side extends aluminium sheet
2-1-2 is stacked on one another together, and the short aluminium sheet 2-2 of eight pieces of other length identicals is divided into two groups of A, B, the wherein short aluminum of A groups of lower floor
Plate is overlayed above long aluminium sheet 2-1, and the short aluminium sheet of B groups on upper strata overlays right side and extends below aluminium sheet 2-1-2.Using multilamellar
Aluminum layer stacks the Stress Release that the form put contributes to during bending between each layer aluminium sheet, many after being also beneficial to bend
Layer aluminium sheet is taken out one by one.
Align with the two ends of the hollow molded cavity for being filled aluminium section bar at the two ends of short aluminium sheet 2-2.Left side extends aluminium sheet 2-1-1
Right-hand member and the hollow molded cavity for being filled aluminium section bar right alignment, left side extends the left end of aluminium sheet 2-1-1 from being filled aluminium profiles
Stretch out in the left end of the hollow molded cavity of material and hanging.Right side extends the left end and the hollow type for being filled aluminium section bar of aluminium sheet 2-1-2
The left alignment in chamber, right side extend the right-hand member of aluminium sheet 2-1-2 and from the right-hand member of hollow molded cavity for being filled aluminium section bar stretch out and hang
It is empty.
As shown in Fig. 9 to Figure 12, using method of the present invention for the cavity filling device of hollow aluminium section bar bending process
Comprise the steps:
Step one, before hollow aluminium section bar is installed to bender, first the short aluminium sheet of A groups of lower floor is inserted one by one and is filled
In the hollow molded cavity 1-1 of aluminium section bar 1, and on the lower surface being laminated in inside hollow molded cavity 1-1, and make the short aluminium sheet of lower floor's A groups
Alignd with the two ends of hollow molded cavity 1-1 respectively at two ends.
Step 2, by left side extend aluminium sheet 2-1-1 right-hand members lower surface be laminated in the short aluminium sheet of lower floor's A groups top insert in
In the 1-1 of casement chamber, and make the right-hand member that left side extends aluminium sheet 2-1-1 be alignd with the right-hand member of 1-1 in hollow molded cavity respectively, prolong left side
The left end of long aluminium sheet 2-1-1 is stretched out from hollow molded cavity 1-1 and hanging.
Step 3, by right side extend aluminium sheet 2-1-2 left ends lower surface be laminated in left side extend aluminium sheet 2-1-1 top insert
Enter in hollow molded cavity 1-1, and make the left end that right side extends aluminium sheet 2-1-2 be alignd with the left end of 1-1 in hollow molded cavity respectively, make the right side
Side extends the right-hand member of aluminium sheet 2-1-2 and stretches out from hollow molded cavity 1-1 and hanging.
Step 4, by the short aluminium sheet of B groups on upper strata inserted in hollow molded cavity 1-1 one by one and be laminated in right side extend aluminium sheet 2-1-
The top of 2 upper surfaces, makes the short aluminium sheet of B groups on upper strata fill up remaining gap in hollow molded cavity 1-1, and makes the short aluminum of B groups on upper strata
The two ends of plate are alignd respectively with the two ends of 1-1 in hollow molded cavity, complete the lumen loading operation of hollow aluminium section bar 1.
Step 5, the hollow aluminium section bar 1 that step 4 has filled aluminium sheet is hung on the operating platform of bender using crane,
Bending and molding is carried out using cavity filling device 2 of the bender according to the actual requirements to hollow aluminium section bar 1 together with its inside,
After 1 molding of hollow aluminium section bar, two operator stand the two ends of hollow aluminium section bar 1 after shaping respectively, an operator
Extraction left side in the dog hole that left side extends aluminium sheet 2-1-1 left ends, and hollow molded cavity 1-1 is inserted with crowbar and extends aluminium sheet 2-1-1, separately
One operator inserts the dog hole that right side extends aluminium sheet 2-1-2 right-hand members with crowbar, and promotes right side to extend aluminium sheet 2- to the left
1-2, two operator make a concerted effort for left side to extend aluminium sheet 2-1-1 and right side prolongation aluminium sheet 2-1-2 is synchronous from hollow molded cavity 1-1
Extract out.
Step 6, the short aluminium sheet 2-2 of remaining polylith rectangle in hollow molded cavity 1-1 is taken out one by one by two operator,
And then complete the taking-up operation of 1 lumen loading thing of hollow aluminium section bar.
Hereafter, to cavity filling device 2 in each block of aluminium sheet respectively implement deformation correction so as to revert to again square
Shape flat board, you can complete deformation and resume operation, realizes recycling to cavity filling device 2, so as to save production cost, carries
High efficiency and economic benefit.
Claims (5)
1. the cavity filling device of hollow aluminium section bar bending process is used for, it is characterised in that the cavity filling device (2) is by two pieces
Short aluminium sheet (2-2) composition of the long aluminium sheet (2-1) and polylith rectangle of rectangle, the thickness of this two block length aluminium sheet (2-1) is than short aluminium sheet
(2-2) thickness is thick;The length of short aluminium sheet (2-2) with the equal length for being filled aluminium section bar, the thickness phase of short aluminium sheet (2-2)
Together;The width of the long aluminium sheet (2-1) and short aluminium sheet (2-2) is equal with the width of the hollow molded cavity for being filled aluminium section bar, and two
Block length aluminium sheet (2-1) and the short aluminium sheet of polylith (2-2) gross thickness being stacked together jointly and the hollow molded cavity for being filled aluminium section bar
It is highly equal;The deformation coefficient of two block length aluminium sheets (2-1) and the short aluminium sheet of polylith (2-2) with the deformation system for being filled aluminium section bar
Number is identical.
2. the cavity filling device of hollow aluminium section bar bending process is used for as claimed in claim 1, it is characterised in that described two
The length of block length aluminium sheet (2-1) is 1.05~1.1 times of short aluminium sheet length, and the thickness of this two block length aluminium sheet (2-1) is short aluminium sheet
(2-2) 1.2~1.5 times of thickness.
3. the cavity filling device of hollow aluminium section bar bending process is used for as claimed in claim 1 or 2, it is characterised in that institute
State two block length aluminium sheets (2-1) and extend aluminium sheet (2-1-1) and right side prolongation aluminium sheet (2-1-2) including left side, left side extends aluminium sheet (2-
Two ends 1-1) are equipped with dog hole, and the structure that right side extends aluminium sheet (2-1-2) is complete with the structure that left side extends aluminium sheet (2-1-1)
It is identical;The stacked position relation of two block length aluminium sheets (2-1) and the short aluminium sheet of polylith (2-2) is:Left side extends aluminium sheet (2-1-1) and the right side
Side extends aluminium sheet (2-1-2) and is stacked on one another together, and the short aluminium sheet (2-2) of other length identical polyliths is divided into two groups of A, B, wherein
The short aluminium sheet of A groups of lower floor is overlayed above long aluminium sheet (2-1), and the short aluminium sheet of B groups on upper strata overlays right side and extends aluminium sheet (2-1-
2) below.
4. the cavity filling device of hollow aluminium section bar bending process is used for as claimed in claim 3, it is characterised in that described short
Align with the two ends of the hollow molded cavity for being filled aluminium section bar at the two ends of aluminium sheet (2-2);Left side extends the right-hand member of aluminium sheet (2-1-1)
With the right alignment of the hollow molded cavity for being filled aluminium section bar, left side extends the left end of aluminium sheet (2-1-1) from being filled aluminium section bar
Stretch out in the left end of hollow molded cavity and hanging;Right side extends the left end and the hollow molded cavity for being filled aluminium section bar of aluminium sheet (2-1-2)
Left alignment, right side extend aluminium sheet (2-1-2) right-hand member from the right-hand member of hollow molded cavity for being filled aluminium section bar stretch out and hang
It is empty.
5. the using method of the cavity filling device of hollow aluminium section bar bending process is used for as described in any one of claim 1-4,
Characterized in that, the method comprises the steps:
Step one, before hollow aluminium section bar is installed to bender, first the short aluminium sheet of A groups of lower floor is inserted one by one and is filled aluminium profiles
In the hollow molded cavity (1-1) of material (1), and it is laminated on the internal lower surface of hollow molded cavity (1-1), and makes the short aluminium sheet of lower floor's A groups
Two ends alignd with the two ends of hollow molded cavity (1-1) respectively;
Step 2, left side is extended aluminium sheet (2-1-1) right-hand member lower surface be laminated in the short aluminium sheet of lower floor's A groups top insertion it is hollow
In die cavity (1-1), and make the right-hand member that left side extends aluminium sheet (2-1-1) be alignd with the right-hand member of (1-1) in hollow molded cavity respectively, make a left side
Side extends the left end of aluminium sheet (2-1-1) and stretches out from hollow molded cavity (1-1) and hanging;
Step 3, right side is extended aluminium sheet (2-1-2) left end lower surface be laminated in left side extend aluminium sheet (2-1-1) top insert
Enter in hollow molded cavity (1-1), and make the left end on right side prolongation aluminium sheet (2-1-2) right respectively with the left end of (1-1) in hollow molded cavity
Together, the right-hand member that right side extends aluminium sheet (2-1-2) is made to stretch out from hollow molded cavity (1-1) and hanging;
Step 4, by the short aluminium sheet of B groups on upper strata inserted in hollow molded cavity (1-1) one by one and be laminated in right side extend aluminium sheet (2-1-
2) top of upper surface, makes the short aluminium sheet of B groups on upper strata fill up remaining gap in hollow molded cavity (1-1), and makes the B groups on upper strata short
The two ends of aluminium sheet are alignd respectively with the two ends of (1-1) in hollow molded cavity, complete the lumen loading operation of hollow aluminium section bar (1);
Step 5, the hollow aluminium section bar (1) that step 4 has filled aluminium sheet is hung on the operating platform of bender using crane, profit
It is bent into cavity filling device (2) of the bender according to the actual requirements to hollow aluminium section bar (1) together with its inside
Type, after the molding of hollow aluminium section bar (1), two operator stand the two ends of hollow aluminium section bar (1) after shaping respectively, a behaviour
Make personnel and the dog hole that left side extends aluminium sheet (2-1-1) left end is inserted with crowbar, and the interior left side of extracting of hollow molded cavity (1-1) extends aluminum
Plate (2-1-1), another operator insert the dog hole that right side extends aluminium sheet (2-1-2) right-hand member with crowbar, and promote to the left
Right side extends aluminium sheet (2-1-2), and two operator make a concerted effort for left side to extend aluminium sheet (2-1-1) and right side extends aluminium sheet (2-1-
2) it is synchronous to extract out from hollow molded cavity (1-1);
Step 6, the short aluminium sheet (2-2) of remaining polylith rectangle in hollow molded cavity (1-1) is taken out one by one by two operator,
And then complete the taking-up operation of hollow aluminium section bar (1) lumen loading thing.