CN106531010A - Manufacturing process of signboard - Google Patents
Manufacturing process of signboard Download PDFInfo
- Publication number
- CN106531010A CN106531010A CN201611228857.4A CN201611228857A CN106531010A CN 106531010 A CN106531010 A CN 106531010A CN 201611228857 A CN201611228857 A CN 201611228857A CN 106531010 A CN106531010 A CN 106531010A
- Authority
- CN
- China
- Prior art keywords
- mark
- signboard
- plate
- dried
- mark plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a manufacturing process of a signboard. The manufacturing process is characterized in that the reflective signboard is manufactured by virtue of such processes as conducting surface treatment on the signboard, cutting the signboard, wiping the signboard with alcohol, grinding the signboard, wiping the signboard with alcohol, etching the signboard, printing the signboard, conducting drying treatment, covering the signboard with a film, inspecting the signboard, packaging the signboard and the like. According to the manufacturing process provided by the invention, by wiping the signboard with the alcohol twice, the surface smoothness of the signboard can be improved; by grinding the signboard with reflecting powder on the surface thereof, the reflecting powder can be mixed in the signboard, so that the reflecting performance of the signboard is improved; and by covering the reflecting film on the signboard which is printed and dried, the reflecting performance of the signboard is further enhanced, so that the display effect of the signboard is improved and the service life of the signboard is prolonged.
Description
Technical field
The present invention relates to Sign Board technical field, specifically a kind of processing technology of Sign Board.
Background technology
Label is exactly, for the direction board for making mark, have the contents such as word, pattern to play the side of indicating above as its name suggests
To the effect with warning.Common label has electroforming label, company's label, copper word label, Warning board, with the use of nameplate
Place is more and more, and the processing technology of nameplate is also constantly changing progress.But existing Sign Board is most without reflective work(
Can, not only it is not easy to the observation of people, is also not easy to improve the bandwagon effect of Sign Board, a small amount of Sign Board with reflection action
It is that reflectorized material is attached on Sign Board mostly, the not good capability and performance for reducing Sign Board of the quality puted up, while there is also
Manufacture difficulty is big, the deficiency that make efficiency is low.
The content of the invention
The purpose of the present invention is that have reflection action, a small amount of reflecting marking board making for many inequalities of existing Sign Board
Manufacture difficulty that process is present is big, make efficiency is low, the quality of reflecting marking board makes not good problem, there is provided a kind of operation side
Just, manufacture difficulty is little, the processing technology of the Sign Board that high working efficiency, Sign Board fabricating quality are good.
Present invention solves the technical problem that the technical scheme taken is：
A kind of processing technology of Sign Board, it is characterised in that described manufacture method is comprised the following steps：
The first step, marking plate surface treatment：The spot of the mark plate surface of metal material, oil stain, wax stain are cleaned with cleaning solution, then
Chemical derusting, oil removing are carried out with rust cleaning water, the cloth for then cleaning is stained with the surface of degreaser erasing marking plate and at once with another
The cloth of cleaning is dried；
Second step, cutting：Marking plate after surface treatment is cut into into mark plate on request；
3rd step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 62%；
4th step, polishing：Reflective powder is smeared into uniform on mark plate, THICKNESS CONTROL is in 5mm, anti-to scribbling using polisher
The mark plate of light powder is polished, and polishing rotating speed is controlled to 210r/min, and polishing time control is 40min；
5th step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 77%；
6th step, etching：Mark plate after surface treatment is etched using etching solution in etching machine, etching solution is set
The liquor ferri trichloridi that Baume degrees are 32 degree is set to, the rotating speed of etching machine is controlled to 107r/s；
7th step, will be spraying on phthalic resin mark plate after the etching uniform, make phthalic resin in mark
The surface thickness for knowing plate is uniform, after anti-corrosion material spraying is uniform, mark plate is dried 45min at 52 DEG C；
8th step, printing：The word and/or figure that need mark are printed on into the mark after baking vanish by the way of silk screen printing
On panel surface；
9th step, dried：Mark plate after printing is put in drying baker to be dried or be put in baking room and is toasted, dried
At 177 DEG C, baking time is 25min to roasting temperature；
Tenth step, overlay film：Mark panel surface with laminating machine after dried carries out covering pressure engineering reflecting film, and mark is obtained
Know board finished product；
11st step, inspection, packaging：Mark finished product after overlay film is tested, what inspection occurred in whole technological process
Dirt pits, bubble, situation is not in place printed.
Further, described marking plate is set to one kind of high molecule plastic class or metal apoplexy due to endogenous wind.
Beneficial effect：The present invention carries out alcohol wipe twice to marking plate, can remove the impurity that mark plate surface has, improve
The fineness of mark plate surface, and then improve the fabricating quality of Sign Board, by reflective powder mark plate surface with marking plate together
Polishing, enables reflective powder to circulate in marking plate, so that marking plate has certain reflection action, improves the reflective of Sign Board
Performance, after marking plate printing, being dried, carries out covering pressure reflective membrane to marking plate, further increases the reflective function of Sign Board,
Strengthen the capability and performance of Sign Board, improve the bandwagon effect of Sign Board, extend the service life of Sign Board, meanwhile, this making work
Skill also has the advantages that manufacture difficulty is little, is easy to grasp, make efficiency is high.
Specific embodiment
Hereinafter the present invention will be described in detail.
Embodiment one：
A kind of processing technology of Sign Board, it is characterised in that：Described manufacture method is comprised the following steps：
The first step, marking plate surface treatment：The spot of the mark plate surface of metal material, oil stain, wax stain are cleaned with cleaning solution, then
Chemical derusting, oil removing are carried out with rust cleaning water, the cloth for then cleaning is stained with the surface of degreaser erasing marking plate and at once with another
The cloth of cleaning is dried；
Second step, cutting：Marking plate after surface treatment is cut into into mark plate on request；
3rd step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 68%；
4th step, polishing：Reflective powder is smeared into uniform on mark plate, THICKNESS CONTROL is in 2mm, anti-to scribbling using polisher
The mark plate of light powder is polished, and polishing rotating speed is controlled to 230r/min, and polishing time control is 30min；
5th step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 75%；
6th step, etching：Mark plate after surface treatment is etched using etching solution in etching machine, etching solution is set
The liquor ferri trichloridi that Baume degrees are 39 degree is set to, the rotating speed of etching machine is controlled to 103r/s；
7th step, printing：The word and/or figure that need mark are printed on into the mark after baking vanish by the way of silk screen printing
On panel surface；
8th step, dried：Mark plate after printing is put in drying baker to be dried or be put in baking room and is toasted, dried
At 174 DEG C, baking time is 20min to roasting temperature；
9th step, overlay film：Mark panel surface with laminating machine after dried carries out covering pressure engineering reflecting film, and mark is obtained
Know board finished product；
Tenth step, inspection, packaging：Mark finished product after overlay film is tested, the dirt occurred in whole technological process is checked
Point, bubble, situation is not in place printed.
Embodiment two：
A kind of processing technology of Sign Board, it is characterised in that：Described manufacture method is comprised the following steps：
The first step, marking plate surface treatment：The spot of the mark plate surface of glass material, oil stain, wax stain are cleaned with cleaning solution, then
Chemical derusting, oil removing are carried out with rust cleaning water, the cloth for then cleaning is stained with the surface of degreaser erasing marking plate and at once with another
The cloth of cleaning is dried；
Second step, cutting：Marking plate after surface treatment is cut into into mark plate on request；
3rd step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 75%；
4th step, polishing：Reflective powder is smeared into uniform on mark plate, THICKNESS CONTROL is in 3mm, anti-to scribbling using polisher
The mark plate of light powder is polished, and polishing rotating speed is controlled to 240r/min, and polishing time control is 25min；
5th step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 76%；
6th step, etching：Mark plate after surface treatment is etched using etching solution in etching machine, etching solution is set
The liquor ferri trichloridi that Baume degrees are 40 degree is set to, the rotating speed of etching machine is controlled to 102r/s；
7th step, printing：The word and/or figure that need mark are printed on into the mark after baking vanish by the way of silk screen printing
On panel surface；
8th step, dried：Mark plate after printing is put in drying baker to be dried or be put in baking room and is toasted, dried
At 173 DEG C, baking time is 24min to roasting temperature；
9th step, overlay film：Mark panel surface with laminating machine after dried carries out covering pressure engineering reflecting film, and mark is obtained
Know board finished product；
Tenth step, inspection, packaging：Mark finished product after overlay film is tested, the dirt occurred in whole technological process is checked
Point, bubble, situation is not in place printed.
Embodiment three：
A kind of processing technology of Sign Board, it is characterised in that：Described manufacture method is comprised the following steps：
The first step, marking plate surface treatment：The spot of the mark plate surface of acrylic material, oil stain, wax stain are cleaned with cleaning solution,
Chemical derusting, oil removing are carried out with rust cleaning water again, the cloth for then cleaning is stained with the surface of degreaser erasing marking plate and at once with separately
The cloth of one cleaning is dried；
Second step, cutting：Marking plate after surface treatment is cut into into mark plate on request；
3rd step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 78%；
4th step, polishing：Reflective powder is smeared into uniform on mark plate, THICKNESS CONTROL is in 4mm, anti-to scribbling using polisher
The mark plate of light powder is polished, and polishing rotating speed is controlled to 250r/min, and polishing time control is 50min；
5th step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 85%；
6th step, etching：Mark plate after surface treatment is etched using etching solution in etching machine, etching solution is set
The liquor ferri trichloridi that Baume degrees are 43 degree is set to, the rotating speed of etching machine is controlled to 108r/s；
7th step, printing：The word and/or figure that need mark are printed on into the mark after baking vanish by the way of silk screen printing
On panel surface；
8th step, dried：Mark plate after printing is put in drying baker to be dried or be put in baking room and is toasted,
45min is toasted at 73 DEG C；
9th step, overlay film：Mark panel surface with laminating machine after dried carries out covering pressure engineering reflecting film, and mark is obtained
Know board finished product；
Tenth step, inspection, packaging：Mark finished product after overlay film is tested, the dirt occurred in whole technological process is checked
Point, bubble, situation is not in place printed.
The foregoing is only presently preferred embodiments of the present invention, not to limit the present invention, all spirit in the present invention and
Any modification, equivalent and improvement for being made within principle etc., should be included within the scope of the present invention.
Part that the present invention does not relate to is same as the prior art or can be realized using prior art.
Claims (1)
1. a kind of processing technology of Sign Board, it is characterised in that described manufacture method is comprised the following steps：
The first step, marking plate surface treatment：The spot of the mark plate surface of metal material, oil stain, wax stain are cleaned with cleaning solution, then
Chemical derusting, oil removing are carried out with rust cleaning water, the cloth for then cleaning is stained with the surface of degreaser erasing marking plate and at once with another
The cloth of cleaning is dried；
Second step, cutting：Marking plate after surface treatment is cut into into mark plate on request；
3rd step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 62%；
4th step, polishing：Reflective powder is smeared into uniform on mark plate, THICKNESS CONTROL is in 5mm, anti-to scribbling using polisher
The mark plate of light powder is polished, and polishing rotating speed is controlled to 210r/min, and polishing time control is 40min；
5th step, alcohol wipe：The mark plate after cutting is wiped from the ethanol that concentration is 77%；
6th step, etching：Mark plate after surface treatment is etched using etching solution in etching machine, etching solution is set
The liquor ferri trichloridi that Baume degrees are 32 degree is set to, the rotating speed of etching machine is controlled to 107r/s；
7th step, will be spraying on phthalic resin mark plate after the etching uniform, make phthalic resin in mark
The surface thickness for knowing plate is uniform, after anti-corrosion material spraying is uniform, mark plate is dried 45min at 52 DEG C；
8th step, printing：The word and/or figure that need mark are printed on into the mark after baking vanish by the way of silk screen printing
On panel surface；
9th step, dried：Mark plate after printing is put in drying baker to be dried or be put in baking room and is toasted, dried
At 177 DEG C, baking time is 25min to roasting temperature；
Tenth step, overlay film：Mark panel surface with laminating machine after dried carries out covering pressure engineering reflecting film, and mark is obtained
Know board finished product；
11st step, inspection, packaging：Mark finished product after overlay film is tested, what inspection occurred in whole technological process
Dirt pits, bubble, situation is not in place printed.