CN104341918A - Wear-resistant, high-adhesion, anti-fouling and corrosion-resistant coating material - Google Patents
Wear-resistant, high-adhesion, anti-fouling and corrosion-resistant coating material Download PDFInfo
- Publication number
- CN104341918A CN104341918A CN201410591560.9A CN201410591560A CN104341918A CN 104341918 A CN104341918 A CN 104341918A CN 201410591560 A CN201410591560 A CN 201410591560A CN 104341918 A CN104341918 A CN 104341918A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- adhesion
- wear
- resistant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wear-resistant, high-adhesion, anti-fouling and corrosion-resistant coating material. The wear-resistant, high-adhesion, anti-fouling and corrosion-resistant coating material is prepared from the raw materials in parts by weight: 70-73 parts of acrylic resin, 15-18 parts of keto-aldehyde resin KR-120, 11-14 parts of styrene-acrylic emulsion, 14-17 parts of meerschaum powder, 6-9 parts of bentonite, 3.3-3.6 parts of dibutyl zirconium dilaurate, 1-2 parts of aluminum caprylate, 1.1-1.4 parts of mono-alkoxy titanate coupling agent, 0.5-0.8 part of defoamer, 0.8-1.2 parts of leveling agent, 0.5-0.8 part of mildew preventive, 1.5-1.8 parts of pigment and 52-55 parts of solvent. The wear-resistant, high-adhesion, anti-fouling and corrosion-resistant coating material disclosed by the invention has excellent wear-resistant, anti-fouling and corrosion-resistant performance and is high in adhesion.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to the antifouling corrosion resistant coating of a kind of wear resistant high-adhesion.
Background technology
Ocean environment is very harsh corrosive environment, ship housing is in such environment for a long time, corrode extremely serious, simultaneously, marine organisms are with chemical bonding, diffusion, the modes such as electrostatic interaction are attached to ship housing surface, to peel off, the modes such as shearing come off from ship housing surface, and the coating of ship housing is peeled off from ship housing, the havoc integrity of hull, great safety is brought to safety of navigation, in addition, boats and ships are pulling in shore, in navigation process, foreign matter in inevitable and harbour and ocean produces and rubs, and coating is as ship housing the first layer " umbrella ", main anticorrosion of ship housing, wear-resisting, antifouling, corrosion-resistant means, therefore, develop a kind of high adhesive force and wear-resisting, antifouling, corrosion resistant coating is very necessary.
Summary of the invention
The technical problem that basic background technology exists, the present invention proposes the antifouling corrosion resistant coating of a kind of wear resistant high-adhesion, have excellent wear-resisting, antifouling, corrosion resistance nature, and sticking power is high.
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 70-73 part, ketone resin KR-120 15-18 part, benzene emulsion 11-14 part, sepiolite powder 14-17 part, wilkinite 6-9 part, di lauric dibutyl zirconium 3.3-3.6 part, aluminium octoate 1-2 part, monoalkoxy type titanate coupling agent 1.1-1.4 part, defoamer 0.5-0.8 part, advection agent 0.8-1.2 part, mould inhibitor 0.5-0.8 part, pigment 1.5-1.8 part, solvent 52-55 part.
Preferably, the weight ratio of acrylic resin, ketone resin KR-120, benzene emulsion is 71-72:16-17:12-13.
Preferably, its raw material comprises by weight: acrylic resin 71-72 part, ketone resin KR-120 16-17 part, benzene emulsion 12-13 part, sepiolite powder 15-16 part, wilkinite 7-8 part, di lauric dibutyl zirconium 3.4-3.5 part, aluminium octoate 1.5-1.8 part, monoalkoxy type titanate coupling agent 1.2-1.3 part, defoamer 0.6-0.7 part, advection agent 0.9-1.1 part, mould inhibitor 0.6-0.7 part, pigment 1.6-1.7 part, solvent 53-54 part.
Preferably, its raw material comprises by weight: acrylic resin 71.5 parts, ketone resin KR-120 16.5 parts, benzene emulsion 12.5 parts, sepiolite powder 15.5 parts, wilkinite 7.5 parts, di lauric dibutyl zirconium 3.45 parts, aluminium octoate 1.6 parts, monoalkoxy type titanate coupling agent 1.25 parts, defoamer 0.65 part, advection agent 1 part, mould inhibitor 0.65 part, pigment 1.65 parts, solvent 53.5 parts.
Adopt olefin(e) acid resin, ketone resin KR-120 as filmogen in the present invention, significantly improve wear-resisting and sticking power of the present invention, also make the present invention have good antifouling, corrosion resistance nature simultaneously, the auxiliary benzene emulsion added is rare by benzene second and the cruel monomer of acrylic acid obtains through emulsion copolymerization, substantially increases antifouling property of the present invention and corrosion resistance nature; Sepiolite powder, bentonitic interpolation further increase wear resisting property of the present invention, sticking power and corrosion resistance nature; And di lauric dibutyl zirconium and linolic acid aluminium are combined to form curing system, greatly improve curing speed of the present invention, and the in-situ hybridization that organic and inorganic occurs in the curing process is cross-linked to form three-dimensional netted crosslinking structure, because sepiolite powder, wilkinite have very high specific surface area, impel crosslinking structure extremely tight, improve antifouling corrosion resistance of the present invention further.
Embodiment
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 73 parts, ketone resin KR-120 15 parts, benzene emulsion 14 parts, sepiolite powder 17 parts, wilkinite 6 parts, di lauric dibutyl zirconium 3.6 parts, aluminium octoate 1 part, monoalkoxy type titanate coupling agent 1.4 parts, defoamer 0.5 part, advection agent 1.2 parts, mould inhibitor 0.5 part, pigment 1.8 parts, solvent 52 parts.
Embodiment 2
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 70 parts, ketone resin KR-120 18 parts, benzene emulsion 11 parts, sepiolite powder 14 parts, wilkinite 9 parts, di lauric dibutyl zirconium 3.3 parts, aluminium octoate 2 parts, monoalkoxy type titanate coupling agent 1.1 parts, defoamer 0.8 part, advection agent 0.8 part, mould inhibitor 0.8 part, pigment 1.5 parts, solvent 55 parts.
Embodiment 3
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 72 parts, ketone resin KR-120 16 parts, benzene emulsion 13 parts, sepiolite powder 16 parts, wilkinite 7 parts, di lauric dibutyl zirconium 3.5 parts, aluminium octoate 1.5 parts, monoalkoxy type titanate coupling agent 1.3 parts, defoamer 0.6 part, advection agent 1.1 parts, mould inhibitor 0.6 part, pigment 1.7 parts, solvent 53 parts.
Embodiment 4
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 71 parts, ketone resin KR-120 17 parts, benzene emulsion 12 parts, sepiolite powder 15 parts, wilkinite 8 parts, di lauric dibutyl zirconium 3.4 parts, aluminium octoate 1.8 parts, monoalkoxy type titanate coupling agent 1.2 parts, defoamer 0.7 part, advection agent 0.9 part, mould inhibitor 0.7 part, pigment 1.6 parts, solvent 54 parts.
Embodiment 5
The antifouling corrosion resistant coating of a kind of wear resistant high-adhesion that the present invention proposes, its raw material comprises by weight: acrylic resin 71.5 parts, ketone resin KR-120 16.5 parts, benzene emulsion 12.5 parts, sepiolite powder 15.5 parts, wilkinite 7.5 parts, di lauric dibutyl zirconium 3.45 parts, aluminium octoate 1.6 parts, monoalkoxy type titanate coupling agent 1.25 parts, defoamer 0.65 part, advection agent 1 part, mould inhibitor 0.65 part, pigment 1.65 parts, solvent 53.5 parts.
Carry out performance test to embodiment 1-5, select the commercially available acrylic coating of certain money as a control group, its result is as follows:
Test item | Embodiment 1-5 mean value | Control group | Establishing criteria |
Sticking power | 1 grade | 1 grade | GB/T9286-1998 |
Hardness | H | HB | GB/T6739-2006 |
Shock-resistant (kgcm) | 62 | 55 | GB/T1732-1993 |
Salt fog resistance (h) | 288 | 192 | GB/T1771-1991 |
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (4)
1. the antifouling corrosion resistant coating of wear resistant high-adhesion, is characterized in that, its raw material comprises by weight: acrylic resin 70-73 part, ketone resin KR-12015-18 part, benzene emulsion 11-14 part, sepiolite powder 14-17 part, wilkinite 6-9 part, di lauric dibutyl zirconium 3.3-3.6 part, aluminium octoate 1-2 part, monoalkoxy type titanate coupling agent 1.1-1.4 part, defoamer 0.5-0.8 part, advection agent 0.8-1.2 part, mould inhibitor 0.5-0.8 part, pigment 1.5-1.8 part, solvent 52-55 part.
2. the antifouling corrosion resistant coating of wear resistant high-adhesion according to claim 1, it is characterized in that, the weight ratio of acrylic resin, ketone resin KR-120, benzene emulsion is 71-72:16-17:12-13.
3. the antifouling corrosion resistant coating of wear resistant high-adhesion according to claim 1 or 2, it is characterized in that, its raw material comprises by weight: acrylic resin 71-72 part, ketone resin KR-12016-17 part, benzene emulsion 12-13 part, sepiolite powder 15-16 part, wilkinite 7-8 part, di lauric dibutyl zirconium 3.4-3.5 part, aluminium octoate 1.5-1.8 part, monoalkoxy type titanate coupling agent 1.2-1.3 part, defoamer 0.6-0.7 part, advection agent 0.9-1.1 part, mould inhibitor 0.6-0.7 part, pigment 1.6-1.7 part, solvent 53-54 part.
4. the antifouling corrosion resistant coating of wear resistant high-adhesion according to any one of claim 1-3, it is characterized in that, its raw material comprises by weight: acrylic resin 71.5 parts, ketone resin KR-12016.5 part, benzene emulsion 12.5 parts, sepiolite powder 15.5 parts, wilkinite 7.5 parts, di lauric dibutyl zirconium 3.45 parts, aluminium octoate 1.6 parts, monoalkoxy type titanate coupling agent 1.25 parts, defoamer 0.65 part, advection agent 1 part, mould inhibitor 0.65 part, pigment 1.65 parts, solvent 53.5 parts.