CN107779046A - Electric automobile Wear-resistant corrosion-resistant coating - Google Patents
Electric automobile Wear-resistant corrosion-resistant coating Download PDFInfo
- Publication number
- CN107779046A CN107779046A CN201711058458.2A CN201711058458A CN107779046A CN 107779046 A CN107779046 A CN 107779046A CN 201711058458 A CN201711058458 A CN 201711058458A CN 107779046 A CN107779046 A CN 107779046A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric automobile
- agent
- resistant
- resistant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses electric automobile Wear-resistant corrosion-resistant coating, it is prepared by the raw material of following parts by weight:80 110 parts of epoxy resin, 40 60 parts of acrylic resin, 20 25 parts of trioctyl phosphate, 10 15 parts of lac, 26 parts of silicon carbide micro-powder, 48 parts of bamboo charcoal micropowder, 13 parts of rutile titanium white powder, 12 parts of lanthanum hexaboride, 58 parts of Tissuemat E, poly- 15 parts of azelaic acid acid anhydride, 4 10 parts of adhesion promoter, biological 25 parts of antirust agent, 13 parts of antiseptic, 12 parts of curing agent, 14 parts of defoamer, 28 parts of coupling agent, 13 parts of anti-settling agent, 26 parts of diluent.The present invention selects rational raw material and proportioning, each raw material synergy, complements each other, with stronger waterproof, wear-resisting, high-temperature stability, and its good insulating, adhesive force are strong, it is very suitable for shared electric automobile to use, can effectively increases the service life of electric automobile.
Description
Technical field
The present invention relates to electric automobile application techniques field, more particularly to a kind of electric automobile Wear-resistant corrosion-resistant coating.
Background technology
With the development of society, global energy crisis constantly aggravates, petroleum resources exhaustion, atmosphere pollution and global gas increasingly
Temperature is warmed getting worse, and automobile is gone on a journey the indispensable vehicles as people, is usually relied on oil firing driving, can be aggravated energy
Source and environmental crisis.On the other hand, automobile industry is proposed New-energy electric vehicle, oil firing can be avoided or reduced, may advantageously facilitate ring
The short crisis of traditional energy is protected and alleviated in border, has wide market development prospect.
With the propulsion of China's energy-saving and emission-reduction policy, new energy vehicle is widely applied, particularly electric vehicle, is adopted
With driven by power, exhaust emission is not produced, is the vital measure for realizing communications and transportation aspect energy-saving and emission-reduction.
In recent years, shared electric automobile engenders, due to its character of use, causes its frequency of use very high, during operation
Between it is long, therefore higher is required to the coating quality on its surface, common coating can not meet indices, and common coating has following lack
Point:
(1) common coating poor insulativity, using having potential safety hazard on electric automobile;
(2) common coating non-refractory, for a long time in the case where burning sun is exposed to the sun, it may occur that ftracture, bubble, come off;
(3) common coating water-proof is poor, easily by rain penetration, causes inside to be corroded;
(4) common coating wears no resistance intolerant to colliding with, poor adhesive force, after accidentally scratching, it may appear that depainting phenomenon, enter
And easily it is corroded.
The content of the invention
It is an object of the invention to overcome the above-mentioned problems in the prior art, and then it is wear-resisting to provide a kind of electric automobile
Anti-corrosive paints.
The technical problems to be solved by the invention are realized using following technical scheme:
Electric automobile Wear-resistant corrosion-resistant coating, is prepared by the raw material of following parts by weight:Epoxy resin 80-110 parts,
Acrylic resin 40-60 parts, trioctyl phosphate 20-25 parts, lac 10-15 parts, silicon carbide micro-powder 2-6 parts, bamboo charcoal micropowder 4-8
Part, rutile titanium white powder 1-3 parts, lanthanum hexaboride 1-2 parts, Tissuemat E 5-8 parts, poly- azelaic acid acid anhydride 1-5 parts, adhesion promoter
4-10 parts, biological antirust agent 2-5 parts, antiseptic 1-3 parts, curing agent 1-2 parts, defoamer 1-4 parts, coupling agent 2-8 parts, anti-settling agent
1-3 parts, diluent 2-6 parts.
Further, the preferred weight number of each raw material is:100 parts of epoxy resin, 50 parts of acrylic resin, tricresyl phosphate is pungent
22 parts of ester, 12 parts of lac, 4 parts of silicon carbide micro-powder, 6 parts of bamboo charcoal micropowder, 2 parts of rutile titanium white powder, 1.5 parts of lanthanum hexaboride, poly- second
6 parts of alkene wax, poly- 2 parts of azelaic acid acid anhydride, 6 parts of adhesion promoter, biological 3 parts of antirust agent, 2 parts of antiseptic, 1 part of curing agent, defoaming
2 parts of agent, 4 parts of coupling agent, 2 parts of anti-settling agent, 4 parts of diluent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the preparation method of the biological antirust agent is:Take the Isuzu Motors of equivalent beautiful, orange peel, Chinese aloe leaf, stone
Pomegranate skin, the absolute ethyl alcohol of above-mentioned four kinds of raw material gross weights 70% is added, mixing is fully smashed with pulverizer, then extruding, mistake
Filter, concentration, obtain biological antirust agent.
Further, the antiseptic is sodium alginate fiber, tea fiber, ammonium dihydrogen phosphate, lithium carbonate by 6:2:2:1
Ratio mixes.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the defoamer is silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxy Propanolamine
Ether, polypropylene glycerol aether press 5:3:2:1 ratio mixes.
Further, the coupling agent is the mixture of silane coupler and titanate coupling agent, weight between the two
Than for 4:1.
Further, the anti-settling agent is castor oil derivative, polyolefin-wax, the one or more of polyamide wax.
Further, the diluent is acetone, MEK, cyclohexanone, benzene,toluene,xylene, n-butanol, styrene
One or more.
Beneficial effects of the present invention:The present invention selects rational raw material and proportioning, each raw material synergy, complements each other,
With stronger waterproof, wear-resisting, high-temperature stability, and its good insulating, adhesive force is strong, is very suitable for shared electric automobile
Use, can effectively increase the service life of electric automobile.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
Electric automobile Wear-resistant corrosion-resistant coating, is prepared by the raw material of following parts by weight:100 parts of epoxy resin, third
50 parts of olefin(e) acid resin, 22 parts of trioctyl phosphate, 12 parts of lac, 4 parts of silicon carbide micro-powder, 6 parts of bamboo charcoal micropowder, rutile titanium white powder 2
Part, 1.5 parts of lanthanum hexaboride, 6 parts of Tissuemat E, poly- 2 parts of azelaic acid acid anhydride, 6 parts of adhesion promoter, biological 3 parts of antirust agent, antibacterial
2 parts of agent, 1 part of curing agent, 2 parts of defoamer, 4 parts of coupling agent, 2 parts of anti-settling agent, 4 parts of diluent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the preparation method of the biological antirust agent is:Take the Isuzu Motors of equivalent beautiful, orange peel, Chinese aloe leaf, stone
Pomegranate skin, the absolute ethyl alcohol of above-mentioned four kinds of raw material gross weights 70% is added, mixing is fully smashed with pulverizer, then extruding, mistake
Filter, concentration, obtain biological antirust agent.
Further, the antiseptic is sodium alginate fiber, tea fiber, ammonium dihydrogen phosphate, lithium carbonate by 6:2:2:1
Ratio mixes.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the defoamer is silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxy Propanolamine
Ether, polypropylene glycerol aether press 5:3:2:1 ratio mixes.
Further, the coupling agent is the mixture of silane coupler and titanate coupling agent, weight between the two
Than for 4:1.
Further, the anti-settling agent is castor oil derivative, polyolefin-wax, the one or more of polyamide wax.
Further, the diluent is acetone, MEK, cyclohexanone, benzene,toluene,xylene, n-butanol, styrene
One or more.
Embodiment 2
Electric automobile Wear-resistant corrosion-resistant coating, is prepared by the raw material of following parts by weight:90 parts of epoxy resin, propylene
55 parts of acid resin, 22 parts of trioctyl phosphate, 11 parts of lac, 3 parts of silicon carbide micro-powder, 5 parts of bamboo charcoal micropowder, 2 parts of rutile titanium white powder,
1 part of lanthanum hexaboride, 6 parts of Tissuemat E, poly- 4 parts of azelaic acid acid anhydride, 9 parts of adhesion promoter, biological 4 parts of antirust agent, antiseptic 2
Part, 2 parts of curing agent, 3 parts of defoamer, 7 parts of coupling agent, 2 parts of anti-settling agent, 5 parts of diluent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the preparation method of the biological antirust agent is:Take the Isuzu Motors of equivalent beautiful, orange peel, Chinese aloe leaf, stone
Pomegranate skin, the absolute ethyl alcohol of above-mentioned four kinds of raw material gross weights 70% is added, mixing is fully smashed with pulverizer, then extruding, mistake
Filter, concentration, obtain biological antirust agent.
Further, the antiseptic is sodium alginate fiber, tea fiber, ammonium dihydrogen phosphate, lithium carbonate by 6:2:2:1
Ratio mixes.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the defoamer is silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxy Propanolamine
Ether, polypropylene glycerol aether press 5:3:2:1 ratio mixes.
Further, the coupling agent is the mixture of silane coupler and titanate coupling agent, weight between the two
Than for 4:1.
Further, the anti-settling agent is castor oil derivative, polyolefin-wax, the one or more of polyamide wax.
Further, the diluent is acetone, MEK, cyclohexanone, benzene,toluene,xylene, n-butanol, styrene
One or more.
Embodiment 3
Electric automobile Wear-resistant corrosion-resistant coating, is prepared by the raw material of following parts by weight:110 parts of epoxy resin, third
45 parts of olefin(e) acid resin, 22 parts of trioctyl phosphate, 14 parts of lac, 6 parts of silicon carbide micro-powder, 7 parts of bamboo charcoal micropowder, rutile titanium white powder 3
Part, 2 parts of lanthanum hexaboride, 7 parts of Tissuemat E, poly- 4 parts of azelaic acid acid anhydride, 5 parts of adhesion promoter, biological 3 parts of antirust agent, antiseptic
2 parts, 1 part of curing agent, 1 part of defoamer, 3 parts of coupling agent, 1 part of anti-settling agent, 3 parts of diluent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the preparation method of the biological antirust agent is:Take the Isuzu Motors of equivalent beautiful, orange peel, Chinese aloe leaf, stone
Pomegranate skin, the absolute ethyl alcohol of above-mentioned four kinds of raw material gross weights 70% is added, mixing is fully smashed with pulverizer, then extruding, mistake
Filter, concentration, obtain biological antirust agent.
Further, the antiseptic is sodium alginate fiber, tea fiber, ammonium dihydrogen phosphate, lithium carbonate by 6:2:2:1
Ratio mixes.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the defoamer is silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxy Propanolamine
Ether, polypropylene glycerol aether press 5:3:2:1 ratio mixes.
Further, the coupling agent is the mixture of silane coupler and titanate coupling agent, weight between the two
Than for 4:1.
Further, the anti-settling agent is castor oil derivative, polyolefin-wax, the one or more of polyamide wax.
Further, the diluent is acetone, MEK, cyclohexanone, benzene,toluene,xylene, n-butanol, styrene
One or more.
Further, the preparation method of the electric automobile Wear-resistant corrosion-resistant coating comprises the following steps:
(1) epoxy resin, acrylic resin, trioctyl phosphate and lac are added in reactor, stirred at 80-90 DEG C
React 30-40 minutes, mixing speed is 450-500 revs/min;
(2) it is 60-70 DEG C to adjust whipping temp, adds silicon carbide micro-powder, bamboo charcoal micropowder and rutile titanium white powder, is kept
450-500 revs/min of mixing speed, stir 15-20 minutes;
(3) mixture in reactor is poured out and is ground, grinding temperature is maintained at 40-45 DEG C, be ground to fineness≤
50 μm, filtering;
(4) material after filtering is rejoined to the reactor for cleaning drying, then in order by lanthanum hexaboride, Tissuemat E
It is added to poly- azelaic acid acid anhydride in reactor, 40-60 minutes, whipping temp 50-55 is stirred with 600-700 revs/min of speed
℃;
(5) mixture for obtaining step 4 is poured into ultrasonic dispersing machine, adds adhesion promoter, biological antirust
Agent, antiseptic, curing agent, defoamer, coupling agent, anti-settling agent and diluent, carry out ultrasonic wave and disperse, ultrasonic power 200-
220W, jitter time are 30-50 minutes, and dispersion temperature is 100-115 DEG C;
(6) mixture for obtaining step 5 shears speed using high-speed shearing machine in 150-160 DEG C, 8000-9000 revs/min
Spend down cut and disperse 25-30 minutes;
(7) mixture obtained to step 6 carries out secondary grinding, is ground to fineness≤30 μm, refilters, that is, obtains into
Product.
Performance measurement is carried out to the coating of embodiment 1,2,3, obtains following table:
Measurement result shows that the present invention has stronger waterproof, wear-resisting, high-temperature stability, and its good insulating, attachment
Power is strong, is very suitable for shared electric automobile and uses, can effectively increase the service life of electric automobile.
The general principle and principal character of the present invention has been shown and described above.It should be understood by those skilled in the art that
The present invention is not limited to the above embodiments, merely illustrating the principles of the invention described in above-described embodiment and specification,
Without departing from the spirit and scope, various changes and modifications of the present invention are possible, and these changes and improvements all fall
Enter in scope of the claimed invention.The scope of the present invention is defined by the appended claims and its equivalents.
Claims (10)
1. electric automobile Wear-resistant corrosion-resistant coating, it is characterised in that be prepared by the raw material of following parts by weight:Epoxy resin
80-110 parts, acrylic resin 40-60 parts, trioctyl phosphate 20-25 parts, lac 10-15 parts, silicon carbide micro-powder 2-6 parts, bamboo charcoal
Micro mist 4-8 parts, rutile titanium white powder 1-3 parts, lanthanum hexaboride 1-2 parts, Tissuemat E 5-8 parts, poly- azelaic acid acid anhydride 1-5 parts, attachment
Power accelerator 4-10 parts, biological antirust agent 2-5 parts, antiseptic 1-3 parts, curing agent 1-2 parts, defoamer 1-4 parts, coupling agent 2-8
Part, anti-settling agent 1-3 parts, diluent 2-6 parts.
2. electric automobile Wear-resistant corrosion-resistant coating according to claim 1, it is characterised in that preferred weight part of each raw material
Number is:100 parts of epoxy resin, 50 parts of acrylic resin, 22 parts of trioctyl phosphate, 12 parts of lac, 4 parts of silicon carbide micro-powder, bamboo charcoal
6 parts of micro mist, 2 parts of rutile titanium white powder, 1.5 parts of lanthanum hexaboride, 6 parts of Tissuemat E, poly- 2 parts of azelaic acid acid anhydride, adhesion promoter 6
Part, biological 3 parts of antirust agent, 2 parts of antiseptic, 1 part of curing agent, 2 parts of defoamer, 4 parts of coupling agent, 2 parts of anti-settling agent, 4 parts of diluent.
3. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the adhesive force promotes
Agent is compound bifunctional silane.
4. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the biological antirust agent
Preparation method be:Take the Isuzu Motors of equivalent beautiful, orange peel, Chinese aloe leaf, granatum, add above-mentioned four kinds of raw material gross weights
70% absolute ethyl alcohol, mixing is fully smashed with pulverizer, then extrude, filter, concentration, obtaining biological antirust agent.
5. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the antiseptic is sea
Mosanom fiber, tea fiber, ammonium dihydrogen phosphate, lithium carbonate press 6:2:2:1 ratio mixes.
6. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the curing agent is poly-
Close macromolecule amine reagent.
7. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the defoamer is breast
SiClx oil, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether press 5:3:2:1 ratio
Example mixes.
8. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the coupling agent is silicon
The mixture of alkane coupling agent and titanate coupling agent, weight ratio between the two is 4:1.
9. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the anti-settling agent is castor
Sesame oil derivative, polyolefin-wax, the one or more of polyamide wax.
10. electric automobile Wear-resistant corrosion-resistant coating according to claim 1 or 2, it is characterised in that the diluent is third
Ketone, MEK, cyclohexanone, benzene,toluene,xylene, n-butanol, the one or more of styrene.