CN107331324A - A kind of manufacturing process with night bright reflection function label - Google Patents
A kind of manufacturing process with night bright reflection function label Download PDFInfo
- Publication number
- CN107331324A CN107331324A CN201710693485.0A CN201710693485A CN107331324A CN 107331324 A CN107331324 A CN 107331324A CN 201710693485 A CN201710693485 A CN 201710693485A CN 107331324 A CN107331324 A CN 107331324A
- Authority
- CN
- China
- Prior art keywords
- label
- label plate
- reflective
- sign board
- manufacturing process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacturing process with night bright reflection function label, it is characterised in that：Described there is night bright reflection function label to be fabricated by by processes such as the surface treatment of label plate, cutting, preservative treatment, priming paint overcoat, polishing, alcohol wipe, polishing, alcohol wipe, patch reflective membrane, printing, spraying overcoat, drying process, overlay film, inspection, packagings.The present invention is polished sign board twice, alcohol wipe twice, polishing can improve the profile pattern of sign board for the first time, reflective powder can be polished to the surface of sign board by second of polishing, improve the reflective function of Sign Board, also the impurity that label plate surface has can be removed, improve the finish of label plate surface, and then improve the making quality of label, in sign board printing, after drying, sign board is carried out to cover pressure reflective membrane, further increase the reflective function of label, strengthen the capability and performance of label, also label can be made to be provided with night bright function, extend the service life of label.
Description
Technical field
The present invention relates to Sign Board technical field, specifically a kind of manufacturing process with night bright reflection function label.
Background technology
Label is exactly the direction board for being used to make mark as its name suggests, has the contents such as word, pattern to play the side of indicating above
To the effect with warning.Common label has electroforming label, company's label, copper word label, Warning board, with the use of nameplate
Place is more and more, and the manufacture craft of nameplate also changes progress continuous.But existing Sign Board is most without reflective work(
Can, not only it is not easy to the observation of people, is also not easy to improve the bandwagon effect of Sign Board, a small amount of Sign Board with reflection action
It is that reflectorized material is attached on Sign Board mostly, a kind of patent disclosure night bright reflective length of such as Application No. 201710337354.9
The manufacture method of afterglow sign board, which solves the problem of label service life is short, reflector layer easily comes off, but there is making
The deficiency that difficulty is big, producing efficiency is low, label reflective function is not high.
The content of the invention
The purpose of the present invention is to exist for what existing label was present most without reflection action, a small amount of reflecting marking board
Manufacture difficulty that manufacturing process is present is big, there is provided one kind operation the problem of producing efficiency is low, reflecting label reflective function is not high
It is convenient, manufacture difficulty is small, operating efficiency is high, sign manufacturing quality is good, reflective function is good has night bright reflection function label
Manufacturing process.
Present invention solves the technical problem that the technical scheme taken is：
A kind of manufacturing process with night bright reflection function label, it is characterised in that described manufacturing process comprises the following steps：
A. label plate is surface-treated：Spot, oil stain, the wax stain of label plate surface are cleaned with cleaning solution, then is carried out with derusting water
Chemical derusting, oil removing, the surface of degreaser erasing sign board is then stained with the cloth of cleaning and is smeared at once with the cloth of another cleaning
It is dry；
B. cut：Sign board after surface treatment is cut into label plate on request；
C. preservative treatment：The label plate surface spraying of anti-corrosion material after dicing is uniform, make anti-corrosion material in label plate
Surface thickness is uniform, and after anti-corrosion material spraying is uniform, label plate is dried into 20-30min at 50-55 DEG C；
D. priming paint overcoat：To the epoxy vehicle paint base that dried label plate surface spraying thickness is 0.006-0.008mm,
Label plate is dried into 20-30min in the environment of 55-60 DEG C after spray-applied primer；
E. polish：Label plate after spray-applied primer is polished the surface of label plate using sand paper；
F. alcohol wipe：The label plate after polishing is wiped for 65-75% alcohol from concentration；
G. polish：Reflective powder is smeared on label plate to uniform, thickness control is reflective to scribbling using sander in 1-2mm
The label plate of powder is polished, and polishing rotating speed control is 180-200r/min, and polishing time control is 20-40min；
H. alcohol wipe：The label plate after cutting is wiped for 70-80% alcohol from concentration, by label plate
Unnecessary reflective powder erasing；
I. reflective membrane is pasted：With laminating machine reflective membrane is sticked in the label panel surface for removing reflective powder；
J. print：The word and/or figure that identify will be needed to be printed on the label after patch reflective membrane by the way of silk-screen printing
On panel surface；
L. overcoat is sprayed：Label plate surface spraying protective coating after printing, forms overcoat；
K. drying process：Label plate after printing is put into drying baker to dry or be put into baking room and toasted, metal class,
The label plate baking temperature of glass-like materials is at 120-125 DEG C, and baking time is 30-35min, and Plastic label plate exists
25-30min is toasted at 75-80 DEG C；
L. overlay film：Carry out covering pressure engineering reflecting film with label panel surface of the laminating machine after drying process, be made label into
Product；
M. check, pack：Label finished product after overlay film is tested, dirt pits, the gas occurred in whole technological process is checked
Bubble, situation in place is not printed.
Preferably, described label plate sets any one in metal class, category of glass or Plastic, enriches the original of label
Material, expands the species of label.
Preferably, in step C, described anti-corrosion material is set to epoxy resin, furane resins, polyester, vinylester resin, no
Any one or more mixing in permeability graphite or phthalic resin, the anti-corrosion of label can be improved by anti-corrosion material
Performance, extends the service life of label.
Preferably, in step I, described patch reflective membrane is carried out in dust-free workshop, and temperature control is 20-25 DEG C, and humidity is
30-35%, improves compactness of the reflective membrane on label, improves the quality of label.
Preferably, in step L, described coating is times in acrylic resin, vinylester resin or phthalic resin
Meaning is a kind of, and the surface of label can be protected by coating, further improves the product quality of label.
Beneficial effect：The present invention carries out polishing, twice alcohol wipe twice to sign board, and polishing for the first time can improve sign board
Profile pattern, reflective powder can be polished to the surface of sign board, reflective powder is circulated sign board by second polishing
In block, so that sign board has certain reflection action, the reflective function of Sign Board is improved, alcohol wipe can not only twice
Unnecessary reflective powder on sign board is removed, the reflection function of sign board is improved, can also remove that label plate surface has is miscellaneous
Matter, improves the finish of label plate surface, and then improves the making quality of label, after sign board printing, drying, to sign board
Pressure reflective membrane is covered in progress, further increases the reflective function of label, strengthens the capability and performance of label, can also be provided with label
Night bright function, extends the service life of label.
Embodiment
The present invention will be described in detail below.
Embodiment one：
A kind of manufacturing process with night bright reflection function label, it is characterised in that described manufacturing process comprises the following steps：
A. label plate is surface-treated：Clean spot, oil stain, the wax stain of metal class label plate surface with cleaning solution, then with derusting
Water carries out chemical derusting, oil removing, the surface of degreaser erasing sign board is then stained with the cloth of cleaning and at once with another cleaning
Cloth dry；
B. cut：Sign board after surface treatment is cut into label plate on request；
C. preservative treatment：The label plate surface spraying of anti-corrosion material after dicing is uniform, make anti-corrosion material in label plate
Surface thickness is uniform, and after anti-corrosion material spraying is uniform, label plate is dried into 25min at 53 DEG C；
D. priming paint overcoat：To the epoxy vehicle paint base that dried label plate surface spraying thickness is 0.007mm, bottom is sprayed
Label plate is dried into 25min in the environment of 58 DEG C after paint；
E. polish：Label plate after spray-applied primer is polished the surface of label plate using sand paper；
F. alcohol wipe：The label plate after polishing is wiped for 68% alcohol from concentration；
G. polish：Reflective powder is smeared on label plate to uniform, thickness control is reflective to scribbling using sander in 1.5mm
The label plate of powder is polished, and polishing rotating speed control is 180r/min, and polishing time control is 30min；
H. alcohol wipe：The label plate after cutting is wiped for 75% alcohol from concentration, will be many on label plate
Remaining reflective powder erasing；
I. reflective membrane is pasted：With laminating machine reflective membrane is sticked in the label panel surface for removing reflective powder；
J. print：The word and/or figure that identify will be needed to be printed on the label after patch reflective membrane by the way of silk-screen printing
On panel surface；
L. overcoat is sprayed：Label plate surface spraying protective coating after printing, forms overcoat；
K. drying process：Label plate after printing is put into drying baker to dry or be put into baking room and toasted, baking temperature
Degree is at 123 DEG C, and baking time is 32min；
L. overlay film：Carry out covering pressure engineering reflecting film with label panel surface of the laminating machine after drying process, be made label into
Product；
M. check, pack：Label finished product after overlay film is tested, dirt pits, the gas occurred in whole technological process is checked
Bubble, situation in place is not printed.
Preferably, in step C, described anti-corrosion material is set to furane resins, and label can be improved by anti-corrosion material
Antiseptic property, extends the service life of label.
Preferably, in step I, described patch reflective membrane is carried out in dust-free workshop, and temperature control is 23 DEG C, and humidity is 32%,
Compactness of the reflective membrane on label is improved, the quality of label is improved.
Preferably, in step L, described coating is phthalic resin, and the surface of label can be carried out by coating
Protection, further improves the product quality of label.
Embodiment two：
A kind of manufacturing process with night bright reflection function label, it is characterised in that described manufacturing process comprises the following steps：
A. label plate is surface-treated：Spot, oil stain, the wax stain of the label plate surface of glass material are cleaned with cleaning solution, then is used
The water that derusts carries out chemical derusting, oil removing, the surface of degreaser erasing sign board is then stained with the cloth of cleaning and at once with another
The cloth of cleaning is dried；
B. cut：Sign board after surface treatment is cut into label plate on request；
C. preservative treatment：The label plate surface spraying of anti-corrosion material after dicing is uniform, make anti-corrosion material in label plate
Surface thickness is uniform, and after anti-corrosion material spraying is uniform, label plate is dried into 18min at 56 DEG C；
D. priming paint overcoat：To the epoxy vehicle paint base that dried label plate surface spraying thickness is 0.009mm, bottom is sprayed
Label plate is dried into 15min in the environment of 65 DEG C after paint；
E. polish：Label plate after spray-applied primer is polished the surface of label plate using sand paper；
F. alcohol wipe：The label plate after polishing is wiped for 78% alcohol from concentration；
G. polish：Reflective powder is smeared on label plate to uniform, thickness control is reflective to scribbling using sander in 2.1mm
The label plate of powder is polished, and polishing rotating speed control is 220r/min, and polishing time control is 45min；
H. alcohol wipe：The label plate after cutting is wiped for 68% alcohol from concentration, will be many on label plate
Remaining reflective powder erasing；
I. reflective membrane is pasted：With laminating machine reflective membrane is sticked in the label panel surface for removing reflective powder；
J. print：The word and/or figure that identify will be needed to be printed on the label after patch reflective membrane by the way of silk-screen printing
On panel surface；
L. overcoat is sprayed：Label plate surface spraying protective coating after printing, forms overcoat；
K. drying process：Label plate after printing is put into drying baker to dry or be put into baking room and toasted, metal class,
The label plate baking temperature of glass-like materials is at 126 DEG C, and baking time is 36min, and Plastic label plate dries at 72 DEG C
Roasting 32min；
L. overlay film：Carry out covering pressure engineering reflecting film with label panel surface of the laminating machine after drying process, be made label into
Product；
M. check, pack：Label finished product after overlay film is tested, dirt pits, the gas occurred in whole technological process is checked
Bubble, situation in place is not printed.
Preferably, in step C, it is 1 by weight that described anti-corrosion material, which is set to epoxy resin, polyester, vinylester resin,:
1:1 mixture, the antiseptic property of label can be improved by anti-corrosion material, extend the service life of label.
Preferably, in step I, described patch reflective membrane is carried out in dust-free workshop, and temperature control is 26 DEG C, and humidity is 37%,
Compactness of the reflective membrane on label is improved, the quality of label is improved.
Preferably, in step L, described coating is acrylic resin, and the surface of label can be protected by coating,
Further improve the product quality of label.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, it is all the present invention spirit and
Any modifications, equivalent substitutions and improvements made within principle etc., should be included in the scope of the protection.
Claims (5)
1. a kind of manufacturing process with night bright reflection function label, it is characterised in that described manufacturing process includes following step
Suddenly：
A. label plate is surface-treated：Spot, oil stain, the wax stain of label plate surface are cleaned with cleaning solution, then is carried out with derusting water
Chemical derusting, oil removing, the surface of degreaser erasing sign board is then stained with the cloth of cleaning and is smeared at once with the cloth of another cleaning
It is dry；
B. cut：Sign board after surface treatment is cut into label plate on request；
C. preservative treatment：The label plate surface spraying of anti-corrosion material after dicing is uniform, make anti-corrosion material in label plate
Surface thickness is uniform, and after anti-corrosion material spraying is uniform, label plate is dried into 20-30min at 50-55 DEG C；
D. priming paint overcoat：To the epoxy vehicle paint base that dried label plate surface spraying thickness is 0.006-0.008mm,
Label plate is dried into 20-30min in the environment of 55-60 DEG C after spray-applied primer；
E. polish：Label plate after spray-applied primer is polished the surface of label plate using sand paper；
F. alcohol wipe：The label plate after polishing is wiped for 65-75% alcohol from concentration；
G. polish：Reflective powder is smeared on label plate to uniform, thickness control is reflective to scribbling using sander in 1-2mm
The label plate of powder is polished, and polishing rotating speed control is 180-200r/min, and polishing time control is 20-40min；
H. alcohol wipe：The label plate after cutting is wiped for 70-80% alcohol from concentration, by label plate
Unnecessary reflective powder erasing；
I. reflective membrane is pasted：With laminating machine reflective membrane is sticked in the label panel surface for removing reflective powder；
J. print：The word and/or figure that identify will be needed to be printed on the label after patch reflective membrane by the way of silk-screen printing
On panel surface；
L. overcoat is sprayed：Label plate surface spraying protective coating after printing, forms overcoat；
K. drying process：Label plate after printing is put into drying baker to dry or be put into baking room and toasted, metal class,
The label plate baking temperature of glass-like materials is at 120-125 DEG C, and baking time is 30-35min, and Plastic label plate exists
25-30min is toasted at 75-80 DEG C；
L. overlay film：Carry out covering pressure engineering reflecting film with label panel surface of the laminating machine after drying process, be made label into
Product；
M. check, pack：Label finished product after overlay film is tested, dirt pits, the gas occurred in whole technological process is checked
Bubble, situation in place is not printed.
2. the manufacturing process according to claim 1 with night bright reflection function label, it is characterised in that：Described label
Plate sets any one in metal class, category of glass or Plastic.
3. the manufacturing process according to claim 1 with night bright reflection function label, it is characterised in that：In step C,
Described anti-corrosion material is set to epoxy resin, furane resins, polyester, vinylester resin, impermeable graphite or phthalic acid
Any one or more mixing in resin.
4. the manufacturing process according to claim 1 with night bright reflection function label, it is characterised in that：In step I,
Described patch reflective membrane is carried out in dust-free workshop, and temperature control is 20-25 DEG C, and humidity is 30-35%.
5. the manufacturing process according to claim 1 with night bright reflection function label, it is characterised in that：In step L,
Described coating is any one in acrylic resin, vinylester resin or phthalic resin.