CN102029769A - Processing process of honeycomb plate - Google Patents
Processing process of honeycomb plate Download PDFInfo
- Publication number
- CN102029769A CN102029769A CN 201010518134 CN201010518134A CN102029769A CN 102029769 A CN102029769 A CN 102029769A CN 201010518134 CN201010518134 CN 201010518134 CN 201010518134 A CN201010518134 A CN 201010518134A CN 102029769 A CN102029769 A CN 102029769A
- Authority
- CN
- China
- Prior art keywords
- honeycomb core
- cellular board
- panel
- processing technology
- honeycomb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a processing process of a honeycomb plate. The honeycomb plate comprises a honeycomb core, and both sides of the honeycomb core are both adhered with panels. The processing process of the honeycomb plate comprises the following steps of: (1) stretching the honeycomb core: stretching the honeycomb core to unfold cells inside the honeycomb core into a polygonized structure; (2) compounding: gluing both sides of the honeycomb core and the panels, and then respectively adhering the two panels to both sides of the honeycomb core; (3) solidifying: exerting pressure on the panels so that the panels are firmly adhered to the honeycomb core; and (4) cutting: cutting the solidified honeycomb plate for forming. The processing process of the honeycomb plate is characterized in that in the compounding process, indoor temperature needs to be kept between 15 DEG C and 25 DEG C, and humidity needs to be kept between 10% RH and 60% RH. The processing process of the honeycomb plate limits the glue using amount, the glue scraping direction and the appropriate environmental temperature and humidity during operation, thereby ensuring the adhesion effect of the glue and enhancing the adhesion strength; and in addition, the invention has easy implementation, good product quality, and the like.
Description
Technical field
The present invention relates to a kind of sheet material processing technology, especially the processing metal cellular board.
Background technology
Metal honeycomb plate is that a kind of middle one deck is a metal honeycomb core, and the both side surface of honeycomb core is the sheet material of adhesion sheet metal respectively.The characteristics of cellular board are that strength-weight ratio is big, stressed evenly, compression resistance is strong, thermal conductivity is low, shock resistance reaches indeformable, light weight well, soundproof effect is arranged.Therefore, cellular board has obtained in fields such as aviation, buildings using widely.Because by the special gelatin adhesion, so the intensity of adhesion is directly connected to the quality of cellular board between honeycomb core and the sheet metal.Therefore when this sheet material of processing, the technology of gluing is extremely important.The method of the cleanliness factor of the temperature during gluing, humidity, panel, the use amount of glue and gluing all can play direct effect to the effect of adhesion.At present, factory lacks enough understanding to the importance of coating technique, assert simply glue coated equably to get final product.Therefore lack corresponding standard in operation, randomness is bigger, therefore causes the of low quality of whole sheet material.
Summary of the invention
The invention provides a kind of solution of the above problems, a kind of simple to operate, effective cellular board processing technology is provided.
Technical scheme of the present invention provides a kind of cellular board processing technology, and described cellular board comprises honeycomb core, and the equal adhesion in described honeycomb core both sides has panel, and it may further comprise the steps:
(1) stretching honeycomb core: the described honeycomb core that stretches makes cell wherein be launched into polygonized structure;
(2) compound: cementing on the both sides of described honeycomb core and described panel sticks in two described panels respectively the both sides of described honeycomb core then;
(3) solidify: exerting pressure on described panel makes itself and described honeycomb core adhesion firm,
(4) cutting: the cellular board excision forming after will solidifying;
It is characterized in that: in the described compound working procedure, indoor temperature will remain between 15 ℃-25 ℃, and humidity will remain between the 10%RH-60%RH.
Preferably, in the described compound working procedure, after described panel and the described honeycomb core adhesion, upper and lower panel dislocation deviation is in 5mm.
Preferably, in the described compound working procedure, use earlier isopropyl alcohol with described panel cleaning to there not being spot, and dry, and then cementing thereon.
Preferably, in the described compound working procedure, according to the even frictioning of glue consumption of every square metre of 400g-500g of single face.
Preferably, in the described compound working procedure, use scraper plate on described panel, to press the even frictioning of W direction.
Preferably, in the described curing process, indoor temperature will remain between 15 ℃-25 ℃, and humidity will remain between the 10%RH-60%RH.
Cellular board processing technology of the present invention is by limiting glue consumption and frictioning direction, and the environment temperature and the humidity that are fit to when defining operation, thereby guaranteed the adhesion effect of glue, improved adhesion intensity.Has easy enforcement, advantages such as good product quality.
Description of drawings
Fig. 1 is the schematic diagram of the frictioning direction of cellular board processing technology of the present invention.
The specific embodiment
Below the specific embodiment of the present invention is described in further detail.
Cellular board processing technology of the present invention comprises:
1. stretching honeycomb core: because the honeycomb core that buying is come in, for ease of transportation and avoid damaging, compressive state normally, promptly its cell is closely to press together.Therefore, by artificial or special equipment honeycomb core is stretched earlier, its each cell is fully put on display, revert to the polygonal shape of design, be generally equilateral hexagon.
2. compound: as panel to be cleaned with isopropyl alcohol, make its no spot, treat on panel, to smear the glue that modulates after its bone dry.The cleanliness factor of panel directly influences the adhesion effect, because when ash, spot are arranged, glue can not act directly on panel surface.During spreading glue, press the consumption of every square metre of 400g-500g of single face, and use scraper to press direction shown in Figure 1, make it be covered with whole front panel 10 equably with glue 12 drawouts.Thereby glue consumption can cause the too big adhesion intensity that reduces of the distance of honeycomb core and panel too much, and glue consumption then can directly reduce adhesion intensity very little.Then, honeycomb core that previous step is stretched in rapid and panel 10 are by the level of panel-honeycomb core-panel, and promptly honeycomb core is clipped in the middle of two panels, is pasted together.During stickup, upper and lower panel dislocation deviation should be controlled in the 5mm.So just can guarantee that the each several part glue consumption is even, avoided the subregion because of glue very little or the too many adhesion of glue not firm.In order to guarantee glue in operating process, can not go bad, decompose, solidify etc. unusual, therefore in the whole operation process, keep indoor temperature between 15 ℃-25 ℃, humidity will remain between the 10%RH-60%RH.
3, solidify: compound good semi-finished product cellular board must be cured in half an hour, promptly applied certain pressure in the both sides of cellular board, and kept 8 hours, made the glue finish-drying.In the whole operation process, will keep indoor temperature equally between 15 ℃-25 ℃, humidity will remain between the 10%RH-60%RH, can reach best drying effect like this.
4, cutting: with the cellular board that is cured excision forming as required.
Above embodiment only is the present invention's a kind of embodiment wherein, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to claim of the present invention.Should be pointed out that for the person of ordinary skill of the art without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (6)
1.
A kind of cellular board processing technology, described cellular board comprises honeycomb core, and the equal adhesion in described honeycomb core both sides has panel, and it may further comprise the steps.
The stretching honeycomb core: the described honeycomb core that stretches makes cell wherein be launched into polygonized structure;
Compound: cementing on the both sides of described honeycomb core and described panel sticks in two described panels respectively the both sides of described honeycomb core then;
Solidify: exerting pressure on described panel makes itself and described honeycomb core adhesion firm,
Cutting: the cellular board excision forming after will solidifying; It is characterized in that: in the described compound working procedure, indoor temperature will remain between 15 ℃-25 ℃, and humidity will remain between the 10%RH-60%RH.
2.
Cellular board processing technology according to claim 1 is characterized in that: in the described compound working procedure, after described panel and the described honeycomb core adhesion, upper and lower panel dislocation deviation is in 5mm.
3.
Cellular board processing technology according to claim 2 is characterized in that: in the described compound working procedure, use earlier isopropyl alcohol with described panel cleaning to there not being spot, and dry, and then cementing thereon.
4.
Cellular board processing technology according to claim 3 is characterized in that: in the described compound working procedure, according to the even frictioning of glue consumption of every square metre of 400g-500g of single face.
5.
Cellular board processing technology according to claim 4 is characterized in that: in the described compound working procedure, use scraper plate to press the even frictioning of W direction on described panel.
6.
Cellular board processing technology according to claim 1 is characterized in that: in the described curing process, indoor temperature will remain between 15 ℃-25 ℃, and humidity will remain between the 10%RH-60%RH.