CN106519978A - Environment-friendly marine anti-fouling paint - Google Patents
Environment-friendly marine anti-fouling paint Download PDFInfo
- Publication number
- CN106519978A CN106519978A CN201510572325.1A CN201510572325A CN106519978A CN 106519978 A CN106519978 A CN 106519978A CN 201510572325 A CN201510572325 A CN 201510572325A CN 106519978 A CN106519978 A CN 106519978A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly
- fouling paint
- marine anti
- fouling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of chemical paints, and specifically relates to an environment-friendly marine anti-fouling paint. The marine anti-fouling paint is prepared from the following components in percentage by weight: 8 to 15% of polydivinyl acetylene resin, 10 to 20% of rosin, 1 to 3% of nano silica, 1 to 10% of environment-friendly anti-fouling agent, 10 to 20% of calcium carbonate, 5 to 10% of iron oxide yellow, 5 to 10% of xylene, 1 to 5% of sodium benzoate, 1 to 3% of tributyl phosphate, 1 to 3% of poly(methyl phenyl siloxane), 1 to 3% of petroleum ether, and 1 to 3% of calcium isocaprylate. The invention aims to provide an environment-friendly marine anti-fouling paint having the advantages of wide inhibition range and long service life.
Description
Technical field
The present invention relates to the technical field of chemistry painting industry, specifically a kind of environment-friendly type marine antifouling coating.
Background technology
The ship important problem for running into that sails in a mighty ocean is exactly marine organisms to the attachment of hull bottom and is stained, marime fouling
Biological attachment can increase ship resistance, reduce ship's speed, consumes fuel more in hull bottom；It is attached to sea farming netting gear, meeting
Result in blockage mesh, reduction exchange of seawater efficiency, can cause to cultivate fish and shellfish dysplasia even death；It is attached to sea
On foreign instrument, instrument signal distortion, hydraulic performance decline can be caused；Torpedo is attached to, is increased weight and ship resistance, is made
Into the unbalance failure of torpedo, so as to cause heavy losses.Application antifouling paint be solve to be stained problem it is not only economical but also efficient
Important channel.It is annual to have a very big expense to be used in compensation as anti-fouling paint failure causes in deceleration, in order to again again
Application antirust, antifouling paint will also spend substantial amounts of expense.Therefore the antifouling paint of high-efficiency environment friendly is developed, is one heavy
The problem wanted.Antifouling paint is typically mainly made up of compositions such as base material, anti-fouling agent, auxiliary material, color stuffing and solvents.
By the attachment and life that are gradually released in sea water suppress and prevent biology on the ocean structures such as ship of anti-fouling agent
It is long, so as to reach antifouling purpose.It is anti-fouling agent that antifouling paint uses Red copper oxide in a large number at present, due to Red copper oxide
Stronger than great and hydrophilic, easily there is cohesion, deposited phenomenon in Red copper oxide during antifouling paint storage, to antifouling
Performance brings many adverse effects.In addition at present there are biological species and suppress that scope is less, anti-fouling agent release speed in anti-fouling agent
The problems such as unstable grade of rate causes the service life of antifouling paint impermanent.
The content of the invention
It is an object of the invention to provide a kind of suppression scope is wide, the environment-friendly type marine antifouling coating of long service life.
A kind of environment-friendly type marine antifouling coating is the technical scheme is that, each material is by following components by weight hundred
Ratio is divided to be formulated：Poly divinyl acetylene resin 8-15%, Colophonium 10-20%, nano silicon 1-3%, environmental protection are anti-
Dirty agent 1-10%, Calcium Carbonate 10-20%, iron oxide yellow 5-10%, dimethylbenzene 5-10%, sodium benzoate 1-5%, phosphoric acid
Tributyl 1-3%, PSI 1-3%, petroleum ether 1-3%, calcium iso-octoate 1-3%.
It is an advantage of the invention that being to solve the marine growth species that current antifouling paint is present to suppress that scope is little, anti-fouling agent release
Speed is unstable, the problem that antifouling paint service life is short.
Specific embodiment
The present invention is further described with the following Examples,
Embodiment 1, a kind of environment-friendly type marine antifouling coating, each material are prepared by weight percentage by following components
Form：Poly divinyl acetylene resin 15%, Colophonium 10%, nano silicon 3%, environment-friendly antifouling agent 1%, Calcium Carbonate
20%th, iron oxide yellow 5%, dimethylbenzene 10%, sodium benzoate 1%, tributyl phosphate 3%, PSI 1%,
Petroleum ether 3%, calcium iso-octoate 1%.
Embodiment 2, a kind of environment-friendly type marine antifouling coating, each material are prepared by weight percentage by following components
Form：Poly divinyl acetylene resin 12%, Colophonium 15%, nano silicon 2%, environment-friendly antifouling agent 5%, Calcium Carbonate
15%th, iron oxide yellow 8%, dimethylbenzene 7%, sodium benzoate 3%, tributyl phosphate 2%, PSI 2%,
Petroleum ether 2%, calcium iso-octoate 2%.
Embodiment 3, a kind of environment-friendly type marine antifouling coating, each material are prepared by weight percentage by following components
Form：Poly divinyl acetylene resin 8%, Colophonium 20%, nano silicon 1%, environment-friendly antifouling agent 10%, Calcium Carbonate
10%th, iron oxide yellow 10%, dimethylbenzene 5%, sodium benzoate 5%, tributyl phosphate 1%, PSI 3%,
Petroleum ether 1%, calcium iso-octoate 3%.
It should be understood that the embodiment is only illustrative of the invention and is not intended to limit the scope of the invention.Furthermore, it is to be understood that
After the content for having read instruction of the present invention, those skilled in the art can be made various changes or modifications to the present invention,
These equivalent form of values are equally fallen within the protection domain limited by the application appended claims.
Claims (1)
1. a kind of environment-friendly type marine antifouling coating, it is characterised in that each material is prepared by weight percentage by following components
Form：Poly divinyl acetylene resin 8-15%, Colophonium 10-20%, nano silicon 1-3%, environment-friendly antifouling agent 1-10%,
Calcium Carbonate 10-20%, iron oxide yellow 5-10%, dimethylbenzene 5-10%, sodium benzoate 1-5%, tributyl phosphate 1-3%,
PSI 1-3%, petroleum ether 1-3%, calcium iso-octoate 1-3%.