CN201761109U - Foamed aluminum-plastic composite board - Google Patents
Foamed aluminum-plastic composite board Download PDFInfo
- Publication number
- CN201761109U CN201761109U CN2010205064435U CN201020506443U CN201761109U CN 201761109 U CN201761109 U CN 201761109U CN 2010205064435 U CN2010205064435 U CN 2010205064435U CN 201020506443 U CN201020506443 U CN 201020506443U CN 201761109 U CN201761109 U CN 201761109U
- Authority
- CN
- China
- Prior art keywords
- aluminum
- thick
- plastic
- board
- plastic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an aluminum-plastic composite board, in particular an aluminum-plastic composite board with a foamed plastic board in the middle. The aluminum-plastic composite board comprises an outer aluminum board, a middle foamed polyethylene board and an inner aluminum board which are adhered together. The middle plastic board is the foamed polyethylene board, the aluminum-plastic composite board not only saves costs of polyethylene and raw materials, but is low in weight, and is equivalent to a common aluminum-plastic composite board in mechanical property, which has equal thickness of the aluminum-plastic composite board, the processing property is unchanged, the processing method is the same and equally convenient to that of the common aluminum-plastic composite board, and the aluminum-plastic composite board is higher in pressure resistance, and can adapt to requirements of modern building field and decoration industry, advertisement industry and the like.
Description
[technical field]
The utility model relates to a kind of composited aluminum and plastic decking, and relating in particular to a kind of centre is the foaming composited aluminum and plastic decking of foamed plastic plate.
[background technology]
Produce first composited aluminum and plastic decking from A Lukebang in 1969, composited aluminum and plastic decking is in the application scenario, production Technology, application technologies etc. are rapidly developed, particularly to the durability of composited aluminum and plastic decking, intensity behind the knuckle, bear after wind load ability etc. done a large amount of experimental study work, composited aluminum and plastic decking is widely used in the curtain buildings decoration industry, composited aluminum and plastic decking enters China from the nineties, obtained develop rapidly, be widely used in curtain wall, indoor and outdoor is decorated, advertisement and furniture, the short more than ten years, China has become the largest production state of composited aluminum and plastic decking, country of consumption and exported country; Further expansion along with the aluminium-plastic panel application, those have, and quality is special light, having certain anti-bending strength and have billboard, the Indoor decorative plate of excellent surface quality will be very popular, for some conventional billboards, the present quality of indoor aluminium-plastic panel still lays particular stress on, can not make the client very satisfied, while is along with the continuous minimizing of crude oil, the energy in short supply, it is more and more precious that the subsequent product-polyethylene of crude oil also seems, also be specific requirement energy-conservation in order to respond, that low-carbon (LC) is produced in addition, exploitation foaming composited aluminum and plastic decking has very important significance.
[summary of the invention]
At the problems referred to above, the purpose of this invention is to provide a kind of light weight, function admirable and foaming composited aluminum and plastic decking with low cost.
For achieving the above object, technical solution adopted in the utility model is as follows:
A kind of foaming composited aluminum and plastic decking comprises the outer aluminium sheet, middle level polyethylene foamed plate, the internal layer aluminium sheet that are bonded mutually.
The thickness of whole foaming composited aluminum and plastic decking is 2.5-6.0mm, and the thickness of middle level polyethylene foamed plate is 2.3-5.6mm.
More preferably, the thickness of whole foaming composited aluminum and plastic decking is 4.0mm, and the thickness of middle level polyethylene foamed plate is 3.0mm.
Described polyethylene foamed plate adopts the foaming of micropore blind hole, and expansion ratio is 1.4-1.6 times.
Preferably, the ectonexine aluminium sheet is an aluminium alloy plate.
The utility model not only can be saved the polyethylene and the cost of raw material, and make it lighter by about 25% than common plate owing to the plastic plate with the middle level uses the polyethylene foamed plate.Compared with prior art, have following advantage: 1, reduce the overall cost of composited aluminum and plastic decking, thickness is that the foaming composited aluminum and plastic decking of 0.1+2.8+0.1mm reduces 15-20% with respect to the composited aluminum and plastic decking cost that is the equal specification of foaming; 2, save oil product polyethylene 30-40%; 3, can alleviate the 20-25% of product gross weight; 4, the conventional aluminium plastic clad plate of the mechanical property of foaming composited aluminum and plastic decking and uniform thickness is suitable; 5, the processing characteristics of foaming composited aluminum and plastic decking is constant, and is the same with the processing method of conventional aluminium plastic clad plate, same convenient, do not change mounting structure and site operation.
The performance comparison result such as the following table of the utility model foaming composited aluminum and plastic decking and conventional aluminium plastic clad plate:
Can be found out that by last table result mechanical property, the surface quality of the utility model foaming composited aluminum and plastic decking are suitable with the conventional aluminium plastic clad plate, quality is lighter by 25% than common plate, can also save the polyethylene and the cost of raw material.
[description of drawings]
Fig. 1 is a side view of the present utility model.
Among the figure, 1 is that outer aluminium sheet, 2 is that middle level polyethylene foamed plate, 3 is the internal layer aluminium sheet.
[specific embodiment]
The utility model is described in further detail below in conjunction with the drawings and specific embodiments.
The composited aluminum and plastic decking of a kind of total thickness 3mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.1mm, and the middle level is thick 2.8mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.1mm.
The composited aluminum and plastic decking of a kind of total thickness 3mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.12mm, and the middle level is thick 2.76mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.12mm.
The composited aluminum and plastic decking of a kind of total thickness 3mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.1mm, and the middle level is thick 2.8mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.1mm.
Embodiment 4
The composited aluminum and plastic decking of a kind of total thickness 3mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.21mm, and the middle level is thick 2.58mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.21mm.
Embodiment 5
The composited aluminum and plastic decking of a kind of total thickness 2.5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.1mm, and the middle level is thick 2.3mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.1mm.
Embodiment 6
The composited aluminum and plastic decking of a kind of total thickness 4mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.15mm, and the middle level is thick 3.7mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.15mm.
Embodiment 7
The composited aluminum and plastic decking of a kind of total thickness 4mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.1mm, and the middle level is thick 3.8mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.1mm.
Embodiment 8
The composited aluminum and plastic decking of a kind of total thickness 4mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.26mm, and the middle level is thick 3.48mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.26mm.
Embodiment 9
The composited aluminum and plastic decking of a kind of total thickness 4mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.3mm, and the middle level is thick 3.4mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.3mm.
Embodiment 10
The composited aluminum and plastic decking of a kind of total thickness 5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.1mm, and the middle level is thick 4.8mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.1mm.
Embodiment 11
The composited aluminum and plastic decking of a kind of total thickness 5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.15mm, and the middle level is thick 4.7mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.15mm.
Embodiment 12
The composited aluminum and plastic decking of a kind of total thickness 5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.21mm, and the middle level is thick 4.58mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.21mm.
Embodiment 13
The composited aluminum and plastic decking of a kind of total thickness 5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.3mm, and the middle level is thick 4.4mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.3mm.
Embodiment 14
The composited aluminum and plastic decking of a kind of total thickness 5mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.4mm, and the middle level is thick 4.2mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.4mm.
Embodiment 15
The composited aluminum and plastic decking of a kind of total thickness 6mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.21mm, and the middle level is thick 5.58mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.21mm.
Embodiment 16
The composited aluminum and plastic decking of a kind of total thickness 6mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.3mm, and the middle level is thick 5.4mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.3mm.
Embodiment 17
The composited aluminum and plastic decking of a kind of total thickness 6mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.4mm, and the middle level is thick 5.2mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.4mm.
Embodiment 18
The composited aluminum and plastic decking of a kind of total thickness 6mm forms by the macromolecule glue mucous membrane is bonding, and its ectomesoderm is the aluminium alloy plate 1 of thick 0.5mm, and the middle level is thick 5.0mm polyethylene foamed plate 2, and internal layer is the aluminium alloy plate 3 of thick 0.5mm.
Claims (5)
1. a foaming composited aluminum and plastic decking is characterized in that comprising the outer aluminium sheet (1), middle level polyethylene foamed plate (2), the internal layer aluminium sheet (3) that are bonded mutually.
2. foaming composited aluminum and plastic decking as claimed in claim 1 is characterized in that its general thickness is 2.5-6.0mm, and the thickness of middle level polyethylene foamed plate (2) is 2.3-5.6mm.
3. foaming composited aluminum and plastic decking as claimed in claim 2 is characterized in that its general thickness is 4.0mm, and the thickness of middle level polyethylene foamed plate (2) is 3.0mm.
4. as claim 2 or 3 described foaming composited aluminum and plastic deckings, it is characterized in that described polyethylene foamed plate (2) adopts the foaming of micropore blind hole, expansion ratio is 1.4-1.6 times.
5. as claim 2 or 3 described foaming composited aluminum and plastic deckings, it is characterized in that outer aluminium sheet (1) and internal layer aluminium sheet (3) are aluminium alloy plate.