CN106565185A - High-performance mortar for EPS decorative lines and preparation method thereof - Google Patents
High-performance mortar for EPS decorative lines and preparation method thereof Download PDFInfo
- Publication number
- CN106565185A CN106565185A CN201610999335.8A CN201610999335A CN106565185A CN 106565185 A CN106565185 A CN 106565185A CN 201610999335 A CN201610999335 A CN 201610999335A CN 106565185 A CN106565185 A CN 106565185A
- Authority
- CN
- China
- Prior art keywords
- parts
- performance mortar
- high performance
- mixture
- eps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention specifically relates to a high-performance mortar for EPS decorative lines and a preparation method thereof, belonging to the technical field of chemical engineering. The high-performance mortar comprises the following raw materials by weight: 200 to 300 parts of cement, 100 to 150 parts of an admixture, 250 to 300 parts of 40-to-70-mesh quartz sand, 250 to 350 parts of 70-to-140-mesh quartz sand, 30 to 40 parts of dispersible latex powder, 4 to 10 parts of an auxiliary agent and 10 to 50 parts of an iron oxide pigment. Compared with the prior art, the formula and preparation method for the high-performance mortar are designed in the invention; and the EPS decorative lines prepared from the high-performance mortar have the advantages of good adhesion, good elasticity, good durability and excellent weatherability and is free of cracking after long-term usage.
Description
Technical field
The present invention relates to chemical technology field, specifically a kind of High Performance Mortar and system for EPS mouldings
Preparation Method.
Background technology
EPS mouldings can be prevented fires and will not be sent noxious substance, be the high-quality decorative building material product of environmental protection.It is one
New decoration of exterior wall line and component are planted, is more suitable for installing, on the body of wall of exterior wall EPS, XPS insulation, can be embodied European
Classic, graceful decorated style, can guarantee that main building exterior wall occurs without hot and cold bridge effect again.With it is easy for installation, economical,
The advantages such as durability length.
EPS mouldings are compared with plaster line with GRC cement lines, and light weight is easy for installation, numerous in variety, durable
Property is good, is not in crack, energy-conserving and environment-protective, with great advantage.
Common EPS mouldings are processed with a scale by EPS sheet material Jing autoCAD designs and automatization's cutting equipment
The core of very little and moulding, pastes one layer of alkaline-resisting grid cloth in advance on its surface, then pushes away slurry equipment through special, special in one layer of surface layer covering
Decorative mortar is planted, so as to form one layer of compound protective layer.This mortar due to being fitted with EPS mouldings, while
EPS moulding products radian is big, easily forms the problems such as cracking, delamination.
Accordingly, it would be desirable to design a kind of good, good endurance good to EPS decorative threads adhesiveness, elastic, life-time service is indehiscent
High Performance Mortar and preparation method.
The content of the invention
The purpose of the present invention is to overcome the deficiencies in the prior art, there is provided a kind of good, elastic to EPS decorative threads adhesiveness
Good, good endurance, the indehiscent High Performance Mortar of life-time service and preparation method.
In order to achieve the above object, the present invention is a kind of High Performance Mortar for EPS mouldings, it is characterised in that：
It is made up of the raw material of following weight portion：200～300 parts of cement, 100～150 parts of admixture, 40-70 mesh quartz sand 250～300
Part, 70～140 250～350 parts of mesh quartz sands, 30～40 parts of polymer dispersion powder, 4～10 parts of auxiliary agent, iron oxide pigment 10～
50 parts.
Described cement be common silicate cement or portland cement or the one kind in sulphate aluminium cement and more than one
Mixture.
Described admixture be silicon ash or dry powder coal ash or levigate stove ash or the one kind in volcanic ash and more than one
Mixture.
Described auxiliary agent is made up of the commercial weight of following weight portion：1.0～2.0 parts of water-retaining agent, 1.0～2.0 parts of water reducer resist
Split 0.5～1.5 part of fiber.
Described water-retaining agent be cellulose ether or methylcellulose or the one kind in hydroxymethyl cellulose and more than one
Mixture.
Described water reducer be polycarboxylate water-reducer or naphthalene water reducer or one kind and one kind in melamine based water reducer with
On mixture.
Described anti-crack fiber is the mixture of polypropylene fibre or glass fibre or polypropylene fibre and glass fibre.
It is described dispersible rubber powder for VAE rubber powders or AS rubber powders or PVA rubber powders or the one kind in SBR rubber powders and more than one
Mixture.
Prepare according to the following steps：Step 1, by cement, quartz sand, admixture, polymer dispersion powder through in automatic weighing
Setting and control in system, puts into dry powder blender, and main frame mixes 3 minutes；Step 2, input auxiliary agent, iron oxide pigment, opens
Dynamic high speed fly cutter, stirs 1 minute；Step 3, after main frame mixes 2 minutes, blowing, packaging.
The present invention compared with the existing technology, devises the formula and preparation method of High Performance Mortar, by present invention preparation
EPS mouldings out, have the advantages that good adhesiveness, elastic good, good endurance, weatherability are strong, and life-time service is without cracking
Phenomenon.
Specific embodiment
Now the present invention is described further.
The present invention is a kind of High Performance Mortar for EPS mouldings, it is characterised in that：By the raw material of following weight portion
Composition：200～300 parts of cement, 100～150 parts of admixture, 250～300 parts of 40-70 mesh quartz sand, 70～140 mesh quartz sands
250～350 parts, 30～40 parts of polymer dispersion powder, 4～10 parts of auxiliary agent, 10～50 parts of iron oxide pigment.
In the present invention, cement be common silicate cement or portland cement or one kind and one kind in sulphate aluminium cement with
On mixture.
Admixture is silicon ash or dry powder coal ash or levigate stove ash or one kind and more than one mixture in volcanic ash.
Auxiliary agent is made up of the commercial weight of following weight portion：1.0～2.0 parts of water-retaining agent, 1.0～2.0 parts of water reducer, anti-crack fiber
0.5～1.5 part.
Water-retaining agent is cellulose ether or methylcellulose or the one kind in hydroxymethyl cellulose and more than one mixture.
Water reducer is polycarboxylate water-reducer or naphthalene water reducer or the one kind in melamine based water reducer and more than one is mixed
Compound.
Anti-crack fiber is the mixture of polypropylene fibre or glass fibre or polypropylene fibre and glass fibre.
Rubber powder is dispersibled for VAE rubber powders or AS rubber powders or PVA rubber powders or the one kind in SBR rubber powders and more than one mixing
Thing.
The present invention is prepared according to the following steps：Step 1, by cement, quartz sand, admixture, polymer dispersion powder through certainly
Setting and control on dynamic Weighing system, puts into dry powder blender, and main frame mixes 3 minutes；Step 2, input auxiliary agent, ferrum oxide face
Material, starts high speed fly cutter, stirs 1 minute；Step 3, after main frame mixes 2 minutes, blowing, packaging.
Embodiment one
In this example, auxiliary agent includes 1.5 kilograms of water-retaining agent, 1.2 kilograms of water reducer, 1 kilogram of anti-crack fiber, and mix homogeneously is standby.Protect
Water preparation is specially 1 kilogram of methylcellulose, the mixture that 0.5 kilogram of cellulose ether.Water reducer is specially polycarboxylate water-reducer 1.2
Kilogram.Anti-crack fiber is specially 1 kilogram of the polypropylene fibre of 3MM.
Common 200 kilograms of silicate cement, 50 kilograms of sulphate aluminium cement, flyash 120 kg, 40-70 mesh quartz sand 260
Kilogram, 270 kilograms of 70-140 mesh quartz sand, 35 kilograms of polymer dispersion powder, in input dry powder blender, main frame mixes 3 points
Clock；.
The iron oxide pigment of matched somebody with somebody auxiliary agent above and 10 kilograms is added in dry powder blender, high speed fly cutter is started,
Stirring 1 minute.
It is last stirred 2 minutes by main frame after, blowing, packaging, and take ready-made mortar and prepare sample block test performance.
Claims (9)
1. a kind of High Performance Mortar for EPS mouldings, it is characterised in that：It is made up of the raw material of following weight portion：Cement
200～300 parts, 100～150 parts of admixture, 250～300 parts of 40-70 mesh quartz sand, 70～140 mesh quartz sands 250～350
Part, 30～40 parts of polymer dispersion powder, 4～10 parts of auxiliary agent, 10～50 parts of iron oxide pigment.
2. a kind of High Performance Mortar for EPS mouldings according to claim 1, it is characterised in that：Described water
Mud is common silicate cement or portland cement or the one kind in sulphate aluminium cement and more than one mixture.
3. a kind of High Performance Mortar for EPS mouldings according to claim 1, it is characterised in that：Described mixes
Material is closed for silicon ash or dry powder coal ash or levigate stove ash or one kind and more than one mixture in volcanic ash.
4. a kind of High Performance Mortar for EPS mouldings according to claim 1, it is characterised in that：Described helps
Agent is made up of the commercial weight of following weight portion：1.0～2.0 parts of water-retaining agent, 1.0～2.0 parts of water reducer, anti-crack fiber 0.5～1.5
Part.
5. a kind of High Performance Mortar for EPS mouldings according to claim 2, it is characterised in that：Described guarantor
Water preparation is cellulose ether or methylcellulose or the one kind in hydroxymethyl cellulose and more than one mixture.
6. a kind of High Performance Mortar for EPS mouldings according to claim 2, it is characterised in that：Described subtracts
Water preparation is polycarboxylate water-reducer or naphthalene water reducer or one kind and more than one mixture in melamine based water reducer.
7. a kind of High Performance Mortar for EPS mouldings according to claim 2, it is characterised in that：Described is anti-
Fiber is split for polypropylene fibre or the mixture of glass fibre or polypropylene fibre and glass fibre.
8. a kind of High Performance Mortar for EPS mouldings according to claim 1, it is characterised in that：Described can
Dispersion rubber powder is VAE rubber powders or AS rubber powders or PVA rubber powders or one kind and more than one mixture in SBR rubber powders.
9. a kind of preparation method of the as claimed in claim 1 High Performance Mortar for being used for EPS mouldings, it is characterised in that：
Prepare according to the following steps：Step 1, by cement, quartz sand, admixture, polymer dispersion powder through on automatic weighing system
Setting and control, put into dry powder blender, and main frame mixes 3 minutes；Step 2, input auxiliary agent, iron oxide pigment, starts and flies at a high speed
Knife, stirs 1 minute；Step 3, after main frame mixes 2 minutes, blowing, packaging.