CN106517907A - External wall body material for building - Google Patents

External wall body material for building Download PDF

Info

Publication number
CN106517907A
CN106517907A CN201610976661.7A CN201610976661A CN106517907A CN 106517907 A CN106517907 A CN 106517907A CN 201610976661 A CN201610976661 A CN 201610976661A CN 106517907 A CN106517907 A CN 106517907A
Authority
CN
China
Prior art keywords
wall body
body material
external wall
building
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610976661.7A
Other languages
Chinese (zh)
Inventor
刘飞
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sanmenxia Qingshan Abrasive Products Co Ltd
Original Assignee
Sanmenxia Qingshan Abrasive Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanmenxia Qingshan Abrasive Products Co Ltd filed Critical Sanmenxia Qingshan Abrasive Products Co Ltd
Priority to CN201610976661.7A priority Critical patent/CN106517907A/en
Publication of CN106517907A publication Critical patent/CN106517907A/en
Pending legal-status Critical Current

Abstract

The invention discloses an external wall body material for a building. The external wall body material is a mixture prepared from the following raw materials in parts by weight: 30-50 parts of walnut shell powder of 10-30 meshes, 20-40 parts of cement, 3-10 parts of a binder and 5-20 parts of magnesium oxide. The external wall body material has the advantages of low cost, simplicity and quickness in construction, fracturing resistance, light weight, thermal insulation and environment friendliness. During use, all a user needs to do is to mix the external wall body material with water into slurry and uniformly spray the mixed slurry onto an external wall of the building by spraying equipment.

Description

A kind of outer wall body material for building
Technical field
The present invention relates to a kind of construction material, specifically a kind of outer wall body material for building.
Background technology
At present building industry using the mode of outer wall body material typically have sandblasting, brush exterior wall paint, tiling etc..Sandblasting The outer wall body material of mode is insecure due to boning, and Jing is often cracked, comes off, and affects to be incubated and attractive in appearance；Exterior wall paint is brushed, due to Exterior wall paint price costly, using appearance colour fading all different degrees of after several years, crack, extremely peeling, cause partial exfoliation, affects to build Build the attractive in appearance of thing；Ceramic tile price is also more expensive, and the labour cost in work progress is also more expensive, taller idle job, and construction is inconvenient, Both the heavy burden of building had been increased, the feature of environmental protection is also poor, had been exposed to the weather long, some ceramic tiles had loosened, come off, and were likely to result in personnel Injury and property loss.
The content of the invention
The task of the present invention is to provide a kind of low cost, simple and fast of constructing, and freedom from cracking, lightweight, heat-insulation and heat-preservation are environmentally friendly Outer wall body material for building.
To realize above-mentioned task, the technical solution of the present invention is：
A kind of outer wall body material for building, it is the mixture by made by the raw material of following weight (part) proportioning：Walnut Shell powder (10-30 mesh) 30-50, cement 20-40, binding agent 3-10, magnesia 5-20.
The present invention formula preferred weight (part) ratio range be：
Walnut shell powder (10-30 mesh) 35-45, cement 25-35, binding agent 4-8, magnesia 8-15.
The present invention optimum weight (part) proportioning be：
Walnut shell powder (10-30 mesh) 40, cement 30, binding agent 7, magnesia 12.
Above-mentioned each component is made the preparation method is that：Lustration raw material needed for selecting, is prepared in proportion, and mixing is equal It is even, you can.
The present invention has low cost, simple and fast of constructing, freedom from cracking, lightweight, heat-insulation and heat-preservation, the advantage of environmental protection.
When the present invention is used, and water stirs into slurry, with spraying equipment by the slurry even application being stirred in building 3 millimeters thick on exterior wall.
Specific embodiment
Embodiment 1, raw material (kilogram) is weighed by following proportionings：Walnut shell powder (10-30 mesh) 40, cement 30, binding agent silicon Resin 7, fire retardant magnesia 12, is well mixed, you can.
Embodiment 2, raw material (kilogram) is weighed by following proportionings：Walnut shell powder (10-30 mesh) 50, cement 20, binding agent can Redisperse latex powder 10, fire retardant magnesia 20, is well mixed, you can.
, by performance test repeatedly to product, the test result of the product is as follows for the present invention：Resistance to water：168 hours nothings It is abnormal；Washability：4000 times without exception；Adhesion strength：0.5mpa；Artificial weathering ageing resistance：800 times it is non-foaming, do not peel off, Not crackle；Alkali resistance：48 hours without exception.

Claims (3)

1. a kind of outer wall body material for building, it is characterised in that it is the mixture by made by the raw material of following weight proportioning： Walnut shell powder (10-30 mesh) 30-50, cement 20-40, binding agent 3-10, magnesia 5-20.
2. a kind of outer wall body material for building according to claim 1, wherein the weight proportion of each raw material is：Walnut shell Powder (10-30 mesh) 35-45, cement 25-35, binding agent 4-8, magnesia 8-15.
3. a kind of outer wall body material for building according to claim 1, wherein the weight proportion of each raw material is：Walnut shell Powder (10-30 mesh) 40, cement 30, binding agent 7, magnesia 12.
CN201610976661.7A 2016-11-08 2016-11-08 External wall body material for building Pending CN106517907A (en)