A kind of adhesion technique of aluminum honeycomb panel
Technical field
The present invention relates to a kind of adhesion technique of aluminum honeycomb panel, belongs to sheet material production technical field.
Background technology
In world wide, raw material is in short supply, and the enhancing of mankind's environmental consciousness, promotes the use of lightweight, energy-saving material,
Not only economize on resources, and in terms of transport, consume energy it is low, have good economy and social effect.And in the evolution of the mankind
In, we use various sheet materials, such as plank, metallic plate, plastic plate, cement plate etc. in a large number, and they are widely used in all trades and professions,
Such as Aero-Space, building, Furniture manufacture, transport, packaging etc..Compared with solid material, effective material that cellular composite material is used
Material is only that, by the 1-5% of alternative materials, it is clearly a kind of materials province, the light material of the little great potential that consumes energy.Many
Application in, honeycomb plywood sheet almost can substitute the use of all kinds of solid slabs completely, reduce the usage amount of raw material, reach
To the purpose of efficient, energy-conservation.Cellular board is as lightweight, intensity is high, rigidity is big, good stability, heat-and sound-insulating etc. are a series of excellent
Point, widely uses in the fields such as aircraft, vehicle, ship, building.
In the production process of aluminum honeycomb panel, need to be glued the upper and lower surface of strip aluminium honeycomb core respectively with aluminium sheet
Close, then form aluminum honeycomb panel, but as the actual adhesion area of aluminium honeycomb core upper and lower surface is less, which relies primarily on glue and exists
The thickness in aluminium honeycomb core upper and lower ends face is piled up and is bonded, and its bonding strength is poor, and glue consumption is big.
The content of the invention
The technical problem to be solved is to provide a kind of adhesion technique of aluminum honeycomb panel for above-mentioned prior art,
It substantially increases the bonding strength of aluminum honeycomb panel, while greatly reducing the glue consumption of bonding.
The present invention the adopted technical scheme that solves the above problems is:
Compared with prior art, it is an advantage of the current invention that:
A kind of adhesion technique of aluminum honeycomb panel of the present invention, it carries out fluting operation by the honeycomb core to non-stretched expansion, so as to
So that the honeycomb core generation of slotted section is toppled over when upper lower aluminum sheet is pressed, it is viscous between honeycomb core and aluminium sheet so as to considerably increase
Area is closed, the bonding strength of honeycomb aluminum plate is improve, while greatly reducing the glue consumption of bonding, whole technological operation is simple,
It is easy to implement, with very high practical value.
Description of the drawings
Fig. 1 be a kind of aluminum honeycomb panel of the invention adhesion technique in honeycomb core non-stretched expansion when structural representation.
Fig. 2 be a kind of aluminum honeycomb panel of the invention adhesion technique in honeycomb core stretching launch after structural representation.
Specific embodiment
The present invention is described in further detail below in conjunction with accompanying drawing embodiment.
A kind of adhesion technique of the aluminum honeycomb panel in the present embodiment, it comprises the following steps that:
Step one, referring to Fig. 1, fluting operation is carried out to the upper and lower both sides of honeycomb core of non-stretched expansion, groove depth can be according to tool
Body is selected, and spacing of slotting is preferably the half of the single honeycomb length of side of honeycomb core;
Step 2, referring to Fig. 2, the honeycomb core stretching after fluting is launched;
Step 3, gluing operation is carried out in upper aluminium sheet and lower aluminum sheet surface;
Step 4, stretching is launched after honeycomb core be positioned between upper aluminium sheet and lower aluminum sheet and pressed, so as to complete honeycomb
Bond between core and upper aluminium sheet and lower aluminum sheet.
In addition to the implementation, present invention additionally comprises there is other embodiment, all employing equivalents or equivalence replacement
The technical scheme that mode is formed, all should fall within the scope of the hereto appended claims.