CN106519722A - Preparation technology of antistatic bamboo board - Google Patents
Preparation technology of antistatic bamboo board Download PDFInfo
- Publication number
- CN106519722A CN106519722A CN201610965039.6A CN201610965039A CN106519722A CN 106519722 A CN106519722 A CN 106519722A CN 201610965039 A CN201610965039 A CN 201610965039A CN 106519722 A CN106519722 A CN 106519722A
- Authority
- CN
- China
- Prior art keywords
- parts
- antistatic
- bamboo
- preparation technology
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a preparation technology of an antistatic bamboo board. The preparation process includes the steps of: 1) material preparation: passing bamboo sawdust through a sieve with a pore size of 90-120 meshes, performing drying to a moisture content of less than or equal to 3%, and preparing a commercially available waste plastic with a standard particle size; 2) premixing: kneading the bamboo sawdust and the waste plastic of step 1) with assistants in a kneading pot according to a weight ratio to obtain a premix; 3) mixing granulation: employing a twin-screw mechanism to perform mixing granulation on the premix to obtain a mixture; 5) drying: subjecting the mixture to heating drying in a material cylinder; and 6) extrusion molding: extruding the mixture by a single-screw mechanism and conducting moulding by a die. The bamboo board is prepared from bamboo sawdust and waste plastic, has greatly reduced cost, also meets the strength requirement of outdoor building materials, has good corrosion resistance and stable antistatic performance, can eliminate static electricity, avoids electric shock phenomenon, eliminates discomfort caused by electric shock, and promotes body health.
Description
Technical field
The present invention relates to building materials field, more particularly to a kind of preparation technology of antistatic bamboo plate.
Background technology
Bamboo-plastic composite material (Bamboo-plastic Composites, abridge BPC) is with bamboo sawdust, bamboo scraps, bamboo slag etc.
Bamboo fibre is primary raw material, using the characteristics of polymer chemistry interface fusion principle and filling-modified enhancing, is compounded certain proportion
Plastic matrix, be aided with appropriate processing aid, Jing special process process after machine-shaping it is a kind of with many of Reversible Cycle
Plant the new material of purposes.This kind of material surface is bright and clean, and quality is closely knit, has both overcome that strength of wood is low and variability etc. uses office
It is sex-limited, the low shortcoming of organic material modulus is overcome again, with preferable mechanics and sound absorption qualities, and which is corrosion-resistant, anti-insect,
Water imbibition is little, easily reclaims, and is a kind of new generation wood environment-friendly materials.
In daily life, especially in dry winter, electrostatic phenomenon can all occur whenever and wherever possible, the life band for giving people
Carry out many puzzlements, the body & mind that these shock phenomenons can give people brings very big harm, affect the life of personal human body
Pat weighing apparatus.As bamboo-plastic composite material is closely related with the life of people, office, family, factory, store, supermarket etc. are all
Can touch bamboo-plastic composite material application, therefore bamboo-plastic composite material antistatic process is a need for.
The content of the invention
In view of this, it is an object of the invention to provide a kind of preparation technology of antistatic bamboo plate, the building materials can be effective
Using waste or used plastics, natural bamboo utilization rate can be also improved, and anti-corrosion humidity resistance is good, while also having anti-static function;This
Another purpose of invention is to provide a kind of antistatic bamboo plate.
An object of the present invention is achieved through the following technical solutions:
A kind of preparation technology of antistatic bamboo plate, by weight, the antistatic bamboo plate includes following component:Bamboo
Bits 50-80 parts;Waste or used plastics 35-50 parts;Auxiliary agent 3-6 parts;The auxiliary agent includes the dilute resin of stearic acid, terpene, silane coupler, phthalein
Sour fat coupling agent, Tissuemat E, glass fiber powder, iron oxide red, titanium dioxide, antistatic agent, antioxidant;Preparation technology includes following
Step:
1) get the raw materials ready:By aperture sieve of the bamboo scraps by 90-120 mesh, drying to moisture≤3%;Prepare commercial standard grain
The waste or used plastics in footpath;
2) premix:By weight ratio by step 1) in bamboo scraps, waste or used plastics and auxiliary agent mediate in kneading pot and obtain
Pre-composition;
3) mixing granulation:Using double-helical screw mechanism to pre-composition mixing granulation, mixture is obtained;
4) it is dried:To mixture heating, drying in barrel;
5) extrusion molding:Mixture is extruded through mouth mold shaping by single screw mechanism used;
6) cool down.
Especially, by weight, the auxiliary agent includes following components:Stearic acid 10-20 parts;The dilute resin 8-12 parts of terpene;
Silane coupler 2-4 parts;Phthalic acid ester coupling agent 2-4 parts;Tissuemat E 5-7 parts;Glass fiber powder 2-8 parts;Iron oxide red 15-24 parts;
Titanium dioxide 20-30 parts;Antistatic agent 3-8 parts;Antioxidant 1-3 parts.
Especially, described antistatic agent is macromolecule antistatic agent.
Especially, the temperature control of the barrel is between 170-200 DEG C.
The second object of the present invention is achieved through the following technical solutions:
According to the antistatic bamboo plate that a kind of aforesaid preparation technology of antistatic bamboo plate is prepared.
The invention has the beneficial effects as follows:
The bamboo plate of the present invention is because adding waste or used plastics to be prepared from using bamboo scraps so as to which cost is substantially reduced, while meeting
The intensity and hardness of outdoor building materials is high, resistance to acids and bases, the requirement of anticorrosive, indeformable, easy recovery, and the present invention not only has good
Good antiseptic property, and antistatic performance is stable, can eliminate electrostatic, it is to avoid shock phenomenon, eliminates electric shock and brings not
It is suitable, promote healthy.
Other advantages of the present invention, target and feature will be illustrated to a certain extent in the following description, and
And to a certain extent, based on being will be apparent to investigating hereafter to those skilled in the art, Huo Zheke
To be instructed from the practice of the present invention.The present invention target and other advantages can be realized by description below and
Obtain.
Specific embodiment
Hereinafter the preferred embodiments of the present invention will be described in detail.It should be appreciated that preferred embodiment is only for saying
The bright present invention, rather than in order to limit the scope of the invention.
Embodiment 1
In the present embodiment, by weight, antistatic bamboo plate includes following component:50 parts of bamboo scraps;35 parts of waste or used plastics;
3 parts of auxiliary agent;
Auxiliary agent includes following components:10 parts of stearic acid;8 parts of the dilute resin of terpene;2 parts of silane coupler;Phthalic acid ester coupling agent 2
Part;5 parts of Tissuemat E;2 parts of glass fiber powder;15 parts of iron oxide red;20 parts of titanium dioxide;3 parts of antistatic agent;1 part of antioxidant.This reality
Apply in example, antistatic agent is macromolecule antistatic agent, using conventional antistatic agent on the market.
Preparation process is as follows:
1) get the raw materials ready:By aperture sieve of the bamboo scraps by 90 mesh, drying to moisture≤3%;Prepare commercial standard particle diameter
Waste or used plastics;
2) premix:By weight ratio by step 1) in bamboo scraps, waste or used plastics and auxiliary agent mediate in kneading pot and obtain
Pre-composition;
3) mixing granulation:Using double-helical screw mechanism to pre-composition mixing granulation;
4) it is dried:To mixture heating, drying in barrel, barrel temperature is 180 DEG C;
5) extrusion molding:Mixture is extruded through mouth mold shaping by single screw mechanism used;
6) cool down:Using water-cooling pattern to step 6) section bar cooling, obtain finished product.
Embodiment 2
In the present embodiment, by weight, antistatic bamboo plate includes following component:60 parts of bamboo scraps;40 parts of waste or used plastics;
5 parts of auxiliary agent;
Auxiliary agent includes following components:15 parts of stearic acid;10 parts of the dilute resin of terpene;3 parts of silane coupler;Phthalic acid ester coupling agent 3
Part;6 parts of Tissuemat E;6 parts of glass fiber powder;20 parts of iron oxide red;25 parts of titanium dioxide;6 parts of antistatic agent;2 parts of antioxidant.
Preparation process is as follows:
1) get the raw materials ready:By aperture sieve of the bamboo scraps by 100 mesh, drying to moisture≤3%;Prepare commercial standard particle diameter
Waste or used plastics;
2) premix:By weight by step 1) in bamboo scraps, waste or used plastics and auxiliary agent mediate in kneading pot and obtain pre-composition;
3) mixing granulation:Using double-helical screw mechanism to pre-composition mixing granulation;
4) it is dried:To mixture heating, drying in barrel;Barrel temperature is 200 DEG C;
5) extrusion molding:Mixture is extruded through mouth mold shaping by single screw mechanism used;
6) cool down:Using water-cooling pattern to step 6) section bar cooling, obtain finished product.
Embodiment 3
In the present embodiment, by weight, antistatic bamboo plate includes following component:80 parts of bamboo scraps;50 parts of waste or used plastics;
6 parts of auxiliary agent;
Auxiliary agent includes following components:20 parts of stearic acid;12 parts of the dilute resin of terpene;4 parts of silane coupler;Phthalic acid ester coupling agent 4
Part;7 parts of Tissuemat E;8 parts of glass fiber powder;24 parts of iron oxide red;30 parts of titanium dioxide;8 parts of antistatic agent;3 parts of antioxidant.
Preparation method comprises the steps:
1) get the raw materials ready:By aperture sieve of the bamboo scraps by 120 mesh, drying to moisture≤3%;Prepare commercial standard particle diameter
Waste or used plastics;
2) premix:By weight by step 1) in bamboo scraps, waste or used plastics and auxiliary agent mediate in kneading pot and premixed
Thing;
3) mixing granulation:Using double-helical screw mechanism to pre-composition mixing granulation;
4) it is dried:To mixture heating, drying in barrel;Barrel temperature is 220 DEG C;
5) extrusion molding:Mixture is extruded through mouth mold shaping by single screw mechanism used;
6) cooling obtains finished product.
Finally illustrate, above example is only unrestricted to illustrate technical scheme, although with reference to compared with
Good embodiment has been described in detail to the present invention, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent, and without deviating from the objective and scope of the technical program, which all should be covered in the present invention
Right in the middle of.
Claims (5)
1. a kind of preparation technology of antistatic bamboo plate, it is characterised in that:By weight, the antistatic bamboo plate include with
Lower component:Bamboo scraps 50-80 part;Waste or used plastics 35-50 parts;Auxiliary agent 3-6 parts;The auxiliary agent includes the dilute resin of stearic acid, terpene, silane
Coupling agent, phthalic acid ester coupling agent, Tissuemat E, glass fiber powder, iron oxide red, titanium dioxide, antistatic agent, antioxidant;Prepare work
Skill is comprised the following steps:
1) get the raw materials ready:By aperture sieve of the bamboo scraps by 90-120 mesh, drying to moisture≤3%;Prepare commercial standard particle diameter
Waste or used plastics;
2) premix:By weight ratio by step 1) in bamboo scraps, waste or used plastics and auxiliary agent mediate in kneading pot and premixed
Thing;
3) mixing granulation:Using double-helical screw mechanism to pre-composition mixing granulation, mixture is obtained;
4) it is dried:To mixture heating, drying in barrel;
5) extrusion molding:Mixture is extruded through mouth mold shaping by single screw mechanism used;
6) cool down.
2. the preparation technology of a kind of antistatic bamboo plate according to claim 1, it is characterised in that:By weight, institute
Stating auxiliary agent includes following components:Stearic acid 10-20 parts;The dilute resin 8-12 parts of terpene;Silane coupler 2-4 parts;Phthalic acid ester coupling agent
2-4 parts;Tissuemat E 5-7 parts;Glass fiber powder 2-8 parts;Iron oxide red 15-24 parts;Titanium dioxide 20-30 parts;Antistatic agent 3-8 parts;
Antioxidant 1-3 parts.
3. the preparation technology of a kind of antistatic bamboo plate according to claim 1, it is characterised in that:Described antistatic agent
For macromolecule antistatic agent.
4. the preparation technology of a kind of antistatic bamboo plate according to claim 1, it is characterised in that:The temperature of the barrel
Control is between 180-220 DEG C.
5. according to the preparation technology of the arbitrary described a kind of antistatic bamboo plate of claim 1-4 be prepared from it is antistatic bamboo
Plate.