CN106515094B - 一种高性能防滑土工布及其制备方法 - Google Patents

一种高性能防滑土工布及其制备方法 Download PDF

Info

Publication number
CN106515094B
CN106515094B CN201610910308.9A CN201610910308A CN106515094B CN 106515094 B CN106515094 B CN 106515094B CN 201610910308 A CN201610910308 A CN 201610910308A CN 106515094 B CN106515094 B CN 106515094B
Authority
CN
China
Prior art keywords
wefts
fiber
fibers
geotextile
base layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610910308.9A
Other languages
English (en)
Other versions
CN106515094A (zh
Inventor
张伟
何红伟
王建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Shangshan Molding Technology Co.,Ltd.
Original Assignee
Nantong Shangshan Molding Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Shangshan Molding Technology Co ltd filed Critical Nantong Shangshan Molding Technology Co ltd
Priority to CN201610910308.9A priority Critical patent/CN106515094B/zh
Publication of CN106515094A publication Critical patent/CN106515094A/zh
Application granted granted Critical
Publication of CN106515094B publication Critical patent/CN106515094B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高性能防滑土工布及其制备方法，所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2，所述基层上表面和底层底部设有防滑的点状颗粒。所述土工布力学性能优良，具有较强的抗拉强度和抗变形能力，防腐性好，在路面的改造中起到加强、防渗、防反射裂缝作用，能够进一步延长路面使用寿命。

Description

一种高性能防滑土工布及其制备方法
技术领域
本发明属于建材领域，涉及一种土工布及其制备方法，具体而言涉及一种高性能防滑土工布及其制备方法。
背景技术
目前，土工布主要应用于水利、港口、航道、铁路、公路等泥沙直径小受力大的工程，其起到的主要作用包括1：隔离作用，对不同物理性质的建筑材料进行隔离，使材料不混杂，保持材料的整体性；2：过滤作用，当水由细料土层流入粗料土层时，利用土工布的透水性，让水通过而拦截住土颗粒、细沙等物料；3：稳定作用，增强土体抗拉抗变形能力，增强建筑结构稳定性。
而现有的常用土工布结构单一，抗拉强度和抗变形能力低，使土工布的寿命减短，因此，本领域技术人员亟需提供一种加强型土工布，能有效地提高抗拉强度和抗变形能力，延长土工布的使用寿命。
发明内容
本发明提供一种高性能防滑土工布，力学性能优良，具有较强的抗拉强度和抗变形能力，防腐性好，在路面的改造中起到加强、防渗、防反射裂缝作用，能够进一步延长路面使用寿命。
具体的，本发明提供一种高性能防滑土工布，所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2，所述基层上表面和底层底部设有防滑的点状颗粒。
所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料10-20份、聚甲醛1-4份、石蜡油60-80份、木质素0.5-3份、纳米有机膨润土0.5-2份在混合釜中混合一起，加热搅拌，加热温度130℃～150℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为150℃-250℃，螺杆挤出速度为200-250转/分，喷丝板100～150孔，孔径0.5～0.8mm，喷丝熔体温度控制在200℃～220℃，喷头牵伸5～15m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维。
优选的，所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料15份、聚甲醛3份、石蜡油70份、木质素2份、纳米有机膨润土1份在混合釜中混合一起，加热搅拌，加热温度140℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为200℃，螺杆挤出速度为220转/分，喷丝板130孔，孔径0.6mm，喷丝熔体温度控制在210℃，喷头牵伸10m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维。
优选地，所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料10份、聚甲醛1份、石蜡油60份、木质素0.5份、纳米有机膨润土0.5份在混合釜中混合一起，加热搅拌，加热温度130℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为150℃，螺杆挤出速度为200转/分，喷丝板100孔，孔径0.5mm，喷丝熔体温度控制在200℃，喷头牵伸5m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维。
优选地，所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料20份、聚甲醛4份、石蜡油80份、木质素3份、纳米有机膨润土2份在混合釜中混合一起，加热搅拌，加热温度150℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为250℃，螺杆挤出速度为250转/分，喷丝板150孔，孔径0.8mm，喷丝熔体温度控制在220℃，喷头牵伸15m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维。
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维。
所述的防滑的点状颗粒为高密度聚乙烯材料制成，该点状颗粒均匀的粘贴在基层和底层的外表面上；即本发明的土工布外表面设置有防滑点状颗粒。
所述基层和底层通过粘结剂粘接在一起；优选地，所述粘结剂是聚酯粉末。
具体实施方式
实施例1：一种高性能防滑土工布
所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2；所述基层上表面和底层底部设有防滑的点状颗粒；
所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料15份、聚甲醛3份、石蜡油70份、木质素2份、纳米有机膨润土1份在混合釜中混合一起，加热搅拌，加热温度140℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为200℃，螺杆挤出速度为220转/分，喷丝板130孔，孔径0.6mm，喷丝熔体温度控制在210℃，喷头牵伸10m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维；
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维；
所述基层和底层通过聚酯粉末粘接在一起。
实施例2一种高性能防滑土工布
土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2；所述基层上表面和底层底部设有防滑的点状颗粒；
所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料10份、聚甲醛1份、石蜡油60份、木质素0.5份、纳米有机膨润土0.5份在混合釜中混合一起，加热搅拌，加热温度130℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为150℃，螺杆挤出速度为200转/分，喷丝板100孔，孔径0.5mm，喷丝熔体温度控制在200℃，喷头牵伸5m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维；
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维；
所述基层和底层通过聚酯粉末粘接在一起。
实施例3一种高性能防滑土工布的制备
所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2；所述基层上表面和底层底部设有防滑的点状颗粒；
所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料20份、聚甲醛4份、石蜡油80份、木质素3份、纳米有机膨润土2份在混合釜中混合一起，加热搅拌，加热温度150℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为250℃，螺杆挤出速度为250转/分，喷丝板150孔，孔径0.8mm，喷丝熔体温度控制在220℃，喷头牵伸15m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维；
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维；
所述基层和底层通过聚酯粉末粘接在一起。
对比例1：（底层省略聚酰亚胺纤维）
所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括玻璃纤维以及高强纤维，两种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；玻璃纤维、高强纤维的重量比为4：4：2；其他同实施例1。
对比例2：（省略聚甲醛）
所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料15份、石蜡油70份、木质素2份、纳米有机膨润土1份在混合釜中混合一起，加热搅拌，加热温度140℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为200℃，螺杆挤出速度为220转/分，喷丝板130孔，孔径0.6mm，喷丝熔体温度控制在210℃，喷头牵伸10m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维；其他同实施例1。
对比例3（ 省略第三纬线）
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线按比例1:1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维；其他同实施例1。
对比例4（改变第一经线和第二经线的配比）
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例1：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维；其他同实施例1。
实施例4：性能测试
测试本发明实施例1-3以及对比例1-4制备的高性能防滑土工布的机械性能，结果见表1。
表1 本发明高性能防滑土工布的机械性能
断裂强力（KN/m） CBR顶破强力（KN）
实施例1 68 7.6
实施例2 67 7.8
实施例3 70 7.5
对比例1 35 4.6
对比例2 41 5.3
对比例3 34 4.7
对比例4 38 5.4
表1的结果表明，本发明实施例1-3制备的土工布就有优良的力学性能，而对比例1-4的力学性能显著下降。

Claims (4)

1.一种高性能防滑土工布，其特征在于，所述土工布包括基层以及底层；所述基层由经线与纬线编织而成；所述底层包括聚酰亚胺纤维、玻璃纤维以及高强纤维，三种纤维经开松、混合、梳理、铺网后，通过针刺、热定型交织在一起；聚酰亚胺纤维、玻璃纤维、高强纤维的重量比为4：4：2；所述基层上表面和底层底部设有防滑的点状颗粒；
其中所述的高强纤维是将分子量为150-200万的超高分子量聚乙烯粉料10-20份、聚甲醛1-4份、石蜡油60-80份、木质素0.5-3份、纳米有机膨润土0.5-2份在混合釜中混合一起，加热搅拌，加热温度130℃～150℃，得膨胀液，自然降温形成冻胶块，取出冻胶块并在碎料设备上将其粉碎成粒料，然后用脱油设备脱去部分溶剂，将粒料输入到螺杆挤压机熔融纺丝：螺杆长径比为1∶40，螺杆各段温度为150℃-250℃，螺杆挤出速度为200-250转/分，喷丝板100～150孔，孔径0.5～0.8mm，喷丝熔体温度控制在200℃～220℃，喷头牵伸5～15m/分，然后预拉伸卷绕，再经过萃取、干燥和超倍拉伸工艺，得到高强纤维；
所述基层由经线与纬线编织而成，所述纬线包括第一纬线、第二纬线和第三纬线，经线包括第一经线和第二经线，其中第一纬线、第二纬线和第三纬线按比例1:1：1排列，第一经线和第二经线按比例2：1排列，所述第一经线采用聚酰胺纤维，第二经线采用聚丙烯腈纤维，第一纬线采用聚酯纤维，第二纬线采用玻璃纤维，第三纬线采用亚麻纤维。
2.根据权利要求1所述的高性能防滑土工布，其中所述的防滑的点状颗粒为高密度聚乙烯材料制成，该点状颗粒均匀的粘贴在基层和底层的外表面上。
3.根据权利要求1所述的高性能防滑土工布，所述基层和底层通过粘结剂粘接在一起。
4.根据权利要求3所述的高性能防滑土工布，所述粘结剂是聚酯粉末。
CN201610910308.9A 2016-10-19 2016-10-19 一种高性能防滑土工布及其制备方法 Active CN106515094B (zh)